CN107746627A - A kind of negative ion ink and preparation method thereof - Google Patents
A kind of negative ion ink and preparation method thereof Download PDFInfo
- Publication number
- CN107746627A CN107746627A CN201711175124.3A CN201711175124A CN107746627A CN 107746627 A CN107746627 A CN 107746627A CN 201711175124 A CN201711175124 A CN 201711175124A CN 107746627 A CN107746627 A CN 107746627A
- Authority
- CN
- China
- Prior art keywords
- negative ion
- ink
- modified
- tourmaline
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of negative ion ink, including following component by weight：Tourmaline 20 45%, quartz 10 20%, calcite 3 10%, potassium feldspar 15 25%, washing soil 5 15%, praseodymium oxide 3 9%, zirconium silicate 2 8%, polyethylene glycol 5 15%, glycerine 10 20%, sodium tripolyphosphate 0.1 0.5%, sodium carboxymethylcellulose pyce 0.05 0.1%, surplus is water；The present invention improves its activity by being modified to the tourmaline anion powder for producing anion；Then cladding processing is carried out to modified tourmaline anion powder, makes it in the case of high-temperature calcination, its structure is not changed, it is ensured that its activity；Ink finally is made in modified and cladding tourmaline anion powder.The negative ion ink that the present invention is prepared can discharge anion, effectively purify air, improve IAQ, also have the function that antibacterial, be beneficial to health.
Description
Technical field
The present invention relates to ceramics technical field of ink, more particularly to a kind of negative ion ink and preparation method thereof.
Background technology
Bacterium, mould have very big harm to the mankind and animals and plants as pathogen, influence the health of people or even jeopardize life
Life, brings great economic loss.Therefore the research of anti-biotic material and its product increasingly causes the concern of people, antibacterial product
Demand will form huge market.
For in terms of environmental protection, negative aeroion can eliminate foreign flavor indoors and various pernicious gases.Fit up indoors
During leftovers leftovers in the art work that the uses benzene, formaldehyde, ketone, the irritative gas such as ammonia and the daily life that evaporate
The harmful peculiar smell such as acid smell, cigarette, with the material rich in anion, its negative aeroion discharged can be effectively
Eliminated, reach the purpose of purification air, and have good suppression to golden staphylococci, Escherichia coli, candida albicans and mould etc.
Make and use.
Ceramic ink jet technology is as a kind of new contactless, no pressure, the printing technology without printing plate, undoubtedly by current ceramic tile
Fashion, personalization, art up, small lot, multi-color, the development trend of low-carbon environment-friendly have pushed a new height to.From
Since China introduces First ceramic ink jet machine within 2009, the development of ceramic ink jet printing technology is advanced by leaps and bounds, and is obtained a large amount of
Using.Through development in a few years, the occupation rate of market more and more higher of ceramic ink jet product, also the advantage of ceramic ink jet technology is sent out
Wave incisively and vividly.
However, there has been no the negative ion ink for being exclusively used in ceramics on the market at present.
The content of the invention
It is an object of the invention to provide a kind of negative ion ink and preparation method thereof.
To achieve these goals, the present invention uses following technical scheme：
A kind of negative ion ink, including following component by weight：
The preparation method of above-mentioned negative ion ink, comprises the following steps：
(1) after being well mixed tourmaline, calcite, quartz, potassium feldspar, washing soil and praseodymium oxide, after being calcined, make
With ball mill ball milling, modified negative-ion powder is obtained；
(2) after the modified negative-ion powder that step (1) obtains is well mixed with calcite, zirconium silicate, after being calcined, make
It is standby with ball mill ball milling；
(3) product that step (2) obtains is mixed with polyethylene glycol, glycerine, water, sodium tripolyphosphate, sodium carboxymethylcellulose pyce
After uniformly, crushed using ultrasonic vibration, obtain the negative ion ink.Preferably, in step (1), calcining heat 1100
DEG C -1500 DEG C, calcination time is 5-10 hours.
Preferably, in step (2), calcining heat is 1100 DEG C -1500 DEG C, and calcination time is 5-10 hours.
Beneficial effects of the present invention：
The present invention improves its activity by being modified to the tourmaline anion powder for producing anion；Then to modification
Tourmaline anion powder afterwards carries out cladding processing, makes it in the case of high-temperature calcination, and its structure is not changed, it is ensured that it is lived
Property；Ink finally is made in modified and cladding tourmaline anion powder.The negative ion ink that the present invention is prepared can be released
Anion is put, effectively purifies air, IAQ is improved, also there is antibacterial, be beneficial to health.
Embodiment
Embodiment 1
A kind of negative ion ink, including following component by weight：
The preparation method of above-mentioned negative ion ink, comprises the following steps：
(1) after being well mixed tourmaline, calcite, quartz, potassium feldspar, washing soil and praseodymium oxide, forged at 1500 DEG C
After burning 8 hours, using ball mill ball milling, modified negative-ion powder is obtained；
(2) after the modified negative-ion powder that step (1) obtains is well mixed with calcite, zirconium silicate, forged at 1300 DEG C
It is standby using ball mill ball milling after burning 10 hours；
(3) product that step (2) obtains is mixed with polyethylene glycol, glycerine, water, sodium tripolyphosphate, sodium carboxymethylcellulose pyce
After uniformly, crushed using ultrasonic vibration, obtain the negative ion ink.
Embodiment 2
A kind of negative ion ink, including following component by weight：
The preparation method of above-mentioned negative ion ink, comprises the following steps：
(1) after being well mixed tourmaline, calcite, quartz, potassium feldspar, washing soil and praseodymium oxide, forged at 1500 DEG C
After burning 8 hours, using ball mill ball milling, modified negative-ion powder is obtained；
(2) after the modified negative-ion powder that step (1) obtains is well mixed with calcite, zirconium silicate, forged at 1300 DEG C
It is standby using ball mill ball milling after burning 10 hours；
(3) product that step (2) obtains is mixed with polyethylene glycol, glycerine, water, sodium tripolyphosphate, sodium carboxymethylcellulose pyce
After uniformly, crushed using ultrasonic vibration, obtain the negative ion ink.
Claims (4)
1. a kind of negative ion ink, it is characterised in that including following component by weight：
2. the preparation method of 1 negative ion ink is sought according to right, it is characterised in that comprise the following steps：
(1) after being well mixed tourmaline, calcite, quartz, potassium feldspar, washing soil and praseodymium oxide, after being calcined, ball is used
Grinding machine ball milling, obtain modified negative-ion powder；
(2) after the modified negative-ion powder that step (1) obtains is well mixed with calcite, zirconium silicate, after being calcined, ball is used
Grinding machine ball milling, it is standby；
(3) product that step (2) obtains is well mixed with polyethylene glycol, glycerine, water, sodium tripolyphosphate, sodium carboxymethylcellulose pyce
Afterwards, crushed using ultrasonic vibration, obtain the negative ion ink.
3. the preparation method of 2 negative ion inks is sought according to right, it is characterised in that in step (1), calcining heat is
1100 DEG C -1500 DEG C, calcination time is 5-10 hours.
4. the preparation method of 2 negative ion inks is sought according to right, it is characterised in that in step (2), calcining heat is
1100 DEG C -1500 DEG C, calcination time is 5-10 hours.