CN107698245A - A kind of antidetonation is resistance to fall pottery blank - Google Patents
A kind of antidetonation is resistance to fall pottery blank Download PDFInfo
- Publication number
- CN107698245A CN107698245A CN201710981532.1A CN201710981532A CN107698245A CN 107698245 A CN107698245 A CN 107698245A CN 201710981532 A CN201710981532 A CN 201710981532A CN 107698245 A CN107698245 A CN 107698245A
- Authority
- CN
- China
- Prior art keywords
- parts
- antidetonation
- resistance
- pottery
- fall
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of antidetonation is resistance to fall pottery blank, and it is made of following raw materials according:Feldspar, kaolin, flint slope soil, carclazyte, yellow cash, black clay, quartzy sandstone, nanometer boron fibre, butyl rubber and polyurethane resin;The present invention passes through reasonable selection formula, and add appropriate nanometer boron fibre, butyl rubber and polyurethane resin, the intensity and toughness of pottery can be improved, ensure that its antidetonation is resistance to fall, the heat-resisting quantity and wearability of porcelain can be improved again, pottery stable performance prepared by pottery blank produced by the present invention, antidetonation is resistance to fall, it is easy to use, wide adaptability.
Description
Technical field
The invention belongs to pottery field of material technology, and in particular to a kind of antidetonation is resistance to fall pottery blank.
Background technology
Pottery is using glaze thickness as this, and in its color or heavy glaze bottom or outstanding glaze or floating glaze table, the thick muddy work of glaze, glaze layer opalescence jade-like stone moisten,
Work of being administrations with multiplied departments is intended to drip, and third dimension is extremely strong.For pottery using transmutation as god, natural transmutation is the elite place of pottery art, and
Pottery is rely the four seas of becoming famous, the rare part for porcelain woods of making a name.With applying a kind of glaze in firing, once burn till then in it is multicoloured i.e.
" it is of the same colour entering kiln, kiln discharge ten thousand is color ".Protean transmutation effect, forms the infinite mystery of colors changing hue, it is red it is inner it is purple, purple in
Resided in dark blue, blue or green it is white, white in it is general red, multicolored imbibition, form a brightening, and have the title of " pottery without right, transmutation is unparalleled ".
When pottery is made, although present technology has been achieved for remarkable progress, but some defects be present,
Pottery, from sorting to finished product is fired, during which undergoes tens of road production processes in manufacturing process, and the careless of process can also make
Into all that has been achieved is spoiled, this is also pottery the reason for yield is extremely low all the time.
The blank that pottery uses is not quite similar by its performance requirement is raw materials used, its blank used be typically all using clay as
Primary raw material, alternatively referred to as clayey blank.Clayey blank is to make the raw clay that ceramics generally use at all times, by geology
Origin cause of formation clay is commonly divided into two types, i.e. primary clay and sedimentary clay, and clay is characterized in after being combined with appropriate water
With very strong plasticity, the clay of plastic forming is fabricated to the sintering that can become to have some strength after certain body roasting
Base substrate afterwards.Pottery, stove an ancient unit of weight are no exception.
China is in the world earliest using one of country of porcelain.Porcelain vessel because of its practicality and is examined as daily utensil
U.S.'s property is used till today.Even to this day, due to the progress of science and technology, there are many materials that can replace porcelain vessel, such as
Stainless steel, plastics etc., compared with vessel made of these materials, traditional lacquer vessel also there is the shortcomings that poor mechanical property,
Antidetonation is not resistance to falls, and is come off and is easily broken into pieces using process imprudence, therefore, it is necessary to a kind of brand-new porcelain vessel, to solve it not
Antidetonation is intolerant to the performance fallen.
The content of the invention
In order to solve the above problems, a kind of antidetonation of present invention offer is resistance to fall pottery blank.
The technical solution adopted by the present invention is:
A kind of antidetonation is resistance to fall pottery blank, and it is made of following raw materials according:Feldspar, kaolin, flint slope soil, carclazyte, yellow cash,
Black clay, quartzy sandstone, nanometer boron fibre, butyl rubber and polyurethane resin.
A kind of antidetonation is resistance to fall pottery blank, and it is made from the following raw materials in parts by weight:Feldspar 30-40 parts, kaolin
30-50 parts, flint slope soil 20-30 parts, carclazyte 10-20 parts, yellow cash 10-20 parts, black clay 20-30 parts, quartzy sandstone 10-20
Part, nanometer boron fibre 3-9 parts, butyl rubber 3-9 parts and polyurethane resin 3-9 parts.
A kind of antidetonation is resistance to fall pottery blank, and it is made from the following raw materials in parts by weight:35 parts of feldspar, kaolin 40
Part, 25 parts of flint slope soil, 15 parts of carclazyte, 15 parts of yellow cash, 25 parts of black clay, 6 parts of 15 part, nanometer boron fibre of quartzy sandstone, butyl
6 parts of 6 parts of rubber and polyurethane resin.
The beneficial effects of the invention are as follows:The present invention adds appropriate nanometer boron fibre, butyl by reasonable selection formula
Rubber and polyurethane resin, the intensity and toughness of pottery can be improved, ensure that its antidetonation is resistance to and fall, the resistance to height of porcelain can be improved again
Warm nature and wearability, pottery stable performance prepared by pottery blank produced by the present invention, antidetonation is resistance to fall, easy to use, adaptability
Extensively.
Embodiment
A kind of antidetonation is resistance to fall pottery blank, and it is made of following raw materials according:Feldspar, kaolin, flint slope soil, carclazyte,
Yellow cash, black clay, quartzy sandstone, nanometer boron fibre, butyl rubber and polyurethane resin.
A kind of antidetonation is resistance to fall pottery blank, and it is made from the following raw materials in parts by weight:Feldspar 30-40 parts, kaolin
30-50 parts, flint slope soil 20-30 parts, carclazyte 10-20 parts, yellow cash 10-20 parts, black clay 20-30 parts, quartzy sandstone 10-20
Part, nanometer boron fibre 3-9 parts, butyl rubber 3-9 parts and polyurethane resin 3-9 parts.
A kind of antidetonation is resistance to fall pottery blank, and it is made from the following raw materials in parts by weight:35 parts of feldspar, kaolin 40
Part, 25 parts of flint slope soil, 15 parts of carclazyte, 15 parts of yellow cash, 25 parts of black clay, 6 parts of 15 part, nanometer boron fibre of quartzy sandstone, butyl
6 parts of 6 parts of rubber and polyurethane resin.
In use, first pouring into each raw material weighed up in ball grinder, expect:Ball:Ratio=1 of water:(1.5-2):(0.8-
1.2), instill two and drip glass as electrolyte, ball milling 20-30 minutes.Then by the good slurry of ball milling through screen filtration,
Remove the impurity of larger particles.The slurry filtered is poured into ready mould to absorb water to mould and pinched.By plastic forming
Raw material be fabricated to base substrate after the sintering that can become that there is some strength after the roasting of certain body.Again glazing, be finally fired by glaze.
Embodiment 1
A kind of antidetonation is resistance to fall pottery blank, and it is made from the following raw materials in parts by weight:35 parts of feldspar, 40 parts of kaolin, fire
25 parts of stoneledge soil, 15 parts of carclazyte, 15 parts of yellow cash, 25 parts of black clay, 6 parts of 15 part, nanometer boron fibre of quartzy sandstone, butyl rubber 6
6 parts of part and polyurethane resin.
In use, first pouring into each raw material weighed up in ball grinder, expect:Ball:Ratio=1 of water:1.8:1.0, instill two
Glass drip as electrolyte, ball milling 20-30 minutes.Then the good slurry of ball milling is removed larger through screen filtration
The impurity of grain.The slurry filtered is poured into ready mould to absorb water to mould and pinched.The raw material of plastic forming is made
Base substrate after the sintering that can become there is some strength after being calcined into certain body.Again glazing, be finally fired by glaze.
Embodiment 2
A kind of antidetonation is resistance to fall pottery blank, and it is made from the following raw materials in parts by weight:30 parts of feldspar, 30 parts of kaolin, fire
20 parts of stoneledge soil, 10 parts of carclazyte, 10 parts of yellow cash, 20 parts of black clay, 3 parts of 10 part, nanometer boron fibre of quartzy sandstone, butyl rubber 3
3 parts of part and polyurethane resin.
In use, first pouring into each raw material weighed up in ball grinder, expect:Ball:Ratio=1 of water:1.5:0.8, instill two
Glass drip as electrolyte, ball milling 20-30 minutes.Then the good slurry of ball milling is removed larger through screen filtration
The impurity of grain.The slurry filtered is poured into ready mould to absorb water to mould and pinched.The raw material of plastic forming is made
Base substrate after the sintering that can become there is some strength after being calcined into certain body.Again glazing, be finally fired by glaze.
Embodiment 3
A kind of antidetonation is resistance to fall pottery blank, and it is made from the following raw materials in parts by weight:40 parts of feldspar, 50 parts of kaolin, fire
30 parts of stoneledge soil, 20 parts of carclazyte, 20 parts of yellow cash, 30 parts of black clay, 9 parts of 20 part, nanometer boron fibre of quartzy sandstone, butyl rubber 9
9 parts of part and polyurethane resin.
In use, first pouring into each raw material weighed up in ball grinder, expect:Ball:Ratio=1 of water:2:1.2, instill two drops
Waterglass is as electrolyte, ball milling 20-30 minutes.Then the good slurry of ball milling is removed into larger particles through screen filtration
Impurity.The slurry filtered is poured into ready mould to absorb water to mould and pinched.The raw material of plastic forming is fabricated to
Base substrate after the sintering that can become there is some strength after certain body roasting.Again glazing, be finally fired by glaze.
Claims (3)
1. a kind of antidetonation is resistance to fall pottery blank, it is characterised in that:It is made of following raw materials according:Feldspar, kaolin, flint slope
Soil, carclazyte, yellow cash, black clay, quartzy sandstone, nanometer boron fibre, butyl rubber and polyurethane resin.
2. a kind of antidetonation according to claim 1 is resistance to fall pottery blank, it is characterised in that:It is by the original of following parts by weight
Made of material:It is feldspar 30-40 parts, kaolin 30-50 parts, flint slope soil 20-30 parts, carclazyte 10-20 parts, yellow cash 10-20 parts, black
Clay 20-30 parts, quartzy sandstone 10-20 parts, nanometer boron fibre 3-9 parts, butyl rubber 3-9 parts and polyurethane resin 3-9 parts.
3. a kind of antidetonation according to claim 1 is resistance to fall pottery blank, it is characterised in that:It is by the original of following parts by weight
Made of material:35 parts of feldspar, 40 parts of kaolin, 25 parts of flint slope soil, 15 parts of carclazyte, 15 parts of yellow cash, 25 parts of black clay, quartz sand
6 parts of 6 parts of 15 part, nanometer boron fibre of rock, 6 parts of butyl rubber and polyurethane resin.