CN107858830A - A kind of linen Anti-bacterial and Crease method - Google Patents
A kind of linen Anti-bacterial and Crease method Download PDFInfo
- Publication number
- CN107858830A CN107858830A CN201711181946.2A CN201711181946A CN107858830A CN 107858830 A CN107858830 A CN 107858830A CN 201711181946 A CN201711181946 A CN 201711181946A CN 107858830 A CN107858830 A CN 107858830A
- Authority
- CN
- China
- Prior art keywords
- parts
- linen
- solution
- bacterial
- polyphenol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of linen Anti-bacterial and Crease method, comprise the following steps:(1)The maltodextrin aqueous solution is configured, acetic acid anhydride reactant is added in maltodextrin solution;(2)In step(1)Corn peptide and glyoxal are added in solution, is stirred, then the linen of degumming process is rolled by two leachings two, then dried;(3)Step will be passed through(2)Treated fabric is first immersed in vine polyphenol, Punica granatum L. polyphenol and mulberry leaf water extract mixed aqueous solution and handled, and washes, drying;(4)Again by fabric alum, octamethylcy-clotetrasiloxane, APES, glycol monoethyl ether, alkanolamide and water composition mixed solution in constant temperature handle, wash, drying.The crease-shedding finishing agent of the present invention, the ultimate strength influence on fabric is smaller, and takes into account good anti-wrinkle effect, still has very strong antibacterial effect after ten washings, this finishing agent green non-pollution, disclosure satisfy that textile security requirement.
Description
Technical field
The present invention relates to textile finishing technology, and in particular to a kind of linen antibacterial crease-resistant method.
Background technology
Linen is a kind of typical tropical suiting, there is good gas permeability, hygroscopicity and thermal conductivity;But then,
As other bast fibers, linen is harder, and Young's modulus is big, and fiber is thicker in addition, and cross-sectional area is again big, because
It is rougher that this fabric touches up feel, is easily wrinkled in wearing process, therefore influences the outward appearance and snugness of fit of fabric, this
Outside, the weaving process of linen is often carried out in the higher manual environment of humidity ratio, so for many years, poor is non-ironing whole
Reason effect has had a strong impact on that the large area of flaxen fiber utilizes, and in recent years, with the development of synthetic fibers, people are more likely to
" wash and wear fabrics ", the demand of bast fiber fabrics are greatly decreased.Although linen has preferably anti-compared to other natural fibers
The antibacterial effect of bacterium, but this natural health-care effect is limited, it is impossible to play a permanent beneficial antibacterial effect.And mesh
Preceding many fabric face residues of formaldehyde Jing Guo final finishing are more, more or less injury to human body be present.
The content of the invention
Technical problems to be solved:It is an object of the invention to provide a kind of linen Anti-bacterial and Crease method, overcomes existing
There is the defects of finishing technique, by the afterfinish method of green, improve the wrinkle resistance and anti-microbial property of linen.
Technical scheme:A kind of linen Anti-bacterial and Crease method, comprises the following steps:
(1)The 5-10wt% maltodextrin aqueous solution is configured, acetic anhydride, the addition of acetic anhydride are added in maltodextrin solution
For the 1/10-1/5 of maltodextrin solution quality, regulation pH is 8-9, and the reaction time is 1-2 hours at being 22-30 DEG C in temperature;
(2)In step(1)Corn peptide and glyoxal are added in solution, wherein corn peptide addition is 50-80g/L, and glyoxal adds
It is 10-20g/L to enter amount, is stirred, and then the linen of degumming process is rolled by two leachings two, then dries, washes 2-3
It is secondary, five minutes naturally dries every time;
(3)Step will be passed through(2)Treated fabric is first immersed in vine polyphenol, Punica granatum L. polyphenol and mulberry leaf water extract mixing water
In solution, wherein the concentration of vine polyphenol is 5-13g/L, and the concentration of Punica granatum L. polyphenol is 2-9g/L, and the concentration of mulberry leaf water extract is
0.2-1.5g/L, 40-100min is handled in 50-80 DEG C of constant temperature, is washed, drying;
(4)Again by fabric in alum, octamethylcy-clotetrasiloxane, APES, glycol monoethyl ether, alkanol
50-80 DEG C of constant temperature processing 30-60min in acid amides and water composition mixed solution, is washed, drying, wherein mixed solution press with
Lower parts by weight composition:Alum 0.2-0.5 parts, octamethylcy-clotetrasiloxane 2-8 parts, APES 2-8 parts, second
100 parts of glycol monomethyl ether 1-5 parts, alkanolamide 0.5-5 parts and water.
Further, a kind of described linen Anti-bacterial and Crease method, step(1)The aqueous solution of middle maltodextrin is dense
It is the 1/8-1/5 of maltodextrin solution quality to spend for 6-8wt%, the addition of acetic anhydride, when being reacted at being 25-30 DEG C in temperature
Between be 1-2 hours.
Further, a kind of described linen Anti-bacterial and Crease method, step(2)Middle corn peptide addition is 60-
75g/L, glyoxal addition are 15-20g/L.
Further, a kind of described linen Anti-bacterial and Crease method, step(3)The concentration of middle vine polyphenol is 7-
10g/L, the concentration of Punica granatum L. polyphenol is 4-7g/L, and the concentration of mulberry leaf water extract is 0.5-1g/L.
Further, a kind of described linen Anti-bacterial and Crease method, step(3)In handled in 55-65 DEG C of constant temperature
60-90min。
Further, a kind of described linen Anti-bacterial and Crease method, step(4)It is middle by fabric in mixed solution
60-70 DEG C, constant temperature processing 40-50min.
Further, a kind of described linen Anti-bacterial and Crease method, step(4)Middle alum 0.3-0.4 parts,
Octamethylcy-clotetrasiloxane 4-6 parts, APES 2-6 parts, glycol monoethyl ether 2-4 parts, alkanolamide 1.5-3 parts
With 100 parts of water.
Beneficial effect:The anti-crease finishing method of the present invention, the ultimate strength influence on fabric is smaller, and takes into account good resist
Wrinkle effect, still there is very strong antibacterial effect after ten washings, this finishing agent green non-pollution, disclosure satisfy that textile is pacified
Full property requirement.
Embodiment
Embodiment 1
A kind of linen Anti-bacterial and Crease method, comprises the following steps:
(1)The 10wt% maltodextrin aqueous solution is configured, acetic anhydride is added in maltodextrin solution, the addition of acetic anhydride is
The 1/5 of maltodextrin solution quality, regulation pH is 8, and the reaction time is 2 hours at being 22 DEG C in temperature;
(2)In step(1)Add corn peptide and glyoxal in solution, wherein corn peptide addition is 80g/L, glyoxal addition
For 10g/L, stir, then the linen of degumming process is rolled by two leachings two, then dries, washes 2 times, every time five points
Clock naturally dry;
(3)Step will be passed through(2)Treated fabric is first immersed in vine polyphenol, Punica granatum L. polyphenol and mulberry leaf water extract mixing water
In solution, wherein the concentration of vine polyphenol is 5g/L, and the concentration of Punica granatum L. polyphenol is 9g/L, and the concentration of mulberry leaf water extract is 1.5g/
L, 100min is handled in 50 DEG C of constant temperature, is washed, drying;
(4)Again by fabric in alum, octamethylcy-clotetrasiloxane, APES, glycol monoethyl ether, alkanol
80 DEG C of constant temperature processing 30min, are washed, drying, wherein mixed solution presses following weight in acid amides and water composition mixed solution
Part composition:0.2 part of alum, 8 parts of octamethylcy-clotetrasiloxane, 2 parts of APES, 5 parts of glycol monoethyl ether,
100 parts of 0.5 part of alkanolamide and water.
Embodiment 2
A kind of linen Anti-bacterial and Crease method, comprises the following steps:
(1)The 5wt% maltodextrin aqueous solution is configured, acetic anhydride is added in maltodextrin solution, the addition of acetic anhydride is wheat
The 1/10 of bud dextrin solution quality, regulation pH is 9, and the reaction time is 1 hour at being 30 DEG C in temperature;
(2)In step(1)Add corn peptide and glyoxal in solution, wherein corn peptide addition is 50g/L, glyoxal addition
For 20g/L, stir, then the linen of degumming process is rolled by two leachings two, then dries, washes 3 times, every time five points
Clock naturally dry;
(3)Step will be passed through(2)Treated fabric is first immersed in vine polyphenol, Punica granatum L. polyphenol and mulberry leaf water extract mixing water
In solution, wherein the concentration of vine polyphenol is 13g/L, and the concentration of Punica granatum L. polyphenol is 2g/L, and the concentration of mulberry leaf water extract is 0.2g/
L, 40min is handled in 80 DEG C of constant temperature, is washed, drying;
(4)Again by fabric in alum, octamethylcy-clotetrasiloxane, APES, glycol monoethyl ether, alkanol
50 DEG C of constant temperature processing 60min, are washed, drying, wherein mixed solution presses following weight in acid amides and water composition mixed solution
Part composition:0.5 part of alum, 2 parts of octamethylcy-clotetrasiloxane, 8 parts of APES, 1 part of glycol monoethyl ether,
100 parts of 5 parts of alkanolamide and water.
Embodiment 3
A kind of linen Anti-bacterial and Crease method, comprises the following steps:
(1)The 6wt% maltodextrin aqueous solution is configured, acetic anhydride is added in maltodextrin solution, the addition of acetic anhydride is wheat
The 1/8 of bud dextrin solution quality, regulation pH is 8, and the reaction time is 1 hour at being 25 DEG C in temperature;
(2)In step(1)Add corn peptide and glyoxal in solution, wherein corn peptide addition is 60g/L, glyoxal addition
For 15g/L, stir, then the linen of degumming process is rolled by two leachings two, then dries, washes 2 times, every time five points
Clock naturally dry;
(3)Step will be passed through(2)Treated fabric is first immersed in vine polyphenol, Punica granatum L. polyphenol and mulberry leaf water extract mixing water
In solution, wherein the concentration of vine polyphenol is 7g/L, and the concentration of Punica granatum L. polyphenol is 7g/L, and the concentration of mulberry leaf water extract is 0.5g/
L, 60min is handled in 65 DEG C of constant temperature, is washed, drying;
(4)Again by fabric in alum, octamethylcy-clotetrasiloxane, APES, glycol monoethyl ether, alkanol
60 DEG C of constant temperature processing 40min, are washed, drying, wherein mixed solution presses following weight in acid amides and water composition mixed solution
Part composition:0.3 part of alum, 4 parts of octamethylcy-clotetrasiloxane, 2 parts of APES, 4 parts of glycol monoethyl ether,
100 parts of 1.5 parts of alkanolamide and water.
Embodiment 4
A kind of linen Anti-bacterial and Crease method, comprises the following steps:
(1)The 8wt% maltodextrin aqueous solution is configured, acetic anhydride is added in maltodextrin solution, the addition of acetic anhydride is wheat
The 1/5 of bud dextrin solution quality, regulation pH is 9, and the reaction time is 2 hours at being 30 DEG C in temperature;
(2)In step(1)Add corn peptide and glyoxal in solution, wherein corn peptide addition is 75g/L, glyoxal addition
For 20g/L, stir, then the linen of degumming process is rolled by two leachings two, then dries, washes 3 times, every time five points
Clock naturally dry;
(3)Step will be passed through(2)Treated fabric is first immersed in vine polyphenol, Punica granatum L. polyphenol and mulberry leaf water extract mixing water
In solution, wherein the concentration of vine polyphenol is 10g/L, and the concentration of Punica granatum L. polyphenol is 4g/L, and the concentration of mulberry leaf water extract is 1g/L,
90min is handled in 55 DEG C of constant temperature, is washed, drying;
(4)Again by fabric in alum, octamethylcy-clotetrasiloxane, APES, glycol monoethyl ether, alkanol
70 DEG C of constant temperature processing 50min, are washed, drying, wherein mixed solution presses following weight in acid amides and water composition mixed solution
Part composition:0.4 part of alum, 6 parts of octamethylcy-clotetrasiloxane, 6 parts of APES, 2 parts of glycol monoethyl ether,
100 parts of 3 parts of alkanolamide and water.
Embodiment 5
A kind of linen Anti-bacterial and Crease method, comprises the following steps:
(1)The 7wt% maltodextrin aqueous solution is configured, acetic anhydride is added in maltodextrin solution, the addition of acetic anhydride is wheat
The 1/6 of bud dextrin solution quality, regulation pH is 8, and the reaction time is 2 hours at being 30 DEG C in temperature;
(2)In step(1)Add corn peptide and glyoxal in solution, wherein corn peptide addition is 72g/L, glyoxal addition
For 16g/L, stir, then the linen of degumming process is rolled by two leachings two, then dries, washes 3 times, every time five points
Clock naturally dry;
(3)Step will be passed through(2)Treated fabric is first immersed in vine polyphenol, Punica granatum L. polyphenol and mulberry leaf water extract mixing water
In solution, wherein the concentration of vine polyphenol is 8g/L, and the concentration of Punica granatum L. polyphenol is 6g/L, and the concentration of mulberry leaf water extract is 0.9g/
L, 80min is handled in 60 DEG C of constant temperature, is washed, drying;
(4)Again by fabric in alum, octamethylcy-clotetrasiloxane, APES, glycol monoethyl ether, alkanol
65 DEG C of constant temperature processing 45min, are washed, drying, wherein mixed solution presses following weight in acid amides and water composition mixed solution
Part composition:0.3 part of alum, 5 parts of octamethylcy-clotetrasiloxane, 4 parts of APES, 3 parts of glycol monoethyl ether,
100 parts of 2.5 parts of alkanolamide and water.
Comparative example 1
A kind of linen Anti-bacterial and Crease method, comprises the following steps:
(1)80g/L corn peptide solution is configured, then the linen of degumming process is rolled by two leachings two, then dries, washes
2 times, five minutes naturally dries every time;
(2)Step will be passed through(1)Treated fabric is first immersed in vine polyphenol, Punica granatum L. polyphenol and mulberry leaf water extract mixing water
In solution, wherein the concentration of vine polyphenol is 5g/L, and the concentration of Punica granatum L. polyphenol is 9g/L, and the concentration of mulberry leaf water extract is 1.5g/
L, 100min is handled in 50 DEG C of constant temperature, is washed, drying;
(3)Again by fabric in alum, octamethylcy-clotetrasiloxane, APES, glycol monoethyl ether, alkanol
80 DEG C of constant temperature processing 30min, are washed, drying, wherein mixed solution presses following weight in acid amides and water composition mixed solution
Part composition:0.2 part of alum, 8 parts of octamethylcy-clotetrasiloxane, 2 parts of APES, 5 parts of glycol monoethyl ether,
100 parts of 0.5 part of alkanolamide and water.
Comparative example 2
A kind of linen Anti-bacterial and Crease method, comprises the following steps:
(1)The 5wt% maltodextrin aqueous solution is configured, acetic anhydride is added in maltodextrin solution, the addition of acetic anhydride is wheat
The 1/10 of bud dextrin solution quality, regulation pH is 9, and the reaction time is 1 hour at being 30 DEG C in temperature;
(2)In step(1)Add corn peptide and glyoxal in solution, wherein corn peptide addition is 50g/L, glyoxal addition
For 20g/L, stir, then the linen of degumming process is rolled by two leachings two, then dries, washes 3 times, every time five points
Clock naturally dry;
(3)Step will be passed through(2)Treated fabric soaks octamethylcy-clotetrasiloxane, APES, ethylene glycol
Monomethyl ether, alkanolamide and water composition mixed solution in 50 DEG C of constant temperature processing 60min, wash, drying, wherein mixed solution
Formed by following parts by weight:0.5 part of alum, 2 parts of octamethylcy-clotetrasiloxane, 8 parts of APES, ethylene glycol
100 parts of 1 part of monomethyl ether, 5 parts of alkanolamide and water.
Comparative example 3
A kind of linen Anti-bacterial and Crease method, comprises the following steps:
(1)The 5wt% maltodextrin aqueous solution is configured, acetic anhydride is added in maltodextrin solution, the addition of acetic anhydride is wheat
The 1/10 of bud dextrin solution quality, regulation pH is 9, and the reaction time is 1 hour at being 30 DEG C in temperature;
(2)In step(1)Add corn peptide and glyoxal in solution, wherein corn peptide addition is 50g/L, glyoxal addition
For 20g/L, stir, then the linen of degumming process is rolled by two leachings two, then dries, washes 3 times, every time five points
Clock naturally dry;
(3)Step will be passed through(2)Treated fabric is first immersed in the vine polyphenol aqueous solution, and the concentration of wherein vine polyphenol is
13g/L, 40min is handled in 80 DEG C of constant temperature, is washed, drying;
(4)Again by fabric in alum, octamethylcy-clotetrasiloxane, APES, glycol monoethyl ether, alkanol
50 DEG C of constant temperature processing 60min, are washed, drying, wherein mixed solution presses following weight in acid amides and water composition mixed solution
Part composition:0.5 part of alum, 2 parts of octamethylcy-clotetrasiloxane, 8 parts of APES, 1 part of glycol monoethyl ether,
100 parts of 5 parts of alkanolamide and water.
Comparative example 4
A kind of linen Anti-bacterial and Crease method, comprises the following steps:
(1)The 6wt% maltodextrin aqueous solution is configured, acetic anhydride is added in maltodextrin solution, the addition of acetic anhydride is wheat
The 1/8 of bud dextrin solution quality, regulation pH is 8, and the reaction time is 1 hour at being 25 DEG C in temperature;
(2)In step(1)Glyoxal is added in solution, wherein glyoxal addition is 15g/L, is stirred, then by degumming
The linen of processing rolls by two leachings two, then dries, washing 2 times, every time five minutes naturally dries;
(3)Step will be passed through(2)Treated fabric is first immersed in vine polyphenol, Punica granatum L. polyphenol and mulberry leaf water extract mixing water
In solution, wherein the concentration of vine polyphenol is 7g/L, and the concentration of Punica granatum L. polyphenol is 7g/L, and the concentration of mulberry leaf water extract is 0.5g/
L, 60min is handled in 65 DEG C of constant temperature, is washed, drying;
(4)Again by fabric in alum, octamethylcy-clotetrasiloxane, APES, glycol monoethyl ether, alkanol
60 DEG C of constant temperature processing 40min, are washed, drying, wherein mixed solution presses following weight in acid amides and water composition mixed solution
Part composition:0.3 part of alum, 4 parts of octamethylcy-clotetrasiloxane, 2 parts of APES, 4 parts of glycol monoethyl ether,
100 parts of 1.5 parts of alkanolamide and water.
Performance test:
Ultimate strength:With reference to GB/T 3923.1-1997《Textile thing tensile property Part I:Ultimate strength and fracture are stretched
Long rate determines galley proof method》, it is measured using YG (B) 026D -250 type imported electronic fabric strength testers;
Creasy recovery angle:With reference to GB/T 3819-1997《The measure of textile thing wrinkle recovery property replys horn cupping》Surveyed
It is fixed.
Material:Etramee(184/10cm × 220 piece of 35.7tex × 27.7tex/cm).
Test result according to table 1 can be seen that the crease-shedding finishing agent by the present invention, to the ultimate strength of fabric
Influence is smaller, and takes into account good anti-wrinkle effect, still has very strong antibacterial effect, this finishing agent green after ten washings
It is pollution-free, it disclosure satisfy that textile security requirement.
The property indices of 1 anti-crease finishing of the present invention of table
Claims (7)
- A kind of 1. linen Anti-bacterial and Crease method, it is characterised in that comprise the following steps:(1)The 5-10wt% maltodextrin aqueous solution is configured, acetic anhydride, the addition of acetic anhydride are added in maltodextrin solution For the 1/10-1/5 of maltodextrin solution quality, regulation pH is 8-9, and the reaction time is 1-2 hours at being 22-30 DEG C in temperature;(2)In step(1)Corn peptide and glyoxal are added in solution, wherein corn peptide addition is 50-80g/L, and glyoxal adds It is 10-20g/L to enter amount, is stirred, and then the linen of degumming process is rolled by two leachings two, then dries, washes 2-3 It is secondary, five minutes naturally dries every time;(3)Step will be passed through(2)Treated fabric is first immersed in vine polyphenol, Punica granatum L. polyphenol and mulberry leaf water extract mixing water In solution, wherein the concentration of vine polyphenol is 5-13g/L, and the concentration of Punica granatum L. polyphenol is 2-9g/L, and the concentration of mulberry leaf water extract is 0.2-1.5g/L, 40-100min is handled in 50-80 DEG C of constant temperature, is washed, drying;(4)Again by fabric in alum, octamethylcy-clotetrasiloxane, APES, glycol monoethyl ether, alkanol 50-80 DEG C of constant temperature processing 30-60min in acid amides and water composition mixed solution, is washed, drying, wherein mixed solution press with Lower parts by weight composition:Alum 0.2-0.5 parts, octamethylcy-clotetrasiloxane 2-8 parts, APES 2-8 parts, second 100 parts of glycol monomethyl ether 1-5 parts, alkanolamide 0.5-5 parts and water.
- A kind of 2. linen Anti-bacterial and Crease method according to claim 1, it is characterised in that:Step(1)Middle malt The concentration of aqueous solution of dextrin is 6-8wt%, and the addition of acetic anhydride is the 1/8-1/5 of maltodextrin solution quality, is in temperature The reaction time is 1-2 hours at 25-30 DEG C.
- A kind of 3. linen Anti-bacterial and Crease method according to claim 1, it is characterised in that:Step(2)Middle corn Peptide addition is 60-75g/L, and glyoxal addition is 15-20g/L.
- A kind of 4. linen Anti-bacterial and Crease method according to claim 1, it is characterised in that:Step(3)Middle grape The concentration of polyphenol is 7-10g/L, and the concentration of Punica granatum L. polyphenol is 4-7g/L, and the concentration of mulberry leaf water extract is 0.5-1g/L.
- A kind of 5. linen Anti-bacterial and Crease method according to claim 1, it is characterised in that:Step(3)In in 55- 65 DEG C of constant temperature handle 60-90min.
- A kind of 6. linen Anti-bacterial and Crease method according to claim 1, it is characterised in that:Step(4)In will knit Thing is 60-70 DEG C in mixed solution, constant temperature processing 40-50min.
- A kind of 7. linen Anti-bacterial and Crease method according to claim 1, it is characterised in that:Step(4)Middle sulfuric acid Aluminium potassium 0.3-0.4 parts, octamethylcy-clotetrasiloxane 4-6 parts, APES 2-6 parts, glycol monoethyl ether 2-4 parts, 100 parts of alkanolamide 1.5-3 parts and water.