CN107779869A - 一种铸铁搪瓷燃烧器及其制备工艺 - Google Patents
一种铸铁搪瓷燃烧器及其制备工艺 Download PDFInfo
- Publication number
- CN107779869A CN107779869A CN201610726392.9A CN201610726392A CN107779869A CN 107779869 A CN107779869 A CN 107779869A CN 201610726392 A CN201610726392 A CN 201610726392A CN 107779869 A CN107779869 A CN 107779869A
- Authority
- CN
- China
- Prior art keywords
- burner
- cast iron
- enamel
- preparation technology
- resistance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种铸铁搪瓷燃烧器及其制备工艺，将该燃烧器的火盖、燃烧盘和引射器等零件的内腔及其外部表面根据使用需要以及燃烧器的类型分别喷涂有搪瓷涂料层，该涂料层具有抗氧化性，增强其外表面的耐酸碱性、耐老化和抗锈蚀性。使搪瓷燃烧器处在远高于600℃的工作环境使用，甚至在明火中燃烧而不黄变、爆瓷。且更加耐酸碱、耐热震、耐高温、抗冲击，不含任何对人体有害的元素等特点。
Description
技术领域
本发明属于铸造技术领域，具体涉及一种铸铁搪瓷燃烧器及其制备工艺。
背景技术
近两年来燃气器频繁尝试国产瓷膜涂料技术，但还存在一些缺点，冷热温度较有机涂料不足，容易做到亚光到中光，但做高光很难，丰满度也差，双组份施工稍嫌复杂(涂料在喷涂前需两种液态材料搅拌混合，需经八小时的熟化)，而燃气灶的燃烧器要长时期工作在600℃以上，而且是明火，而瓷膜涂料不能满足在600℃以上的高温环境中长时间工作，不黄变、不脱落的要求。尤其现有涂料不宜作为易氧化生锈铁质燃烧器装饰材料。
发明内容
为了克服现有技术领域存在的上述技术问题，本发明的目的在于，提供一种铸铁搪瓷燃烧器及其制备工艺，采用低碳的铸铁材料，一次涂搪、一次烧制完成，搪瓷层为单层结构，工艺简单。使用中耐高温、不爆瓷、不黄变。
本发明提供的一种铸铁搪瓷燃烧器及其制备工艺，包括以下步骤：
（1）制备搪瓷釉浆；
（2）制造燃烧器，其中采用HT150至HT250的铸铁材料制造燃烧器中的燃烧盘；
（3）采用湿涂工艺在制造好的燃烧盘表面喷涂步骤（1）制备的搪瓷釉浆；
（4）将喷涂好搪瓷釉浆的燃烧盘放入炉中烧制，炉温在660℃～880℃之间，烧制时间在10分钟～20分钟之间；
（5）装配完成。
本发明提供的一种铸铁搪瓷燃烧器及其制备工艺，其有益效果在于，铸铁搪瓷燃烧器中的燃烧盘表面具有搪瓷层，燃烧器长期在高温环境中不会黄变、爆瓷、脱落。并且增强抗氧化性，增强其外表面的耐酸碱性、耐老化和抗锈蚀性。
具体实施方式
下面结合一个实施例，对本发明提供的一种铸铁搪瓷燃烧器及其制备工艺进行详细的说明。
实施例
本实施例的一种铸铁搪瓷燃烧器及其制备工艺，包括以下步骤：
（1）制备搪瓷釉浆；
（2）制造燃烧器，其中采用HT250的铸铁材料制造燃烧器中的燃烧盘；
（3）采用湿涂工艺在制造好的燃烧盘表面喷涂步骤（1）制备的搪瓷釉浆；
（4）将喷涂好搪瓷釉浆的燃烧盘放入炉中烧制，炉温为880℃，烧制时间为20分钟；
（5）装配完成。
Claims (1)
1.一种铸铁搪瓷燃烧器及其制备工艺，其特征在于：包括以下步骤：
（1）制备搪瓷釉浆；
（2）制造燃烧器，其中采用HT150至HT250的铸铁材料制造燃烧器中的燃烧盘；
（3）采用湿涂工艺在制造好的燃烧盘表面喷涂步骤（1）制备的搪瓷釉浆；
（4）将喷涂好搪瓷釉浆的燃烧盘放入炉中烧制，炉温在660℃～880℃之间，烧制时间在10分钟～20分钟之间；
（5）装配完成。