CN107805732A - A kind of new alloy material for electric heater - Google Patents
A kind of new alloy material for electric heater Download PDFInfo
- Publication number
- CN107805732A CN107805732A CN201710992094.9A CN201710992094A CN107805732A CN 107805732 A CN107805732 A CN 107805732A CN 201710992094 A CN201710992094 A CN 201710992094A CN 107805732 A CN107805732 A CN 107805732A
- Authority
- CN
- China
- Prior art keywords
- electric heater
- alloy material
- new alloy
- percentage
- strength
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
There is a kind of new alloy material for electric heater of the invention good thermal conductivity simultaneously, to have higher elevated temperature strength and hardness, and the high-strength high-conductivity heat-resistant copper and its manufacture method of elongation percentage well again with wear resistance.Its chemical composition (percentage by weight) is:Cr:0.3~1.1%, Zr:0.05~0.4%, W:0.06~0.12%, V:0.03~0.11%, Nb:0.04~0.1%, Mg:0.02~0.05%, Ce:0.02~0.07%, Y:0.02~0.05%, Cu:Surplus.
Description
Technical field
The present invention relates to alloy material preparing technical field, and in particular to a kind of novel alloy material for electric heater
Material.
Background technology
At present, electrical heating utensil, such as Electric radiant Heating Film enamelware pot, Electric radiator etc or duct type water heater etc. are sent out rapidly
Exhibition.Electric radiant Heating Film on electrical heating utensil, usually using conducting film made of the materials such as chloride.This Electric radiant Heating Film is due to same
Utensil or pipeline external surface can not combine closely integrally, and its heat conduction efficiency is not high enough causes Electric radiant Heating Film red-hot in itself
Rubescent temperature is very high.Therefore, the electric heating film service life made of this material is limited, and the thermal efficiency is not also high.
The content of the invention
In order to overcome the above mentioned problem of existing electric heating material, it is an object of the invention to provide one kind to be used for electric heater
New alloy material there is good thermal conductivity and wear resistance to have higher elevated temperature strength and hardness again simultaneously, with
And the high-strength high-conductivity heat-resistant copper and its manufacture method of good elongation percentage.
To reach above-mentioned purpose, according to a kind of new alloy material for electric heater of the present invention, a kind of high-strength height
Lead Heat-resisting Copper Alloy And Manufacturing Approach.Its chemical composition (percentage by weight) is:Cr:0.3~1.1%, Zr:0.05~
0.4%, W:0.06~0.12%, V:0.03~0.11%, Nb:0.04~0.1%, Mg:0.02~0.05%, Ce:0.02~
0.07%, Y:0.02~0.05%, Cu:Surplus.
A kind of preparation method of new alloy material for electric heater of the present invention comprises the following steps:
1st, copper is melted with heating furnace and is warming up to 1260~1400 DEG C, addition metal Cr, Zr, W, 20~30 points of insulation
Clock;
2nd, after pulling clinker out, V, Nb, Mg, Cu, Y and Ce alloy is added and is stirred.Then tapping casting, and control stove
Temperature is at 1300~1350 DEG C;
3rd, casting is forged as needed or pressure processing is into parts, parts are then heated to 965~985 DEG C of guarantors
Warm 1~2 hour hardening, then be incubated 2~3 hours at a temperature of 465~490 DEG C and carry out Ageing Treatment.
Beneficial effect:It is an object of the invention to provide a kind of new alloy material for electric heater to have well
Thermal conductivity simultaneously, has higher elevated temperature strength and hardness, and the high-strength highly-conductive of elongation percentage well again with wear resistance
Heat-resisting Copper Alloy And Manufacturing Approach.
Embodiment
Embodiment 1
A kind of new alloy material for electric heater, a kind of high-strength high-conductivity heat-resistant copper and its manufacture method.Its
Chemical composition (percentage by weight) is:Cr:1.1%, Zr:0.4%, W:0.12%, V:0.11%, Nb:0.1%, Mg:
0.05%, Ce:0.07%, Y:0.05%, Cu:Surplus.
A kind of preparation method of new alloy material for electric heater of the present invention comprises the following steps:
1st, copper is melted with heating furnace and is warming up to 1400 DEG C, addition metal Cr, Zr, W, insulation 30 minutes;
2nd, after pulling clinker out, V, Nb, Mg, Cu, Y and Ce alloy is added and is stirred.Then tapping casting, and control stove
Temperature is at 1350 DEG C;
3rd, casting is forged as needed or pressure processing is into parts, it is small that parts are then heated to 985 DEG C of insulations 2
When hardening, then be incubated at a temperature of 490 DEG C 3 hours and carry out Ageing Treatment.
Embodiment 2
A kind of new alloy material for electric heater, a kind of high-strength high-conductivity heat-resistant copper and its manufacture method.Its
Chemical composition (percentage by weight) is:Cr:0.3%, Zr:0.05%, W:0.06%, V:0.11%, Nb:0.1%, Mg:
0.02%, Ce:0.02~0.07%, Y:0.02%, Cu:Surplus.
A kind of preparation method of new alloy material for electric heater of the present invention comprises the following steps:
1st, copper is melted with heating furnace and is warming up to 1400 DEG C, addition metal Cr, Zr, W, insulation 30 minutes;
2nd, after pulling clinker out, V, Nb, Mg, Cu, Y and Ce alloy is added and is stirred.Then tapping casting, and control stove
Temperature is at 1350 DEG C;
3rd, casting is forged as needed or pressure processing is into parts, it is small that parts are then heated to 985 DEG C of insulations 1
When hardening, then be incubated at a temperature of 490 DEG C 3 hours and carry out Ageing Treatment.
Embodiment 3
A kind of new alloy material for electric heater, a kind of high-strength high-conductivity heat-resistant copper and its manufacture method.Its
Chemical composition (percentage by weight) is:Cr:1%, Zr:0.25%, W:0.1%, V:0.1%, Nb:0.1%, Mg:0.03%,
Ce:0.05%, Y:0.04%, Cu:Surplus.
A kind of preparation method of new alloy material for electric heater of the present invention comprises the following steps:
1st, copper is melted with heating furnace and is warming up to 1300 DEG C, addition metal Cr, Zr, W, insulation 30 minutes;
2nd, after pulling clinker out, V, Nb, Mg, Cu, Y and Ce alloy is added and is stirred.Then tapping casting, and control stove
Temperature is at 1320 DEG C;
3rd, casting is forged as needed or pressure processing is into parts, parts are then heated to 965~985 DEG C of guarantors
Warm 1~2 hour hardening, then be incubated 2~3 hours at a temperature of 480 DEG C and carry out Ageing Treatment.
Although the present invention is described in detail with reference to the foregoing embodiments, for those skilled in the art,
It can still modify to the technical scheme described in foregoing embodiments, or which part technical characteristic is carried out etc.
With replacing, within the spirit and principles of the invention, any modification, equivalent substitution and improvements made etc., this should be included in
Within the protection domain of invention.
Claims (2)
- A kind of 1. new alloy material for electric heater, it is characterised in that the alloy composition (percentage by weight) For:Cr:0.3~1.1%, Zr:0.05~0.4%, W:0.06~0.12%, V:0.03~0.11%, Nb:0.04~0.1%, Mg:0.02~0.05%, Ce:0.02~0.07%, Y:0.02~0.05%, Cu:Surplus.
- A kind of 2. new alloy material for electric heater according to right wants 1, it is characterised in that the alloy Composition (percentage by weight) is:Cr:0.3%, Zr:0.4%, W:0.06%, V:0.11%, Nb:0.1%, Mg:0.05%, Ce: 0.02%, Y:0.02%, Cu:Surplus.