CN107674616A - A kind of preparation method of concave convex rod wlding adhesive specially - Google Patents
A kind of preparation method of concave convex rod wlding adhesive specially Download PDFInfo
- Publication number
- CN107674616A CN107674616A CN201711102745.9A CN201711102745A CN107674616A CN 107674616 A CN107674616 A CN 107674616A CN 201711102745 A CN201711102745 A CN 201711102745A CN 107674616 A CN107674616 A CN 107674616A
- Authority
- CN
- China
- Prior art keywords
- parts
- adhesive
- wlding
- convex rod
- concave convex
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation method of concave convex rod wlding adhesive specially, the raw material that the concave convex rod wlding adhesive specially includes following parts by weight is made:56 parts of 12 13 parts of PVA protecting colloids, 24 parts of defoamer, 35 parts of wetting agent, 13 parts of butyl acrylate, 56 parts of adhesive, 56 parts of high-cis butadiene rubber, 23 parts of oil-extended styrene buadiene rubber, 24 parts of accelerator, 57 parts of age resistor, 34 parts of tackifying resin, 8 10 parts of inorganic silicate, 24 parts of inorganic phosphate, 1 part of sodium chloride, 56 parts of vinyl acetate and initiator.PVA protecting colloids substitute poisonous solvent-based adhesive; stable performance; it is more environmentally-friendly; reduce the injury to human body and environment; there is the irreplaceable superiority of other adhesive in terms of bonding, in terms of environmental protection and in terms of the transport of product; and preparation technology is simple, it is not necessary to large-scale, high precision instrument equipment.
Description
Technical field
The present invention relates to concave convex rod technical field, more particularly to a kind of concave convex rod wlding adhesive specially.
Background technology
Attapulgite is also known as palygorskite (Palygorskite) or Palygorskite, is a kind of to have chain layer structure and contain Shuifu County
Magnesium silicate clay mineral.Its structure belongs to 2:1 type clay mineral.Each 2:In 1 unit structure layer, tetrahedron chip angle top every
Certain distance direction overturns, forming layer chain.The passage parallel with chain is formed in tetrahedron bar interband.Features of Attapulgite Minerals is almost
Various regions all over the world, but the mineral deposit proportion with industrial significance is little, is only limitted to the U.S., China, Spain, France, soil
Ear its, Senegal, South Africa, Australia, Brazil, Israel, Saudi Arabia, Switzerland, Britain, Russia (Irkutsk
, Irkutsk), Kirghizstan, Kazakhstan, Ukraine, Armenia, Azerbaijan, Byelorussia, Nepal
Deng state, according to incompletely statistics, about 1,400,000,000 tons of world's proved reserves.Concave-convex clay rod refers to using attapulgite as key component
A kind of clay mineral.Attapulgite is that a kind of crystalloid is hydrated alumina magnesia silicate, has unique layer chain structure feature,
Crystal lattice in its structure be present, help to contain variable amount of Na in crystal+、Ca2+、Fe3+、Al3+, crystal is in needle-like, threadiness
Or fiber collection shape.Attapulgite has good colloidal nature and the higher absorption such as unique scattered, high temperature resistant, salt resistance alkali
Decoloring ability.And there is certain plasticity and cohesive force, its preferable chemical molecular formula is:Mg5Si8O20(OH)2(OH2)4·
4H2O.With the intermediate structure between chain structure and layer structure.Attapulgite originates in deposition in earthy, compact massive
In rock and weathering crust, color is white, canescence, cinerous, celadon or weak silky luster.Soil property is fine and smooth, there is oily soapy,
It is light, property is crisp, fracture is in conchoidal or irregular shape, and water imbibition is strong.Has viscosity and plasticity when wet, dry after-contraction is small, less
Aobvious crackle, water immersion disintegration.Suspension meets dielectric not flocculation sediment.
For the adhesive of concave convex rod wlding, traditional adhesive is typically with S:S, SIS, EVA, acrylic resin etc. are
Matrix resin, with toluene, ethyl acetate, gasoline etc. for solvent, aid in being made with auxiliary agents such as tackifying resin, plasticizer.Except viscous
Connect outside better performances, solvent-based adhesive also has many shortcomings, and such as solvent volatilization pollutes, be inflammable and explosive, having
Certain limitation.
The content of the invention
The invention aims to solve shortcoming present in prior art, and a kind of concave convex rod wlding proposed is special
The preparation method of adhesive.
To achieve these goals, present invention employs following technical scheme:
A kind of concave convex rod wlding adhesive specially, the concave convex rod wlding adhesive specially include the raw material system of following parts by weight
Into:PVA protecting colloid 12-13 parts, defoamer 2-4 parts, wetting agent 3-5 parts, butyl acrylate 1-3 parts, adhesive 5-6 parts, height
Cis butadiene rubber 5-6 parts, oil-extended styrene buadiene rubber 2-3 parts, accelerator 2-4 parts, age resistor 5-7 parts, tackifying resin 3-4 parts, nothing
Machine silicate 8-10 parts, inorganic phosphate 2-4 parts, 1 part of sodium chloride, vinyl acetate 5-6 parts and initiator 5-6 parts.
Preferably, the inorganic silicate is graininess, and the inorganic silicate is the mixed of dicalcium silicate and tricalcium silicate
The blend gravity of compound, dicalcium silicate and tricalcium silicate concretely 1:2.
Preferably, the inorganic phosphate is the mixture of dihydric phosphate, hydrophosphate and orthophosphates, and mixes
Proportion can be 1:2:3.
Preferably, described adhesive be one kind in calcium sulfate, calcium carbonate, pregelatinized starch, sodium carboxymethylcellulose or
Several, the defoamer is silicone emulsion, polyoxyethylene polyoxy propyl alcohol amidogen ether, polypropylene glycerol aether, polyoxypropylene polyoxy second
At least one of alkene glycerin ether and dimethyl silicone polymer, the wetting agent are at least one of propane diols and glycerine.
Preferably, cis Isosorbide-5-Nitrae content is 96%~99% in the high-cis butadiene rubber.
Preferably, the accelerator includes at least one of nitrogenous and organic compound of sulfur-bearing, described nitrogenous and contain
The organic compound of sulphur includes accelerator H, accelerator D, vulcanization accelerator TT, accelerator M and two thio ammonia
At least one of base formates.
Preferably, the tackifying resin has excellent polymer compatibility, each component institute accounting wherein in tackifying resin
Example be:Dimethyl methyl acid resin 60%, phenolphthalein resin 25%, 201 resins 15%, each component proportion is in the old agent:It is anti-old
Agent CPPD50%, anti-aging agent RD 25%, antioxidant D 25%.
A kind of preparation method of concave convex rod wlding adhesive specially, specifically comprises the following steps:
S1:PVA protecting colloids, defoamer, wetting agent, butyl acrylate, adhesive, high-cis butadiene rubber, oil-filled butylbenzene rubber
Glue, accelerator, age resistor, tackifying resin, inorganic silicate, inorganic phosphate, sodium chloride, vinyl acetate, initiator and water are pressed
Ratio weigh measure it is standby;
S2:By the PVA protecting colloids in step S1, wetting agent, butyl acrylate, adhesive, high-cis butadiene rubber, oil-filled fourth
Benzene rubber, tackifying resin, inorganic silicate, inorganic phosphate, sodium chloride and vinyl acetate are added in grinding drum, utilize grinding
Bucket is ground, material is mixed it is abundant, milling time between 0.5h-0.6h, grinding temperature control 45-85 degrees Celsius it
Between, the rotating speed of grinder is 1000-1200 revs/min, and standby, raw material sealing guarantor is collected mixed material after terminating in grinding
Deposit;
S3:The material obtained in step S2 is added in agitator, control agitator rotating speed be no more than 1000-1200 turn/
Minute, between 40-50 degrees Celsius of reaction temperature, defoamer is then added into agitator, the reaction time is controlled in 0.5h-0.6h
Between;
S4:Accelerator and the control of water reaction time are added in agitator into step S3 between 0.4h-0.5h, reaction temperature
Between 40-50 degrees Celsius;
S5:Age resistor is added in agitator into step S4, the reaction time is controlled between 0.4h-0.5h, and reaction temperature exists
Between 50-60 degrees Celsius;
S6:Initiator is added in agitator into step S5, temperature control polymerize 2-3 hour plastics at 40-50 degrees Celsius,
Then it is granulated and is collected standby;
S7:The material obtained in step S6 is dried using air-heater, the water content in material is no more than 5%, drying temperature
Degree is collected standby between 50-60 degrees Celsius;
S8:The material obtained in step S7 is crushed using pulverizer, and the material after crushing is sieved, using 60-80
Mesh sieve, ensure that material particles are uniform, then by material collection.
A kind of preparation method of concave convex rod wlding adhesive specially provided by the invention, the substitution of PVA protecting colloids are poisonous
Solvent-based adhesive, stable performance is more environmentally-friendly, reduces the injury to human body and environment, in terms of bonding, in terms of environmental protection
And have the irreplaceable superiority of other adhesive in terms of the transport of product, and preparation technology is simple, it is not necessary to large-scale,
High precision instrument equipment.
Embodiment
In order to make the purpose , technical scheme and advantage of the present invention be clearer, below in conjunction with specific embodiment, to this
Invention is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, not
For limiting the present invention.
Embodiment 1
A kind of concave convex rod wlding adhesive specially, the concave convex rod wlding adhesive specially include the raw material system of following parts by weight
Into:12 parts of PVA protecting colloids, 2 parts of defoamer, 3 parts of wetting agent, 1 part of butyl acrylate, 5 parts of adhesive, high-cis butadiene rubber
5 parts, 2 parts of oil-extended styrene buadiene rubber, 2 parts of accelerator, 5 parts of age resistor, 3 parts of tackifying resin, 8 parts of inorganic silicate, inorganic phosphate 2
Part, 1 part of sodium chloride, 5 parts of vinyl acetate and 5 parts of initiator, the inorganic silicate are graininess, and the inorganic silicate is silicon
The blend gravity of the mixture of sour dicalcium and tricalcium silicate, dicalcium silicate and tricalcium silicate concretely 1:2, the inorganic phosphate
Salt is the mixture of dihydric phosphate, hydrophosphate and orthophosphates, and blend gravity can be 1:2:3, described adhesive is
One or more in calcium sulfate, calcium carbonate, pregelatinized starch, sodium carboxymethylcellulose, the defoamer are silicone emulsion, gathered
In oxygen ethene polyoxy propyl alcohol amidogen ether, polypropylene glycerol aether, polyoxyethylene polyoxypropylene glycerin ether and dimethyl silicone polymer
At least one, the wetting agent are at least one of propane diols and glycerine, cis Isosorbide-5-Nitrae content in the high-cis butadiene rubber
For 96%~99%, the accelerator includes at least one of nitrogenous and organic compound of sulfur-bearing, described nitrogenous and sulfur-bearing
Organic compound includes accelerator H, accelerator D, vulcanization accelerator TT, accelerator M and dithiocarbamates first
At least one of hydrochlorate, the tackifying resin has excellent polymer compatibility, wherein in tackifying resin shared by each component
Ratio is:Dimethyl methyl acid resin 60%, phenolphthalein resin 25%, 201 resins 15%, each component proportion is in the old agent:It is anti-
Old agent CPPD50%, anti-aging agent RD 25%, antioxidant D 25%.
A kind of preparation method of concave convex rod wlding adhesive specially, specifically comprises the following steps:
S1:PVA protecting colloids, defoamer, wetting agent, butyl acrylate, adhesive, high-cis butadiene rubber, oil-filled butylbenzene rubber
Glue, accelerator, age resistor, tackifying resin, inorganic silicate, inorganic phosphate, sodium chloride, vinyl acetate, initiator and water are pressed
Ratio weigh measure it is standby;
S2:By the PVA protecting colloids in step S1, wetting agent, butyl acrylate, adhesive, high-cis butadiene rubber, oil-filled fourth
Benzene rubber, tackifying resin, inorganic silicate, inorganic phosphate, sodium chloride and vinyl acetate are added in grinding drum, utilize grinding
Bucket is ground, material is mixed it is abundant, milling time between 0.5h-0.6h, grinding temperature control 45-85 degrees Celsius it
Between, the rotating speed of grinder is 1000-1200 revs/min, and standby, raw material sealing guarantor is collected mixed material after terminating in grinding
Deposit;
S3:The material obtained in step S2 is added in agitator, control agitator rotating speed be no more than 1000-1200 turn/
Minute, between 40-50 degrees Celsius of reaction temperature, defoamer is then added into agitator, the reaction time is controlled in 0.5h-0.6h
Between;
S4:Accelerator and the control of water reaction time are added in agitator into step S3 between 0.4h-0.5h, reaction temperature
Between 40-50 degrees Celsius;
S5:Age resistor is added in agitator into step S4, the reaction time is controlled between 0.4h-0.5h, and reaction temperature exists
Between 50-60 degrees Celsius;
S6:Initiator is added in agitator into step S5, temperature control polymerize 2-3 hour plastics at 40-50 degrees Celsius,
Then it is granulated and is collected standby;
S7:The material obtained in step S6 is dried using air-heater, the water content in material is no more than 5%, drying temperature
Degree is collected standby between 50-60 degrees Celsius;
S8:The material obtained in step S7 is crushed using pulverizer, and the material after crushing is sieved, using 60-80
Mesh sieve, ensure that material particles are uniform, then by material collection.
Embodiment 2
A kind of concave convex rod wlding adhesive specially, the concave convex rod wlding adhesive specially include the raw material system of following parts by weight
Into:11 parts of PVA protecting colloids, 3 parts of defoamer, 4 parts of wetting agent, 2 parts of butyl acrylate, 5.5 parts of adhesive, high-cis are along fourth rubber
5.5 parts of glue, 2.5 parts of oil-extended styrene buadiene rubber, 3 parts of accelerator, 6 parts of age resistor, 3.5 parts of tackifying resin, 9 parts of inorganic silicate, nothing
5.6 parts of 3 parts of machine phosphate, 1 part of sodium chloride, 5.5 parts of vinyl acetate and initiator, the inorganic silicate is graininess, described
Inorganic silicate is the mixture of dicalcium silicate and tricalcium silicate, the blend gravity of dicalcium silicate and tricalcium silicate concretely 1:
2, the inorganic phosphate is the mixture of dihydric phosphate, hydrophosphate and orthophosphates, and blend gravity can be 1:2:
3, described adhesive is the one or more in calcium sulfate, calcium carbonate, pregelatinized starch, sodium carboxymethylcellulose, the defoaming
Agent is silicone emulsion, polyoxyethylene polyoxy propyl alcohol amidogen ether, polypropylene glycerol aether, polyoxyethylene polyoxypropylene glycerin ether and poly- two
At least one of methylsiloxane, the wetting agent are at least one of propane diols and glycerine, and the high-cis is along fourth rubber
Cis Isosorbide-5-Nitrae content is 96%~99% in glue, and the accelerator includes at least one of nitrogenous and organic compound of sulfur-bearing, institute
Stating the nitrogenous and organic compound of sulfur-bearing includes accelerator H, accelerator D, vulcanization accelerator TT, accelerator M
At least one of with dithiocar-bamate, the tackifying resin has excellent polymer compatibility, wherein thickening tree
Each component proportion is in fat:Dimethyl methyl acid resin 60%, phenolphthalein resin 25%, 201 resins 15%, each group in the old agent
Point proportion is:Age resistor CPPD50%, anti-aging agent RD 25%, antioxidant D 25%.
A kind of preparation method of concave convex rod wlding adhesive specially, specifically comprises the following steps:
S1:PVA protecting colloids, defoamer, wetting agent, butyl acrylate, adhesive, high-cis butadiene rubber, oil-filled butylbenzene rubber
Glue, accelerator, age resistor, tackifying resin, inorganic silicate, inorganic phosphate, sodium chloride, vinyl acetate, initiator and water are pressed
Ratio weigh measure it is standby;
S2:By the PVA protecting colloids in step S1, wetting agent, butyl acrylate, adhesive, high-cis butadiene rubber, oil-filled fourth
Benzene rubber, tackifying resin, inorganic silicate, inorganic phosphate, sodium chloride and vinyl acetate are added in grinding drum, utilize grinding
Bucket is ground, material is mixed it is abundant, milling time between 0.5h-0.6h, grinding temperature control 45-85 degrees Celsius it
Between, the rotating speed of grinder is 1000-1200 revs/min, and standby, raw material sealing guarantor is collected mixed material after terminating in grinding
Deposit;
S3:The material obtained in step S2 is added in agitator, control agitator rotating speed be no more than 1000-1200 turn/
Minute, between 40-50 degrees Celsius of reaction temperature, defoamer is then added into agitator, the reaction time is controlled in 0.5h-0.6h
Between;
S4:Accelerator and the control of water reaction time are added in agitator into step S3 between 0.4h-0.5h, reaction temperature
Between 40-50 degrees Celsius;
S5:Age resistor is added in agitator into step S4, the reaction time is controlled between 0.4h-0.5h, and reaction temperature exists
Between 50-60 degrees Celsius;
S6:Initiator is added in agitator into step S5, temperature control polymerize 2-3 hour plastics at 40-50 degrees Celsius,
Then it is granulated and is collected standby;
S7:The material obtained in step S6 is dried using air-heater, the water content in material is no more than 5%, drying temperature
Degree is collected standby between 50-60 degrees Celsius;
S8:The material obtained in step S7 is crushed using pulverizer, and the material after crushing is sieved, using 60-80
Mesh sieve, ensure that material particles are uniform, then by material collection.
Embodiment 3
A kind of concave convex rod wlding adhesive specially, the concave convex rod wlding adhesive specially include the raw material system of following parts by weight
Into:13 parts of PVA protecting colloids, 4 parts of defoamer, 5 parts of wetting agent, 3 parts of butyl acrylate, 6 parts of adhesive, high-cis butadiene rubber
6 parts, 3 parts of oil-extended styrene buadiene rubber, 4 parts of accelerator, 7 parts of age resistor, 4 parts of tackifying resin, 10 parts of inorganic silicate, inorganic phosphate
6 parts of 4 parts, 1 part of sodium chloride, 6 parts of vinyl acetate and initiator, the inorganic silicate are graininess, and the inorganic silicate is
The blend gravity of the mixture of dicalcium silicate and tricalcium silicate, dicalcium silicate and tricalcium silicate concretely 1:2, the Phos
Hydrochlorate is the mixture of dihydric phosphate, hydrophosphate and orthophosphates, and blend gravity can be 1:2:3, described adhesive
The one or more in calcium sulfate, calcium carbonate, pregelatinized starch, sodium carboxymethylcellulose, the defoamer be silicone emulsion,
In polyoxyethylene polyoxy propyl alcohol amidogen ether, polypropylene glycerol aether, polyoxyethylene polyoxypropylene glycerin ether and dimethyl silicone polymer
At least one, the wetting agent is at least one of propane diols and glycerine, and cis Isosorbide-5-Nitrae contains in the high-cis butadiene rubber
Measure as 96%~99%, the accelerator includes at least one of nitrogenous and organic compound of sulfur-bearing, described nitrogenous and sulfur-bearing
Organic compound include accelerator H, accelerator D, vulcanization accelerator TT, accelerator M and dithiocarbamates
At least one of formates, the tackifying resin have excellent polymer compatibility, each component institute wherein in tackifying resin
Accounting example is:Dimethyl methyl acid resin 60%, phenolphthalein resin 25%, 201 resins 15%, each component proportion is in the old agent:
Age resistor CPPD50%, anti-aging agent RD 25%, antioxidant D 25%.
A kind of preparation method of concave convex rod wlding adhesive specially, specifically comprises the following steps:
S1:PVA protecting colloids, defoamer, wetting agent, butyl acrylate, adhesive, high-cis butadiene rubber, oil-filled butylbenzene rubber
Glue, accelerator, age resistor, tackifying resin, inorganic silicate, inorganic phosphate, sodium chloride, vinyl acetate, initiator and water are pressed
Ratio weigh measure it is standby;
S2:By the PVA protecting colloids in step S1, wetting agent, butyl acrylate, adhesive, high-cis butadiene rubber, oil-filled fourth
Benzene rubber, tackifying resin, inorganic silicate, inorganic phosphate, sodium chloride and vinyl acetate are added in grinding drum, utilize grinding
Bucket is ground, material is mixed it is abundant, milling time between 0.5h-0.6h, grinding temperature control 45-85 degrees Celsius it
Between, the rotating speed of grinder is 1000-1200 revs/min, and standby, raw material sealing guarantor is collected mixed material after terminating in grinding
Deposit;
S3:The material obtained in step S2 is added in agitator, control agitator rotating speed be no more than 1000-1200 turn/
Minute, between 40-50 degrees Celsius of reaction temperature, defoamer is then added into agitator, the reaction time is controlled in 0.5h-0.6h
Between;
S4:Accelerator and the control of water reaction time are added in agitator into step S3 between 0.4h-0.5h, reaction temperature
Between 40-50 degrees Celsius;
S5:Age resistor is added in agitator into step S4, the reaction time is controlled between 0.4h-0.5h, and reaction temperature exists
Between 50-60 degrees Celsius;
S6:Initiator is added in agitator into step S5, temperature control polymerize 2-3 hour plastics at 40-50 degrees Celsius,
Then it is granulated and is collected standby;
S7:The material obtained in step S6 is dried using air-heater, the water content in material is no more than 5%, drying temperature
Degree is collected standby between 50-60 degrees Celsius;
S8:The material obtained in step S7 is crushed using pulverizer, and the material after crushing is sieved, using 60-80
Mesh sieve, ensure that material particles are uniform, then by material collection.
A kind of preparation method of concave convex rod wlding adhesive specially provided by the invention, the substitution of PVA protecting colloids are poisonous
Solvent-based adhesive, stable performance is more environmentally-friendly, reduces the injury to human body and environment, in terms of bonding, in terms of environmental protection
And have the irreplaceable superiority of other adhesive in terms of the transport of product, and preparation technology is simple, it is not necessary to large-scale,
High precision instrument equipment.
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto,
Any one skilled in the art the invention discloses technical scope in, technique according to the invention scheme and its
Inventive concept is subject to equivalent substitution or change, should all be included within the scope of the present invention.
Claims (8)
- A kind of 1. concave convex rod wlding adhesive specially, it is characterised in that:The concave convex rod wlding adhesive specially includes following heavy The raw material of amount part is made:It is PVA protecting colloid 12-13 parts, defoamer 2-4 parts, wetting agent 3-5 parts, butyl acrylate 1-3 parts, viscous Mixture 5-6 parts, high-cis butadiene rubber 5-6 parts, oil-extended styrene buadiene rubber 2-3 parts, accelerator 2-4 parts, age resistor 5-7 parts, thickening Resin 3-4 parts, inorganic silicate 8-10 parts, inorganic phosphate 2-4 parts, 1 part of sodium chloride, vinyl acetate 5-6 parts and initiator 5-6 Part.
- A kind of 2. concave convex rod wlding adhesive specially according to claim 1, it is characterised in that:The inorganic silicate is Graininess, the inorganic silicate are the mixing ratio of the mixture of dicalcium silicate and tricalcium silicate, dicalcium silicate and tricalcium silicate Weight concretely 1:2.
- A kind of 3. concave convex rod wlding adhesive specially according to claim 1, it is characterised in that:The inorganic phosphate is The mixture of dihydric phosphate, hydrophosphate and orthophosphates, and blend gravity can be 1:2:3.
- A kind of 4. concave convex rod wlding adhesive specially according to claim 1, it is characterised in that:Described adhesive is sulfuric acid One or more in calcium, calcium carbonate, pregelatinized starch, sodium carboxymethylcellulose, the defoamer are silicone emulsion, polyoxy second In alkene polyoxy propyl alcohol amidogen ether, polypropylene glycerol aether, polyoxyethylene polyoxypropylene glycerin ether and dimethyl silicone polymer at least One kind, the wetting agent are at least one of propane diols and glycerine.
- A kind of 5. concave convex rod wlding adhesive specially according to claim 1, it is characterised in that:The high-cis is along fourth rubber Cis-1,4 content is 96%~99% in glue.
- A kind of 6. concave convex rod wlding adhesive specially according to claim 1, it is characterised in that:The accelerator includes containing At least one of organic compound of nitrogen and sulfur-bearing, the described nitrogenous and organic compound of sulfur-bearing include accelerator H, sulphur Change at least one of diphenylguanidine, vulcanization accelerator TT, accelerator M and dithiocar-bamate.
- A kind of 7. concave convex rod wlding adhesive specially according to claim 1, it is characterised in that:The tackifying resin has Each component proportion is in excellent polymer compatibility, wherein tackifying resin:Dimethyl methyl acid resin 60%, phenolphthalein resin 25%, 201 resins 15%, each component proportion is in the old agent:Age resistor CPPD50%, anti-aging agent RD 25%, age resistor D25%。
- 8. the preparation method of the concave convex rod wlding adhesive specially according to claim any one of 1-7, it is characterised in that:Bag Include following steps:S1:PVA protecting colloids, defoamer, wetting agent, butyl acrylate, adhesive, high-cis butadiene rubber, oil-filled butylbenzene rubber Glue, accelerator, age resistor, tackifying resin, inorganic silicate, inorganic phosphate, sodium chloride, vinyl acetate, initiator and water are pressed Ratio weigh measure it is standby;S2:By the PVA protecting colloids in step S1, wetting agent, butyl acrylate, adhesive, high-cis butadiene rubber, oil-filled fourth Benzene rubber, tackifying resin, inorganic silicate, inorganic phosphate, sodium chloride and vinyl acetate are added in grinding drum, utilize grinding Bucket is ground, material is mixed it is abundant, milling time between 0.5h-0.6h, grinding temperature control 45-85 degrees Celsius it Between, the rotating speed of grinder is 1000-1200 revs/min, and standby, raw material sealing guarantor is collected mixed material after terminating in grinding Deposit;S3:The material obtained in step S2 is added in agitator, control agitator rotating speed be no more than 1000-1200 turn/ Minute, between 40-50 degrees Celsius of reaction temperature, defoamer is then added into agitator, the reaction time is controlled in 0.5h-0.6h Between;S4:Accelerator and the control of water reaction time are added in agitator into step S3 between 0.4h-0.5h, reaction temperature Between 40-50 degrees Celsius;S5:Age resistor is added in agitator into step S4, the reaction time is controlled between 0.4h-0.5h, and reaction temperature exists Between 50-60 degrees Celsius;S6:Initiator is added in agitator into step S5, temperature control polymerize 2-3 hour plastics at 40-50 degrees Celsius, Then it is granulated and is collected standby;S7:The material obtained in step S6 is dried using air-heater, the water content in material is no more than 5%, drying temperature Degree is collected standby between 50-60 degrees Celsius;S8:The material obtained in step S7 is crushed using pulverizer, and the material after crushing is sieved, using 60-80 Mesh sieve, ensure that material particles are uniform, then by material collection.