CN107841867A - A kind of preparation method of resistance to washing oil sense coating fabric - Google Patents

A kind of preparation method of resistance to washing oil sense coating fabric Download PDF

Info

Publication number
CN107841867A
CN107841867A CN201711237684.7A CN201711237684A CN107841867A CN 107841867 A CN107841867 A CN 107841867A CN 201711237684 A CN201711237684 A CN 201711237684A CN 107841867 A CN107841867 A CN 107841867A
Authority
CN
China
Prior art keywords
parts
fabric
resistance
preparation
washing oil
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201711237684.7A
Other languages
Chinese (zh)
Inventor
王学珍
王丽佳
王月忠
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Embroidery Art World Embroidery Technology Co Ltd
Original Assignee
Suzhou Embroidery Art World Embroidery Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Embroidery Art World Embroidery Technology Co Ltd filed Critical Suzhou Embroidery Art World Embroidery Technology Co Ltd
Priority to CN201711237684.7A priority Critical patent/CN107841867A/en
Publication of CN107841867A publication Critical patent/CN107841867A/en
Withdrawn legal-status Critical Current

Abstract

The invention discloses a kind of preparation method of resistance to washing oil sense coating fabric, after the surface of fabric first is cleaned into drying, it is placed in low-temperature plasma device, under oxygen atmosphere, fabric that Low Temperature Plasma Treating is pre-processed；Fabric is impregnated under the drive of forming machine by maceration extract, completion again, unnecessary maceration extract is then shut out by roll again；Then by the shell fabric after padding at 80 95 DEG C the 8min of preliminary drying 5；It is then placed in training baking machine and carries out training baking processing, 110 120 DEG C of temperature is dried in training, and locomotive speed is 40 50m/min；Then the fabric trained after drying is put into forming machine and carries out heat treatment, 115 DEG C of setting temperature, locomotive speed is 55 65m/min；Fabric is wound after finally sizing is terminated.The invention provides a kind of preparation method of resistance to washing oil sense coating fabric, this method is used for fabric final finishing, realizes existing oil sense and has the characteristics of fastness, and realizing has durable washing oil sense effect.

Description

A kind of preparation method of resistance to washing oil sense coating fabric
Technical field
The present invention relates to a kind of preparation method of resistance to washing oil sense coating fabric, belong to textile processing field.
Technical background
Fabric final finishing is to improve outward appearance and feel, the enhancement wearability or tax of fabric by main method chemically or physically The technical process of specific function is given, is the process of textile " making something perfect even more perfect ".The development court of present fabric final finishing technology Product function, differential, superior, processing technology variation, depth direction are developed, and emphasize to improve taking for product Performance, increase value-added content of product.In recent years, constantly introduced from other technologies field and use for reference various new technologies, added with improving Work depth, obtain good running product.With mankind's environmental pollution and the concern destroyed, health is increasingly paid attention to, carried " low-carbon " economy is advocated, final finishing technical requirements carry out environmentally friendly " green " processing, production " cleaning ", the textile product of " low-carbon ".Face The basic afterfinish method of material has：Stable dimensions, improve outward appearance method for sorting, improve feel optimization performance method for sorting, The arrangement for making fabric obtain multi-functional, high added value method for sorting, make the advanced method for sorting of fabric, meet particular/special requirement Method.
In recent years, piece market increases the demand of oil sense coating adhesive year by year, is mainly used in cowboy style easy suit Processing.Prior art makes weaving face fabric realize that oil sense effect is utilized in spun bonded agent directly addition oily substance compounding Final finishing processing is carried out to weaving face fabric afterwards, but oil sense effect gradually fades away after family washes, without good wash resistant Property, textile finishing effect is not lasting, complex process, increases cost, so as to limit the popularization in market.And with environmental protection and The it is proposed of comprehensive utilization of energy problem, finishing agent develop towards low energy consumption, free of contamination direction.Because different finishing agents can produce Raw different effect, therefore suitable finishing agent and its addition agent aid etc. are selected, Optimizing Technical, it is to improve the resistance to washing oil of fabric Feel the key of finishing effect.Only by selecting suitable finishing agent and additive, process optimization, oil sense washable to fabric are carried out Arrange, can just reach the requirement of advanced dress ornament.
The content of the invention
In view of the above-mentioned deficiencies in the prior art, it is an object of the present invention to provide a kind of preparation side of resistance to washing oil sense coating fabric Method.
The present invention is achieved by the following technical solutions：A kind of preparation method of resistance to washing oil sense coating fabric, including with Lower step：
（1）After the surface of fabric is cleaned into drying, it is placed in low-temperature plasma device, under oxygen atmosphere, low-temperature plasma Body handles the fabric pre-processed；
（2）Fabric is impregnated under the drive of forming machine by maceration extract, completion, unnecessary dipping is then shut out by roll again Liquid；The maceration extract is made up of the component of following parts by weight：Styrene-acrylic emulsion 15-16 parts, seven water sodium sulfite 4-7 parts, dehydration Sorbitol monooleate 18-22 parts, tertiary ethylene carbonate 5-10 parts, ethylene glycol 22-25 parts, 1,2- benzisothiazole-3-ketones 4-8 parts, tung oil 1-3 parts, PDDA 3-7 parts, morpholine Anaesthetie Ether 5-8 parts, dihydroxymethyl dihydroxy second Alkene urea 1-6 parts, rice bran wax 1-2 parts, the pick-up are 70-80%；
（3）By the shell fabric after padding at 80-95 DEG C preliminary drying 5-8min；It is then placed in training baking machine and carries out training baking processing, 110-120 DEG C of temperature is dried in training, and locomotive speed is 40-50m/min；Then the fabric trained after drying is put into forming machine and carried out at sizing Reason, 115 DEG C of setting temperature, locomotive speed is 55-65m/min；Fabric is wound after finally sizing is terminated.
Further, in the step (1), the power of Low Temperature Plasma Treating is 350-500W, time 30-60s.
Further, the ph values for padding the maceration extract in step are controlled in 6.0-7.5.
Further, the maceration extract is made up of the component of following parts by weight：1.5 parts of styrene-acrylic emulsion, seven water sulfurous acid 5.5 parts of sodium, 20 parts of sorbitan monooleate, 7.5 parts of tertiary ethylene carbonate, 23.5 parts of ethylene glycol, 1,2- benzisothiazoles 6 parts of quinoline -3- ketone, 2 parts of tung oil, 5 parts of PDDA, 6.5 parts of morpholine Anaesthetie Ether, dihydroxymethyl dihydroxy second 3.5 parts of alkene urea, 1.5 parts of rice bran wax.
Further, the pick-up is 75%.
Beneficial effect：The invention provides a kind of preparation method of resistance to washing oil sense coating fabric, and this method is for after fabric Arrange, realize existing oil sense and have the characteristics of fastness, realizing has durable washing oil sense effect.
Embodiment
Example of the present invention is the description of the invention and can not limit the present invention, in the implication suitable with the present invention Any change and adjustment with scope, are all considered as within the scope of the invention.
Embodiment 1
A kind of preparation method of resistance to washing oil sense coating fabric, comprises the following steps：
（1）After the surface of fabric is cleaned into drying, it is placed in low-temperature plasma device, under oxygen atmosphere, low-temperature plasma Body handles the fabric pre-processed；The power of Low Temperature Plasma Treating is 350-500W, time 30-60s.
（2）Fabric is impregnated under the drive of forming machine by maceration extract, completion, unnecessary leaching is then shut out by roll again Stain liquid；The maceration extract is made up of the component of following parts by weight：15 parts of styrene-acrylic emulsion, 4 parts of seven water sodium sulfite, Sorbitan It is 18 parts of alcohol monoleate, 5 parts of tertiary ethylene carbonate, 22 parts of ethylene glycol, 4 parts of 1,2- benzisothiazole-3-ketones, 1 part of tung oil, poly- 3 parts of dimethyl diallyl ammonium chloride, 5 parts of morpholine Anaesthetie Ether, 1 part of dihydroxymethyl dihydroxy ethylene urea, 1 part of rice bran wax, it is described Pick-up is 70-80%；The ph values for padding the maceration extract in step are controlled in 6.0-7.5.
（3）By the shell fabric after padding at 80-95 DEG C preliminary drying 5-8min；It is then placed in training baking machine and train at baking 110-120 DEG C of temperature is dried in reason, training, and locomotive speed is 40-50m/min；Then the fabric trained after drying is put into forming machine and determined Type processing, 115 DEG C of setting temperature, locomotive speed is 55-65m/min；Fabric is wound after finally sizing is terminated.
Embodiment 2
A kind of preparation method of resistance to washing oil sense coating fabric, comprises the following steps：
（1）After the surface of fabric is cleaned into drying, it is placed in low-temperature plasma device, under oxygen atmosphere, low-temperature plasma Body handles the fabric pre-processed；The power of Low Temperature Plasma Treating is 350-500W, time 30-60s.
（2）Fabric is impregnated under the drive of forming machine by maceration extract, completion, unnecessary leaching is then shut out by roll again Stain liquid；The maceration extract is made up of the component of following parts by weight：16 parts of styrene-acrylic emulsion, 7 parts of seven water sodium sulfite, Sorbitan 22 parts of alcohol monoleate, 10 parts of tertiary ethylene carbonate, 25 parts of ethylene glycol, 8 parts of 1,2- benzisothiazole-3-ketones, 3 parts of tung oil, 7 parts of PDDA, 8 parts of morpholine Anaesthetie Ether, 6 parts of dihydroxymethyl dihydroxy ethylene urea, 2 parts of rice bran wax, institute It is 70-80% to state pick-up；The ph values for padding the maceration extract in step are controlled in 6.0-7.5.
（3）By the shell fabric after padding at 80-95 DEG C preliminary drying 5-8min；It is then placed in training baking machine and train at baking 110-120 DEG C of temperature is dried in reason, training, and locomotive speed is 40-50m/min；Then the fabric trained after drying is put into forming machine and determined Type processing, 115 DEG C of setting temperature, locomotive speed is 55-65m/min；Fabric is wound after finally sizing is terminated.
Embodiment 3
A kind of preparation method of resistance to washing oil sense coating fabric, comprises the following steps：
（1）After the surface of fabric is cleaned into drying, it is placed in low-temperature plasma device, under oxygen atmosphere, low-temperature plasma Body handles the fabric pre-processed；The power of Low Temperature Plasma Treating is 350-500W, time 30-60s.
（2）Fabric is impregnated under the drive of forming machine by maceration extract, completion, unnecessary leaching is then shut out by roll again Stain liquid；The maceration extract is made up of the component of following parts by weight：1.5 parts of styrene-acrylic emulsion, 5.5 parts of seven water sodium sulfite, dehydration 20 parts of sorbitol monooleate, 7.5 parts of tertiary ethylene carbonate, 23.5 parts of ethylene glycol, 6 parts of 1,2- benzisothiazole-3-ketones, paulownia 2 parts of oil, 5 parts of PDDA, 6.5 parts of morpholine Anaesthetie Ether, dihydroxymethyl dihydroxy ethylene urea 3.5 part, meter 1.5 parts of chaff wax, the pick-up are 70-80%；The ph values for padding the maceration extract in step are controlled in 6.0-7.5.
（3）By the shell fabric after padding at 80-95 DEG C preliminary drying 5-8min；It is then placed in training baking machine and train at baking 110-120 DEG C of temperature is dried in reason, training, and locomotive speed is 40-50m/min；Then the fabric trained after drying is put into forming machine and determined Type processing, 115 DEG C of setting temperature, locomotive speed is 55-65m/min；Fabric is wound after finally sizing is terminated.

Claims (5)

1. a kind of preparation method of resistance to washing oil sense coating fabric, it is characterised in that the described method comprises the following steps：
（1）After the surface of fabric is cleaned into drying, it is placed in low-temperature plasma device, under oxygen atmosphere, low-temperature plasma Body handles the fabric pre-processed；
（2）Fabric is impregnated under the drive of forming machine by maceration extract, completion, unnecessary dipping is then shut out by roll again Liquid；The maceration extract is made up of the component of following parts by weight：Styrene-acrylic emulsion 15-16 parts, seven water sodium sulfite 4-7 parts, dehydration Sorbitol monooleate 18-22 parts, tertiary ethylene carbonate 5-10 parts, ethylene glycol 22-25 parts, 1,2- benzisothiazole-3-ketones 4-8 parts, tung oil 1-3 parts, PDDA 3-7 parts, morpholine Anaesthetie Ether 5-8 parts, dihydroxymethyl dihydroxy second Alkene urea 1-6 parts, rice bran wax 1-2 parts, the pick-up are 70-80%；
（3）By the shell fabric after padding at 80-95 DEG C preliminary drying 5-8min；It is then placed in training baking machine and carries out training baking processing, 110-120 DEG C of temperature is dried in training, and locomotive speed is 40-50m/min；Then the fabric trained after drying is put into forming machine and carried out at sizing Reason, 115 DEG C of setting temperature, locomotive speed is 55-65m/min；Fabric is wound after finally sizing is terminated.
A kind of 2. preparation method of resistance to washing oil sense coating fabric according to claim 1, it is characterised in that：The maceration extract It is made up of the component of following parts by weight：1.5 parts of styrene-acrylic emulsion, 5.5 parts of seven water sodium sulfite, sorbitan monooleate 20 Part, 7.5 parts of tertiary ethylene carbonate, 23.5 parts of ethylene glycol, 6 parts of 1,2- benzisothiazole-3-ketones, 2 parts of tung oil, poly dimethyl two 5 parts of allyl ammonium chloride, 6.5 parts of morpholine Anaesthetie Ether, 3.5 parts of dihydroxymethyl dihydroxy ethylene urea, 1.5 parts of rice bran wax.
A kind of 3. preparation method of resistance to washing oil sense coating fabric according to claim 1, it is characterised in that：The step (1) in, the power of Low Temperature Plasma Treating is 350-500W, time 30-60s.
A kind of 4. preparation method of resistance to washing oil sense coating fabric according to claim 1, it is characterised in that：It is described to pad step The ph values of maceration extract in rapid are controlled in 6.0-7.5.
A kind of 5. preparation method of resistance to washing oil sense coating fabric according to claim 1, it is characterised in that：The pick-up For 75%.
CN201711237684.7A 2017-11-30 2017-11-30 A kind of preparation method of resistance to washing oil sense coating fabric Withdrawn CN107841867A (en)