CN107857943A - A kind of PPR warm-air pipes formula - Google Patents
A kind of PPR warm-air pipes formula Download PDFInfo
- Publication number
- CN107857943A CN107857943A CN201711345092.7A CN201711345092A CN107857943A CN 107857943 A CN107857943 A CN 107857943A CN 201711345092 A CN201711345092 A CN 201711345092A CN 107857943 A CN107857943 A CN 107857943A
- Authority
- CN
- China
- Prior art keywords
- parts
- ppr
- warm
- air pipes
- bbp
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of PPR warm-air pipes formula, including PPR, lead salicylate, 2,6, DI-tert-butylphenol compounds, BBP(Butyl Benzyl Phthalate, epoxy soybean grease, quinoline any ketone, copolymerization ether diamine, triethyl citrate, cyclohexanone, paraffin and fluorescent whitening agent.The present invention extends the service life of PPR warm-air pipes, improves the resistance to elevated temperatures of PPR warm-air pipes.
Description
Technical field
The present invention relates to a kind of PPR warm-air pipes formula, belong to plastic conduit technical field.
Background technology
PPR pipe has energy-saving material-saving, environmental protection, light compared with the pipelines such as traditional cast iron pipe, coating steel pipe, pipe of cement
Matter is high-strength, construction and simple and convenient for maintenance.In recent years, with construction industry, municipal works, hydraulic engineering, agricultural and industry etc.
Industry market demand continues to increase, and Chinese PPR pipe industry presents high speed development situation.
PPR pipe road is with more in life, and wherein warm-air pipe is its most common use, and warm-air pipe can touch High Temperature Gas
Body, so requiring higher to the resistance to elevated temperatures of PPR warm-air pipes.
The content of the invention
To overcome above-mentioned deficiency, the object of the invention provides a kind of PPR warm-air pipes formula.
The solution of the present invention is as follows：A kind of PPR warm-air pipes formula, it is made up of according to parts by weight following raw material：PPR80~
150 parts, 10 ~ 25 parts of lead salicylate, 2,6-, 10 ~ 20 parts of DI-tert-butylphenol compounds, 8 ~ 15 parts of BBP(Butyl Benzyl Phthalate, epoxy are big
2 ~ 5 parts of soya-bean oil fat, quinoline any ketone 10 ~ 20 parts, 5 ~ 10 parts of ether diamine of copolymerization, 5 ~ 10 parts of triethyl citrate, 3 ~ 8 parts of cyclohexanone, stone
1 ~ 3 part of 2 ~ 6 parts of wax and fluorescent whitening agent.
Further, it is made up of according to parts by weight following raw material：PPR90 parts, 15 parts of lead salicylate, 2,6-, di-t-butyl
12 parts of phenol, 9 parts of BBP(Butyl Benzyl Phthalate, 3 parts of epoxy soybean grease, quinoline any ketone 15 parts, 6 parts of ether diamine of copolymerization, citric acid
3 parts of 7 parts of triethyl, 4 parts of cyclohexanone, 3 parts of paraffin and fluorescent whitening agent.
Further, it is made up of according to parts by weight following raw material：PPR120 parts, 20 parts of lead salicylate, 2,6-, di-t-butyl
15 parts of phenol, 12 parts of BBP(Butyl Benzyl Phthalate, 4 parts of epoxy soybean grease, quinoline any ketone 18 parts, 7 parts of ether diamine of copolymerization, citric acid
2 parts of 8 parts of triethyl, 5 parts of cyclohexanone, 4 parts of paraffin and fluorescent whitening agent.
Further, it is made up of according to parts by weight following raw material：PPR135 parts, 22 parts of lead salicylate, 2,6-, di-t-butyl
17 parts of phenol, 13 parts of BBP(Butyl Benzyl Phthalate, 3 parts of epoxy soybean grease, quinoline any ketone 16 parts, 8 parts of ether diamine of copolymerization, citric acid
1 part of 6 parts of triethyl, 6 parts of cyclohexanone, 5 parts of paraffin and fluorescent whitening agent.
Beneficial effects of the present invention：The present invention extends the service life of PPR warm-air pipes, improves the high temperature resistant of PPR warm-air pipes
Performance.
Embodiment
Embodiment 1
A kind of PPR warm-air pipes formula, it is made up of according to parts by weight following raw material：It is made up of according to parts by weight following raw material：
PPR90 parts, 15 parts of lead salicylate, 2,6-, 12 parts of DI-tert-butylphenol compounds, 9 parts of BBP(Butyl Benzyl Phthalate, epoxy soybean grease 3
Part, quinoline any ketone 15 parts, 6 parts of ether diamine of copolymerization, 7 parts of triethyl citrate, 4 parts of cyclohexanone, 3 parts of paraffin and 3 parts of fluorescent whitening agent.
Embodiment 2
A kind of PPR warm-air pipes formula, it is made up of according to parts by weight following raw material：It is made up of according to parts by weight following raw material：
PPR120 parts, 20 parts of lead salicylate, 2,6-, 15 parts of DI-tert-butylphenol compounds, 12 parts of BBP(Butyl Benzyl Phthalate, epoxy soybean grease
4 parts, quinoline any ketone 18 parts, 7 parts of ether diamine of copolymerization, 8 parts of triethyl citrate, 5 parts of cyclohexanone, 4 parts of paraffin and fluorescent whitening agent 2
Part.
Embodiment 3
A kind of PPR warm-air pipes formula, it is made up of according to parts by weight following raw material：It is made up of according to parts by weight following raw material：
PPR135 parts, 22 parts of lead salicylate, 2,6-, 17 parts of DI-tert-butylphenol compounds, 13 parts of BBP(Butyl Benzyl Phthalate, epoxy soybean grease
3 parts, quinoline any ketone 16 parts, 8 parts of ether diamine of copolymerization, 6 parts of triethyl citrate, 6 parts of cyclohexanone, 5 parts of paraffin and fluorescent whitening agent 1
Part.
Although giving detailed description and explanation to the embodiment of the present invention above, it should be noted that
We can carry out various equivalent changes and modification to above-mentioned embodiment according to the conception of the present invention, and its caused function is made
, all should be within protection scope of the present invention during with the spirit still covered without departing from specification.
Claims (4)
1. a kind of PPR warm-air pipes formula, it is characterised in that be made up of according to parts by weight following raw material：PPR80 ~ 150 part, water
10 ~ 25 parts of poplar lead plumbate, 2,6-, 10 ~ 20 parts of DI-tert-butylphenol compounds, 8 ~ 15 parts of BBP(Butyl Benzyl Phthalate, epoxy soybean grease 2 ~ 5
Part, quinoline any ketone 10 ~ 20 parts, 5 ~ 10 parts of ether diamine of copolymerization, 5 ~ 10 parts of triethyl citrate, 3 ~ 8 parts of cyclohexanone, 2 ~ 6 parts of paraffin and
1 ~ 3 part of fluorescent whitening agent.
2. a kind of PPR warm-air pipes formula according to claim 1, it is characterised in that according to parts by weight by following raw material group
Into：PPR90 parts, 15 parts of lead salicylate, 2,6-, 12 parts of DI-tert-butylphenol compounds, 9 parts of BBP(Butyl Benzyl Phthalate, epoxidized soybean oil
3 parts of fat, quinoline any ketone 15 parts, 6 parts of ether diamine of copolymerization, 7 parts of triethyl citrate, 4 parts of cyclohexanone, 3 parts of paraffin and fluorescent whitening agent 3
Part.
3. a kind of PPR warm-air pipes formula according to claim 1, it is characterised in that according to parts by weight by following raw material group
Into：PPR120 parts, 20 parts of lead salicylate, 2,6-, 15 parts of DI-tert-butylphenol compounds, 12 parts of BBP(Butyl Benzyl Phthalate, epoxy soybean
4 parts of grease, quinoline any ketone 18 parts, 7 parts of ether diamine of copolymerization, 8 parts of triethyl citrate, 5 parts of cyclohexanone, 4 parts of paraffin and fluorescent brightening
2 parts of agent.
4. a kind of PPR warm-air pipes formula according to claim 1, it is characterised in that according to parts by weight by following raw material group
Into：PPR135 parts, 22 parts of lead salicylate, 2,6-, 17 parts of DI-tert-butylphenol compounds, 13 parts of BBP(Butyl Benzyl Phthalate, epoxy soybean
3 parts of grease, quinoline any ketone 16 parts, 8 parts of ether diamine of copolymerization, 6 parts of triethyl citrate, 6 parts of cyclohexanone, 5 parts of paraffin and fluorescent brightening
1 part of agent.