CN107856367A - Water proof fire retardant tarpaulin - Google Patents
Water proof fire retardant tarpaulin Download PDFInfo
- Publication number
- CN107856367A CN107856367A CN201711070858.5A CN201711070858A CN107856367A CN 107856367 A CN107856367 A CN 107856367A CN 201711070858 A CN201711070858 A CN 201711070858A CN 107856367 A CN107856367 A CN 107856367A
- Authority
- CN
- China
- Prior art keywords
- layer
- base cloth
- water proof
- fire retardant
- proof fire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of water proof fire retardant tarpaulin with multiple functions such as preferable water proofing property, anti-flammability, gas permeabilities.A kind of water proof fire retardant tarpaulin, including base cloth layer, described base cloth layer is interwoven by cotton ramie blended spinning fiber and polyester fiber, spandex, base cloth layer side is provided with waterproof layer, the opposite side of base cloth layer is provided with flame-retardant layer, waterproof layer is provided with the first wearing layer back to the side of base cloth layer, and flame-retardant layer is provided with the second wearing layer back to the side of base cloth layer;Waterproof layer is the polyvinyl chloride film that surface is provided with some pores;Flame-retardant layer is the refractory fibre layer of cloth made of glass fibre;First wearing layer and the second wearing layer are polyester resin wear-resistant coating.The present invention by setting waterproof layer and flame-retardant layer to play water proof fire retardant function respectively in base cloth layer both sides, wearing layer is set to play wear-resisting functions in outermost layer, waterproof layer surface is provided with pore, and ventilative effect is played while waterproof, is highly suitable as the covering and protection of special cargo.
Description
Technical field
The present invention relates to a kind of fabric, more particularly to a kind of water proof fire retardant tarpaulin.
Background technology
Tarpaulin, there is good waterproof, fungicidal properties, while tensile strength is high, acid-alkali-corrosive-resisting, scrubs Foldable square
Just, the covering or outdoor tent that can be used in rainy day goods are built, such as train, automobile, the covering for taking turns Cargo On Deck, temporarily
Pile up covering of goods etc..
Existing common tarpaulin has the form using one layer of base fabric two sides film, and this tarpaulin has problems with:It is thick
Spend thin, stretching resistance and lear energy is poor, waterproof effect is general.The form of multilayer multimembrane is also used, this tarpaulin is present
Problems with:Weight is big, poor air permeability.And above tarpaulin does not all have preferable anti-flammability, this prevents it from meeting reality
In some particular applications, for example store of goods is extremely sensitive to the environment of surrounding, and burning can be caused by running into high temperature, kindling material,
More steam is run into it can also happen that reaction, this goods is typically disposed in the shady and cool warehouse memory storage for drying ventilation, but transports the phase
Between sometimes have no alternative but temporarily outdoor to shelve, and common tarpaulin can not carry out good covering and protection to such article.
In summary, it is necessary to develop a kind of new tarpaulin with water proof fire retardant function.
The content of the invention
It is an object of the invention to provide a kind of with the anti-of the multiple functions such as preferable water proofing property, anti-flammability, gas permeability
Water resistance fires tarpaulin, solves the problems, such as to propose in background above technology.
The technical solution adopted for the present invention to solve the technical problems is:
A kind of water proof fire retardant tarpaulin, including base cloth layer, described base cloth layer are handed over by cotton ramie blended spinning fiber and polyester fiber, spandex
Knit and form, base cloth layer side is provided with waterproof layer, and the opposite side of base cloth layer is provided with flame-retardant layer, and the side of waterproof layer back to base cloth layer is set
There is the first wearing layer, flame-retardant layer is provided with the second wearing layer back to the side of base cloth layer;Described waterproof layer is surface provided with some
The polyvinyl chloride film of pore, described polyvinyl chloride film include the component of following parts by weight:100 parts of polyvinyl chloride resin, adjacent benzene
Diformazan dioctyl phthalate 35-40 parts, tricresyl phosphate 5-15 parts, complex lead salt stabilizer 3-5 parts, 0.5 part of lubricant, DOP45-
55 parts, calcium carbonate powder 5-10 parts, PNBR 15-20 parts;Described flame-retardant layer is the fire resisting made of glass fibre
Scrim cloth;Described the first wearing layer and the second wearing layer is polyester resin wear-resistant coating.The cotton ramie blended spinning of base cloth layer is fine
Dimension has the advantages of cost is low, and polyester fiber has higher intensity and elastic recovery capability, and strong durable, spandex has preferably
Fast light, acidproof, alkaline-resisting, wearability and certain intensity, the base cloth layer being interwoven by above material have that cost is low, intensity
High, the advantages of wearability is good;If punctulate polyvinyl chloride film has water proofing property and preferable gas permeability, in tarpaulin outer layer
Play waterproof action;Polyester resin wear-resistant coating is the functional paint for having specific function, has excellent wear resistance.
Preferably, described some pores are aperture 0.3-0.4um through hole, some pores are with pitch of holes 0.45-
0.55um is evenly distributed on waterproof layer surface.Pore can pass through laser, electrochemistry ULTRASONIC COMPLEX or porous anodic aluminium oxide mould
Plate processing method is realized on waterproof layer.
Preferably, described polyester resin wear-resistant coating is the saturated polyester type coating containing benzene ring structure.Synthesis is poly-
Ester resin uses the polyacid and polyol reaction of phenyl ring, and synthesis obtains the saturated polyester resin containing benzene ring structure, phenyl ring
Rigidity characteristic can assign polyester resin with hardness so as to obtaining preferable wearability.
Preferably, the first described wear-resisting layer surface is provided with the reflective tape of some evenly spaced strips.Reflective tape with
The mode of spraying or adhesion is fixed on the first wear-resisting layer surface, can remind tarpaulin position in night reflected light, and
And differentiate the positive effect of tarpaulin with help user of service.
Preferably, the width of described reflective tape is 5-20cm.
The beneficial effects of the invention are as follows:
The water proof fire retardant tarpaulin of the present invention, by setting waterproof layer and flame-retardant layer to play water proof fire retardant respectively in base cloth layer both sides
Function, wearing layer is set to play wear-resisting functions in outermost layer, waterproof layer surface is provided with pore, played while waterproof ventilative
Effect, is highly suitable as the covering and protection of special cargo.
Brief description of the drawings
Fig. 1 is the main structure diagram of the present invention;
Fig. 2 is the structural representation of the pore of the present invention;
Fig. 3 is the structural representation of the reflective tape of the present invention.
In figure:1st, base cloth layer, 2, waterproof layer, 3, flame-retardant layer, the 4, first wearing layer, the 5, second wearing layer, 6, pore, 7, anti-
Light belt.
Embodiment
Below by specific embodiment, and with reference to accompanying drawing, technical scheme is described in further detail.Should
Work as understanding, implementation of the invention is not limited to the following examples, any formal accommodation for being done to the present invention and/or
Change falls within the scope of the present invention.
Embodiment:
A kind of water proof fire retardant tarpaulin as shown in Figure 1, including base cloth layer 1, described base cloth layer is by cotton ramie blended spinning fiber and gathers
Ester fiber, spandex are interwoven, and base cloth layer side is provided with waterproof layer 2, and the opposite side of base cloth layer is provided with flame-retardant layer 3, the waterproof layer back of the body
First wearing layer 4 is provided with to the side of base cloth layer, flame-retardant layer is provided with the second wearing layer 5 back to the side of base cloth layer.
As shown in Fig. 2 waterproof layer is the polyvinyl chloride film that surface is provided with some pores 6, some pores are aperture
0.4um through hole, some pores are evenly distributed on waterproof layer surface with pitch of holes 0.5um.Pore can pass through laser, electrochemistry
ULTRASONIC COMPLEX or porous anodic alumina template processing method are realized on waterproof layer.Polyvinyl chloride film includes following parts by weight
Component:100 parts of polyvinyl chloride resin, 35 parts of dioctyl phthalate, 6 parts of tricresyl phosphate, 3 parts of complex lead salt stabilizer, profit
0.5 part of lubrication prescription, DOP50 parts, 8 parts of calcium carbonate powder, 18 parts of PNBR.Its individual layer performance can reach tensile strength
23MPA, elongation 285%, and from self-extinguishment in 15s after fire, also there is flame retardant effect outside the function of waterproof and breathable.
Flame-retardant layer is the refractory fibre layer of cloth made of glass fibre.
First wearing layer and the second wearing layer are polyester resin wear-resistant coating.Polyester resin wear-resistant coating is to contain phenyl ring
The saturated polyester type coating of structure.Synthesizing polyester resin uses the polyacid and polyol reaction of phenyl ring, and synthesis is obtained containing benzene
The saturated polyester resin of ring structure, the rigidity characteristic of phenyl ring can assign polyester resin with hardness so as to obtaining preferable wearability.
The cotton ramie blended spinning fiber of base cloth layer has the advantages of cost is low, and there is polyester fiber higher intensity to recover with elasticity
Ability, strong durable, spandex has preferable fast light, acidproof, alkaline-resisting, wearability and certain intensity, interweaved by above material and
Into base cloth layer there is the advantages of cost is low, intensity is high, wearability is good;If punctulate polyvinyl chloride film have water proofing property and
Preferable gas permeability, waterproof action is played in tarpaulin outer layer;Polyester resin wear-resistant coating is that the function with specific function applies
Material, has excellent wear resistance.
As shown in figure 3, the first wear-resisting layer surface is provided with the reflective tape 7 of some evenly spaced strips, the width of reflective tape
For 10cm.Reflective tape is located at the first wear-resisting layer surface with spraying method, in night reflected light tarpaulin institute can be reminded in place
Put, and the positive effect of tarpaulin is differentiated with help user of service.
Embodiment described above is a kind of preferable scheme of the present invention, not the present invention is made any formal
Limitation, there are other variants and remodeling on the premise of without departing from the technical scheme described in claim.
Claims (9)
1. a kind of water proof fire retardant tarpaulin, including base cloth layer(1), it is characterised in that:Described base cloth layer is by cotton ramie blended spinning fiber
It is interwoven with polyester fiber, spandex, base cloth layer side is provided with waterproof layer(2), the opposite side of base cloth layer is provided with flame-retardant layer(3),
Waterproof layer is provided with the first wearing layer back to the side of base cloth layer(4), flame-retardant layer is provided with the second wearing layer back to the side of base cloth layer
(5);Described waterproof layer is that surface is provided with some pores(6)Polyvinyl chloride film, described polyvinyl chloride film includes
The component of following parts by weight:It is 100 parts of polyvinyl chloride resin, dioctyl phthalate 35-40 parts, tricresyl phosphate 5-15 parts, compound
0.5 part of lead salt stabilizer 3-5 parts, lubricant, DOP45-55 parts, calcium carbonate powder 5-10 parts, PNBR 15-20 parts;
Described flame-retardant layer is the refractory fibre layer of cloth made of glass fibre;Described the first wearing layer and the second wearing layer is poly-
Ester resin wear-resistant coating.
2. water proof fire retardant tarpaulin according to claim 1, it is characterised in that:Described some pores are aperture 0.3-
0.4um through hole, some pores are evenly distributed on waterproof layer surface with pitch of holes 0.45-0.55um.
3. water proof fire retardant tarpaulin according to claim 1 or 2, it is characterised in that:Described polyester resin wear-resistant coating
For the saturated polyester type coating containing benzene ring structure.
4. water proof fire retardant tarpaulin according to claim 1 or 2, it is characterised in that:The first described wear-resisting layer surface is set
There is the reflective tape of some evenly spaced strips.
5. water proof fire retardant tarpaulin according to claim 3, it is characterised in that:If the first described wear-resisting layer surface is provided with
Do the reflective tape of evenly spaced strip.
6. water proof fire retardant tarpaulin according to claim 1 or 2, it is characterised in that:The width of described reflective tape is 5-
20cm。
7. water proof fire retardant tarpaulin according to claim 3, it is characterised in that:The width of described reflective tape is 5-
20cm。
8. water proof fire retardant tarpaulin according to claim 4, it is characterised in that:The width of described reflective tape is 5-
20cm。
9. water proof fire retardant tarpaulin according to claim 5, it is characterised in that:The width of described reflective tape is 5-
20cm。