CN107737904A - 一种用于制备注塑模具的铸造工艺 - Google Patents

一种用于制备注塑模具的铸造工艺 Download PDF

Info

Publication number
CN107737904A
CN107737904A CN201710985456.1A CN201710985456A CN107737904A CN 107737904 A CN107737904 A CN 107737904A CN 201710985456 A CN201710985456 A CN 201710985456A CN 107737904 A CN107737904 A CN 107737904A
Authority
CN
China
Prior art keywords
sandbox
injection mold
cooled
casting technique
casting
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710985456.1A
Other languages
English (en)
Inventor
贾宁霞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Mountain Tianxing Suzhou City Precision Die Co Ltd
Original Assignee
Mountain Tianxing Suzhou City Precision Die Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mountain Tianxing Suzhou City Precision Die Co Ltd filed Critical Mountain Tianxing Suzhou City Precision Die Co Ltd
Priority to CN201710985456.1A priority Critical patent/CN107737904A/zh
Publication of CN107737904A publication Critical patent/CN107737904A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种用于制备注塑模具的铸造工艺，具体包括如下工艺：先按照注塑模具的外形、尺寸要求制造对应的砂箱；再选取注塑模具的原材料，将其混合投入高温熔炉中进行熔融混合，得到合金液；接着向砂箱的型腔内部冲入氮气，直至型腔内氧气全部排出，随后将上述合金液浇注至砂箱内；最后采用密封盖封住砂箱的浇注口，再采用氮气枪炬砂箱侧表面进行风冷处理，风冷温度为10‑30℃，风冷时间为20‑30min，随后再密封保温40‑60min后取走密封盖，最终自然冷却至室温，取出模具体，通过上述方式，本发明能够不仅能够保证产品在浇铸过程中不被氧化，而且能够减少模具在成型过程中的变形量，大幅提高模具质量。

Description

一种用于制备注塑模具的铸造工艺
技术领域
本发明涉及一种模具的制备方法，特别涉及一种用于制备注塑模具的铸造工艺。
背景技术
注塑模具是一种生产塑胶制品的工具，也是赋予塑胶制品完整结构和精确尺寸的工具，目前传统的注塑模具的制备方法均采用铸造工艺进行，而在铸造的过程，不仅会受到环境中氧气的影响，而造成模具材料部分被氧化，影响模具质量，此外在浇铸完成后大多均直接采用自然冷却的方式，不仅生产缓慢，而且还会增加模具在冷却成型过程中的变形率。
发明内容
本发明主要解决的技术问题是提供一种用于制备注塑模具的铸造工艺，不仅能够保证产品在浇铸过程中不被氧化，而且能够减少模具在成型过程中的变形量，大幅提高模具质量。
为解决上述技术问题，本发明采用的一个技术方案是：提供一种用于制备注塑模具的铸造工艺，具体包括如下工艺：
（1）砂箱制造：按照注塑模具的外形、尺寸要求制造对应的砂箱；
（2）材料熔融：选取注塑模具的原材料，将其混合投入高温熔炉中进行熔融混合，得到合金液；
（3）真空浇铸：向砂箱的型腔内部冲入氮气，直至型腔内氧气全部排出，随后将上述合金液浇注至砂箱内；
（4）冷却成型：采用密封盖封住砂箱的浇注口，再采用氮气枪炬砂箱侧表面进行风冷处理，风冷温度为10-30℃，风冷时间为20-30min，随后再密封保温40-60min后取走密封盖，最终自然冷却至室温，取出模具体。
在本发明一个较佳实施例中，所述步骤（2）中的熔融温度为660-680℃。
在本发明一个较佳实施例中，所述步骤（3）中的浇注温度为580-620℃。
在本发明一个较佳实施例中，所述砂箱内部开设有补缩流道，能够在合金液冷缩时，对模具进行补缩，防止模具表面产生气孔或者缺陷。
本发明的有益效果是：本发明一种用于制备注塑模具的铸造工艺，通过采用在真空浇铸的方式，能够在模具材料浇注的过程中不被氧化，同时采用先风冷后密封保温，最后自然冷却的冷却方式，能够大幅减少合金液在冷却成型的过程中的变形量，大幅提高模具质量。
具体实施方式
下面对本发明的较佳实施例进行详细阐述，以使本发明的优点和特征能更易于被本领域技术人员理解，从而对本发明的保护范围做出更为清楚明确的界定。
实施例1：
一种用于制备注塑模具的铸造工艺，具体包括如下工艺：
（1）砂箱制造：按照注塑模具的外形、尺寸要求制造对应的砂箱，且砂箱内部开设有补缩流道；
（2）材料熔融：选取注塑模具的原材料，将其混合投入高温熔炉中进行熔融混合，得到合金液，熔融温度为660℃；
（3）真空浇铸：向砂箱的型腔内部冲入氮气，直至型腔内氧气全部排出，随后将上述合金液浇注至砂箱内，浇注温度为580℃；
（4）冷却成型：采用密封盖封住砂箱的浇注口，再采用氮气枪炬砂箱侧表面进行风冷处理，风冷温度为10℃，风冷时间为30min，随后再密封保温40min后取走密封盖，最终自然冷却至室温，取出模具体。
实施例2：
一种用于制备注塑模具的铸造工艺，具体包括如下工艺：
（1）砂箱制造：按照注塑模具的外形、尺寸要求制造对应的砂箱，且砂箱内部开设有补缩流道；
（2）材料熔融：选取注塑模具的原材料，将其混合投入高温熔炉中进行熔融混合，得到合金液，熔融温度为680℃；
（3）真空浇铸：向砂箱的型腔内部冲入氮气，直至型腔内氧气全部排出，随后将上述合金液浇注至砂箱内，浇注温度为620℃；
（4）冷却成型：采用密封盖封住砂箱的浇注口，再采用氮气枪炬砂箱侧表面进行风冷处理，风冷温度为30℃，风冷时间为20min，随后再密封保温60min后取走密封盖，最终自然冷却至室温，取出模具体。
实施例3：
一种用于制备注塑模具的铸造工艺，具体包括如下工艺：
（1）砂箱制造：按照注塑模具的外形、尺寸要求制造对应的砂箱，且砂箱内部开设有补缩流道；
（2）材料熔融：选取注塑模具的原材料，将其混合投入高温熔炉中进行熔融混合，得到合金液，熔融温度为670℃；
（3）真空浇铸：向砂箱的型腔内部冲入氮气，直至型腔内氧气全部排出，随后将上述合金液浇注至砂箱内，浇注温度为600℃；
（4）冷却成型：采用密封盖封住砂箱的浇注口，再采用氮气枪炬砂箱侧表面进行风冷处理，风冷温度为20℃，风冷时间为25min，随后再密封保温50min后取走密封盖，最终自然冷却至室温，取出模具体。
进一步说明，本发明一种用于制备注塑模具的铸造工艺，通过采用在真空浇铸的方式，能够在模具材料在浇注的过程中不被氧化，同时采用先风冷后密封保温，最后自然冷却的冷却方式，能够大幅减少合金液在冷却成型的过程中的变形量，大幅提高模具质量。
以上所述仅为本发明的优选实施例而已，并不用于限制本发明，对于本领域的技术人员来说，本发明可以有各种更改和变化。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (4)

1.一种用于制备注塑模具的铸造工艺，其特征在于，具体包括如下工艺：
（1）砂箱制造：按照注塑模具的外形、尺寸要求制造对应的砂箱；
（2）材料熔融：选取注塑模具的原材料，将其混合投入高温熔炉中进行熔融混合，得到合金液；
（3）真空浇铸：向砂箱的型腔内部冲入氮气，直至型腔内氧气全部排出，随后将上述合金液浇注至砂箱内；
（4）冷却成型：采用密封盖封住砂箱的浇注口，再采用氮气枪炬砂箱侧表面进行风冷处理，风冷温度为10-30℃，风冷时间为20-30min，随后再密封保温40-60min后取走密封盖，最终自然冷却至室温，取出模具体。
2.根据权利要求1所述的用于制备注塑模具的铸造工艺，其特征在于，所述步骤（2）中的熔融温度为660-680℃。
3.根据权利要求1所述的用于制备注塑模具的铸造工艺，其特征在于，所述步骤（3）中的浇注温度为580-620℃。
4.根据权利要求1所述的用于制备注塑模具的铸造工艺，其特征在于，所述砂箱内部开设有补缩流道。
CN201710985456.1A 2017-10-20 2017-10-20 一种用于制备注塑模具的铸造工艺 Pending CN107737904A (zh)