CN107779009A - A kind of absorbing formaldehyde interior wall coating - Google Patents
A kind of absorbing formaldehyde interior wall coating Download PDFInfo
- Publication number
- CN107779009A CN107779009A CN201711061244.0A CN201711061244A CN107779009A CN 107779009 A CN107779009 A CN 107779009A CN 201711061244 A CN201711061244 A CN 201711061244A CN 107779009 A CN107779009 A CN 107779009A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- styrene
- acrylic emulsion
- interior wall
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to a kind of absorbing formaldehyde interior wall coating, by weight, including：The parts by weight of styrene-acrylic emulsion 20~30, the parts by weight of diatomite 20~40, the parts by weight of styrene-acrylic emulsion 5~10, the parts by weight of bentonite 10~15, the parts by weight of defoamer 0.5~1, the parts by weight of pigment 10~20, the parts by weight of activated carbon 30~50, the parts by weight of white carbon 4~8 and the parts by weight of water 10~15.The absorbing formaldehyde interior wall coating of the present invention, surface oleophobic is hydrophobic, can effectively prevent water droplet seepage, good water-proof effect can also effectively absorb the formaldehyde in the house after fitting up, more environmentally-friendly.
Description
Technical field
The present invention relates to paint field, specifically, is related to a kind of absorbing formaldehyde interior wall coating.
Background technology
As China is come into operation with 1,000,000,000 square metres of civil buildings every year, building energy consumption accounts for the ratio of whole society's total energy consumption
Example 10% rises to current 27.5% from 1978.The coating industry of China has obtained fast development, and coating is decorated
For the required course of house decoration.
But existing decorative paint free monomer content of formaldehyde is high, has often and cause cough after fitting up, have sore throat, smell order
The insufferable situation of people occurs, and human respiratory tract is caused serious injury.
The content of the invention
The technical problems to be solved by the invention are to provide absorbing formaldehyde interior wall coating.
The technical scheme that the present invention solves above-mentioned technical problem is as follows：
The present invention provides a kind of absorbing formaldehyde interior wall coating, by weight, including：The parts by weight of styrene-acrylic emulsion 20~30, silicon
The parts by weight of diatomaceous earth 20~40, the parts by weight of styrene-acrylic emulsion 5~10, the parts by weight of bentonite 10~15, the parts by weight of defoamer 0.5~1, face
Expect 10~20 parts by weight, the parts by weight of activated carbon 30~50, the parts by weight of white carbon 4~8 and the parts by weight of water 10~15.
The beneficial effects of the invention are as follows：The absorbing formaldehyde interior wall coating of the present invention, surface oleophobic is hydrophobic, can effectively prevent water
Seepage is dripped, good water-proof effect can also effectively absorb the formaldehyde in the house after fitting up, more environmentally-friendly..
On the basis of above-mentioned technical proposal, the present invention can also do following improvement：
Further, by weight, including：The parts by weight of styrene-acrylic emulsion 20, the parts by weight of diatomite 20, the weight of styrene-acrylic emulsion 5
Part, the parts by weight of bentonite 10, the parts by weight of defoamer 0.5, the parts by weight of pigment 10, the parts by weight of activated carbon 30, the parts by weight of white carbon 4 and
The parts by weight of water 10.
Further, by weight, including：The parts by weight of styrene-acrylic emulsion 30, the parts by weight of diatomite 40, the weight of styrene-acrylic emulsion 10
Part, the parts by weight of bentonite 15, the parts by weight of defoamer 1, the parts by weight of pigment 20, the parts by weight of activated carbon 50, the parts by weight of white carbon 8 and water
15 parts by weight.
Further, by weight, including：The parts by weight of styrene-acrylic emulsion 22, the parts by weight of diatomite 31, the weight of styrene-acrylic emulsion 8
Part, the parts by weight of bentonite 12, the parts by weight of defoamer 0.8, the parts by weight of pigment 12, the parts by weight of activated carbon 38, the parts by weight of white carbon 6 and
The parts by weight of water 13.
Further, the absorbing formaldehyde interior wall coating is prepared via a method which：By the parts by weight of styrene-acrylic emulsion 20~30, diatom
Native 20~40 parts by weight, the parts by weight of styrene-acrylic emulsion 5~10, the parts by weight of bentonite 10~15, the parts by weight of defoamer 0.5~1, pigment
10~20 parts by weight, the parts by weight of activated carbon 30~50, the parts by weight of white carbon 4~8 and the mixing of the parts by weight of water 10~15, mechanical agitation
15 minutes, to being well mixed, obtain the absorbing formaldehyde interior wall coating.
Embodiment
The principle and feature of the present invention are described with reference to embodiments, the given examples are served only to explain the present invention,
It is not intended to limit the scope of the present invention.
Embodiment 1
A kind of absorbing formaldehyde interior wall coating, by weight, including：The parts by weight of styrene-acrylic emulsion 20, the parts by weight of diatomite 20, benzene
The parts by weight of acrylic emulsion 5, the parts by weight of bentonite 10, the parts by weight of defoamer 0.5, the parts by weight of pigment 10, the parts by weight of activated carbon 30, hard charcoal
Black 4 parts by weight and the parts by weight of water 10.
The absorbing formaldehyde interior wall coating is prepared via a method which：By the parts by weight of styrene-acrylic emulsion 20, the parts by weight of diatomite 20,
It is the parts by weight of styrene-acrylic emulsion 5, the parts by weight of bentonite 10, the parts by weight of defoamer 0.5, the parts by weight of pigment 10, the parts by weight of activated carbon 30, white
The parts by weight of carbon black 4 and the mixing of the parts by weight of water 10, mechanical agitation 15 minutes, to being well mixed, obtain the absorbing formaldehyde interior wall coating.
Embodiment 2
A kind of absorbing formaldehyde interior wall coating, by weight, including：The parts by weight of styrene-acrylic emulsion 30, the parts by weight of diatomite 40, benzene
The parts by weight of acrylic emulsion 10, the parts by weight of bentonite 15, the parts by weight of defoamer 1, the parts by weight of pigment 20, the parts by weight of activated carbon 50, hard charcoal
Black 8 parts by weight and the parts by weight of water 15.
The absorbing formaldehyde interior wall coating is prepared via a method which：By the parts by weight of styrene-acrylic emulsion 30, the parts by weight of diatomite 40,
It is the parts by weight of styrene-acrylic emulsion 10, the parts by weight of bentonite 15, the parts by weight of defoamer 1, the parts by weight of pigment 20, the parts by weight of activated carbon 50, white
The parts by weight of carbon black 8 and the mixing of the parts by weight of water 15, mechanical agitation 15 minutes, to being well mixed, obtain the absorbing formaldehyde interior wall coating.
Embodiment 3
A kind of absorbing formaldehyde interior wall coating, by weight, including：The parts by weight of styrene-acrylic emulsion 22, the parts by weight of diatomite 31, benzene
The parts by weight of acrylic emulsion 8, the parts by weight of bentonite 12, the parts by weight of defoamer 0.8, the parts by weight of pigment 12, the parts by weight of activated carbon 38, hard charcoal
Black 6 parts by weight and the parts by weight of water 13.
The absorbing formaldehyde interior wall coating is prepared via a method which：By the parts by weight of styrene-acrylic emulsion 22, the parts by weight of diatomite 31,
It is the parts by weight of styrene-acrylic emulsion 8, the parts by weight of bentonite 12, the parts by weight of defoamer 0.8, the parts by weight of pigment 12, the parts by weight of activated carbon 38, white
The parts by weight of carbon black 6 and the mixing of the parts by weight of water 13, mechanical agitation 15 minutes, to being well mixed, obtain the absorbing formaldehyde interior wall coating.
Comparative example 1
Commercially available common interior wall coating
The coating in embodiment 1-3 and comparative example 1 is coated uniformly in mould, and is poured in mould containing certain
The air of formaldehyde is measured, is stopped 24 hours, the content of formaldehyde in testing mould, acquired results see the table below.
The foregoing is only presently preferred embodiments of the present invention, be not intended to limit the invention, it is all the present invention spirit and
Within principle, any modification, equivalent substitution and improvements made etc., it should be included in the scope of the protection.
Claims (5)
- A kind of 1. absorbing formaldehyde interior wall coating, it is characterised in that by weight, including：The parts by weight of styrene-acrylic emulsion 20~30, diatom Native 20~40 parts by weight, the parts by weight of styrene-acrylic emulsion 5~10, the parts by weight of bentonite 10~15, the parts by weight of defoamer 0.5~1, pigment 10~20 parts by weight, the parts by weight of activated carbon 30~50, the parts by weight of white carbon 4~8 and the parts by weight of water 10~15.
- A kind of 2. absorbing formaldehyde interior wall coating according to claim 1, it is characterised in that by weight, including：Styrene-acrylic emulsion 20 parts by weight, the parts by weight of diatomite 20, the parts by weight of styrene-acrylic emulsion 5, the parts by weight of bentonite 10, the parts by weight of defoamer 0.5, pigment 10 Parts by weight, the parts by weight of activated carbon 30, the parts by weight of white carbon 4 and the parts by weight of water 10.
- A kind of 3. absorbing formaldehyde interior wall coating according to claim 1, it is characterised in that by weight, including：Styrene-acrylic emulsion 30 parts by weight, the parts by weight of diatomite 40, the parts by weight of styrene-acrylic emulsion 10, the parts by weight of bentonite 15, the parts by weight of defoamer 1, pigment 20 Parts by weight, the parts by weight of activated carbon 50, the parts by weight of white carbon 8 and the parts by weight of water 15.
- A kind of 4. absorbing formaldehyde interior wall coating according to claim 1, it is characterised in that by weight, including：Styrene-acrylic emulsion 22 parts by weight, the parts by weight of diatomite 31, the parts by weight of styrene-acrylic emulsion 8, the parts by weight of bentonite 12, the parts by weight of defoamer 0.8, pigment 12 Parts by weight, the parts by weight of activated carbon 38, the parts by weight of white carbon 6 and the parts by weight of water 13.
- 5. according to a kind of any absorbing formaldehyde interior wall coatings of claim 1-4, it is characterised in that the absorbing formaldehyde interior wall coating It is prepared via a method which：By the parts by weight of styrene-acrylic emulsion 20~30, the parts by weight of diatomite 20~40, the weight of styrene-acrylic emulsion 5~10 Part, the parts by weight of bentonite 10~15, the parts by weight of defoamer 0.5~1, the parts by weight of pigment 10~20, the parts by weight of activated carbon 30~50, The parts by weight of white carbon 4~8 and the mixing of the parts by weight of water 10~15, mechanical agitation 15 minutes, to being well mixed, obtain the absorbing formaldehyde Interior wall coating.