CN107854324A - A kind of preparation method of the antibacterial mask substrate of the high water conservation of graphene oxide - Google Patents
A kind of preparation method of the antibacterial mask substrate of the high water conservation of graphene oxide Download PDFInfo
- Publication number
- CN107854324A CN107854324A CN201711053956.8A CN201711053956A CN107854324A CN 107854324 A CN107854324 A CN 107854324A CN 201711053956 A CN201711053956 A CN 201711053956A CN 107854324 A CN107854324 A CN 107854324A
- Authority
- CN
- China
- Prior art keywords
- graphene oxide
- layer web
- mask substrate
- high water
- water conservation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation method of the antibacterial mask substrate of the high water conservation of graphene oxide, the base fabric is combined by nutritive layer web and hydrophobic framework layer web, described nutritive layer web is by graphene oxide nylon fibre and biomass fiber homogeneous blend, is prepared by spunlace non-woven cloth technique；Described hydrophobic framework layer web is that graphene oxide nylon fibre is prepared by spunlace non-woven cloth technique.The antibacterial mask substrate skin-friendly of the high water conservation of graphene oxide of the present invention, antibiotic property, moisture retention are good, simple in construction, and production efficiency is high, cost is low, and use is safer.Mask substrate meets green, ecology, environmental protection, the requirement of health, can obtain relatively more preferable facial beauty care effect without using preservative.
Description
Technical field
The present invention relates to weaving and makeups articles for use field, and in particular to a kind of antibacterial mask substrate of high water conservation of graphene oxide
Preparation method.
Background technology
Facial mask is just increasingly liked that mounted facial mask is mainly made up of mask substrate, nutrition Essence by consumer.Often
Advise mask substrate generally use terylene short fiber and short rayon fiber shredding mixes, then shaped through cross lapping, then through Hydroentangled
It is made.In order to control bacterial reproduction on facial mask for a long time, antiseptic and antibiotic agent must be artificially added in nutrition Essence.It is but added
Antiseptic and antibiotic agent suppresses to skin cell proliferation, the skin histology of contact is had undesirable effect, this makes it possible to face
Film can exist in various degree when in use produces certain stimulation, hereby endophytic bacteria to skin, or even produces thorn to skin
Swash infringement, so that situations such as allergic phenomena occurs.
Therefore in order to improve security that facial mask uses, it is necessary to be improved in the raw material selection of mask substrate, make
Mask substrate itself has certain antibacterial functions.Graphene oxide (GO) has good anti-microbial property.Chinese section in 2010
Shanghai Applied Physics research institute of institute Hu W et al. publish an article in ACS Nano, have studied graphene oxide (GO) first, go back
The anti-microbial property of former graphene oxide (RGO).GO, RGO can effectively suppress the growth of EHEC, and cytotoxicity
Very little.Graphene can occur very strong dispersion with the phospholipid molecule on bacterial cell membrane and interact, it is thus possible to extensive
The phospholipid molecule on cell membrane is directly extracted, bacterium is killed, effectively plays antibacterial action.
The content of the invention
Goal of the invention：The present invention provides a kind of preparation method of the antibacterial mask substrate of high water conservation of graphene oxide.
Technical scheme：A kind of preparation method of the antibacterial mask substrate of high water conservation of graphene oxide, the base fabric is by nutritive layer
Web and hydrophobic framework layer web are combined, and described nutritive layer web is by graphene oxide nylon fibre and life
Material fibrils homogeneous blend, it is prepared by spunlace non-woven cloth technique；Described hydrophobic framework layer web is will to aoxidize stone
Black alkene nylon fibre is prepared by spunlace non-woven cloth technique.
Further, described graphene oxide nylon fibre accounts for the 10-20% of nutritive layer web gross weight, biomass
Fiber accounts for the 80-90% of nutritive layer web gross weight.
Further, described graphene oxide nylon fibre is the described graphite oxide using graphene oxide as raw material
The degree of graphene weight is 0.5-0.9% in alkene nylon fibre.
Further, described graphene oxide nylon fibre specification is 7.22-8.33tex (65-75D)/36F.
Further, described biomass fiber is viscose glue, aloe fibre, copper ion fiber, alginate fibre, ramie pulp fiber
Or the one or more in regenerated celulose fibre.
Further, described nutritive layer web carries out hydrophilic finiss, and moisture absorbing and sweat releasing soil-releasing finishing agent is configured to
10-15% solution, to nutritive layer web carry out spray 80 DEG C of infrared dryings, layer web that have additional nutrients it is hydrophilic, perspire,
Dirt-removing power.
Beneficial effect：The antibacterial mask substrate skin-friendly of the high water conservation of graphene oxide in the present invention, antibiotic property, moisture retention
Good, simple in construction, production efficiency is high, cost is low, and use is safer.Mask substrate meets green, life without using preservative
State, environmental protection, the requirement of health, relatively more preferable facial beauty care effect can be obtained.
Guarantee of the biomass fiber as the carrier and high water conservation of nutrient solution in the present invention, parent is carried out to nutritive layer web
Water arrange augment nutritional layer web it is hydrophilic, perspire, dirt-removing power, graphene oxide nylon fibre provides the anti-of nutrient solution
Bacterium, anti-corrosion function, while graphene oxide nylon fibre line density is small in hydrophobic framework layer web, is formed compared with fine capillary,
Nutritive layer web is formed compared with coarse wool tubule, is formed led from hydrophobic framework layer web to the unidirectional of nutritive layer web between the two
It is moist.Be advantageous to have additional nutrients layer web moisture retention and the nutrient delivery efficiency to face.
Specific embodiment
The technical scheme in the embodiment of the present invention will be clearly and completely described below, so that the technology of this area
Personnel can be better understood from advantages and features of the invention, so as to make apparent boundary to protection scope of the present invention
It is fixed.Embodiment described in the invention is only part of the embodiment of the present invention, rather than whole embodiments, based on the present invention
In embodiment, the every other implementation that those of ordinary skill in the art are obtained on the premise of creative work is not made
Example, belongs to the scope of protection of the invention.
Embodiment 1
A kind of preparation method of the antibacterial mask substrate of high water conservation of graphene oxide, the base fabric is by nutritive layer web and dredges
Water casing play web is combined, and described nutritive layer web is that graphene oxide nylon fibre and biomass fiber is equal
Even blending, it is prepared by spunlace non-woven cloth technique；Described hydrophobic framework layer web is that graphene oxide polyamide fibre is fine
Dimension is prepared by spunlace non-woven cloth technique.
Described graphene oxide nylon fibre accounts for the 20% of nutritive layer web gross weight, and biomass fiber accounts for nutritive layer
The 80% of web gross weight.
Described graphene oxide nylon fibre is the described graphene oxide nylon fibre using graphene oxide as raw material
The degree of middle graphene weight is 0.5%.
Described graphene oxide nylon fibre specification is 7.22tex (65D)/36F.
Described biomass fiber is that viscose glue, aloe fibre, copper ion fiber, alginate fibre, ramie pulp fiber or regeneration are fine
One or more in cellulose fiber.
Described nutritive layer web carries out hydrophilic finiss, by moisture absorbing and sweat releasing soil-releasing finishing agent be configured to 10% it is molten
Liquid, to nutritive layer web carry out spray 80 DEG C of infrared dryings, layer web that have additional nutrients it is hydrophilic, perspire, dirt-removing power.
Embodiment 2
A kind of preparation method of the antibacterial mask substrate of high water conservation of graphene oxide, the base fabric is by nutritive layer web and dredges
Water casing play web is combined, and described nutritive layer web is that graphene oxide nylon fibre and biomass fiber is equal
Even blending, it is prepared by spunlace non-woven cloth technique；Described hydrophobic framework layer web is that graphene oxide polyamide fibre is fine
Dimension is prepared by spunlace non-woven cloth technique.
Described graphene oxide nylon fibre accounts for the 10% of nutritive layer web gross weight, and biomass fiber accounts for nutritive layer
The 90% of web gross weight.
Described graphene oxide nylon fibre is the described graphene oxide nylon fibre using graphene oxide as raw material
The degree of middle graphene weight is 0.9%.
Described graphene oxide nylon fibre specification is 8.33tex (75D)/36F.
Described biomass fiber is that viscose glue, aloe fibre, copper ion fiber, alginate fibre, ramie pulp fiber or regeneration are fine
One or more in cellulose fiber.
Described nutritive layer web carries out hydrophilic finiss, by moisture absorbing and sweat releasing soil-releasing finishing agent be configured to 15% it is molten
Liquid, to nutritive layer web carry out spray 80 DEG C of infrared dryings, layer web that have additional nutrients it is hydrophilic, perspire, dirt-removing power.
Embodiment 3
A kind of preparation method of the antibacterial mask substrate of high water conservation of graphene oxide, the base fabric is by nutritive layer web and dredges
Water casing play web is combined, and described nutritive layer web is that graphene oxide nylon fibre and biomass fiber is equal
Even blending, it is prepared by spunlace non-woven cloth technique；Described hydrophobic framework layer web is that graphene oxide polyamide fibre is fine
Dimension is prepared by spunlace non-woven cloth technique.
Described graphene oxide nylon fibre accounts for the 14% of nutritive layer web gross weight, and biomass fiber accounts for nutritive layer
The 87% of web gross weight.
Described graphene oxide nylon fibre is the described graphene oxide nylon fibre using graphene oxide as raw material
The degree of middle graphene weight is 0.7%.
Described graphene oxide nylon fibre specification is 7.86tex (69D)/36F.
Described biomass fiber is that viscose glue, aloe fibre, copper ion fiber, alginate fibre, ramie pulp fiber or regeneration are fine
One or more in cellulose fiber.
Described nutritive layer web carries out hydrophilic finiss, by moisture absorbing and sweat releasing soil-releasing finishing agent be configured to 13% it is molten
Liquid, to nutritive layer web carry out spray 80 DEG C of infrared dryings, layer web that have additional nutrients it is hydrophilic, perspire, dirt-removing power.
The antibacterial mask substrate skin-friendly of the high water conservation of graphene oxide in the present invention, antibiotic property, moisture retention are good, structure letter
Single, production efficiency is high, cost is low, and use is safer.Mask substrate without use preservative, meet green, ecology, it is environmentally friendly,
The requirement of health, can obtain relatively more preferable facial beauty care effect.
Guarantee of the biomass fiber as the carrier and high water conservation of nutrient solution in the present invention, parent is carried out to nutritive layer web
Water arrange augment nutritional layer web it is hydrophilic, perspire, dirt-removing power, graphene oxide nylon fibre provides the anti-of nutrient solution
Bacterium, anti-corrosion function, while graphene oxide nylon fibre line density is small in hydrophobic framework layer web, is formed compared with fine capillary,
Nutritive layer web is formed compared with coarse wool tubule, is formed led from hydrophobic framework layer web to the unidirectional of nutritive layer web between the two
It is moist.Be advantageous to have additional nutrients layer web moisture retention and the nutrient delivery efficiency to face.
Claims (6)
- A kind of 1. preparation method of the antibacterial mask substrate of high water conservation of graphene oxide, it is characterised in that：The base fabric is by nutritive layer Web and hydrophobic framework layer web are combined, and described nutritive layer web is by graphene oxide nylon fibre and life Material fibrils homogeneous blend, it is prepared by spunlace non-woven cloth technique；Described hydrophobic framework layer web is will to aoxidize stone Black alkene nylon fibre is prepared by spunlace non-woven cloth technique.
- 2. the preparation method of the antibacterial mask substrate of the high water conservation of graphene oxide according to claim 1, it is characterised in that：Institute The graphene oxide nylon fibre stated accounts for the 10-20% of nutritive layer web gross weight, and biomass fiber accounts for nutritive layer web The 80-90% of gross weight.
- 3. the preparation method of the antibacterial mask substrate of the high water conservation of graphene oxide according to claim 2, it is characterised in that：Institute The graphene oxide nylon fibre stated is the graphene weight in described graphene oxide nylon fibre using graphene oxide as raw material The degree of amount is 0.5-0.9%.
- 4. the preparation method of the antibacterial mask substrate of the high water conservation of graphene oxide according to claim 3, it is characterised in that：Institute The graphene oxide nylon fibre specification stated is 7.22-8.33tex (65-75D)/36F.
- 5. the preparation method of the antibacterial mask substrate of the high water conservation of graphene oxide according to claim 1, it is characterised in that：Institute The biomass fiber stated is in viscose glue, aloe fibre, copper ion fiber, alginate fibre, ramie pulp fiber or regenerated celulose fibre One or more.
- 6. the preparation method of the antibacterial mask substrate of the high water conservation of graphene oxide according to claim 1, it is characterised in that：Institute The nutritive layer web stated carries out hydrophilic finiss, moisture absorbing and sweat releasing soil-releasing finishing agent is configured to 10-15% solution, to nutrition Layer web carry out spray 80 DEG C of infrared dryings, layer web that have additional nutrients it is hydrophilic, perspire, dirt-removing power.