CN107857532A - 一种高强度保温吸音墙体材料 - Google Patents
一种高强度保温吸音墙体材料 Download PDFInfo
- Publication number
- CN107857532A CN107857532A CN201711015993.XA CN201711015993A CN107857532A CN 107857532 A CN107857532 A CN 107857532A CN 201711015993 A CN201711015993 A CN 201711015993A CN 107857532 A CN107857532 A CN 107857532A
- Authority
- CN
- China
- Prior art keywords
- parts
- layer
- wall material
- acoustical absorption
- absorption wall
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供的一种高强度保温吸音墙体材料，包括以下重量份的原料：纤维增强材料15~20份、珍珠岩粉10~20份、空心玻璃微珠10~20份、废弃包装泡沫5~8份、粉煤灰15~20份、胶粘剂20~25份、硅酸盐水泥15~20份、半水石膏25~30份、助剂4.8~6.4份、硅酮粉2~6份、氯化镁4‑5份、活性炭4‑5份、硅藻土8‑9份。本发明提供的一种高强度保温吸音墙体材料采用空心玻璃微珠、废弃包装泡沫作为保温吸音填料，同时采用了纤维增强材料增强墙体材料的强度，其保温效果良好、吸音性能较佳，且强度高，同时，采用废弃包装泡沫降低了填料成本，减少了垃圾处理，更加有利于环保。
Description
技术领域
本发明涉及建筑材料领域，具体涉及一种高强度保温吸音墙体材料。
背景技术
随着工业的快速发展，经济发展也相当迅速，全世界对能源的需求也越来越大，在日益增大的总能源消耗中，建筑能耗特别大，约占总能源消耗的11~25%，大量的数据和实验都表明最快最有效的方法就是使用保温节能材料。同时，随着交通运输、城市建筑的发展，以及人口密度的增加，家庭设施（音响、空调、电视机等）的增多，环境噪声日益严重，它以及成为了污染人类社会环境的一大公害。一般人在日常生活中都会有机会暴露在二中不同程度的噪音中，可能发生各种不同程度的听力丧失，噪音也会影响心脏血管的健康、睡眠的品质，甚至胎儿的发育。
因此单一性能的墙体材料已经不能满足日益发展的需求。吸音材料由于孔隙较多，结构疏松，对强度影响较大。因此，急需一种高强度的保温吸音墙体材料满足人们对墙体材料保温、吸音效果良好且强度高的要求。
发明内容
针对现有技术，本发明的目的是为了提供一种高强度保温吸音墙体材料，该墙体材料强度高、保温、吸音效果良好，且采用了废弃包装泡沫作为填料，节约了资源，减少了材料成本，具有较高的实用价值和良好的应用前景。
为解决上述技术问题，本发明提供一种高强度保温吸音墙体材料，所述材料包括以下重量份的原料：纤维增强材料15~20份、珍珠岩粉10~20份、空心玻璃微珠10~20份、废弃包装泡沫5~8份、粉煤灰15~20份、硅酸盐水泥15~20份、胶粘剂20~25份、半水石膏25~30份、助剂4.8~6.4份、硅酮粉2~6份、氯化镁4-5份、活性炭4-5份、硅藻土8-9份。
产品包装过程中常常使用大量的泡沫。包装泡沫使用后，常常直接丢弃，很少回收利用，且泡沫降解不易，又易引起火灾，给垃圾处理带来一定的困难。但泡沫质量轻，孔隙度高，是一种很好的吸引填充材料。
空心玻璃微珠具有重量轻体积大、导热系数低、抗压强度高，分散性、流动性、稳定性好的优点。另外，还具有绝缘、自润滑、隔音、不吸水、耐火、耐腐蚀、防辐射、无毒等优异性能，是做为各种保温、隔音产品的极佳填充剂。
所述纤维增强材料包括玻璃纤维、钢纤维和碳纤维，所述纤维增强材料还包括麻赛尔纤维或木质纤维。所述所述玻璃纤维包括细玻璃纤维和粗玻璃纤维，其重量比为4~6:6~4。
所述细玻璃纤维的直径为 40-60mm，粗玻璃纤维的长度优选60~80mm，在墙体材料中形成玻璃纤维层，具有良好的增强墙体材料强度和吸音效果。
所述硅酮粉可以提高墙体材料的阻燃冲击强度，提高墙体材料的阻燃性能，同时还可以作为分散剂，使助剂、钢纤维、木质纤维、玻璃纤维、碳纤维更好的分散在填料中。
所述助剂包括起泡剂、稳定剂、润湿剂、抗氧剂，其质量比为0.5:3:1.5：1。
包括以下重量份的原料：钢纤维8份、木质纤维4份、玻璃纤维5份、碳纤维3份、珍珠岩粉15份、空心玻璃微珠15份、废弃包装泡沫6份、粉煤灰20份、硅酸盐水泥15份、胶粘剂25份、半水石膏25份、起泡剂0.5份、稳定剂3份、润湿剂1.5份、抗氧剂1份、硅酮粉4份、氯化镁4.5份、活性炭4.5份、硅藻土9份。
所述高强度保温吸音墙体材料包括五层，第一层、第五层为水泥表层，第二层和第四层为隔音保温层，第五层为吸音层。
第一层、第五层由硅酸盐水泥、纤维增强材料、粉煤灰、硅藻土、抗氧剂、稳定剂、珍珠岩粉制备而成，其强度高、由吸音、保温、阻燃的作用；第二层和第四层由胶粘剂、空心玻璃微珠、硅酮粉、润湿剂、氧化镁制备而成，具有隔音、保温的性能；第三层由半水石膏、起泡剂、活性炭、胶粘剂、废弃包装泡沫制备而成，具有吸音保温的性能。
所述高强度保温吸音墙体材料的制备方法，包括以下步骤：
步骤（1）：将纤维增强材料、粉煤灰、硅藻土、珍珠岩粉搅拌均匀，然后加入硅酸盐水泥、抗氧剂、稳定剂加水搅拌均匀后，得到水泥表层材料，注入模具，成型，形成第一层；
步骤（2）：将空心玻璃微珠、硅酮粉、氧化镁搅拌均匀后加入润湿剂和水，搅拌均匀后，加入胶粘剂继续搅拌，使其混合均匀，得到隔音保温层材料，倒入步骤（1）中成型了第一层的模具，使其均匀的铺在第一层上，成型，得到第二层；
步骤（3）：将半水石膏、起泡剂加入水中搅拌气泡后，加入活性炭、胶粘剂、废弃包装泡沫继续搅拌至混合均匀，倒入步骤（2）中成型了第二层的模具，使其均匀的铺在第二层上，成型，得到第三层；
步骤（4）：第四层的隔音保温层材料制备方法与步骤（2）相同，制备后，倒入步骤（3）中成型了第三层的模具，使其均匀的铺在第三层上，成型，得到第四层；
步骤（5）：第五层的水泥表层材料制备方法与步骤（1）相同，制备后，倒入步骤（4）中成型了第四层的模具，使其均匀的铺在第四层上，成型，得到第五层，养护干燥，得到本发明提供的高强度保温吸音墙体材料。
本发明提供的一种高强度保温吸音墙体材料，具有以下有益效果：
（1）本发明提供的一种高强度保温吸音墙体材料采用空心玻璃微珠、废弃包装泡沫作为保温吸音填料，同时采用了纤维增强材料增强墙体材料的强度，其保温效果良好、吸音性能较佳，且强度高，同时，采用废弃包装泡沫降低了填料成本，减少了垃圾处理，更加有利于环保。
（2）本发明提供的一种高强度保温吸音墙体材料具有五层结构，其保温效果好、强度高，还具有阻燃、隔音的效果，制备简单易行，有利于推广。
具体实施方式
以下对本发明进一步说明。
实施例1：
所述的一种高强度保温吸音墙体材料，包括以下重量份的原料：钢纤维6份、木质纤维3份、玻璃纤维5份、碳纤维5份、空心玻璃微珠10份、废弃包装泡沫8份、粉煤灰15份、胶粘剂20份、硅酸盐水泥20份、半水石膏25份、起泡剂0.4份、稳定剂2.4份、润湿剂1.2份、抗氧剂0.8份、硅酮粉2份、氯化镁4份、活性炭5份、硅藻土9份。
所述高强度保温吸音墙体材料的制备方法，包括以下步骤：
步骤（1）：将纤维增强材料、粉煤灰、硅藻土、珍珠岩粉搅拌均匀，然后加入硅酸盐水泥、抗氧剂、稳定剂加水搅拌均匀后，得到水泥表层材料，注入模具，成型，形成第一层；
步骤（2）：将空心玻璃微珠、硅酮粉、氧化镁搅拌均匀后加入润湿剂和水，搅拌均匀后，加入胶粘剂继续搅拌，使其混合均匀，得到隔音保温层材料，倒入步骤（1）中成型了第一层的模具，使其均匀的铺在第一层上，成型，得到第二层；
步骤（3）：将半水石膏、起泡剂加入水中搅拌气泡后，加入活性炭、胶粘剂、废弃包装泡沫继续搅拌至混合均匀，倒入步骤（2）中成型了第二层的模具，使其均匀的铺在第二层上，成型，得到第三层；
步骤（4）：第四层的隔音保温层材料制备方法与步骤（2）相同，制备后，倒入步骤（3）中成型了第三层的模具，使其均匀的铺在第三层上，成型，得到第四层；
步骤（5）：第五层的水泥表层材料制备方法与步骤（1）相同，制备后，倒入步骤（4）中成型了第四层的模具，使其均匀的铺在第四层上，成型，得到第五层，养护干燥，得到本发明提供的高强度保温吸音墙体材料。
实施例2：
所述的一种高强度保温吸音墙体材料，包括以下重量份的原料：所述的一种高强度保温吸音墙体材料，包括以下重量份的原料：钢纤维10份、麻赛尔纤维3份、玻璃纤维3份、碳纤维3份、空心玻璃微珠20份、废弃包装泡沫5份、粉煤灰20份、胶粘剂15份、硅酸盐水泥25份、半水石膏20份、起泡剂0.6份、稳定剂3.6份、润湿剂1.8份、抗氧剂1.2份、硅酮粉6份、氯化镁5份、活性炭4份、硅藻土8份。
所述高强度保温吸音墙体材料的制备方法，包括以下步骤：
步骤（1）：将纤维增强材料、粉煤灰、硅藻土、珍珠岩粉搅拌均匀，然后加入硅酸盐水泥、抗氧剂、稳定剂加水搅拌均匀后，得到水泥表层材料，注入模具，成型，形成第一层；
步骤（2）：将空心玻璃微珠、硅酮粉、氧化镁搅拌均匀后加入润湿剂和水，搅拌均匀后，加入胶粘剂继续搅拌，使其混合均匀，得到隔音保温层材料，倒入步骤（1）中成型了第一层的模具，使其均匀的铺在第一层上，成型，得到第二层；
步骤（3）：将半水石膏、起泡剂加入水中搅拌气泡后，加入活性炭、胶粘剂、废弃包装泡沫继续搅拌至混合均匀，倒入步骤（2）中成型了第二层的模具，使其均匀的铺在第二层上，成型，得到第三层；
步骤（4）：第四层的隔音保温层材料制备方法与步骤（2）相同，制备后，倒入步骤（3）中成型了第三层的模具，使其均匀的铺在第三层上，成型，得到第四层；
步骤（5）：第五层的水泥表层材料制备方法与步骤（1）相同，制备后，倒入步骤（4）中成型了第四层的模具，使其均匀的铺在第四层上，成型，得到第五层，养护干燥，得到本发明提供的高强度保温吸音墙体材料。
实施例3：
钢纤维8份、木质纤维4份、玻璃纤维5份、碳纤维3份、珍珠岩粉15份、空心玻璃微珠15份、废弃包装泡沫6份、粉煤灰20份、硅酸盐水泥15份、胶粘剂25份、半水石膏25份、起泡剂0.5份、稳定剂3份、润湿剂1.5份、抗氧剂1份、硅酮粉4份、氯化镁4.5份、活性炭4.5份、硅藻土9份。
所述高强度保温吸音墙体材料的制备方法，包括以下步骤：
步骤（1）：将纤维增强材料、粉煤灰、硅藻土、珍珠岩粉搅拌均匀，然后加入硅酸盐水泥、抗氧剂、稳定剂加水搅拌均匀后，得到水泥表层材料，注入模具，成型，形成第一层；
步骤（2）：将空心玻璃微珠、硅酮粉、氧化镁搅拌均匀后加入润湿剂和水，搅拌均匀后，加入胶粘剂继续搅拌，使其混合均匀，得到隔音保温层材料，倒入步骤（1）中成型了第一层的模具，使其均匀的铺在第一层上，成型，得到第二层；
步骤（3）：将半水石膏、起泡剂加入水中搅拌气泡后，加入活性炭、胶粘剂、废弃包装泡沫继续搅拌至混合均匀，倒入步骤（2）中成型了第二层的模具，使其均匀的铺在第二层上，成型，得到第三层；
步骤（4）：第四层的隔音保温层材料制备方法与步骤（2）相同，制备后，倒入步骤（3）中成型了第三层的模具，使其均匀的铺在第三层上，成型，得到第四层；
步骤（5）：第五层的水泥表层材料制备方法与步骤（1）相同，制备后，倒入步骤（4）中成型了第四层的模具，使其均匀的铺在第四层上，成型，得到第五层，养护干燥，得到本发明提供的高强度保温吸音墙体材料。
本发明不局限于上述最佳实施方式，任何人在本发明的启示下都可得出其他各种形式的产品，但不论在其形状或结构上作任何变化，凡是具有与本申请相同或相近似的技术方案，均落在本发明的保护范围之内。
Claims (6)
1.一种高强度保温吸音墙体材料，其特征在于：包括以下重量份的原料：纤维增强材料15~20份、珍珠岩粉10~20份、空心玻璃微珠10~20份、废弃包装泡沫5~8份、粉煤灰15~20份、胶粘剂20~25份、硅酸盐水泥15~20份、半水石膏25~30份、助剂4.8~6.4份、硅酮粉2~6份、氯化镁4-5份、活性炭4-5份、硅藻土8-9份。
2.根据权利要求1所述的一种高强度保温吸音墙体材料，其特征在于：所述纤维增强材料包括玻璃纤维、钢纤维和碳纤维，所述纤维增强材料还包括麻赛尔纤维或木质纤维。
3.根据权利要求2所述的一种高强度保温吸音墙体材料，其特征在于：所述所述玻璃纤维包括细玻璃纤维和粗玻璃纤维，其重量比为4~6:6~4。
4.根据权利要求3所述的一种高强度保温吸音墙体材料，其特征在于：所述细玻璃纤维的直径为 40-60mm，粗玻璃纤维的长度优选60~80mm。
5.根据权利要求1所述的一种高强度保温吸音墙体材料，其特征在于：所述助剂包括起泡剂、稳定剂、润湿剂、抗氧剂，其质量比为0.5:3:1.5：1。
6.根据权利要求5所述的一种高强度保温吸音墙体材料，其特征在于：包括以下重量份的原料：钢纤维8份、木质纤维4份、玻璃纤维5份、碳纤维3份、珍珠岩粉15份、空心玻璃微珠15份、废弃包装泡沫6份、粉煤灰20份、硅酸盐水泥15份、胶粘剂25份、半水石膏25份、起泡剂0.5份、稳定剂3份、润湿剂1.5份、抗氧剂1份、硅酮粉4份、氯化镁4.5份、活性炭4.5份、硅藻土9份。