CN108129754A - A kind of PPR pipe road formula - Google Patents
A kind of PPR pipe road formula Download PDFInfo
- Publication number
- CN108129754A CN108129754A CN201711345093.1A CN201711345093A CN108129754A CN 108129754 A CN108129754 A CN 108129754A CN 201711345093 A CN201711345093 A CN 201711345093A CN 108129754 A CN108129754 A CN 108129754A
- Authority
- CN
- China
- Prior art keywords
- parts
- pipe road
- ppr pipe
- propylgallate
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of PPR pipe road formula, including PPR, magnesium stearate, propylgallate, diisooctyl phthalate, methyl methacrylate, adipic acid, zinc silicate, vinyl silanes, aluminium hydroxide, turpentine oil and isoindolone.The present invention extends the service life in PPR pipe road, improves the quality in PPR pipe road.
Description
Technical field
The present invention relates to a kind of PPR pipe road formulas, belong to plastic conduit technical field.
Background technology
PPR pipe has energy-saving material-saving, environmental protection, light compared with the pipelines such as traditional cast iron pipe, coating steel pipe, pipe of cement
Matter is high-strength, construction and simple and convenient for maintenance.In recent years, with construction industry, municipal works, hydraulic engineering, agricultural and industry etc.
Industry market demand continues to increase, and Chinese PPR pipe industry presents high speed development situation.
This requires PPR pipe road will have preferable performance and very long service life.
Invention content
To overcome above-mentioned deficiency, the object of the invention provides a kind of PPR pipe road formula.
The solution of the present invention is as follows：A kind of PPR pipe road formula, is made of following raw material according to parts by weight：PPR80~150
Part, 10 ~ 25 parts of magnesium stearate, 10 ~ 20 parts of propylgallate, 8 ~ 15 parts of diisooctyl phthalate, methyl methacrylate
2 ~ 5 parts of ester, 10 ~ 20 parts of adipic acid, 5 ~ 10 parts of zinc silicate, 5 ~ 10 parts of vinyl silanes, 3 ~ 8 parts of aluminium hydroxide, 2 ~ 6 parts of turpentine oil
With 1 ~ 3 part of isoindolone.
Further, it is made of following raw material according to parts by weight：PPR90 parts, 15 parts of magnesium stearate, propylgallate 12
Part, 9 parts of diisooctyl phthalate, 3 parts of methyl methacrylate, 15 parts of adipic acid, 6 parts of zinc silicate, vinyl silanes 7
Part, 4 parts of aluminium hydroxide, 3 parts of turpentine oil and 3 parts of isoindolone.
Further, it is made of following raw material according to parts by weight：PPR120 parts, 20 parts of magnesium stearate, propylgallate
15 parts, 12 parts of diisooctyl phthalate, 4 parts of methyl methacrylate, 18 parts of adipic acid, 7 parts of zinc silicate, vinyl silanes
2 parts of 8 parts, 5 parts of aluminium hydroxide, 4 parts of turpentine oil and isoindolone.
Further, it is made of following raw material according to parts by weight：PPR135 parts, 22 parts of magnesium stearate, propylgallate
17 parts, 13 parts of diisooctyl phthalate, 3 parts of methyl methacrylate, 16 parts of adipic acid, 8 parts of zinc silicate, vinyl silanes
1 part of 6 parts, 6 parts of aluminium hydroxide, 5 parts of turpentine oil and isoindolone.
Beneficial effects of the present invention：The present invention extends the service life in PPR pipe road, improves the quality in PPR pipe road.
Specific embodiment
Embodiment 1
A kind of PPR pipe road formula, is made of following raw material according to parts by weight：It is made of following raw material according to parts by weight：
PPR90 parts, 15 parts of magnesium stearate, 12 parts of propylgallate, 9 parts of diisooctyl phthalate, methyl methacrylate 3
Part, 15 parts of adipic acid, 6 parts of zinc silicate, 7 parts of vinyl silanes, 4 parts of aluminium hydroxide, 3 parts of turpentine oil and 3 parts of isoindolone.
Embodiment 2
A kind of PPR pipe road formula, is made of following raw material according to parts by weight：It is made of following raw material according to parts by weight：
PPR120 parts, 20 parts of magnesium stearate, 15 parts of propylgallate, 12 parts of diisooctyl phthalate, methyl methacrylate 4
Part, 18 parts of adipic acid, 7 parts of zinc silicate, 8 parts of vinyl silanes, 5 parts of aluminium hydroxide, 4 parts of turpentine oil and 2 parts of isoindolone.
Embodiment 3
A kind of PPR pipe road formula, is made of following raw material according to parts by weight：It is made of following raw material according to parts by weight：
PPR135 parts, 22 parts of magnesium stearate, 17 parts of propylgallate, 13 parts of diisooctyl phthalate, methyl methacrylate 3
Part, 16 parts of adipic acid, 8 parts of zinc silicate, 6 parts of vinyl silanes, 6 parts of aluminium hydroxide, 5 parts of turpentine oil and 1 part of isoindolone.
Although giving detailed description and explanation to the specific embodiment of the present invention above, it should be noted that
We can be according to the present invention conception various equivalent changes and modification are carried out to the above embodiment, generated function is made
It, should all be within protection scope of the present invention during with the spirit still covered without departing from specification.
Claims (4)
1. a kind of PPR pipe road formula, which is characterized in that be made of following raw material according to parts by weight：PPR80 ~ 150 part, tristearin
Sour 10 ~ 25 parts of magnesium, 10 ~ 20 parts of propylgallate, 8 ~ 15 parts of diisooctyl phthalate, 2 ~ 5 parts of methyl methacrylate,
10 ~ 20 parts of adipic acid, 5 ~ 10 parts of zinc silicate, 5 ~ 10 parts of vinyl silanes, 3 ~ 8 parts of aluminium hydroxide, 2 ~ 6 parts of turpentine oil and iso-indoles
1 ~ 3 part of ketone.
2. a kind of PPR pipe road formula according to claim 1, which is characterized in that be made of following raw material according to parts by weight：
PPR90 parts, 15 parts of magnesium stearate, 12 parts of propylgallate, 9 parts of diisooctyl phthalate, methyl methacrylate 3
Part, 15 parts of adipic acid, 6 parts of zinc silicate, 7 parts of vinyl silanes, 4 parts of aluminium hydroxide, 3 parts of turpentine oil and 3 parts of isoindolone.
3. a kind of PPR pipe road formula according to claim 1, which is characterized in that be made of following raw material according to parts by weight：
PPR120 parts, 20 parts of magnesium stearate, 15 parts of propylgallate, 12 parts of diisooctyl phthalate, methyl methacrylate 4
Part, 18 parts of adipic acid, 7 parts of zinc silicate, 8 parts of vinyl silanes, 5 parts of aluminium hydroxide, 4 parts of turpentine oil and 2 parts of isoindolone.
4. a kind of PPR pipe road formula according to claim 1, which is characterized in that be made of following raw material according to parts by weight：
PPR135 parts, 22 parts of magnesium stearate, 17 parts of propylgallate, 13 parts of diisooctyl phthalate, methyl methacrylate 3
Part, 16 parts of adipic acid, 8 parts of zinc silicate, 6 parts of vinyl silanes, 6 parts of aluminium hydroxide, 5 parts of turpentine oil and 1 part of isoindolone.