CN103602179A - 隔热保温涂料 - Google Patents
隔热保温涂料 Download PDFInfo
- Publication number
- CN103602179A CN103602179A CN201310478694.5A CN201310478694A CN103602179A CN 103602179 A CN103602179 A CN 103602179A CN 201310478694 A CN201310478694 A CN 201310478694A CN 103602179 A CN103602179 A CN 103602179A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- heat insulating
- insulating coatings
- thermal insulation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种隔热保温涂料,其组分按重量份数包括:水性丙烯酸乳液200~240份,水120~150分,重钙65~85份,钛白粉40~60份,滑石粉20~30份,煅烧高岭土20~30份,硅酸铝粉10~20份,云母粉10~20份,空心微珠10~15份,乙二醇4~8份,成膜助剂4~8份,分散剂2~4份,消泡剂2~4份,羟乙基纤维素2~3份,增稠剂1~3份,润湿剂1~2份,流平剂1~2份,防腐剂0.5~1.5份,防霉剂0.5~1.5份,多功能助剂0.5~1份。本发明的隔热保温涂料隔热保温效果好,可广泛用于各种建筑外墙,还可用于船舶、矿山机械等,本发明的隔热保温涂料施工工艺简单,施工难度低,成本低廉,便于大规模推广应用。
Description
技术领域
本发明属于化工涂料技术领域,尤其涉及一种隔热保温涂料。
背景技术
在当前全球热效应加剧的今天,节能减排是世界建筑行业普遍面临的问题,我国的资源相对不足,但耗能日巨,能源问题已经成为制约经济发展的主要因素,节约能源刻不容缓,随着我国对节约能源与保护环境的不断重视,建筑节能是大势所趋,建筑结构的保温技术也在日益加强,尤其是外墙保温技术得到长足的发展。目前在外墙保温这个技术体系中有多种多样的做法,比较成熟的建筑外墙保温技术主要是外挂式建筑外墙保温,该技术是采用粘接或者是专用的固定件,将岩(矿)棉板、玻璃棉毡、聚苯乙烯泡沫塑料板、钢丝网架夹芯墙板等保温材料贴、挂在建筑外墙上,然后抹抗裂砂浆,压入玻璃纤维网格布,使其形成保护层,最后加做装饰面。该技术的操作方法较复杂,需要先贴、挂,后又要抹抗裂砂浆和加上玻璃纤维网格布,以及做装饰面,这种外挂式的外墙保温材料虽然成本廉价,但在安装时施工难度大,耗费人力和工时;而且,目前普遍使用的外墙保温材料大部分是可燃的,只是在材料中加入部分阻燃剂才达到了阻燃效果,一旦遇到火宅,它们在焚烧下会产生有毒气体,威胁到人们的生命安全。
随着涂料技术的发展,保温涂料技术日臻成熟,目前由涂刷保温涂料代替外挂式外墙保温层已经成为一种技术趋势,但是受制于涂料的厚度较薄,涂料保温的技术效果还是没有外挂式外墙保温层好,目前急需研发保温效果好的保温涂料。
发明内容
本发明的目的在于针对现有技术的缺陷,提供一种隔热保温效果好的隔热保温涂料。
本发明的目的是通过以下技术方案来实现:
一种隔热保温涂料,所述隔热保温涂料的组分按重量份数包括:
水性丙烯酸乳液200~240份,水120~150分,重钙65~85份,钛白粉40~60份,滑石粉20~30份,煅烧高岭土20~30份,硅酸铝粉10~20份,云母粉10~20份,空心微珠10~15份,乙二醇4~8份,成膜助剂4~8份,分散剂2~4份,消泡剂2~4份,羟乙基纤维素2~3份,增稠剂1~3份,润湿剂1~2份,流平剂1~2份,防腐剂0.5~1.5份,防霉剂0.5~1.5份,多功能助剂0.5~1份。
其中,所述隔热保温涂料的组分按重量份数优选为:
水性丙烯酸乳液220份,水135分,重钙75份,钛白粉50份,滑石粉25份,煅烧高岭土25份,硅酸铝粉15份,云母粉15份,空心微珠12.5份,乙二醇6份,成膜助剂6份,分散剂3份,消泡剂3份,羟乙基纤维素2.5份,增稠剂2份,润湿剂1.5份,流平剂1.5份,防腐剂1份,防霉剂1份,多功能助剂0.75份。
其中,所述钛白粉优选为金红石型钛白粉。
其中,所述硅酸铝粉优选为超细硅酸铝粉。
其中,所述成膜助剂优选为伊斯曼化工有限公司生产的十二碳醇酯型成膜助剂。
其中,所述分散剂优选为巴斯夫股份公司生产的聚羧酸钠盐型分散剂,产品型号为5040。
其中,所述消泡剂优选为有机硅消泡剂。
其中,所述增稠剂优选为罗门哈斯公司生产的缔合型增稠剂,产品型号MC35。
其中,所述防腐剂优选为为罗门哈斯公司生产的异噻唑酮类化合物。
其中,所述防霉剂优选为罗门哈斯公司生产的复配型防真菌防藻菌剂。
其中,所述流平剂优选为聚二甲基硅氧烷。
其中,所述润湿剂优选为烷基聚氧乙烯醚。
其中,所述多功能助剂优选为美国陶氏公司生产的多功能助剂,产品型号为AMP-95。
与现有技术相比,本发明的隔热涂料隔热保温效果好,可广泛用于各种建筑外墙,还可用于船舶、矿山机械等,本发明的隔热保温涂料施工工艺简单,施工难度低,成本低廉,便于大规模推广应用。
具体实施方式
下面结合具体实施例,对本发明作进一步详细的阐述,但本发明的实施方式并不局限于实施例表示的范围。这些实施例仅用于说明本发明,而非用于限制本发明的范围。此外,在阅读本发明的内容后,本领域的技术人员可以对本发明作各种修改,这些等价变化同样落于本发明所附权利要求书所限定的范围。
下述实施例中,十二碳醇酯从伊斯曼化工有限公司购买;聚羧酸钠盐型分散剂从巴斯夫股份公司购买,产品型号为5040;缔合型增稠剂从罗门哈斯公司购买,产品型号MC35,异噻唑酮类化合物从罗门哈斯公司购买,复配型防真菌防藻菌剂从罗门哈斯公司购买;多功能助剂优选从美国陶氏公司购买,产品型号为AMP-95;其余组分也均可从市场上购买得到。
实施例1
一种隔热保温涂料,所述隔热保温涂料的组分按重量份数包括:水性丙烯酸乳液200份,水120分,重钙65份,金红石型钛白粉40份,滑石粉20份,煅烧高岭土20份,超细硅酸铝粉10份,云母粉10份,空心微珠10份,乙二醇4份,十二碳醇酯4份,聚羧酸钠盐型分散剂2份,有机硅消泡剂2份,羟乙基纤维素2份,缔合型增稠剂1份,烷基聚氧乙烯醚1份,聚二甲基硅氧烷1份,异噻唑酮类化合物0.5份,复配型防真菌防藻菌剂0.5份,多功能助剂0.5份。
实施例2
一种隔热保温涂料,所述隔热保温涂料的组分按重量份数包括:水性丙烯酸乳液240份,水150分,重钙85份,金红石型钛白粉60份,滑石粉30份,煅烧高岭土30份,超细硅酸铝粉20份,云母粉20份,空心微珠15份,乙二醇8份,十二碳醇酯8份,聚羧酸钠盐型分散剂4份,有机硅消泡剂4份,羟乙基纤维素3份,缔合型增稠剂3份,烷基聚氧乙烯醚2份,聚二甲基硅氧烷2份,异噻唑酮类化合物1.5份,复配型防真菌防藻菌剂1.5份,多功能助剂1份。
实施例3
一种隔热保温涂料,所述隔热保温涂料的组分按重量份数包括:水性丙烯酸乳液220份,水135分,重钙75份,金红石型钛白粉50份,滑石粉25份,煅烧高岭土25份,超细硅酸铝粉15份,云母粉15份,空心微珠12.5份,乙二醇6份,十二碳醇酯6份,聚羧酸钠盐型分散剂3份,有机硅消泡剂3份,羟乙基纤维素2.5份,缔合型增稠剂2份,烷基聚氧乙烯醚1.5份,聚二甲基硅氧烷1.5份,异噻唑酮类化合物1份,复配型防真菌防藻菌剂1份,多功能助剂.75份。
试验例保温性能测试
采用80cm×50cm×60cm的泡沫保温箱进行试验,箱子上盖的是表面光滑的大理石板,其他五个面采用50mm厚的泡沫构成,在大理石板上涂布不同厚度的涂层,在箱子内部的固定高度(离大理石板10cm)设置温度计,将箱子置于红外灯下,测定涂层下表面温度。涂层下表面温度是指涂层下表面在红外灯照射下,10min内温度不变化时测得的数值。
分别使用本发明实施例1、实施例2、实施例3的隔热保温涂料作为涂层进行试验,对照例采用北京志盛威华公司所生产的保温涂料。
试验数据如表1所示:
表1
涂料 | 涂层下表面温度(℃) |
实施例1 | 47 |
实施例2 | 48 |
实施例3 | 40 |
对照例 | 53 |
表1数据说明,本发明的隔热保温涂料具有较好的隔热保温效果,好于市售的保温涂料,其中以实施例3的隔热保温涂料隔热保温效果最好。
Claims (5)
1.一种隔热保温涂料,其特征在于,所述隔热保温涂料的组分按重量份数包括:
水性丙烯酸乳液200~240份,水120~150分,重钙65~85份,钛白粉40~60份,滑石粉20~30份,煅烧高岭土20~30份,硅酸铝粉10~20份,云母粉10~20份,空心微珠10~15份,乙二醇4~8份,成膜助剂4~8份,分散剂2~4份,消泡剂2~4份,羟乙基纤维素2~3份,增稠剂1~3份,润湿剂1~2份,流平剂1~2份,防腐剂0.5~1.5份,防霉剂0.5~1.5份,多功能助剂0.5~1份。
2.按照权利要求1所述的隔热保温涂料,其特征在于:所述隔热保温涂料的组分按重量份数为:
水性丙烯酸乳液220份,水135分,重钙75份,钛白粉50份,滑石粉25份,煅烧高岭土25份,硅酸铝粉15份,云母粉15份,空心微珠12.5份,乙二醇6份,成膜助剂6份,分散剂3份,消泡剂3份,羟乙基纤维素2.5份,增稠剂2份,润湿剂1.5份,流平剂1.5份,防腐剂1份,防霉剂1份,多功能助剂0.75份。
3.按照权利要求1所述的隔热保温涂料,其特征在于:所述钛白粉为金红石型钛白粉;所述硅酸铝粉为超细硅酸铝粉;所述成膜助剂为伊斯曼化工有限公司生产的十二碳醇酯型成膜助剂;所述分散剂为巴斯夫股份公司生产的聚羧酸钠盐型分散剂,产品型号为5040。
3.按照权利要求1所述的隔热保温涂料,其特征在于:所述消泡剂为有机硅消泡剂;所述增稠剂为罗门哈斯公司生产的缔合型增稠剂,产品型号MC35;所述防腐剂优选为为罗门哈斯公司生产的异噻唑酮类化合物。
4.按照权利要求1所述的隔热保温涂料,其特征在于:所述防霉剂优选为罗门哈斯公司生产的复配型防真菌防藻菌剂;所述流平剂为聚二甲基硅氧烷。
5.按照权利要求1所述的隔热保温涂料,其特征在于:所述润湿剂为烷基聚氧乙烯醚;所述多功能助剂为美国陶氏公司生产的多功能助剂,产品型号为AMP-95。