CN107813881A - 一种防锈的履带底盘 - Google Patents
一种防锈的履带底盘 Download PDFInfo
- Publication number
- CN107813881A CN107813881A CN201710855674.3A CN201710855674A CN107813881A CN 107813881 A CN107813881 A CN 107813881A CN 201710855674 A CN201710855674 A CN 201710855674A CN 107813881 A CN107813881 A CN 107813881A
- Authority
- CN
- China
- Prior art keywords
- parts
- crawler body
- antirust
- raw material
- drying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明提出了一种防锈的履带底盘,在履带底盘上涂覆一层保护层,涂覆方法如下:(1)在履带底盘的外表面上进行喷砂处理;(2)称取原材料:按重量份数计称取环氧树脂15‑28份、异氰酸酯3‑5.6份、二甲苯0.5‑3.2份、二氧化硅2‑6份、乙醇8‑15份、消泡剂0.03‑0.08份、光引发剂0.8‑1.2份;(3)将原材料在40‑55℃的温度下搅拌均匀后涂覆在履带底盘的外表面上,烘干即可,有效防锈,提高了使用寿命。
Description
技术领域
本发明涉及一种履带底盘,具体涉及一种防锈的履带底盘。
背景技术
履带底盘是用于支撑车辆底盘各部件并保证车辆正常行驶的装 置。履带底盘具有牵引力大、接地比压低、稳定性好、爬坡能力强等 优点因此在建筑机械、筑路机械及农业机械等领域广泛应用。在农用 机械领域中,由于其能够适应耕种及具有淤泥的土地,因此在旋耕机 和收割机等农用机构中广泛使用。
现有的履带底盘容易生锈,影响车辆的正常使用。
发明内容
本发明针对上述问题提出了一种防锈的履带底盘,有效防锈,提高了使用寿命。
具体的技术方案如下:
一种防锈的履带底盘,在履带底盘上涂覆一层保护层,涂覆方法如下:
(1)在履带底盘的外表面上进行喷砂处理;
(2)称取原材料:按重量份数计称取环氧树脂15-28份、异氰酸酯3-5.6份、二甲苯0.5-3.2份、二氧化硅2-6份、乙醇8-15份、消泡剂0.03-0.08份、光引发剂0.8-1.2份;
(3)将原材料在40-55℃的温度下搅拌均匀后涂覆在履带底盘的外表面上,烘干即可。
进一步的,所述环氧树脂和异氰酸酯的重量份数比为5:1。
进一步的,所述烘干的温度为100-130℃,烘干时间为10-24h。
本发明的有益效果为:本发明有效防锈,提高了使用寿命。
具体实施方式
为使本发明的技术方案更加清晰明确,下面对本发明进行进一步描述,任何对本发明技术方案的技术特征进行等价替换和常规推理得出的方案均落入本发明保护范围。
实施例一
一种防锈的履带底盘,在履带底盘上涂覆一层保护层,涂覆方法如下:
(1)在履带底盘的外表面上进行喷砂处理;
(2)称取原材料:按重量份数计称取环氧树脂22份、异氰酸酯4.4份、二甲苯2份、二氧化硅5份、乙醇10份、消泡剂0.05份、光引发剂1份;
(3)将原材料在40-55℃的温度下搅拌均匀后涂覆在履带底盘的外表面上,烘干即可。
进一步的,所述环氧树脂和异氰酸酯的重量份数比为5:1。
进一步的,所述烘干的温度为100-130℃,烘干时间为10-24h。
实施例二
一种防锈的履带底盘,在履带底盘上涂覆一层保护层,涂覆方法如下:
(1)在履带底盘的外表面上进行喷砂处理;
(2)称取原材料:按重量份数计称取环氧树脂15份、异氰酸酯3份、二甲苯0.5份、二氧化硅2份、乙醇8份、消泡剂0.03份、光引发剂0.8份;
(3)将原材料在40-55℃的温度下搅拌均匀后涂覆在履带底盘的外表面上,烘干即可。
进一步的,所述环氧树脂和异氰酸酯的重量份数比为5:1。
进一步的,所述烘干的温度为100-130℃,烘干时间为10-24h。
实施例三
一种防锈的履带底盘,在履带底盘上涂覆一层保护层,涂覆方法如下:
(1)在履带底盘的外表面上进行喷砂处理;
(2)称取原材料:按重量份数计称取环氧树脂28份、异氰酸酯5.6份、二甲苯3.2份、二氧化硅6份、乙醇15份、消泡剂0.08份、光引发剂1.2份;
(3)将原材料在40-55℃的温度下搅拌均匀后涂覆在履带底盘的外表面上,烘干即可。
进一步的,所述环氧树脂和异氰酸酯的重量份数比为5:1。
进一步的,所述烘干的温度为100-130℃,烘干时间为10-24h。
Claims (3)
1.一种防锈的履带底盘,其特征为,在履带底盘上涂覆一层保护层,涂覆方法如下:
(1)在履带底盘的外表面上进行喷砂处理;
(2)称取原材料:按重量份数计称取环氧树脂15-28份、异氰酸酯3-5.6份、二甲苯0.5-3.2份、二氧化硅2-6份、乙醇8-15份、消泡剂0.03-0.08份、光引发剂0.8-1.2份;
(3)将原材料在40-55℃的温度下搅拌均匀后涂覆在履带底盘的外表面上,烘干即可。
2.如权利要求1所述的一种防锈的履带底盘,其特征为,所述环氧树脂和异氰酸酯的重量份数比为5:1。
3.如权利要求1所述的一种防锈的履带底盘,其特征为,所述烘干的温度为100-130℃,烘干时间为10-24h。