CN107842418A - A kind of automobile water inlet bend pipe and its forming method - Google Patents
A kind of automobile water inlet bend pipe and its forming method Download PDFInfo
- Publication number
- CN107842418A CN107842418A CN201711099268.5A CN201711099268A CN107842418A CN 107842418 A CN107842418 A CN 107842418A CN 201711099268 A CN201711099268 A CN 201711099268A CN 107842418 A CN107842418 A CN 107842418A
- Authority
- CN
- China
- Prior art keywords
- bend pipe
- water inlet
- parts
- connector
- automobile water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to technical field of automobile accessories, especially a kind of automobile water inlet bend pipe, including body, the body are in 90 ° of radians, and body both ends are welded with connector, filter mechanism is arranged with the connector, and filter mechanism includes two layers of filter screen, two layers of filter screen is arranged at intervals, and filter cloth is additionally provided between it, the cross-sectional area of the filter screen and the interior cross-sectional area of connector match, and sheath is also arranged with the outside of the body, one layer of anti-corrosion layer is also coated with the inside of the body.Present invention also offers a kind of forming method of automobile water inlet bend pipe.The present invention can effectively improve its service life, by changing its making material, make it at different temperatures, it can act freely, also by the setting of filter mechanism, the water source for entering engine can be filtered, not only ensure that the service life of bend pipe, the life-span of engine is also improved indirectly, meets the demand of present people.
Description
Technical field
The present invention relates to technical field of automobile accessories, more particularly to a kind of automobile water inlet bend pipe and its forming method.
Background technology
With the continuous development of economic society, take a bus instead of walking a kind of mode having become in people's life, national income
Continuous improvement, its automobile is gradually come into every household, and vehicle structure mainly includes engine, chassis, electrically and car
One of body, wherein engine are the cores of automobile, around many parts around it, water inlet bend pipe is exactly, prior art
In bend pipe after a long time use, often can be because of uneven heating, so as to be damaged, therefore, we have proposed a kind of vapour
Car water inlet bend pipe and its forming method.
The content of the invention
The invention aims to solve shortcoming present in prior art, and a kind of automobile water inlet bend pipe for proposing and
Its forming method.
To achieve these goals, present invention employs following technical scheme：
Design a kind of automobile water inlet bend pipe, including body, the body is in 90 ° of radians, and the body both ends company of being welded with
Joint, filter mechanism is arranged with the connector, and filter mechanism includes two layers of filter screen, two layers of filter screen is arranged at intervals, and its
Between be additionally provided with filter cloth, the cross-sectional area of the filter screen and the interior cross-sectional area of connector match, on the outside of the body also
Sheath is arranged with, one layer of anti-corrosion layer is also coated with the inside of the body.
Preferably, the anti-corrosion layer is specially zinc coat.
Preferably, the body is specially that alloy material is made.
Preferably, the sheath is specially non-woven fabrics.
Present invention also offers a kind of forming method of automobile water inlet bend pipe, comprise the following steps that：
S1, raw material prepare, and its raw material is as follows by weight：Chromium 0.5-0.8 parts, zinc 0.5-0.8 parts, silicon 0.2-0.6 parts, cadmium
0.2-0.6 parts, nickel 3-6 parts, copper 5-8 parts, manganese 3-6 parts and aluminium 80-90 parts；
S2, each component material in S1 weighed, proportioning is qualified, and caused weight error should be less than thousand points in weighing process
One of；
S3, selection smelting furnace are aid, and after being cleaned to it, are carried out under conditions of 100-200 degrees Celsius
Aluminium, is then put into smelting furnace and carries out melting by preheating, and smelting temperature is controlled between 730-850 degrees Celsius, treats that it melts completely
After change, melting is carried out chromium, zinc, silicon, cadmium, nickel, copper and manganese are added in smelting furnace successively, will during addition
Temperature in smelting furnace is increased to 1200-1300 degrees Celsius, after it melts completely, passes it through filter mechanism and filters out impurity
Afterwards, it is standby；
S4, water pipe mould is chosen again, and it is preheated under conditions of 100-200 degrees Celsius, then by S3
Solution after processing is cast in water pipe mould, and it is quickly cooled down using natural wind, after its first one-step forming, is taken
Go out, and the bend pipe in 90 ° is converted into by bending mechanism, so as to obtain body；
S5, recover to normal temperature after the body in S4, the corner that body has more is placed under repair, by the qualification rate control of body
System is in rational scope；
S6 and then the welding of head is attached at body both ends, and to its internal spray zinc coat, finally sutured sheath
In the outside of body, after the completion of, filter mechanism is fastened in connector, as automobile water inlet bend pipe.
A kind of automobile water inlet bend pipe proposed by the present invention, beneficial effect are：Automobile water inlet bend pipe can effectively improve
Its service life, by changing its making material, make it at different temperatures, can act freely, also pass through filter
The setting of structure, the water source for entering engine can be filtered, not only ensure that the service life of bend pipe, also improve indirectly
In the life-span of engine, meet the demand of present people.
Brief description of the drawings
Fig. 1 is a kind of structural representation of automobile water inlet bend pipe proposed by the present invention.
Fig. 2 is a kind of cross section structure diagram of automobile water inlet bend pipe proposed by the present invention.
Fig. 3 is the connector and pipe connection structure schematic diagram of a kind of automobile water inlet bend pipe proposed by the present invention.
Fig. 4 is a kind of structural representation of the filter mechanism of automobile water inlet bend pipe proposed by the present invention.
In figure：1 body, 2 connectors, 3 filter mechanisms, 31 filter screens, 32 filter clothes, 4 sheaths, 5 anti-corrosion layers.
Embodiment
Below in conjunction with the accompanying drawing in the embodiment of the present invention, the technical scheme in the embodiment of the present invention is carried out clear, complete
Site preparation describes, it is clear that described embodiment is only part of the embodiment of the present invention, rather than whole embodiments.
Reference picture 1-4, a kind of automobile water inlet bend pipe, including body 1, the body 1 are specially that alloy material is made.It is described
Body 1 is in 90 ° of radians, and the both ends of body 1 are welded with connector 2, filter mechanism 3 is arranged with the connector 2, and filter
Mechanism 3 includes two layers of filter screen 31, and two layers of filter screen 31 is arranged at intervals, and filter cloth 32 is additionally provided between it, the horizontal stroke of the filter screen 31
The interior cross-sectional area of sectional area and connector 2 matches, and can be filtered in the water entered inside body 1, outside the body 1
Side is also arranged with sheath 4, and the sheath 4 is specially non-woven fabrics, and the inner side of body 1 is also coated with one layer of anti-corrosion layer 5, described
Anti-corrosion layer 5 is specially zinc coat, it is possible to increase the corrosion resistance inside body 1, so as to improve its service life.
Embodiment 1
Present invention also offers a kind of forming method of automobile water inlet bend pipe, comprise the following steps that：
S1, raw material prepare, and its raw material is as follows by weight：0.5 part of chromium, 0.5 part of zinc, 0.2 part of silicon, 0.2 part of cadmium, 3 parts of nickel,
80 parts of 5 parts of copper, 3 parts of manganese and aluminium；
S2, each component material in S1 weighed, proportioning is qualified, and caused weight error should be less than thousand points in weighing process
One of；
S3, selection smelting furnace are aid, and after being cleaned to it, are preheated under conditions of 100 degrees Celsius,
Then aluminium is put into smelting furnace and carries out melting, smelting temperature control between 730 degrees Celsius, after its completely melt after, according to
Secondary chromium, zinc, silicon, cadmium, nickel, copper and manganese are added in smelting furnace carries out melting, during addition, by smelting furnace
Temperature is increased to 1200 degrees Celsius, after it melts completely, passes it through after filter mechanism filters out impurity, standby；
S4, water pipe mould is chosen again, and it is preheated under conditions of 100 degrees Celsius, then will be handled in S3
Solution afterwards is cast in water pipe mould, and it is quickly cooled down using natural wind, after its first one-step forming, is taken out, and
Bend pipe in 90 ° is converted into by bending mechanism, so as to obtain body 1；
S5, recover to normal temperature after the body 1 in S4, the corner being had more to body 1 places under repair, by the qualified of body 1
Rate is controlled in rational scope；
S6 and then first 2 welding is attached at the both ends of body 1, and to its internal spray zinc coat, finally by sheath 5
The outside of body 1 is sewn to, after the completion of, filter mechanism 3 is fastened in connector 2, as automobile water inlet bend pipe.
Embodiment 2
Present invention also offers a kind of forming method of automobile water inlet bend pipe, comprise the following steps that：
S1, raw material prepare, and its raw material is as follows by weight：0.6 part of chromium, 0.6 part of zinc, 0.3 part of silicon, 0.3 part of cadmium, 4 parts of nickel,
84 parts of 6 parts of copper, 4 parts of manganese and aluminium；
S2, each component material in S1 weighed, proportioning is qualified, and caused weight error should be less than thousand points in weighing process
One of；
S3, selection smelting furnace are aid, and after being cleaned to it, are preheated under conditions of 140 degrees Celsius,
Then aluminium is put into smelting furnace and carries out melting, smelting temperature control between 780 degrees Celsius, after its completely melt after, according to
Secondary chromium, zinc, silicon, cadmium, nickel, copper and manganese are added in smelting furnace carries out melting, during addition, by smelting furnace
Temperature is increased to 1240 degrees Celsius, after it melts completely, passes it through after filter mechanism filters out impurity, standby；
S4, water pipe mould is chosen again, and it is preheated under conditions of 140 degrees Celsius, then will be handled in S3
Solution afterwards is cast in water pipe mould, and it is quickly cooled down using natural wind, after its first one-step forming, is taken out, and
Bend pipe in 90 ° is converted into by bending mechanism, so as to obtain body 1；
S5, recover to normal temperature after the body 1 in S4, the corner being had more to body 1 places under repair, by the qualified of body 1
Rate is controlled in rational scope；
S6 and then first 2 welding is attached at the both ends of body 1, and to its internal spray zinc coat, finally by sheath 5
The outside of body 1 is sewn to, after the completion of, filter mechanism 3 is fastened in connector 2, as automobile water inlet bend pipe.
Embodiment 3
Present invention also offers a kind of forming method of automobile water inlet bend pipe, comprise the following steps that：
S1, raw material prepare, and its raw material is as follows by weight：0.7 part of chromium, 0.7 part of zinc, 0.5 part of silicon, 0.5 part of cadmium, 5 parts of nickel,
88 parts of 7 parts of copper, 5 parts of manganese and aluminium；
S2, each component material in S1 weighed, proportioning is qualified, and caused weight error should be less than thousand points in weighing process
One of；
S3, selection smelting furnace are aid, and after being cleaned to it, are preheated under conditions of 180 degrees Celsius,
Then aluminium is put into smelting furnace and carries out melting, smelting temperature control between 820 degrees Celsius, after its completely melt after, according to
Secondary chromium, zinc, silicon, cadmium, nickel, copper and manganese are added in smelting furnace carries out melting, during addition, by smelting furnace
Temperature is increased to 1280 degrees Celsius, after it melts completely, passes it through after filter mechanism filters out impurity, standby；
S4, water pipe mould is chosen again, and it is preheated under conditions of 180 degrees Celsius, then will be handled in S3
Solution afterwards is cast in water pipe mould, and it is quickly cooled down using natural wind, after its first one-step forming, is taken out, and
Bend pipe in 90 ° is converted into by bending mechanism, so as to obtain body 1；
S5, recover to normal temperature after the body 1 in S4, the corner being had more to body 1 places under repair, by the qualified of body 1
Rate is controlled in rational scope；
S6 and then first 2 welding is attached at the both ends of body 1, and to its internal spray zinc coat, finally by sheath 5
The outside of body 1 is sewn to, after the completion of, filter mechanism 3 is fastened in connector 2, as automobile water inlet bend pipe.
Embodiment 4
Present invention also offers a kind of forming method of automobile water inlet bend pipe, comprise the following steps that：
S1, raw material prepare, and its raw material is as follows by weight：0.8 part of chromium, 0.8 part of zinc, 0.6 part of silicon, 0.6 part of cadmium, 6 parts of nickel,
90 parts of 8 parts of copper, 6 parts of manganese and aluminium；
S2, each component material in S1 weighed, proportioning is qualified, and caused weight error should be less than thousand points in weighing process
One of；
S3, selection smelting furnace are aid, and after being cleaned to it, are preheated under conditions of 200 degrees Celsius,
Then aluminium is put into smelting furnace and carries out melting, smelting temperature control between 850 degrees Celsius, after its completely melt after, according to
Secondary chromium, zinc, silicon, cadmium, nickel, copper and manganese are added in smelting furnace carries out melting, during addition, by smelting furnace
Temperature is increased to 1300 degrees Celsius, after it melts completely, passes it through after filter mechanism filters out impurity, standby；
S4, water pipe mould is chosen again, and it is preheated under conditions of 200 degrees Celsius, then will be handled in S3
Solution afterwards is cast in water pipe mould, and it is quickly cooled down using natural wind, after its first one-step forming, is taken out, and
Bend pipe in 90 ° is converted into by bending mechanism, so as to obtain body 1；
S5, recover to normal temperature after the body 1 in S4, the corner being had more to body 1 places under repair, by the qualified of body 1
Rate is controlled in rational scope；
S6 and then first 2 welding is attached at the both ends of body 1, and to its internal spray zinc coat, finally by sheath 5
The outside of body 1 is sewn to, after the completion of, filter mechanism 3 is fastened in connector 2, as automobile water inlet bend pipe.
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto,
Any one skilled in the art the invention discloses technical scope in, technique according to the invention scheme and its
Inventive concept is subject to equivalent substitution or change, should all be included within the scope of the present invention.
Claims (5)
- The bend pipe 1. a kind of automobile is intake, including body (1), it is characterised in that：The body (1) is in 90 ° of radians, and body (1) Both ends are welded with connector (2), filter mechanism (3) are arranged with the connector (2), and filter mechanism (3) includes two layers Filter screen (31), two layers of filter screen (31) is arranged at intervals, and filter cloth (32) is additionally provided between it, the cross-sectional area of the filter screen (31) Match with the interior cross-sectional area of connector (2), sheath (4), body (1) inner side are also arranged with the outside of the body (1) Also it is coated with one layer of anti-corrosion layer (5).
- 2. a kind of automobile water inlet bend pipe according to claim 1, it is characterised in that the anti-corrosion layer (5) is specially to plate Zinc layers.
- 3. a kind of automobile water inlet bend pipe according to claim 1, it is characterised in that the body (1) is specially alloy material Material is made.
- 4. a kind of automobile water inlet bend pipe according to claim 1, it is characterised in that the sheath (4) is specially non-woven fabrics.
- 5. the forming method of a kind of automobile water inlet bend pipe according to claim 1-4, it is characterised in that specific steps are such as Under：S1, raw material prepare, and its raw material is as follows by weight：Chromium 0.5-0.8 parts, zinc 0.5-0.8 parts, silicon 0.2-0.6 parts, cadmium 0.2- 0.6 part, nickel 3-6 parts, copper 5-8 parts, manganese 3-6 parts and aluminium 80-90 parts；S2, each component material in S1 weighed, proportioning is qualified, in weighing process caused weight error should be less than thousand/ One；S3, selection smelting furnace are aid, and after being cleaned to it, are preheated under conditions of 100-200 degrees Celsius, Then aluminium to be put into smelting furnace and carries out melting, smelting temperature is controlled between 730-850 degrees Celsius, after it melts completely, Melting is carried out chromium, zinc, silicon, cadmium, nickel, copper and manganese are added in smelting furnace successively, during addition, by smelting furnace Interior temperature is increased to 1200-1300 degrees Celsius, after it melts completely, passes it through after filter mechanism filters out impurity, standby With；S4, water pipe mould is chosen again, and it is preheated under conditions of 100-200 degrees Celsius, then will be handled in S3 Solution afterwards is cast in water pipe mould, and it is quickly cooled down using natural wind, after its first one-step forming, is taken out, and Bend pipe in 90 ° is converted into by bending mechanism, so as to obtain body (1)；S5, recover to after normal temperature after the body (1) in S4, the corner being had more to body (1) places under repair, by the conjunction of body (1) Lattice rate is controlled in rational scope；S6 and then the welding of head (2) is attached at body (1) both ends, and to its internal spray zinc coat, finally by sheath (5) outside of body (1) is sewn to, after the completion of, filter mechanism (3) is fastened in connector (2), as automobile water inlet is curved Pipe.