CN107760044A - 耐高温塑料粒子及其制备方法 - Google Patents
耐高温塑料粒子及其制备方法 Download PDFInfo
- Publication number
- CN107760044A CN107760044A CN201711077656.3A CN201711077656A CN107760044A CN 107760044 A CN107760044 A CN 107760044A CN 201711077656 A CN201711077656 A CN 201711077656A CN 107760044 A CN107760044 A CN 107760044A
- Authority
- CN
- China
- Prior art keywords
- parts
- temperature resistance
- resistance plastice
- filler
- particle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种耐高温塑料粒子，由以下重量份数的各组分组成：填料54～83份，紫胶树脂15～42份，邻苯二甲酸二丁酯0.8～1.5份，甲基乙烯基硅油1～3份，硬脂酸钾0.3～0.6份，玻纤粉5～10份，钛白粉17～22份，磷化硼0.9～1.4份，氧化镨0.6～1.1份；本发明还涉及所述耐高温塑料粒子的制备方法：按重量份数取填料，粉碎过250～300目筛，得到填料粉末；在填料粉末中加入剩余原材料，混合均匀后加热炒制20～30min，温度90～120℃；经造粒机继续加热至200～300℃，经磨头挤出块状物，然后破碎，得到耐高温塑料粒子。所得塑料粒子在高温条件下，仍能保持较高机械性能，耐腐蚀、耐应力开裂，尺寸稳定，热变形温度大于193℃，适用于制作灯具外壳、散热元件、电路板等。
Description
技术领域
本发明涉及塑料粒子领域，更具体地，涉及一种耐高温塑料粒子及其制备方法。
背景技术
相对于金属、石材、木材，塑料制品具有成本低、可塑性强等优点，在国民经济中应用广泛，塑料工业在当今世界上占有极为重要的地位，多年来塑料制品的生产在世界各地高速度发展。我国塑料制品产量在世界排名中始终位于前列，其中多种塑料制品产量已经位于全球首位，我国已经成为世界塑料制品生产大国。但是，与金属、陶瓷、玻璃等传统材料相比，塑料的缺点之一为耐热性不高，这往往限制了其在高温场合的使用。
发明内容
本发明的目的是提供一种耐高温塑料粒子。
本发明的另一目的是提供一种所述耐高温塑料粒子的制备方法。
本发明目的通过以下技术方案予以实现：
提供一种耐高温塑料粒子，由以下重量份数的各组分组成：填料54～83份，紫胶树脂15～42份，邻苯二甲酸二丁酯0.8～1.5份，甲基乙烯基硅油1～3份，硬脂酸钾0.3～0.6份，玻纤粉5～10份，钛白粉17～22份，磷化硼0.9～1.4份，氧化镨0.6～1.1份。
优选地，所述耐高温塑料粒子由以下重量份数的各组分组成：填料65份，紫胶树脂35份，邻苯二甲酸二丁酯1.2份，甲基乙烯基硅油2份，硬脂酸钾0.5份，玻纤粉8份，钛白粉18份，磷化硼1.3份，氧化镨0.9份。
进一步地，所述填料包括电熔刚玉。
进一步地，所述填料还包括石墨，红柱石，翠榴石，堇青石，香花石中的至少两种。
进一步地，所述填料中电熔刚玉的质量含量高于30%。
进一步地，所述钛白粉包括金红石型钛白粉和锐钛型钛白粉。
进一步地，所述钛白粉中金红石型钛白粉的质量含量高于70%。
本发明还提供了所述耐高温塑料粒子的制备方法，包括以下步骤：
S1．按重量份数取填料，粉碎过250～300目筛，得到填料粉末；
S2.在填料粉末中加入剩余原材料，混合均匀后加热炒制20～30min，温度90～120℃；
S3. 经造粒机继续加热至200～300℃，经磨头挤出块状物，然后破碎，得到耐高温塑料粒子。
与现有技术相比，本发明具有以下有益效果：
本发明提供了一种耐高温塑料粒子，在高温条件下，仍能保持较高机械性能，耐腐蚀、耐应力开裂，尺寸稳定，热变形温度大于193℃，适用于制作灯具外壳、散热元件、电路板等。
具体实施方式
下面结合具体实施例对本发明作进一步的说明。
实施例1
本实施例公开了一种耐高温塑料粒子，由以下重量份数的各组分组成：电熔刚玉20份，石墨16份，红柱石18份，紫胶树脂42份，邻苯二甲酸二丁酯0.8份，甲基乙烯基硅油3份，硬脂酸钾0.3份，玻纤粉10份，金红石型钛白粉13份，锐钛型钛白粉4份，磷化硼1.4份，氧化镨0.6份。
实施例2
本实施例公开了一种耐高温塑料粒子，由以下重量份数的各组分组成：电熔刚玉30份，石墨3份，红柱石10份，翠榴石8份，堇青石12份，香花石20份，紫胶树脂15份，邻苯二甲酸二丁酯1.5份，甲基乙烯基硅油1份，硬脂酸钾0.6份，玻纤粉5份，金红石型钛白粉16份，锐钛型钛白粉6份，磷化硼0.9份，氧化镨1.1份。
实施例3
本实施例公开了一种耐高温塑料粒子，由以下重量份数的各组分组成：电熔刚玉25份，红柱石15份，翠榴石15份，堇青石10份，紫胶树脂35份，邻苯二甲酸二丁酯1.2份，甲基乙烯基硅油2份，硬脂酸钾0.5份，玻纤粉8份，金红石型钛白粉13份，锐钛型钛白粉5份，磷化硼1.3份，氧化镨0.9份。
实施例4
本实施例公开了一种耐高温塑料粒子，由以下重量份数的各组分组成：电熔刚玉28份，翠榴石22份，堇青石20份，香花石8份，紫胶树脂22份，邻苯二甲酸二丁酯0.9份，甲基乙烯基硅油1.3份，硬脂酸钾0.4份，玻纤粉6份，金红石型钛白粉18份，锐钛型钛白粉3份，磷化硼1份，氧化镨0.7份。
实施例5
本实施例公开了一种耐高温塑料粒子，由以下重量份数的各组分组成：电熔刚玉40份，红柱石10份，翠榴石10份，堇青石10份，香花石10份，紫胶树脂40份，邻苯二甲酸二丁酯1.1份，甲基乙烯基硅油2.5份，硬脂酸钾0.3份，玻纤粉9份，金红石型钛白粉15份，锐钛型钛白粉5份，磷化硼1.2份，氧化镨0.8份。
实施例6
本实施例公开了一种耐高温塑料粒子，由以下重量份数的各组分组成：电熔刚玉32份，翠榴石20份，香花石6份，紫胶树脂25份，邻苯二甲酸二丁酯1.4份，甲基乙烯基硅油2.8份，硬脂酸钾0.6份，玻纤7份，金红石型钛白粉15份，锐钛型钛白粉4份，磷化硼1.3份，氧化镨1份。
实施例7
本实施例公开了一种耐高温塑料粒子，由以下重量份数的各组分组成：电熔刚玉20份，石墨14份，翠榴石15份，堇青石13份，紫胶树脂20份，邻苯二甲酸二丁酯1份，甲基乙烯基硅油2.3份，硬脂酸钾0.4份，玻纤粉5份，金红石型钛白粉20份，锐钛型钛白粉2份，磷化硼0.9份，氧化镨0.7份。
实施例8
取实施例1～7任意实施例的重量组分制备耐高温塑料粒子，制备步骤如下：
S1．按重量份数取填料，粉碎过300目筛，得到填料粉末；
S2.在填料粉末中加入剩余原材料，混合均匀后加热炒制20min，温度120℃；
S3. 经造粒机继续加热至200℃，经磨头挤出块状物，然后破碎，得到耐高温塑料粒子。
实施例9
取实施例1～7任意实施例的重量组分制备耐高温塑料粒子，制备步骤如下：
S1．按重量份数取填料，粉碎过250目筛，得到填料粉末；
S2.在填料粉末中加入剩余原材料，混合均匀后加热炒制30min，温度90℃；
S3. 经造粒机继续加热至300℃，经磨头挤出块状物，然后破碎，得到耐高温塑料粒子。
Claims (8)
1.一种耐高温塑料粒子，其特征在于，由以下重量百分比的各组分组成：填料54～83份，紫胶树脂15～42份，邻苯二甲酸二丁酯0.8～1.5份，甲基乙烯基硅油1～3份，硬脂酸钾0.3～0.6份，玻纤粉5～10份，钛白粉17～22份，磷化硼0.9～1.4份，氧化镨0.6～1.1份。
2.根据权利要求1所述的耐高温塑料粒子，其特征在于，由以下重量份数的各组分组成：填料65份，紫胶树脂35份，邻苯二甲酸二丁酯1.2份，甲基乙烯基硅油2份，硬脂酸钾0.5份，玻纤粉8份，钛白粉18份，磷化硼1.3份，氧化镨0.9份。
3.根据权利要求1或2所述的耐高温塑料粒子，其特征在于，所述填料包括电熔刚玉。
4.根据权利要求1或3所述的耐高温塑料粒子，其特征在于，所述填料还包括石墨，红柱石，翠榴石，堇青石，香花石中的至少两种。
5.根据权利要求4所述的耐高温塑料粒子，其特征在于，所述填料中电熔刚玉的质量含量高于30%。
6.根据权利要求1所述的耐高温塑料粒子，其特征在于，所述钛白粉包括金红石型钛白粉和锐钛型钛白粉。
7.根据权利要求6所述的耐高温塑料粒子，其特征在于，所述钛白粉中金红石型钛白粉的质量含量高于70%。
8.根据权利要求1所述耐高温塑料粒子的制备方法，其特征在于，包括以下步骤：
S1．按重量份数取填料，粉碎过250～300目筛，得到填料粉末；
S2.在填料粉末中加入剩余原材料，混合均匀后加热炒制20～30min，温度90～120℃；
S3. 经造粒机继续加热至200～300℃，经磨头挤出块状物，然后破碎，得到耐高温塑料粒子。