CN107858123A - A kind of photovoltaic module white EVA adhesive film and its preparation technology - Google Patents
A kind of photovoltaic module white EVA adhesive film and its preparation technology Download PDFInfo
- Publication number
- CN107858123A CN107858123A CN201710934197.XA CN201710934197A CN107858123A CN 107858123 A CN107858123 A CN 107858123A CN 201710934197 A CN201710934197 A CN 201710934197A CN 107858123 A CN107858123 A CN 107858123A
- Authority
- CN
- China
- Prior art keywords
- adhesive film
- photovoltaic module
- eva adhesive
- ester
- white eva
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of photovoltaic module white EVA adhesive film and its preparation technology, and the glued membrane raw material, which is formed, to be included:EVA resin:100 parts;Filler:1~10 part;Peroxide cross-linking agent:0.3~1.5 part;Crosslinking coagent:0.3~1.5 part;Antioxidant:0.05~0.5 part;UV absorbers:0.01~0.3 part;Light stabilizer:0.01~0.2 part;Tackifier:0.2~0.6 part.It is contemplated that introducing the sericite in powder of special ratios amount in filler, the specific insulation of the white EVA adhesive film of photovoltaic module, and then the anti-PID performances of lifting assembly are lifted.
Description
Technical field
The present invention relates to a kind of photovoltaic module white EVA adhesive film and its preparation technology, particularly one kind to have anti-PID
Photovoltaic module white EVA adhesive film and its preparation technology of energy.
Background technology
In recent years, as fossil energy increasingly depleted and earth environment pollute continuous serious, regenerative resource and each is made
Kind green energy resource has obtained increasing attention.The use of solar power generation is also increasingly popularized, and solar photovoltaic assembly is just
It is the device converted solar energy into electrical energy.The basic structure of conventional solar photovoltaic assembly is by photovoltaic tempering glass from top to bottom
Glass, upper strata EVA adhesive film, crystalline silicon battery plate, lower floor's EVA adhesive film and photovoltaic back composition.Conventional, photovoltaic back is white
, upper strata EVA adhesive film and lower floor's EVA adhesive film are all transparent, and solar energy is irradiated to crystalline substance through glass and upper strata transparent EVA glued membrane
Boundary layer on body silicon cell, which is absorbed, produces photoelectric current, and it is bigger to be irradiated to the intensity of the light on cell piece surface, caused light
The intensity of electric current is stronger, and the photovoltaic back of white plays the role of reflection light, and its light reflected passes through lower floor's transparent EVA glue
Film understands some light by reflection again and is irradiated to cell piece surface, improves the utilization to light.
As photovoltaic module industrial technology develops, slowly also there are double glass photovoltaic modulies, its structure be from top to bottom by
Photovoltaic safety glass, upper strata transparent EVA glued membrane, crystalline silicon battery plate, lower floor's white EVA adhesive film and photovoltaic safety glass composition.
Wherein, lower floor's white EVA adhesive film is to improve to form on the basis of existing transparent EVA glued membrane, and it is mainly in transparent EVA glued membrane
It is middle to add specific reflective filler, such as titanium dioxide, zinc oxide, to make it have common EVA superperformance and improve component
Reflectivity so that be component synergy.Solar double-glass assemblies, in anti-PID aspect of performances, can be better than normal in theory due to its structural factor
Photovoltaic module is advised, but due to many reasons such as installation environment or assembly reliability, how further to lift double glass light
The anti-PID performances of component are lied prostrate, turn into the problem of to be solved.
The content of the invention
It is an object of the present invention to solves above-mentioned technical problem, there is provided a kind of photovoltaic module with anti-PID performances is with vain
Color EVA adhesive film.
The technical solution adopted in the present invention is:A kind of white EVA adhesive film of photovoltaic module, its raw material is formed, by quality
Number meter, including:
EVA resin:100 parts;
Filler:1~10 part;
Peroxide cross-linking agent:0.3~1.5 part;
Crosslinking coagent:0.3~1.5 part;
Antioxidant:0.05~0.5 part;
UV absorbers:0.01~0.3 part;
Light stabilizer:0.01~0.2 part;
Tackifier:0.2~0.6 part.
In above-mentioned EVA resin, VA contents 27%~33%, melting means 20g/10min~40g/10min;
Above-mentioned filler is formed by titanium dioxide and sericite in powder compounding, and both mass ratioes are 1:1~1:2, corresponding titanium in filler
The amount of white powder or sericite in powder can excessively influence the combination property of glued membrane in itself(Such as adhesive strength), crossing can not reach corresponding at least
Effect(Such as reflectivity and anti-PID performances);
Peroxide cross-linking agent is selected from the peroxidating -2- ethylhexyl carbonates tert-butyl ester or the (tert-butyl group mistakes of 2,5- dimethyl -2,5- two
Oxidation) one kind in hexane;
Crosslinking coagent is selected from iso-cyanuric acid triallyl ester, TAC, trimethylol propane trimethyl propylene
One kind in acid esters;
Antioxidant is selected from β-positive octadecanol ester of (3,5- di-tert-butyl-hydroxy phenyls) propionic acid, three (nonyl phenyl) phosphorous acid
One kind in ester;
UV absorbers are selected from 2-hydroxy-4-n-octoxybenzophenone, 2- (tertiary pentyl -2- hydroxy phenyls of 3,5- bis-) benzo
One kind in triazole, 2- (2'- hydroxyl -5'- t-octyls phenyl) BTA;
Light stabilizer is the double -2,2,6,6- tetramethyl piperidines alcohol esters of decanedioic acid, double (1,2,2,6,6- pentamethyl -4- piperidyls) last of the ten Heavenly stems
One kind in two acid esters;
Tackifier are γ-methacryloxypropyl trimethoxy silane, vinyltrimethoxy silane, the ethoxy of vinyl three
One kind in base silane.
The above-mentioned photovoltaic module preparation technology of white EVA adhesive film, then comprise the following steps:
(1)On the basis of the above-mentioned photovoltaic module with anti-PID performances is formed with the raw material of white EVA adhesive film, raw material is chosen;
(2)By raw material it is well mixed after, put into double screw extruder, be cast extrusion at 90 DEG C, it is embossing, stretch, lead
Draw and be made after winding.
The thickness of the white EVA adhesive film of the photovoltaic module, preferably 0.5mm.
The beneficial effects of the present invention are, during raw material is formed, the sericite in powder of special ratios amount is creatively introduced, by
In the monoclinic crystal that sericite in powder is flakey, its radius-thickness ratio is larger, and has higher resistance, itself is excellent insulation
Material, addition sericite in powder can effectively improve the specific insulation of glued membrane in EVA adhesive film;Sericite in powder has in itself simultaneously
Excellent corrosion resistance and permeability resistance, it can effectively completely cut off steam infiltration, so as to reduce the PID risks of component, lift its anti-PID
Performance.
Embodiment
The present invention is addressed further under below by embodiment, but is not limited thereto.
Embodiment 1:
A kind of white EVA adhesive film of photovoltaic module, according to the mass fraction, chooses following raw materials:100 parts of EVA resin(VA contents
33%, melting means 20g/10min), 6 parts of filler(Including:3 parts of titanium dioxide, 3 parts of sericite in powder), peroxide cross-linking agent(2,5- bis-
Methyl -2,5- two (tert-butyl hydroperoxide) hexane)0.3 part, crosslinking coagent(Trimethylol-propane trimethacrylate)1.5
Part, antioxidant(β-positive octadecanol the ester of (3,5- di-tert-butyl-hydroxy phenyls) propionic acid)0.2 part, UV absorbers(2- hydroxyls
Base -4- oxy-octyl benzophenones)0.1 part, light stabilizer(Double -2,2,6,6- tetramethyl piperidine the alcohol esters of decanedioic acid)0.2 part, with
And tackifier(γ-methacryloxypropyl trimethoxy silane)0.2 part.
After above-mentioned raw materials are well mixed, put into double screw extruder, extrusion, embossing, drawing are cast at 90 DEG C
After stretching, draw and winding, the thick white EVA adhesive films of 0.5mm are made.
A1 is labeled as according to the gained sample of embodiment 1.
Embodiment 2:
A kind of white EVA adhesive film of photovoltaic module, according to the mass fraction, chooses following raw materials:100 parts of EVA resin(VA contents
27%, melting means 40g/10min), 10 parts of filler(Including:4 parts of titanium dioxide, 6 parts of sericite in powder), peroxide cross-linking agent(Peroxide
Change -2- ethylhexyl carbonate the tert-butyl esters)1.5 parts, crosslinking coagent(Iso-cyanuric acid triallyl ester)0.3 part, antioxidant(Three
(nonyl phenyl) phosphite ester) 0.5 part, UV absorbers(2-hydroxy-4-n-octoxybenzophenone)0.3 part, light stabilization
Agent(Double (1,2,2,6,6- pentamethyl -4- piperidyls) sebacates)0.01 part, and tackifier(Vinyl trimethoxy silicon
Alkane)0.6 part.
After above-mentioned raw materials are well mixed, put into double screw extruder, extrusion, embossing, drawing are cast at 90 DEG C
After stretching, draw and winding, the thick white EVA adhesive films of 0.5mm are made.
A2 is labeled as according to the gained sample of embodiment 2.
Embodiment 3:
A kind of white EVA adhesive film of photovoltaic module, according to the mass fraction, chooses following raw materials:100 parts of EVA resin(VA contents
33%, melting means 30g/10min), 1 part of filler(Including:0.05 part of titanium dioxide, 0.05 part of sericite in powder), peroxide cross-linking agent
(2,5- dimethyl -2,5- two (tert-butyl hydroperoxide) hexane)1 part, crosslinking coagent(TAC)1 part, antioxidant
(Three (nonyl phenyl) phosphite esters)0.05 part, UV absorbers(2- (2'- hydroxyl -5'- t-octyls phenyl) BTA)
0.01 part, light stabilizer(Double -2,2,6,6- tetramethyl piperidine the alcohol esters of decanedioic acid)0.1 part, and tackifier(γ-metering system
Acryloxypropylethoxysilane trimethoxy silane)0.4 part.
After above-mentioned raw materials are well mixed, put into double screw extruder, extrusion, embossing, drawing are cast at 90 DEG C
After stretching, draw and winding, the thick white EVA adhesive films of 0.5mm are made.
A3 is labeled as according to the gained sample of embodiment 3.
Comparative example:
Applicant is formed with reference to the raw material of above-described embodiment 1,2 and 3, is deleted the sericite in powder in filler, is made filler only corresponding
The titanium dioxide of mass fraction, other raw material proportionings are constant, and using same preparation technology, the sample of gained is made(Equivalent to normal
The white EVA adhesive film of rule)It is respectively labeled as B1, B2 and B3.
Performance test
By sample B1~B3 obtained by sample A1~A3 obtained by the various embodiments described above and comparative example, performance survey is carried out with reference to relevant criterion
Examination.Wherein, reflectivity reference ASTM E424-T;Specific insulation, hydrothermal aging xanthochromia and the reference of ultraviolet ageing xanthochromia
GB29848-2013;PID test references IEC62804.As a result it is as shown in table 1 below.
Table 1:Performance test table
From upper table 1, the photovoltaic module of gained produced according to the present invention is with white EVA adhesive film, the property with conventional white EVA adhesive film
It can compare, its reflectivity and wet and heat ageing resistant and resistance to UV aging are substantially suitable, but in specific insulation and anti-PID performances
Aspect, then it is obviously improved.
Claims (5)
- A kind of 1. white EVA adhesive film of photovoltaic module, it is characterised in that its raw material is formed according to the mass fraction, including:EVA resin:100 parts;Filler:1~10 part;Peroxide cross-linking agent:0.3~1.5 part;Crosslinking coagent:0.3~1.5 part;Antioxidant:0.05~0.5 part;UV absorbers:0.01~0.3 part;Light stabilizer:0.01~0.2 part;Tackifier:0.2~0.6 part;In the EVA resin, VA contents 27%~33%, melting means 20g/10min~40g/10min;The filler is formed by titanium dioxide and sericite in powder compounding, and both mass ratioes are 1:1~1:2.
- 2. the white EVA adhesive film of photovoltaic module as claimed in claim 1, it is characterised in that the peroxide cross-linking agent choosing One kind from the peroxidating -2- ethylhexyl carbonates tert-butyl ester or 2,5- dimethyl -2,5- two (tert-butyl hydroperoxide) hexane;Institute State crosslinking coagent and be selected from iso-cyanuric acid triallyl ester, TAC, trimethylol propane trimethyl acrylic acid One kind in ester;The antioxidant is selected from β-positive octadecanol ester of (3,5- di-tert-butyl-hydroxy phenyls) propionic acid, three (nonyls Phenyl) one kind in phosphite ester;The UV absorbers are selected from 2-hydroxy-4-n-octoxybenzophenone, 2- (3,5- bis- Tertiary pentyl -2- hydroxy phenyls) BTA, one kind in 2- (2'- hydroxyl -5'- t-octyls phenyl) BTA;The light is steady Agent is determined in the double -2,2,6,6- tetramethyl piperidines alcohol esters of decanedioic acid, double (1,2,2,6,6- pentamethyl -4- piperidyls) sebacates One kind;The tackifier are γ-methacryloxypropyl trimethoxy silane, vinyltrimethoxy silane, ethene One kind in ethyl triethoxy silicane alkane.
- 3. a kind of photovoltaic module preparation technology of white EVA adhesive film, it is characterised in that comprise the following steps:(1)By 100 parts of EVA resin, 1~10 part of filler, 0.3~1.5 part of peroxide cross-linking agent, 0.3~1.5 part Crosslinking coagent, 0.05~0.5 part of antioxidant, 0.01~0.3 part of UV absorbers, 0.01~0.2 part of light stabilizer, And 0.2~0.6 part of tackifier are well mixed;(2)Material that will be well mixed, puts into double screw extruder, is cast extrusion at 90 DEG C, embossing, stretch, lead Draw and be made after winding;The step(1)In, VA contents 27%~33% in EVA resin, melting means 20g/10min~40g/10min;The filler is formed by titanium dioxide and sericite in powder compounding, and both mass ratioes are 1:1~1:2.
- 4. the photovoltaic module as claimed in claim 4 preparation technology of white EVA adhesive film, it is characterised in that:The peroxidating Thing crosslinking agent is selected from the peroxidating -2- ethylhexyl carbonates tert-butyl ester or 2,5- dimethyl -2,5- two (tert-butyl hydroperoxide) hexane In one kind;The crosslinking coagent is selected from iso-cyanuric acid triallyl ester, TAC, trimethylolpropane tris One kind in methacrylate;The antioxidant is selected from β-positive octadecanol of (3,5- di-tert-butyl-hydroxy phenyls) propionic acid One kind in ester, three (nonyl phenyl) phosphite esters;The UV absorbers are selected from 2- hydroxyl -4- n-octyloxy hexichol first In ketone, 2- (tertiary pentyl -2- hydroxy phenyls of 3,5- bis-) BTA, 2- (2'- hydroxyl -5'- t-octyls phenyl) BTA It is a kind of;The light stabilizer is the double -2,2,6,6- tetramethyl piperidines alcohol esters of decanedioic acid, double (1,2,2,6,6- pentamethyl -4- piperidines Base) one kind in sebacate;The tackifier are γ-methacryloxypropyl trimethoxy silane, vinyl front three One kind in TMOS, VTES.
- 5. the white EVA adhesive film of a kind of photovoltaic module, it is characterised in that the photovoltaic module is with white EVA adhesive film by such as right It is required that the preparation technology described in 3~4 any one is prepared, and the photovoltaic module is with the thickness of white EVA adhesive film 0.5mm。