CN104880752A - High-efficiency broad width air-permeable fancy reflection material and preparation method thereof - Google Patents
High-efficiency broad width air-permeable fancy reflection material and preparation method thereof Download PDFInfo
- Publication number
- CN104880752A CN104880752A CN201510299090.3A CN201510299090A CN104880752A CN 104880752 A CN104880752 A CN 104880752A CN 201510299090 A CN201510299090 A CN 201510299090A CN 104880752 A CN104880752 A CN 104880752A
- Authority
- CN
- China
- Prior art keywords
- hot melt
- melt adhesive
- coating
- layer
- fancy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-efficiency broad width air-permeable fancy reflection material, comprising a substrate, hot melt adhesive film layers, composite adhesive layers, clad layers, focusing layers, and glass bead layers. Part of the substrate is provided with the hot melt adhesive film layers. The composite adhesive layer is arranged on the hot melt adhesive film layer. The clad layer is arranged on the composite adhesive layer. The focusing layer is arranged on the clad layer. The glass bead layer is arranged on the focusing layer. The hot melt adhesive film layers have fancy patterns. The ventilating fancy reflection material is novel in style, and the fancy patterns can reflect light, various fancy patterns can be made. Through adding pigment and filler in a hot melt adhesive film or a composite adhesive, a material in various colors can be made. The material has air permeability, and can be directly used as a garment material, and can be made into garment and reflective business cards. The invention also relates to a preparation technology of the high-efficiency broad width air-permeable fancy reflection material. The technology coats in wide width and full page, and is clear in patterns. The technology is a continuous one-step production method, and the patterns are seamless.
Description
Technical field
The invention belongs to reflectorized material and preparation field thereof, be specifically related to a kind of high-level efficiency wide cut and breathe freely fancy reflection material and preparation method thereof.
Background technology
Reflectorized material is also referred to as reflecting material, and it puts on base material by glass microballoon, and the optical principle returned after utilizing light to reflect reflection in glass microballoon, makes reflected light penetrate light direction by people and mostly return light source direction.This reflector is the glass microballoon retroreflecting principle using high index of refraction, is made by the advanced technologies of aftertreatment of focusing.Distant place direct light line reflection can be postbacked light place by it, no matter by day or all have good reflex reflection optical property night, especially evening, can play the high-visibility as daytime.
But, traditional civilian reflectorized material is generally all used on fabric, seldom relate in papery, and the single gray of color, style is single in comprehensively reflective, does not possess the performances such as ventilative and absorbing sweat, so a kind of appearance of novel fancy reflection material product becomes valuable, it both had reflecting signal function, and new style, there is various fancy and color.
Summary of the invention
For the deficiencies in the prior art, the invention provides a kind of high-level efficiency wide cut to breathe freely fancy reflection material and preparation method thereof, obtain ventilative fancy reflection material, not only new style, there is required various fancy and color, but also directly can be used as garment material, ready-made clothes can be processed or be made into reflective business card etc.
For achieving the above object, the present invention takes following technical scheme:
High-level efficiency wide cut is breathed freely fancy reflection material, comprise base material, hot melt adhesive rete, composite layer, coating, focus layer and soot layer, described part thereof is provided with hot melt adhesive rete, and described hot melt adhesive rete is provided with composite layer, described composite layer is provided with coating, described coating is provided with focus layer, and described focus layer is provided with soot layer, and described hot melt adhesive rete has Flower Print.
As preferably, described base material is selected from the one in chemical fabric, TC cloth, stretch fabric, oxford, cotton fire retardant, blending fire retardant, aramid fiber fire retardant, PU leather, leather, PVC leather, warp knitting cloth, bird eye fabric, Nylon Taffeta, Polyester Taffeta, paper.
As preferably, described coating is nontransparent coating or transparent coating or translucent coating; Described nontransparent coating is selected from one or more of aluminium metal coating, Titanium coating, metallic copper coating or plated metallic silver; Described transparent coating is selected from one or more of the transparent coating of zinc sulphide, the transparent coating of cryolite, the transparent coating of silicon monoxide, the transparent coating of monox or the transparent coating of indium oxide; Described translucent coating is the translucent coating of titanium nitride.
As preferably, described hot melt adhesive rete is fire retardant hot-melt film adhesive in user containing color stuffing or non-flame resistant hot melt adhesive rete.
As preferably, described hot melt adhesive film material is selected from one or more in copolyester, copolyamide, ethene and multipolymer thereof, ethylene acrylic acid co polymer, styrene and segmented copolymer thereof, thermoplastic polyurethane, thermoplastic propene's acid esters.
As preferably, described compound adhesive is flame retardant type compound adhesive containing color stuffing or non-flame resistant type compound adhesive.
As preferably, described compound adhesive is made up of the raw material of following weight portion: matrix resin 10 parts, hardening agent 1-10 part, auxiliary agent 0-10 part, thinning agent 60-90 part, fire retardant 0-10 part, color stuffing 1-5 part.
Described matrix resin is the one in solvent type acrylic resin, solvent borne polyurethane, water-borne acrylic resin, waterborne polyurethane resin; Described hardening agent is the one in isocyanate curing agent, aziridine hardener, amino resin curing agents; Described isocyanate curing agent is the one in Bayer N-75, Bayer N-3390, Bayer L-75; Described amino resin curing agents is methyl-etherified amino resins, the one in butylated amino resin; Described auxiliary agent is one or more in wetting agent, spreading agent, coupling agent; Described coupling agent is silane coupling agent KH-560, Silane coupling reagent KH-570, the one in silane coupling agent KH-572; Described thinning agent is the one in ethyl acetate, toluene, butanone, butyl acetate, dimethylbenzene, water; Described color stuffing is the one in aluminium powder, aluminium paste, toner, mill base, calcium carbonate, porcelain earth, titania, silicon dioxide; Described fire retardant is one or more in phosphorus flame retardant, nitrogenated flame retardant, phosphorus-nitrogenated flame retardant, bromide fire retardant inorganic combustion inhibitor; Described phosphorus flame retardant is the one in APP, microcapsule red phosphorus master batch; Described nitrogenated flame retardant is the one in melamine, melamine salt and ammonium polyphosphate; Wherein melamine salt is melamine cyanurate salt, phosphate melamine salt or polyphosphate melamine salt; Described phosphorus-nitrogenated flame retardant is the one in melamine cyanurate, Melamine Polyphosphate, ammonium dihydrogen phosphate (ADP), diammonium hydrogen phosphate, triammonium phosphate; Described bromide fire retardant is TDE, decabromodiphenyl oxide, tetrabromobisphenol A; Described inorganic combustion inhibitor is the one in aluminium hydroxide, magnesium hydroxide, antimony oxide, Firebrake ZB.
As preferably, described Refractive Index of Glass Microspheres scope is: 1.93-2.2, and particle size of glass microspheres scope is: 20-80 μm; The thickness of described hot melt adhesive rete is 0.03mm-0.2mm.
As preferably, the breathe freely initial retro-reflecting coefficient of fancy reflection material of described high-level efficiency wide cut reaches 500cd/ (lxm
2) more than.
The breathe freely beneficial effect of fancy reflection material of high-level efficiency wide cut of the present invention is:
1. this vapor-permeable type fancy reflection material, not only new style, its Flower Print can be reflective, various Flower Print can be made, in hot melt adhesive film or compound adhesive, the material that color stuffing obtains shades of colour is added with passing through, and there is gas penetration potential, directly can be used as garment material, ready-made clothes can be processed and also can be made into reflective business card;
2. the fancy reflection pattern of other modes relative, fancy reflection material is the coating of wide cut justifying, and clear patterns, can bulkly produce; Pattern is without seam; After whole product is carried out, just can use after PE/PET composite membrane can being opened, without the need to waiting for that drying adhesive solidifies at once;
3. adopt hot melt adhesive film, its thickness is thick, can promote the cohesive strength between hot melt adhesive film and base material, and the wearing quality of the product prepared, scratch resistance and washing performance are excellent;
4. hot melt adhesive film form is varied, and optional leeway is large, and particle size of glass microspheres scope is selected also large, add reflectance, namely initial retro-reflecting coefficient is high, reaches 500cd/ (lxm
2) more than;
5. the compound adhesive containing thin layer is protected, and making can be wider for the range of choice of hot melt adhesive film in the selection of material.
6. Christmas tree pattern can change according to the change in pattern of hot melt adhesive film.
Another object of the present invention to be breathed freely fancy reflection material preparation method about this high-level efficiency wide cut, and the technical scheme taked is:
High-level efficiency wide cut is breathed freely the preparation method of fancy reflection material, comprises the steps:
(1) glass microballoon is implanted: PE/PET composite membrane is placed in hot-rolling, and temperature controls between 140-220 DEG C, along with the fusing of PE film, single-glass microballon is deposited on PE film, treat that PE film cools, single-glass microballon is fixed on above PE/PET composite membrane, realizes thus planting pearl;
(2) focus layer: by the surface of coatings at described glass microballoon, formed and the focus layer of glass microballoon with the centre of sphere, through oven for drying solvent film forming, this film is called beads formed film;
(3) coating: by resistance heating manner, becomes gaseous state from Solid State Transformation, sublimates into coating, namely make compound reflecting layer after meeting beads formed film;
(4) composite layer: the beads formed film of coating is coated with one deck compound adhesive, after dry out solvent, rolling is stand-by;
(5) hot melt adhesive rete:
A hot melt adhesive film: adopt justifying coating method justifying on the mylar with separated type material to be coated with hot melt adhesive, after drying tunnel dry out solvent, be hot melt adhesive film;
B fancy hot melt adhesive film: by justifying hot melt adhesive film through having the convex roller of Flower Print, through the effect of excess pressure, justifying hot melt adhesive film is formed by convex roller to be had Flower Print hot melt adhesive film and is layed in and has on the mylar of separated type material, is fancy hot melt adhesive film;
(6) base material: the compound reflecting layer containing composite layer prepared by the fancy hot melt adhesive film (5) prepared or the fancy hot melt adhesive film of outsourcing and step (4) is by hot pressing mode compound, peel off after there is the mylar of separated type material, hot melt adhesive rete and base material are through hot pressing compound, after reflective fabric cooling, peel off PE/PET composite membrane, a kind of high-level efficiency wide cut to breathe freely fancy reflection material.
As preferably, the convex roller protrusion height described in described step (5): 0.02mm-2cm.
The breathe freely beneficial effect of preparation method of fancy reflection material of this high-level efficiency wide cut is:
1. the fancy reflection pattern of other modes relative, the fancy reflection material of this explained hereafter is the coating of wide cut justifying, and clear patterns, can bulkly produce;
2. this wide cut fancy reflection material of breathing freely is continuity One-step production, and pattern is without seam;
3. compare the intaglio plate transfer manufacture craft of solvent-borne type glue, equipment is more simple, and without the need to drying tunnel, production efficiency can be higher, and whole operating environment is more clean, non-exhaust emission, environment protection health;
4., after whole product is carried out, just can using after PE/PET composite membrane can being opened at once, without the need to waiting for that drying adhesive solidifies, improve production efficiency;
5. adopt hot melt adhesive film rubbing method, the thickness of hot melt adhesive film can be made to promote, improve the cohesive strength between hot melt adhesive film and base material, the wearing quality of the product prepared, scratch resistance and washing performance are all better than the recessed roller method of solvent-borne type glue;
6. hot melt adhesive film form is varied, and optional leeway is large, and particle size of glass microspheres scope is selected also large, improve reflectance, namely initial retro-reflecting coefficient is high, reaches 500cd/ (lxm
2) more than, manufacture craft also can change along with latex film property, can adapt to various base material, comprise paper;
7. this kind of preparation technology's reflectorized material washing performance is good, the compound adhesive protection of many thin layers, and making can be wider for the range of choice of hot melt adhesive film in the selection of material;
8. hot melt adhesive film can reuse, cost-saving;
9. Christmas tree pattern can change according to the change in pattern of hot melt adhesive film.
Accompanying drawing explanation
Fig. 1 is that high-level efficiency wide cut of the present invention is breathed freely the structural representation of fancy reflection material;
Fig. 2 is that high-level efficiency wide cut of the present invention is breathed freely the floor map of fancy reflection material;
Wherein, 1. base material, 2. hot melt adhesive rete, 3. coating, 4. focus layer, 5. soot layer, 6. composite layer.
Embodiment
Below in conjunction with specific embodiment, the present invention is further detailed explanation; the content that the present invention protects is not limited to this technique; the present invention is not limited to following examples; above embodiment is the preferred embodiment of the present invention; the restriction to authorized range of the present invention can not be interpreted as; all distortion of making according to the present invention and improvement, comprise Structure and energy and all belong to scope.
Embodiment 1
A kind of high-level efficiency wide cut is as described in Figure 1 breathed freely fancy reflection material, comprise base material 1, hot melt adhesive rete 2, composite layer 6, coating 3, focus layer 4 and soot layer 5, described part thereof 1 is provided with hot melt adhesive rete 2, and described hot melt adhesive rete 2 is provided with composite layer 6, described composite layer 6 is provided with coating 3, described coating 3 is provided with focus layer 4, and described focus layer 4 is provided with soot layer 5, and described hot melt adhesive rete 2 has Flower Print.
Here, described base material is selected from the one in chemical fabric, TC cloth, stretch fabric, oxford, cotton fire retardant, blending fire retardant, aramid fiber fire retardant, PU leather, leather, PVC leather, warp knitting cloth, bird eye fabric, Nylon Taffeta, Polyester Taffeta, paper.
Described coating is nontransparent coating or transparent coating or translucent coating; Described hot melt adhesive rete is the fire retardant hot-melt film adhesive in user or the non-flame resistant hot melt adhesive rete that contain color stuffing.
Described hot melt adhesive film material for for copolyester, copolyamide, ethene and multipolymer, ethylene acrylic acid co polymer, styrene and segmented copolymer thereof, thermoplastic polyurethane, thermoplastic propene's acid esters one or more.
Described compound adhesive is the flame retardant type compound adhesive or the non-flame resistant type compound adhesive that contain color stuffing.
Described compound adhesive is made up of the raw material of following weight portion: matrix resin 10 parts, hardening agent 1-10 part, auxiliary agent 0-10 part, thinning agent 60-90 part, fire retardant 0-10 part, color stuffing 1-5 part.
Described Refractive Index of Glass Microspheres scope is: 1.93-2.2, and particle size of glass microspheres scope is: 20-80 μm; The thickness of described hot melt adhesive rete is 0.03mm-0.2mm.
Embodiment 2: the high-level efficiency wide cut of preparation embodiment 1 is breathed freely the method for fancy reflection material
High-level efficiency wide cut as described in Example 1 is breathed freely the preparation method of fancy reflection material, comprises the steps:
(1) glass microballoon is implanted: PE/PET composite membrane is placed in hot-rolling, and temperature controls between 140 DEG C, along with the fusing of PE film, single-glass microballon is deposited on PE film, treat that PE film cools, single-glass microballon is fixed on above PE/PET composite membrane, realizes thus planting pearl;
(2) focus layer: by the surface of coatings at described glass microballoon, formed and the focus layer of glass microballoon with the centre of sphere, through oven for drying solvent film forming, this film is called beads formed film;
(3) coating: by resistance heating manner, becomes gaseous state from Solid State Transformation, sublimates into coating, namely make compound reflecting layer after meeting beads formed film;
(4) composite layer: the beads formed film of coating is coated with one deck compound adhesive, after dry out solvent, rolling is stand-by;
(6) hot melt adhesive rete:
A hot melt adhesive film: adopt justifying coating method justifying on the mylar with separated type material to be coated with hot melt adhesive, after drying tunnel dry out solvent, be hot melt adhesive film;
B fancy hot melt adhesive film: by justifying hot melt adhesive film through having the convex roller of Flower Print, through the effect of excess pressure, justifying hot melt adhesive film is formed by convex roller to be had Flower Print hot melt adhesive film and is layed in and has on the mylar of separated type material, be fancy hot melt adhesive film, described convex roller protrusion height: 0.02mm;
(6) base material: the compound reflecting layer containing composite layer prepared by the fancy hot melt adhesive film (5) prepared or the fancy hot melt adhesive film bought and (4) is by hot pressing mode compound, peel off after there is the mylar of separated type material, hot melt adhesive rete and base material are through hot pressing compound, after reflective fabric cooling, peel off PE/PET composite membrane, a kind of high-level efficiency wide cut to breathe freely fancy reflection material.
Here coating be transparent coating be selected from aluminium metal coating, Titanium coating, metallic copper coating, plated metallic silver one or more;
Coating be transparent coating be selected from the transparent coating of zinc sulphide, the transparent coating of cryolite, the transparent coating of silicon monoxide, the transparent coating of monox or the transparent coating of indium oxide one or more;
Coating is translucent coating is the translucent coating of titanium nitride.
Described matrix resin is the one in solvent type acrylic resin, solvent borne polyurethane, water-borne acrylic resin, waterborne polyurethane resin; Described hardening agent is the one in isocyanate curing agent, aziridine hardener, amino resin curing agents; Described isocyanate curing agent is the one in Bayer N-75, Bayer N-3390, Bayer L-75; Described amino resin curing agents is methyl-etherified amino resins, the one in butylated amino resin; Described auxiliary agent is one or more in wetting agent, spreading agent, coupling agent; Described coupling agent is silane coupling agent KH-560, Silane coupling reagent KH-570, the one in silane coupling agent KH-572; Described thinning agent is the one in ethyl acetate, toluene, butanone, butyl acetate, dimethylbenzene, water; Described color stuffing is the one in aluminium powder, aluminium paste, toner, mill base, calcium carbonate, porcelain earth, titania, silicon dioxide; Described fire retardant is one or more in phosphorus flame retardant, nitrogenated flame retardant, phosphorus-nitrogenated flame retardant, bromide fire retardant inorganic combustion inhibitor; Described phosphorus flame retardant is the one in APP, microcapsule red phosphorus master batch; Described nitrogenated flame retardant is the one in melamine, melamine salt and ammonium polyphosphate; Wherein melamine salt is melamine cyanurate salt, phosphate melamine salt or polyphosphate melamine salt; Described phosphorus-nitrogenated flame retardant is the one in melamine cyanurate, Melamine Polyphosphate, ammonium dihydrogen phosphate (ADP), diammonium hydrogen phosphate, triammonium phosphate; Described bromide fire retardant is TDE, decabromodiphenyl oxide, tetrabromobisphenol A; Described inorganic combustion inhibitor is the one in aluminium hydroxide, magnesium hydroxide, antimony oxide, Firebrake ZB.
Embodiment 3: the high-level efficiency wide cut of preparation embodiment 1 is breathed freely the method for fancy reflection material
By the method for embodiment 2, distinctive points is that in step step (1), temperature controls between 220 DEG C, and step (5) crowned roll protrusion height is 2cm.
Embodiment 4: the high-level efficiency wide cut of preparation embodiment 1 is breathed freely the method for fancy reflection material
By the method for embodiment 2, distinctive points is that in step step (1), temperature controls between 190 DEG C, and step (5) crowned roll protrusion height is 0.5cm.
Claims (10)
1. high-level efficiency wide cut is breathed freely fancy reflection material, it is characterized in that comprising base material, hot melt adhesive rete, composite layer, coating, focus layer and soot layer, described part thereof is provided with hot melt adhesive layer, and described hot melt adhesive layer is provided with composite layer, described composite layer is provided with coating, described coating is provided with focus layer, and described focus layer is provided with soot layer, and described hot melt adhesive rete has Flower Print.
2. high-level efficiency wide cut according to claim 1 is breathed freely fancy reflection material, it is characterized in that described base material is selected from the one in chemical fabric, TC cloth, stretch fabric, oxford, cotton fire retardant, blending fire retardant, aramid fiber fire retardant, PU leather, leather, PVC leather, warp knitting cloth, bird eye fabric, Nylon Taffeta, Polyester Taffeta, paper.
3. high-level efficiency wide cut according to claim 1 is breathed freely fancy reflection material, it is characterized in that described coating is nontransparent coating or transparent coating or translucent coating; Described nontransparent coating is selected from one or more of aluminium metal coating, Titanium coating, metallic copper coating or plated metallic silver; Described transparent coating is selected from one or more of the transparent coating of zinc sulphide, the transparent coating of cryolite, the transparent coating of silicon monoxide, the transparent coating of monox or the transparent coating of indium oxide; Described translucent coating is the translucent coating of titanium nitride.
4. high-level efficiency wide cut according to claim 1 is breathed freely fancy reflection material, it is characterized in that described hot melt adhesive rete is fire retardant hot-melt film adhesive in user containing color stuffing or non-flame resistant hot melt adhesive rete.
5. high-level efficiency wide cut according to claim 4 is breathed freely fancy reflection material, it is characterized in that described hot melt adhesive film material is selected from copolyester, copolyamide, ethene and multipolymer thereof, ethylene acrylic acid co polymer, styrene and segmented copolymer thereof, thermoplastic polyurethane, thermoplastic propene's acid esters one or more.
6. high-level efficiency wide cut according to claim 1 is breathed freely fancy reflection material, it is characterized in that described compound adhesive is flame retardant type compound adhesive containing color stuffing or non-flame resistant type compound adhesive.
7. high-level efficiency wide cut according to claim 6 is breathed freely fancy reflection material, it is characterized in that described compound adhesive is made up of the raw material of following weight portion: matrix resin 10 parts, hardening agent 1-10 part, auxiliary agent 0-10 part, thinning agent 60-90 part, fire retardant 0-10 part, color stuffing 1-5 part.
8. high-level efficiency wide cut according to claim 1 is breathed freely fancy reflection material, and it is characterized in that described Refractive Index of Glass Microspheres scope is 1.91-2.2, particle size of glass microspheres scope is 20-80 μm; The thickness of described hot melt adhesive rete is 0.03mm-5mm.
9. the high-level efficiency wide cut as described in as arbitrary in claim 1 to 8 is breathed freely the preparation method of fancy reflection material, it is characterized in that comprising the steps:
(1) glass microballoon is implanted: PE/PET composite membrane is placed in hot-rolling, and temperature controls between 140-220 DEG C, along with the fusing of PE film, single-glass microballon is deposited on PE film, treat that PE film cools, single-glass microballon is fixed on above PE/PET composite membrane, realizes thus planting pearl;
(2) focus layer: by the surface of coatings at described glass microballoon, formed and the focus layer of glass microballoon with the centre of sphere, through oven for drying solvent film forming, this film is called beads formed film;
(3) coating: by resistance heating manner, becomes gaseous state from Solid State Transformation, sublimates into coating, namely make compound reflecting layer after meeting beads formed film;
(4) composite layer: be coated with one deck compound adhesive on the beads formed film of coating, after dry out solvent, rolling is stand-by;
(5) hot melt adhesive layer:
A hot melt adhesive film: adopt justifying coating method justifying on the mylar with separated type material to be coated with hot melt adhesive, after drying tunnel dry out solvent, be hot melt adhesive film;
B fancy hot melt adhesive film: by justifying hot melt adhesive film through having the convex roller of Flower Print, through the effect of excess pressure, justifying hot melt adhesive film is formed by convex roller to be had Flower Print hot melt adhesive film and is layed in and has on the mylar of separated type material, is fancy hot melt adhesive film;
(6) base material: the compound reflecting layer containing composite layer prepared by fancy hot melt adhesive film step (5) prepared or the fancy hot melt adhesive film bought and (4) is by hot pressing mode compound, peel off after there is the mylar of separated type material, hot melt adhesive layer and base material are through hot pressing compound, after reflective fabric cooling, peel off PE/PET composite membrane, a kind of high-level efficiency wide cut to breathe freely fancy reflection material.
10. high-level efficiency wide cut as claimed in claim 9 is breathed freely the preparation method of fancy reflection material, it is characterized in that the convex roller protrusion height described in described step (5): 0.02mm-2cm.