CN107721261A - 一种保温防火材料及其制备方法 - Google Patents
一种保温防火材料及其制备方法 Download PDFInfo
- Publication number
- CN107721261A CN107721261A CN201710981966.1A CN201710981966A CN107721261A CN 107721261 A CN107721261 A CN 107721261A CN 201710981966 A CN201710981966 A CN 201710981966A CN 107721261 A CN107721261 A CN 107721261A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- aluminum oxide
- zirconium
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种保温防火材料及其制备方法,以重量份计,包括10份‑30份亚麻油醇酸树脂、10份‑20份氧化铝、30份‑50份聚磷酸铵、18份‑24份纳米钛白粉、10份‑20份硼砂、5份‑10份海泡石、5份‑10份硅酸锆粉或钇稳定氧化锆粉、5份‑10份三聚氰胺、2份‑5份硅酸铝纤维、3份‑7份石棉纤维素、1份‑2份柠檬酸、1份‑2份可膨胀石墨、0.2份‑0.6份高岭土。本发明的防火材料具有耐高温、抗烧裂的特点,且无毒无味,绿色环保,装饰性能好,施工方便,喷刷即可,能保持基材的原貌。
Description
技术领域
本发明涉及新材料技术领域,具体涉及一种保温防火材料及其制备方法。
背景技术
随着全球变暖的加剧,人们注重的多是建筑物的隔热效果,在炎热的夏季能阻挡室外的温度,而使用空调或暖气时,又能达到室内保温的作用。伴随着人们对建筑物节能意识的不断提高,对建筑保温材料和防火材料的要求显著增强,提供一种环保轻质的防火材料是目前的研究重点。
发明内容
本发明所要解决的技术问题是针对现有技术的不足,提供一种环保型防火材料及其制备方法。
本发明解决上述技术问题的技术方案如下:一种保温防火材料,以重量份计,包括30份-50份亚麻油醇酸树脂、10份-20份氧化铝、30份-50份聚磷酸铵、18份-24份纳米钛白粉、10份-20份硼砂、5份-10份海泡石、5份-10份硅酸锆粉或钇稳定氧化锆粉、5份-10份三聚氰胺、2份-5份硅酸铝纤维、3份-7份石棉纤维素、1份-2份柠檬酸、1份-2份可膨胀石墨、0.2份-0.6份高岭土。
本发明的有益效果是:本发明的防火材料具有耐高温、抗烧裂的特点,且无毒无味,绿色环保,装饰性能好,施工方便,喷刷即可,能保持基材的原貌。
在上述技术方案的基础上,本发明还可以做如下改进。
进一步,以重量份计,包括30份亚麻油醇酸树脂、10份氧化铝、30份聚磷酸铵、18份纳米钛白粉、10份硼砂、5份海泡石、5份硅酸锆粉或钇稳定氧化锆粉、5份三聚氰胺、2份硅酸铝纤维、3份石棉纤维素、1份柠檬酸、1份可膨胀石墨、0.2份高岭土。
进一步,以重量份计,包括40份亚麻油醇酸树脂、15份氧化铝、40份聚磷酸铵、20份纳米钛白粉、15份硼砂、8份海泡石、7份硅酸锆粉或钇稳定氧化锆粉、8份三聚氰胺、3份硅酸铝纤维、4份石棉纤维素、1.5份柠檬酸、1.5份可膨胀石墨、0.4份高岭土。
进一步,以重量份计,包括50份亚麻油醇酸树脂、20份氧化铝、50份聚磷酸铵、24份纳米钛白粉、20份硼砂、10份海泡石、10份硅酸锆粉或钇稳定氧化锆粉、10份三聚氰胺、5份硅酸铝纤维、7份石棉纤维素、2份柠檬酸、2份可膨胀石墨、0.6份高岭土。
一种如上所述的保温防火材料的制备方法,包括以下步骤:
步骤1),按重量份称取亚麻油醇酸树脂、纳米钛白粉、聚磷酸铵、硅酸锆粉或钇稳定氧化锆粉、柠檬酸、硼砂、三聚氰胺、硅酸铝纤维和海泡石,并混合均匀得到混合液;
步骤2),按重量份称取氧化铝,并将氧化铝加入到混合液中,搅拌均匀使氧化铝均匀分散到混合液中,得到分散液;
步骤3),将分散液中加入石棉纤维素、可膨胀石墨和高岭土,均匀分散50min-80min,过滤灌装。
本发明的有益效果是:本发明的方法简单,能减少有效成分的破坏。
具体实施方式
以下对本发明的原理和特征进行描述,所举实例只用于解释本发明,并非用于限定本发明的范围。
实施例1
本实施例的一种保温防火材料,以重量份计,包括30份亚麻油醇酸树脂、10份氧化铝、30份聚磷酸铵、18份纳米钛白粉、10份硼砂、5份海泡石、5份硅酸锆粉或钇稳定氧化锆粉、5份三聚氰胺、2份硅酸铝纤维、3份石棉纤维素、1份柠檬酸、1份可膨胀石墨、0.2份高岭土。
本实施例的防火材料具有耐高温、抗烧裂的特点,且无毒无味,绿色环保,装饰性能好,施工方便,喷刷即可,能保持基材的原貌。
本实施例的一种保温防火材料的制备方法,包括以下步骤:
步骤1),按重量份称取亚麻油醇酸树脂、纳米钛白粉、聚磷酸铵、硅酸锆粉或钇稳定氧化锆粉、柠檬酸、硼砂、三聚氰胺、硅酸铝纤维和海泡石,并混合均匀得到混合液;
步骤2),按重量份称取氧化铝,并将氧化铝加入到混合液中,搅拌均匀使氧化铝均匀分散到混合液中,得到分散液;
步骤3),将分散液中加入石棉纤维素、可膨胀石墨和高岭土,均匀分散50min-80min,过滤灌装。
本实施例的方法简单,能减少有效成分的破坏。
实施例2
实施例的一种保温防火材料,以重量份计,包括40份亚麻油醇酸树脂、15份氧化铝、40份聚磷酸铵、20份纳米钛白粉、15份硼砂、8份海泡石、7份硅酸锆粉或钇稳定氧化锆粉、8份三聚氰胺、3份硅酸铝纤维、4份石棉纤维素、1.5份柠檬酸、1.5份可膨胀石墨、0.4份高岭土。
本实施例的一种保温防火材料的制备方法,包括以下步骤:
步骤1),按重量份称取亚麻油醇酸树脂、纳米钛白粉、聚磷酸铵、硅酸锆粉或钇稳定氧化锆粉、柠檬酸、硼砂、三聚氰胺、硅酸铝纤维和海泡石,并混合均匀得到混合液;
步骤2),按重量份称取氧化铝,并将氧化铝加入到混合液中,搅拌均匀使氧化铝均匀分散到混合液中,得到分散液;
步骤3),将分散液中加入石棉纤维素、可膨胀石墨和高岭土,均匀分散50min-80min,过滤灌装。
本实施例的方法简单,能减少有效成分的破坏。
实施例3
实施例的一种保温防火材料,以重量份计,包括50份亚麻油醇酸树脂、20份氧化铝、50份聚磷酸铵、24份纳米钛白粉、20份硼砂、10份海泡石、10份硅酸锆粉或钇稳定氧化锆粉、10份三聚氰胺、5份硅酸铝纤维、7份石棉纤维素、2份柠檬酸、2份可膨胀石墨、0.6份高岭土。
本实施例的一种保温防火材料的制备方法,包括以下步骤:
步骤1),按重量份称取亚麻油醇酸树脂、纳米钛白粉、聚磷酸铵、硅酸锆粉或钇稳定氧化锆粉、柠檬酸、硼砂、三聚氰胺、硅酸铝纤维和海泡石,并混合均匀得到混合液;
步骤2),按重量份称取氧化铝,并将氧化铝加入到混合液中,搅拌均匀使氧化铝均匀分散到混合液中,得到分散液;
步骤3),将分散液中加入石棉纤维素、可膨胀石墨和高岭土,均匀分散50min-80min,过滤灌装。
本实施例的方法简单,能减少有效成分的破坏。
对实施例1-3中的保温防火材料的耐高温性能进行试验。分别取实施例1-3所述的防火材料,分别为防火材料A、防火材料B、防火材料C,然后将防火材料A-C涂覆在墙壁的一侧面上,并对墙壁的另一侧面采用相同的温度进行高温加热且加热时间相同,加热温度为150℃,加热时间为2h。然后对防水材料的另一侧面的温度进行检测,检测结果如表1所示。
表1防火材料的防火性能
由表1可知,本实施例的防火材料能够防火隔热效果好。
以上所述仅为本发明的较佳实施例,并不用以限制本发明,凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (5)
1.一种保温防火材料,其特征在于,以重量份计,包括30份-50份亚麻油醇酸树脂、10份-20份氧化铝、30份-50份聚磷酸铵、18份-24份纳米钛白粉、10份-20份硼砂、5份-10份海泡石、5份-10份硅酸锆粉或钇稳定氧化锆粉、5份-10份三聚氰胺、2份-5份硅酸铝纤维、3份-7份石棉纤维素、1份-2份柠檬酸、1份-2份可膨胀石墨、0.2份-0.6份高岭土。
2.根据权利要求1所述一种保温防火材料,其特征在于,以重量份计,包括30份亚麻油醇酸树脂、10份氧化铝、30份聚磷酸铵、18份纳米钛白粉、10份硼砂、5份海泡石、5份硅酸锆粉或钇稳定氧化锆粉、5份三聚氰胺、2份硅酸铝纤维、3份石棉纤维素、1份柠檬酸、1份可膨胀石墨、0.2份高岭土。
3.根据权利要求1所述一种保温防火材料,其特征在于,以重量份计,包括40份亚麻油醇酸树脂、15份氧化铝、40份聚磷酸铵、20份纳米钛白粉、15份硼砂、8份海泡石、7份硅酸锆粉或钇稳定氧化锆粉、8份三聚氰胺、3份硅酸铝纤维、4份石棉纤维素、1.5份柠檬酸、1.5份可膨胀石墨、0.4份高岭土。
4.根据权利要求1所述一种保温防火材料,其特征在于,以重量份计,包括50份亚麻油醇酸树脂、20份氧化铝、50份聚磷酸铵、24份纳米钛白粉、20份硼砂、10份海泡石、10份硅酸锆粉或钇稳定氧化锆粉、10份三聚氰胺、5份硅酸铝纤维、7份石棉纤维素、2份柠檬酸、2份可膨胀石墨、0.6份高岭土。
5.一种如权利要求1至4任一项所述保温防火材料的制备方法,其特征在于,包括以下步骤:
步骤1),按重量份称取亚麻油醇酸树脂、纳米钛白粉、聚磷酸铵、硅酸锆粉或钇稳定氧化锆粉、柠檬酸、硼砂、三聚氰胺、硅酸铝纤维和海泡石,并混合均匀得到混合液;
步骤2),按重量份称取氧化铝,并将氧化铝加入到混合液中,搅拌均匀使氧化铝均匀分散到混合液中,得到分散液;
步骤3),将分散液中加入石棉纤维素、可膨胀石墨和高岭土,均匀分散50min-80min,过滤灌装。