CN107716840A - A kind of production technology of ring forging - Google Patents
A kind of production technology of ring forging Download PDFInfo
- Publication number
- CN107716840A CN107716840A CN201710892347.5A CN201710892347A CN107716840A CN 107716840 A CN107716840 A CN 107716840A CN 201710892347 A CN201710892347 A CN 201710892347A CN 107716840 A CN107716840 A CN 107716840A
- Authority
- CN
- China
- Prior art keywords
- ring forging
- ring
- deflection
- forging
- production technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention discloses a kind of production technology of ring forging, is raw material from Q345D steel, raw material is forged to obtain ring forging, further comprising the steps of:A, ring forging is heated to 1200 DEG C~1240 DEG C, is incubated 2h;B, after insulation terminates, ring forging is taken out, pulled out, deflection is 50%~55%, carries out jumping-up, and deflection is 60%~65%, and whole deformation temperature control is at 1000 DEG C~1050 DEG C;C, size needed for rolling ring to ring forging, deflection are 40%~50%, and at 850 DEG C~900 DEG C, the wall thickness of ring forging is 90mm~120mm for whole deformation temperature control;D, it is air-cooled to room temperature.Present invention pulling, upset, rolling ring are carried out in same fire time, and deflection, upset deflection, the deflection of rolling ring pulled out by control, and by control pulling, it is upset after temperature and rolling ring after temperature, so that the yield strength for the ring forging produced reaches more than 360MPa, and ring forging does the Charpy-type test of V-notch at 20 DEG C, the average value of its ballistic work reaches more than 120J.
Description
Technical field
The present invention relates to metal material Field of Heat-treatment, more particularly to a kind of production technology of ring forging.
Background technology
At present, for using Q345D steel as raw material, wall thickness requires the ring forging in 90mm~120mm, using tune after forging
Matter processing, to cause its yield strength >=350MPa, and the Charpy-type test of V-notch is done at -20 DEG C, its ballistic work
Average value >=100J, so as to meet customer requirement.However, using modifier treatment after forging, not only processing cost is high, and production efficiency
Relatively low, thus, urgent need seeks a kind of new processing method.
The content of the invention
It is an object of the invention in view of the above-mentioned problems, a kind of production technology of ring forging is provided, to solve existing ring forging
Use modifier treatment after part forging, processing cost height, the problem of low production efficiency.
The purpose of the present invention is to be achieved through the following technical solutions:
A kind of production technology of ring forging, it is raw material from Q345D steel, raw material is forged to obtain ring forging, in addition to
Lower step:
A, ring forging is heated to 1200 DEG C~1240 DEG C, is incubated 2h;
B, after insulation terminates, ring forging is taken out, pulled out, deflection is 50%~55%, then carries out jumping-up,
Deflection is 60%~65%, and whole deformation temperature control is at 1000 DEG C~1050 DEG C;
C, the size needed for ring rolls carries out rolling ring to ring forging, deflection are 40%~50%, whole deformation temperature control
At 850 DEG C~900 DEG C, the wall thickness of ring forging is 90mm~120mm;
D, it is air-cooled to room temperature.
As a preferred embodiment of the present invention, ring forging is put into heating furnace in step a and heated.
As a preferred embodiment of the present invention, pulled out in step b using Single arm, pier is carried out using Single arm
Slightly.
Whole deformation temperature in above-mentioned steps b is pulling, the temperature of upset ring forging later, thus, pulling, upset efficiency
Will height, with ensure ring forging will not it is cold fall.
Whole deformation temperature in above-mentioned steps c is the temperature of ring forging after rolling ring, and thus, rolling ring efficiency is high, to ensure
Ring forging will not it is cold fall.
Beneficial effects of the present invention are that ring forging is heated to 1200 DEG C~1240 by a kind of production technology of ring forging
DEG C, and be incubated after 2h and pulled out, upset, rolling ring, room temperature is finally air-cooled to, it is pulled out, upset, rolling ring is entered in same fire time
OK, and by control pulling deflection, upset deflection, rolling ring deflection, and by control pulling, it is upset after temperature
Temperature after degree and rolling ring so that the yield strength for the ring forging produced reaches more than 360MPa, and ring forging is at -20 DEG C
Under do the Charpy-type test of V-notch, the average value of its ballistic work reaches more than 120J.
Embodiment
Technical scheme is further illustrated below by embodiment.It is understood that this place
The embodiment of description is used only for explaining the present invention, rather than limitation of the invention.
Embodiment 1
A kind of production technology of ring forging, it is raw material from Q345D steel in the present embodiment, raw material is forged to obtain ring
Forging, it is further comprising the steps of:
A, ring forging is put into heating furnace and is heated to 1240 DEG C, be incubated 2h;
B, after insulation terminates, ring forging is taken out, pulled out using Single arm, deflection 55%, is then used
Single arm carries out jumping-up, and deflection 65%, whole deformation temperature control is at 1045 DEG C;
C, the size needed for ring rolls carries out rolling ring to ring forging, deflection 50%, whole deformation temperature control is 865
DEG C, the wall thickness of ring forging is 90mm~120mm;
D, it is air-cooled to room temperature.
The ring forging gone out by using above-mentioned technique productions, its yield strength reaches 361MPa, and does V-arrangement at -20 DEG C
The Charpy-type test of breach, the average value of its ballistic work is 125J.
Embodiment 2
A kind of production technology of ring forging, it is raw material from Q345D steel in the present embodiment, raw material is forged to obtain ring
Forging, it is further comprising the steps of:
A, ring forging is put into heating furnace and is heated to 1220 DEG C, be incubated 2h;
B, after insulation terminates, ring forging is taken out, pulled out using Single arm, deflection 52%, is then used
Single arm carries out jumping-up, and deflection 62%, whole deformation temperature control is at 1025 DEG C;
C, the size needed for ring rolls carries out rolling ring to ring forging, deflection 46%, whole deformation temperature control is 874
DEG C, the wall thickness of ring forging is 90mm~120mm;
D, it is air-cooled to room temperature.
The ring forging gone out by using above-mentioned technique productions, its yield strength reaches 365MPa, and does V-arrangement at -20 DEG C
The Charpy-type test of breach, the average value of its ballistic work is 180J.
Embodiment 3
A kind of production technology of ring forging, it is raw material from Q345D steel in the present embodiment, raw material is forged to obtain ring
Forging, it is further comprising the steps of:
A, ring forging is put into heating furnace and is heated to 1200 DEG C, be incubated 2h;
B, after insulation terminates, ring forging is taken out, pulled out using Single arm, deflection 51%, is then used
Single arm carries out jumping-up, and deflection 60%, whole deformation temperature control is at 1004 DEG C;
C, the size needed for ring rolls carries out rolling ring to ring forging, deflection 42%, whole deformation temperature control is 852
DEG C, the wall thickness of ring forging is 90mm~120mm;
D, it is air-cooled to room temperature.
The ring forging gone out by using above-mentioned technique productions, its yield strength reaches 363MPa, and does V-arrangement at -20 DEG C
The Charpy-type test of breach, the average value of its ballistic work is 150J.
Above example is to elaborate the general principle and characteristic of the present invention, and the present invention is not limited by above-described embodiment,
Without departing from the spirit and scope of the present invention, the present invention also has various change and change, and these changes and modifications all fall
Enter in scope of the claimed invention.The claimed scope of the invention is defined by the following claims.
Claims (3)
1. a kind of production technology of ring forging, being raw material from Q345D steel, raw material is forged to obtain ring forging, it is characterised in that:
It is further comprising the steps of:
A, ring forging is heated to 1200 DEG C~1240 DEG C, is incubated 2h;
B, after insulation terminates, ring forging is taken out, pulled out, deflection is 50%~55%, then carries out jumping-up, is deformed
Measure as 60%~65%, whole deformation temperature control is at 1000 DEG C~1050 DEG C;
C, the size needed for ring rolls carries out rolling ring to ring forging, deflection are 40%~50%, and whole deformation temperature control is 850
DEG C~900 DEG C, the wall thickness of ring forging is 90mm~120mm;
D, it is air-cooled to room temperature.
A kind of 2. production technology of ring forging according to claim 1, it is characterised in that:Ring forging is put into step a
Heated in heating furnace.
A kind of 3. production technology of ring forging according to claim 1, it is characterised in that:Entered in step b using Single arm
Row pulling, carried out using Single arm upset.