CN107746536A - A kind of material for being used to manufacture table tennis - Google Patents
A kind of material for being used to manufacture table tennis Download PDFInfo
- Publication number
- CN107746536A CN107746536A CN201711015442.3A CN201711015442A CN107746536A CN 107746536 A CN107746536 A CN 107746536A CN 201711015442 A CN201711015442 A CN 201711015442A CN 107746536 A CN107746536 A CN 107746536A
- Authority
- CN
- China
- Prior art keywords
- table tennis
- raw material
- present
- manufacture table
- manufacture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
A kind of material for being used to manufacture table tennis of the present invention, its raw material and raw material weight percentage composition are as follows：ABS resin 40 50%, K glue 0.1 1%, lauric acid diethyl amide 0.1 3%, polyvinyl butyral resin 0.1 3%, magnalium flame retardant 0.1 3%, modified polyphenyl alkene 40 60%.The present invention has the characteristics of hardness is high, modulus of elasticity is excellent.
Description
Technical field
The invention belongs to materials science field, more particularly to a kind of material for being used to manufacture table tennis.
Background technology
Since upper world's the '30s, celluloid is used to prepare table tennis for raw material, because it possesses very high hardness
And modulus of elasticity, obtained table tennis have the advantages of thickness is uniform, service life is long, and cause the material continue to use always to
It is modern.But use celluloid to make table tennis for raw material and following drawback be present：
First, celluloid material is using the nitrocellulose of dehydration as primary raw material, its is inflammable and explosive, and it is in feed stage, production rank
The storage of section, larger potential safety hazard be present in transportation, and after table tennis product is made, it is in storage, transportation
In equally exist inflammable hidden danger.
Second, for safety, nitrocotton will add water in transportation, need to be dehydrated during use, substantial amounts of waste liquid be present
Discharge, can bring harm, not environmentally to environment；In addition, its complex manufacturing technology, fabrication cycle are grown.
The content of the invention
To solve above-mentioned existing technical problem, the present invention uses following scheme：
A kind of material for being used to manufacture table tennis, its raw material and raw material weight percentage composition are as follows：
ABS resin 40-50%；
K glue 0.1-1%；
Lauric acid diethyl amide 0.1-3%；
Polyvinyl butyral resin 0.1-3%；
Magnalium flame retardant 0.1-3%；
Modified polyphenyl alkene 40-60%.
The present invention has the characteristics of hardness is high, modulus of elasticity is excellent.
Embodiment
The present invention is described in detail below in conjunction with specific embodiment, herein illustrative examples and explanation of the invention
For explaining the present invention, but it is not as a limitation of the invention.
Embodiment
A kind of material for being used to manufacture table tennis of the present invention, its raw material and raw material weight percentage composition are as follows：ABS trees
Fat 45%, K glue 0.5%, lauric acid diethyl amide 0.5%, polyvinyl butyral resin 1%, magnalium flame retardant 2%, modification
Polyphenyl alkene 51%.
The above-described embodiments merely illustrate the principles and effects of the present invention, not for the limitation present invention.It is any ripe
Know the personage of this technology all can carry out modifications and changes under the spirit and scope without prejudice to the present invention to above-described embodiment.Cause
This, those of ordinary skill in the art is complete without departing from disclosed spirit and institute under technological thought such as
Into all equivalent modifications or change, should by the present invention claim be covered.
Claims (1)
1. a kind of material for being used to manufacture table tennis, it is characterised in that its raw material and raw material weight percentage composition are as follows：
ABS resin 40-50%；
K glue 0.1-1%；
Lauric acid diethyl amide 0.1-3%；
Polyvinyl butyral resin 0.1-3%；
Magnalium flame retardant 0.1-3%；
Modified polyphenyl alkene 40-60%.