CN107794519A - A kind of curved draped method based on nano spray plating - Google Patents
A kind of curved draped method based on nano spray plating Download PDFInfo
- Publication number
- CN107794519A CN107794519A CN201711080453.XA CN201711080453A CN107794519A CN 107794519 A CN107794519 A CN 107794519A CN 201711080453 A CN201711080453 A CN 201711080453A CN 107794519 A CN107794519 A CN 107794519A
- Authority
- CN
- China
- Prior art keywords
- nano spray
- spray plating
- nano
- film
- plating liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of curved draped method based on nano spray plating, it is characterised in that：Comprise the following steps：Step 1: surface preparation；Step 2: nano spray plating：The nano spray plating solution without silver nitrate is prepared, is dried the nano spray plating solution spraying to workpiece surface, conventional cleaning using spray gun；It is Step 3: curved draped：a）The making of water coating transfer film；b）Film paper enters water；c）Transfer；d）Washing；e）Drying；f）Gloss oil；g）Dry.The present invention, as curved draped bottom, can be caused curved draped figure layer adhesive force to greatly improve, can be widely applied to the industries such as bathroom using the nano spray plating solution without silver nitrate.
Description
Technical field
The present invention relates to the technical field of surface treatment, more particularly to a kind of curved draped method based on nano spray plating.
Background technology
Nano spray plating, it is to utilize silver mirror reaction, silver ammino solution is sprayed on into workpiece surface using spray gun forms bloom minute surface
A process.Using the technology spray product, have excellent adhesive force, anti-impact force, corrosion resistance, against weather,
Wearability and marresistance, there is good rustless property, be generally used for sanitary ware industry, domestic and international full-sized car manufacturer and big
The surface treatment of the sophisticated products such as type electrical equipment manufacturer, it can act also as the sprayings such as incrustation and the protection of other industries, technique
Simply, it is green, widely used, be a kind of high-new process for treating surface.
It is curved draped, it is using the water in a kind of dissolve easily in water using coating transfer technique (Cubic Transfer)
Property film carries
Picture and text, because water-based membrane tension is splendid, it is easy to be wound in product surface formed picture and text layer, product surface just as
Spray painting equally obtains completely different outward appearance.It is coated on the workpiece of any shape, solves stereo product printing for manufacturer
Problem.It is curved draped also to add different lines, such as dermatoglyph wood grains emeralds line and marble line, while also may be used in product surface
Keep away diastema often existing in the general space of a whole page stamp of color.In the prior art, the curved draped pattern for causing attachment is easy to because slight
Scraping and it is damaged.
In view of this, the present inventor studies and devises a kind of curved draped method based on nano spray plating, and this case is thus
Produce.
The content of the invention
It is an object of the invention to provide a kind of curved draped method based on nano spray plating, the present invention uses nano spray plating
As curved draped bottom, to cause curved draped figure layer adhesive force more firm.
To achieve these goals, the technical scheme adopted by the invention to solve the technical problem is that：
A kind of curved draped method based on nano spray plating, comprises the following steps：
Step 1: surface preparation：Surface preparation is carried out to workpiece to be processed, removes the ash on workpiece to be processed surface
Dirt, grease；For plastic workpiece, electrostatic precipitation processes are carried out；For there are the metal works of corrosion, the oxidation on its surface is removed
Thing；
Step 2: nano spray plating：The nano spray plating solution without silver nitrate is prepared, using spray gun by the nano spray plating
Solution spraying is dried to workpiece surface, conventional cleaning；
It is Step 3: curved draped：A) making of water coating transfer film, in macromolecule membrane needed for the method for gravure stamps
Picture and text；B) film paper enters water, and, tile 1-2min in water transfer film picture and text upward, treats its flattening；C) transfer, workpiece is pressed close to
The film of activation, picture and text layer are slowly transferred on workpiece, 20-35 DEG C of water temperature, and transfer speed is uniform；D) wash, by workpiece
Take out, mix up hydraulic pressure, residual film and floating layer are cleaned on cleaning machine；E) dry, carried out on dryer, 40-60 DEG C of temperature；F) light
Oil, transfer thing surface spray one layer of gloss oil, protect the decorative pattern of object surface, make body surface glossy；G) dry.
As the preferred embodiment of embodiment, in the step 2, in addition to surfactant solution is prepared, in spraying nanometer
Before spraying plating solution, surfactant solution is sprayed into workpiece surface；
As the preferred embodiment of embodiment, the preparation method of the surfactant solution is often to prepare 5 kilograms of activation
Liquid, take 76-84 grams of stannous chloride, the hydrochloric acid 59-67 milliliters that volume fraction is 38%, distilled water 4750-5250 milliliters, will be above-mentioned
Three is well mixed, and activating solution is made, and stands 8 hours, stand-by.
As the preferred embodiment of embodiment, in the step 2, the preparation method of the nano spray plating solution is, prepares the
A kind of nano spray plating liquid：2.5 kilograms of the first nano spray plating liquid are often prepared, take 1.235-1.365 grams of silver sulfate, sulfate of ammoniac 3.8-
4.2 grams, distilled water 2375-2625 milliliters, above-mentioned three is well mixed, the first nano spray plating liquid is made, it is stand-by；Prepare the
Two kinds of nano spray plating liquid：2.5 kilograms of second of nano spray plating liquid are often prepared, take 10.45-11.55 grams of sodium hydroxide, volume fraction
For 25% ammoniacal liquor 190-210 milliliters, distilled water 2375-2625 milliliters, above-mentioned three is well mixed, is made second nanometer
Plating liquid, it is stand-by；Prepare the third nano spray plating liquid：5 kilograms of the third nano spray plating liquid are often prepared, take hydrazine sulfate 47.5-
52.5 grams, distilled water 4750-5250 milliliters are stand-by by both above-mentioned well mixed, the third obtained nano spray plating liquid.
As the preferred embodiment of embodiment, in the step 3 a), the macromolecule membrane is polyvinyl alcohol film.
As the preferred embodiment of embodiment, in the step 3 b), after its flattening after, include spray can make film dissolving but
The activator of film curing ink is not destroyed.
Because present invention employs above-mentioned technical scheme so that the invention has the advantages that：
The present inventor is in production practices, it has unexpectedly been found that is draped over one's shoulders using the nano spray plating solution without silver nitrate as curved surface
The bottom covered, curved draped figure layer adhesive force can be caused to greatly improve, the development of curved draped technology is greatly facilitated.
Embodiment
The metal of embodiment 1 flower shines curved draped
A kind of metal flower shines the curved draped method of product, comprises the following steps：
Step 1: surface preparation：
Metal is spent to shine and carries out surface preparation, removes dust, grease that metal flower shines, the oxide on surface；
Step 2: nano spray plating：
Surfactant solution is prepared, surfactant solution is sprayed into metal flower shines surface；The surfactant
The preparation method of solution is, often prepares 5 kilograms of activating solutions, take 76 grams of stannous chloride, 59 milliliters of the hydrochloric acid that volume fraction is 38%,
4750 milliliters of distilled water, above-mentioned three is well mixed, and activating solution is made, and stands 8 hours, stand-by；
The nano spray plating solution without silver nitrate is prepared, is spent the nano spray plating solution spraying to metal using spray gun
Shine surface, conventional cleaning drying；The preparation method of the nano spray plating solution is to prepare the first nano spray plating liquid：Often prepare
2.5 kilograms of the first nano spray plating liquid, take 1.235 grams of silver sulfate, 3.8 grams of sulfate of ammoniac, 2375 milliliters of distilled water, by above-mentioned three
It is well mixed, the first nano spray plating liquid is made, it is stand-by；Prepare second of nano spray plating liquid：Often 2.5 kilograms are prepared to receive for second
Rice plating liquid, 10.45 grams of sodium hydroxide is taken, volume fraction is 25% 190 milliliters of ammoniacal liquor, and 2375 milliliters of distilled water will be above-mentioned
Three is well mixed, and second of nano spray plating liquid is made, stand-by；Prepare the third nano spray plating liquid：Often prepare 5 kilograms the third
Nano spray plating liquid, take 47.5 grams of hydrazine sulfate, 4750 milliliters of distilled water, by both above-mentioned well mixed, obtained the third nanometer sprays
Plating solution, it is stand-by；
It is Step 3: curved draped：
A) making of water coating transfer film, required picture and text are stamped with the method for gravure in polyvinyl alcohol film；B) film paper enters
Water, tile 1-2min in water transfer film picture and text upward, treats its flattening；Film dissolving can be made but not destroy film curing ink by spraying
Activator；C) transfer, metal flower is shone to the film of activation, picture and text layer is slowly transferred on workpiece, water temperature 20-35
DEG C, transfer speed is uniform；D) wash, metal is spent to shine and taken out, mixes up hydraulic pressure, residual film and floating layer are cleaned on cleaning machine；e)
Drying, is carried out, 40-60 DEG C of temperature on dryer；F) gloss oil, transfer thing surface spray one layer of gloss oil, protect the flower of object surface
Line, make body surface glossy；G) dry.
The ceramic cup of embodiment 2 it is curved draped
A kind of curved draped method of ceramic cup, comprises the following steps：
Step 1: surface preparation：
Surface preparation is carried out to ceramic cup, removes electrostatic, dust, the grease on ceramic cup surface；
Step 2: nano spray plating：
Surfactant solution is prepared, surfactant solution is sprayed into workpiece surface；The surfactant solution
Preparation method be, often prepare 5 kilograms of activating solutions, take 80 grams of stannous chloride, volume fraction be 38% 62 milliliters of hydrochloric acid, distillation
5000 milliliters of water, above-mentioned three is well mixed, and activating solution is made, and stands 8 hours, stand-by.
The nano spray plating solution without silver nitrate is prepared, using spray gun by the nano spray plating solution spraying to ceramic cup
Surface, conventional cleaning drying；The preparation method of the nano spray plating solution is to prepare the first nano spray plating liquid：Often prepare 2.5
Kilogram the first nano spray plating liquid, 1.3 grams of silver sulfate is taken, 4 grams of sulfate of ammoniac, 2450 milliliters of distilled water, above-mentioned three is mixed equal
It is even, the first nano spray plating liquid is made, it is stand-by；Prepare second of nano spray plating liquid：Often prepare 2.5 kilograms of second of nano spray platings
Liquid, 11 grams of sodium hydroxide is taken, volume fraction is 25% 200 milliliters of ammoniacal liquor, 2450 milliliters of distilled water, above-mentioned three is mixed equal
It is even, second of nano spray plating liquid is made, it is stand-by；Prepare the third nano spray plating liquid：Often prepare 5 kilograms of the third nano spray platings
Liquid, 50 grams of hydrazine sulfate is taken, 5000 milliliters of distilled water will be both above-mentioned well mixed, and the third nano spray plating liquid is made, stand-by.
It is Step 3: curved draped：A) making of water coating transfer film, institute is stamped with the method for gravure in polyvinyl alcohol film
Need picture and text；B) film paper enters water, and, tile 1-2min in water transfer film picture and text upward, treats its flattening；Spray can make film dissolve but
The activator of film curing ink is not destroyed；C) transfer, ceramic cup is pressed close to the film of activation, picture and text layer is slowly transferred to ceramic cup
On, 20-35 DEG C of water temperature, transfer speed will be uniformly；D) wash, ceramic cup is taken out, mixes up hydraulic pressure, residual film is cleaned on cleaning machine
With floating layer；E) dry, carried out on dryer, 40-60 DEG C of temperature；F) gloss oil, transfer thing surface spray one layer of gloss oil, protect object
The decorative pattern on surface, make body surface glossy；G) dry.
The plastic tub of embodiment 3 it is curved draped
A kind of curved draped method of plastic tub, comprises the following steps：
Step 1: surface preparation：
Surface preparation is carried out to plastic tub, removes electrostatic, dust, the grease on plastic tub surface；
Step 2: nano spray plating：
Surfactant solution is prepared, before nano spray plating solution is sprayed, surfactant solution is sprayed into plastic tub
Surface；The preparation method of the surfactant solution is often to prepare 5 kilograms of activating solutions, take 84 grams of stannous chloride, volume fraction
For 38% 67 milliliters of hydrochloric acid, 5250 milliliters of distilled water, above-mentioned three is well mixed, activating solution is made, 8 hours is stood, treats
With；
The nano spray plating solution without silver nitrate is prepared, using spray gun by the nano spray plating solution spraying to plastic tub
Surface, conventional cleaning drying；The preparation method of the nano spray plating solution is to prepare the first nano spray plating liquid：Often prepare 2.5
Kilogram the first nano spray plating liquid, takes 1.365 grams of silver sulfate, 4.2 grams of sulfate of ammoniac, 2625 milliliters of distilled water, above-mentioned three is mixed
Uniform, the first obtained nano spray plating liquid is closed, it is stand-by；Prepare second of nano spray plating liquid：Often prepare 2.5 kilograms second nanometer
Plating liquid, takes 11.55 grams of sodium hydroxide, and volume fraction is 25% 210 milliliters of ammoniacal liquor, 2625 milliliters of distilled water, by above-mentioned three
Person is well mixed, and second of nano spray plating liquid is made, stand-by；Prepare the third nano spray plating liquid：Often prepare 5 kilograms the third receive
Rice plating liquid, take 52.5 grams of hydrazine sulfate, 5250 milliliters of distilled water, by both above-mentioned well mixed, the third obtained nano spray platings
Liquid, it is stand-by.
It is Step 3: curved draped：A) making of water coating transfer film, institute is stamped with the method for gravure in polyvinyl alcohol film
Need picture and text；B) film paper enters water, and, tile 1-2min in water transfer film picture and text upward, treats its flattening；Spray can make film dissolve but
The activator of film curing ink is not destroyed；C) transfer, plastic tub is pressed close to the film of activation, picture and text layer is slowly transferred to ceramic cup
On, 20-35 DEG C of water temperature, transfer speed will be uniformly；D) wash, plastic tub is taken out, mixes up hydraulic pressure, residual film is cleaned on cleaning machine
With floating layer；E) dry, carried out on dryer, 40-60 DEG C of temperature；F) gloss oil, transfer thing surface spray one layer of gloss oil, protect object
The decorative pattern on surface, make body surface glossy；G) dry.
The directly curved draped method of comparative example 1
A kind of metal flower shines the curved draped method of product, comprises the following steps：
Step 1: surface preparation：Using the method for such as embodiment 1.
It is Step 2: curved draped：Using the method for such as embodiment 1.
Curved draped method of the comparative example 2 based on the nano spray plating with silver nitrate
A kind of metal flower shines the curved draped method of product, comprises the following steps：
Step 1: surface preparation：
Using the method for such as embodiment 1；
Step 2: nano spray plating：
Surfactant solution is prepared, using the method for such as embodiment 1；
Preparation of nano spraying plating solution, the nano spray plating solution spraying to metal is spent using spray gun and shines surface, it is conventional
Cleaning and drying；The preparation method of the nano spray plating solution is to prepare the first nano spray plating liquid：Often prepare 2.5 kilogram first
Kind nano spray plating liquid, takes 11.4 grams of silver nitrate, 1.235 grams of silver sulfate, 3.8 grams of sulfate of ammoniac, 2375 milliliters of distilled water, by above-mentioned three
Person is well mixed, and the first nano spray plating liquid is made, stand-by；Prepare second of nano spray plating liquid：Often prepare 2.5 kilograms second
Nano spray plating liquid, 10.45 grams of sodium hydroxide is taken, volume fraction is 25% 190 milliliters of ammoniacal liquor, and 2375 milliliters of distilled water will be upper
State three to be well mixed, second of nano spray plating liquid is made, it is stand-by；Prepare the third nano spray plating liquid：Often prepare 5 kilogram the 3rd
Kind nano spray plating liquid, 47.5 grams of hydrazine sulfate is taken, 4750 milliliters of distilled water will both above-mentioned well mixed, the third obtained nanometers
Plating liquid, it is stand-by；
It is Step 3: curved draped：Using the method for such as embodiment 1.
Cross recess test is carried out according to ASTM D3359 specifications.Specifically, using knife with 1mm interval by sample levels
11 rows and 11 row are vertically cut to form the grid of each 100 grids with 1mm x 1mm (length x width) size
Lattice.Then, the CT-24 adhesive tapes produced by Nichiban companies are attached on the surface of rasterizing, then peeled off to measure
The state that surface is peeled off with adhesive tape is stated, and according to following criterion evaluation measurement result.
Standard for assessing cross score adhesive strength is as follows：
5B：The region not being stripped；
4B：The area of stripping area is less than the 5% of the gross area；
3B：The area of stripping area is the 5% to 15% of the gross area；
2B：The area of stripping area is the 15% to 35% of the gross area；
1B：The area of stripping area is the 35% to 65% of the gross area；
0B：The area of stripping area is more than the 65% of the gross area.
The adhesive strength of table 1 is tested
| Group | Adhesive strength |
| Embodiment 1 | 5B |
| Comparative example 1 | 2B |
| Comparative example 2 | 3B |
It is described above, only present pre-ferred embodiments, therefore the scope that the present invention is implemented can not be limited according to this, i.e., according to
The equivalent changes and modifications that the scope of the claims of the present invention and description are made, all should still it belong in the range of the present invention covers.
Claims (6)
- A kind of 1. curved draped method based on nano spray plating, it is characterised in that：Comprise the following steps：Step 1: surface preparation：Surface preparation is carried out to workpiece to be processed, removes dust, the oil on workpiece to be processed surface Fat；For plastic workpiece, electrostatic precipitation processes are carried out；For there are the metal works of corrosion, the oxide on its surface is removed；Step 2: nano spray plating：The nano spray plating solution without silver nitrate is prepared, using spray gun by the nano spray plating solution Spray to workpiece surface, conventional cleaning drying；It is Step 3: curved draped：a）The making of water coating transfer film, required figure is stamped with the method for gravure in macromolecule membrane Text；b）Film paper enters water, and, tile 1-2min in water transfer film picture and text upward, treats its flattening；c）Transfer, presses close to work by workpiece The film of change, picture and text layer are slowly transferred on workpiece, 20-35 DEG C of water temperature, and transfer speed is uniform；d）Washing, workpiece is taken Go out, mix up hydraulic pressure, residual film and floating layer are cleaned on cleaning machine；e）Drying, is carried out, 40-60 DEG C of temperature on dryer；f）Light Oil, transfer thing surface spray one layer of gloss oil, protect the decorative pattern of object surface, make body surface glossy；g）Dry.
- A kind of 2. curved draped method based on nano spray plating as claimed in claim 1, it is characterised in that：The step 2 In, in addition to surfactant solution is prepared, before nano spray plating solution is sprayed, surfactant solution is sprayed into workpiece table Face.
- A kind of 3. curved draped method based on nano spray plating as claimed in claim 2, it is characterised in that：The surface-active The preparation method of agent solution is often to prepare 5 kilograms of activating solutions, and it is 38% to take 76-84 grams of stannous chloride, volume fraction Hydrochloric acid 59-67 milliliters, distilled water 4750-5250 milliliters, above-mentioned three is well mixed, and activating solution is made, and it is small to stand 8 When, it is stand-by.
- A kind of 4. curved draped method based on nano spray plating as claimed in claim 1, it is characterised in that：The step 2 In, the preparation method of the nano spray plating solution is to prepare the first nano spray plating liquid：Often prepare 2.5 kilograms the first receive Rice plating liquid, 1.235-1.365 grams of silver sulfate is taken, 3.8-4.2 grams of sulfate of ammoniac, distilled water 2375-2625 milliliters will Above-mentioned three is well mixed, and the first nano spray plating liquid is made, stand-by；Prepare second of nano spray plating liquid：Often prepare 2.5 Kilogram second of nano spray plating liquid, takes 10.45-11.55 grams of sodium hydroxide, and volume fraction is 25% ammoniacal liquor 190-210 Milliliter, distilled water 2375-2625 milliliters, above-mentioned three is well mixed, and second of nano spray plating liquid is made, stand-by；Prepare The third nano spray plating liquid：5 kilograms of the third nano spray plating liquid are often prepared, take 47.5-52.5 grams of hydrazine sulfate, distilled water 4750-5250 milliliters, it is stand-by by both above-mentioned well mixed, the third obtained nano spray plating liquid.
- A kind of 5. curved draped method based on nano spray plating as claimed in claim 1, it is characterised in that：The step 3 a） In, the macromolecule membrane is polyvinyl alcohol film.
- A kind of 6. curved draped method based on nano spray plating as claimed in claim 1, it is characterised in that：The step 3 b） In, after its flattening, film dissolving can be made but not destroy the activator of film curing ink by including spraying.