CN107779063A - Finish paint - Google Patents
Finish paint Download PDFInfo
- Publication number
- CN107779063A CN107779063A CN201711114442.9A CN201711114442A CN107779063A CN 107779063 A CN107779063 A CN 107779063A CN 201711114442 A CN201711114442 A CN 201711114442A CN 107779063 A CN107779063 A CN 107779063A
- Authority
- CN
- China
- Prior art keywords
- parts
- finish paint
- acetone
- polyethers
- defoamer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of finish paint, the various components comprising following mass fraction：High function urethane acrylate：10 30 parts；Polyethers acrylic polyester：5 15 parts；Propylene glycol diacrylate：10 20 parts；Acetone：5 10 parts；1173 light triggers：25 parts；Light initiator 184：25 parts；Ceramic:8 15 parts；Levelling agent：0.1 0.5 parts；Defoamer：0.5 1 parts.Its abrasion resistant effect is good, and easy to use, simple, speed is fast, cost-effective, meets market use demand, is advantageous to the popularization of product.
Description
Technical field
The present invention relates to a kind of finish paint.
Background technology
Present customer requirement more and more higher, conventional customer requirement second finish paint only grind 100 circles with 240# sand paper wear resistant instrument,
Abrasion will reach below 0.08g, and we do one of finish paint can and reach requirement in the case where not changing technique now.
The content of the invention
The purpose of the present invention is to propose to a kind of finish paint, and its abrasion resistant effect is good, and easy to use, simple, speed is fast, saves into
This, meets market use demand, is advantageous to the popularization of product.
In order to reach above-mentioned purpose of design, the technical solution adopted by the present invention is as follows：
A kind of finish paint, the various components comprising following mass fraction：High function urethane acrylate：10-30 parts；Polyethers
Acrylic polyester：5-15 parts；Propylene glycol diacrylate：10-20 parts；Acetone：5-10 parts；1173 light triggers：2-5 parts；Light
Initiator -184：2-5 parts；Ceramic:8-15 parts；Levelling agent：0.1-0.5 parts；Defoamer：0.5-1 parts.
Preferably, the finish paint, the various components comprising following mass fraction：High function urethane acrylate：20 parts；
Polyethers acrylic polyester：10 parts；Propylene glycol diacrylate：15 parts；Acetone：7.5 part；1173 light triggers：3.5 part；Light rises
Beginning agent -184：3.5 part；Ceramic:11.5 parts；Levelling agent：0.3 part；Defoamer：0.75 part.
The acetone obtains to be extracted in hexone.
The polyethers acrylic polyester is the polyethers acrylic polyester with ammonia.
The preparation method of the finish paint, it is specially：By high function urethane acrylate, the polyethers acrylic polyester with ammonia,
Propylene glycol diacrylate, acetone, 1173 light triggers, light initiator -184, ceramic powder, levelling agent, the order of defoamer
Reaction cylinder is sequentially added in proportion, is dispersed with stirring, you can.
The mixing speed is 1000-1200r/min, and it is 35-50 minutes to disperse the reaction time.
The beneficial effect of finish paint of the present invention is：Its abrasion resistant effect is good, and easy to use, simple, speed is fast, saves into
This, meets market use demand, is advantageous to the popularization of product.
Embodiment
Preferred embodiment of the invention is described in further detail below.
Embodiment 1：
Finish paint of the present invention, the various components comprising following mass fraction：High function urethane acrylate：10 parts；
Polyethers acrylic polyester：15 parts；Propylene glycol diacrylate：10 parts；Acetone：10 parts；1173 light triggers：2 parts；Light originates
Agent -184：5 parts；Ceramic:8 parts；Levelling agent：0.5 part；Defoamer：0.5 part.
Embodiment 2：
Finish paint of the present invention, the various components comprising following mass fraction：High function urethane acrylate：30 parts；
Polyethers acrylic polyester：5 parts；Propylene glycol diacrylate：20 parts；Acetone：5 parts；1173 light triggers：5 parts；Light initiator-
184：2 parts；Ceramic:15 parts；Levelling agent：0.1 part；Defoamer：1 part.
Embodiment 3：
The finish paint, the various components comprising following mass fraction：High function urethane acrylate：20 parts；Polyethers third
Alkene polyester：10 parts；Propylene glycol diacrylate：15 parts；Acetone：7.5 part；1173 light triggers：3.5 part；Light initiator-
184：3.5 part；Ceramic:11.5 parts；Levelling agent：0.3 part；Defoamer：0.75 part.
In above-described embodiment 1-3, the acetone obtains to be extracted in hexone.
In above-described embodiment 1-3, the polyethers acrylic polyester is the polyethers acrylic polyester with ammonia.
In above-described embodiment 1-3, the finish paint, its preparation method, it is specially：By high function urethane acrylate, band
The polyethers acrylic polyester of ammonia, propylene glycol diacrylate, acetone, 1173 light triggers, light initiator -184, ceramic powder, stream
Flat agent, the order of defoamer sequentially add reaction cylinder in proportion, are dispersed with stirring, you can.
The mixing speed is 1000-1200r/min, and it is 35-50 minutes to disperse the reaction time.
Above content is to combine the further description that specific preferred embodiment is done to the present invention, is easy to the skill
The technical staff in art field is understood that and using the present invention, it is impossible to assert that the specific implementation of the present invention is confined to these explanations.
For general technical staff of the technical field of the invention, it can also make without departing from the inventive concept of the premise
Some simple deduction or replace, without by performing creative labour.Therefore, those skilled in the art's taking off according to the present invention
Show, the simple modifications made to the present invention all should be within protection scope of the present invention.
Claims (6)
- A kind of 1. finish paint, it is characterised in that：Various components comprising following mass fraction：High function urethane acrylate：10- 30 parts；Polyethers acrylic polyester：5-15 parts；Propylene glycol diacrylate：10-20 parts；Acetone：5-10 parts；1173 light triggers： 2-5 parts；Light initiator -184：2-5 parts；Ceramic:8-15 parts；Levelling agent：0.1-0.5 parts；Defoamer：0.5-1 parts.
- 2. finish paint according to claim 1, it is characterised in that：Various components comprising following mass fraction：High function is gathered Urethane acrylate：20 parts；Polyethers acrylic polyester：10 parts；Propylene glycol diacrylate：15 parts；Acetone：7.5 part；1173 light Initiator：3.5 part；Light initiator -184：3.5 part；Ceramic:11.5 parts；Levelling agent：0.3 part；Defoamer：0.75 part.
- 3. finish paint according to claim 2, it is characterised in that：The acetone obtains to be extracted in hexone.
- 4. finish paint according to claim 3, it is characterised in that：The polyethers acrylic polyester is that the polyethers propylene with ammonia gathers Ester.
- 5. finish paint according to claim 4, it is characterised in that：Its preparation method, it is specially：By high functional polyurethanes propylene Acid esters, the polyethers acrylic polyester with ammonia, propylene glycol diacrylate, acetone, 1173 light triggers, light initiator -184, pottery Porcelain powder, levelling agent, the order of defoamer sequentially add reaction cylinder in proportion, are dispersed with stirring, you can.
- 6. finish paint according to claim 5, it is characterised in that：The mixing speed is 1000-1200r/min, is disperseed anti- It it is 35-50 minutes between seasonable.