CN107674269A - The preparation method of Electrostatic Absorption film production mould surfacing - Google Patents
The preparation method of Electrostatic Absorption film production mould surfacing Download PDFInfo
- Publication number
- CN107674269A CN107674269A CN201711080311.3A CN201711080311A CN107674269A CN 107674269 A CN107674269 A CN 107674269A CN 201711080311 A CN201711080311 A CN 201711080311A CN 107674269 A CN107674269 A CN 107674269A
- Authority
- CN
- China
- Prior art keywords
- parts
- absorption film
- electrostatic absorption
- curing agent
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of preparation method of Electrostatic Absorption film production mould surfacing, comprises the following steps:Following component is taken by weight:5 20 parts of polyhexamethylene sebacamide, 5 20 parts of butadiene-styrene rubber, 28 parts of boric acid, 24 parts of sodium carbonate, 24 parts of butanediol, 36 parts of aluminium hydroxide, 26 parts of curing agent;Above-mentioned raw materials are well mixed to obtain compound, the production of Electrostatic Absorption film is warming up to 120 degrees Celsius with the surface of mould, then by organic silica gel by compound uniform adhesion on the surface of mould, thickness is 120 350 μm, then hot pressing is uniform, and hot pressing temperature is 355 degrees Celsius.The remarkable result of the present invention is to be easier to be stripped in the production of Electrostatic Absorption film.
Description
Technical field
The present invention relates to Electrostatic Absorption film field, specifically, is related to a kind of Electrostatic Absorption film production mould surfacing
Preparation method.
Background technology
PE diaphragms make adhesive using Special polyethylene (PE) plastic sheeting as base material, with cross-linking type acrylic acid resin, then
It is process by several special auxiliary agents.Its property is soft, and adhesive performance is good, easily pastes, is easily peeled off, peels off no cull,
Application field is extensive, stainless steel plate, aluminium sheet, aluminium alloy extrusions, plastic-steel section bar and door and window, aluminium-plastic panel, fluorine carbon plate, mirror board, folder
Heart color steel, fire-proof plate, decoration panel, poly (methyl methacrylate) plate, PS, PE, PVC board sunlight board (polycarbonate plate), antitheft door, label,
Coated glass, top-grade furniture, high-grade handicraft, Electric Appliance Cabinet, computer casing, automobile lamp, floor, household appliances shell, instrument
Instrument, various fields are waited to need product surface to be protected all to can be used.
The film of static electrification easily adsorbs dust, makes film surface dirty;The normal operating of electrostatic influence film production, seriously
When can wound operator;The big film of electrostatic influences the normal production of machine, and it is normal that Fei Bao phenomena impairs tobacco factory is produced when serious
Production.It can thus be appreciated that eliminating electrostatic for PE films, meaning is very great.
The content of the invention
It is an object of the invention to provide a kind of preparation method of Electrostatic Absorption film production mould surfacing, with solution
State technical problem.
The present invention using following technical scheme in order to solve the above technical problems, realized:
A kind of preparation method of Electrostatic Absorption film production mould surfacing, it is characterised in that comprise the following steps:
Following component is taken by weight:Polyhexamethylene sebacamide 5-20 parts, butadiene-styrene rubber 5-20 parts, boric acid 2-8 parts, carbonic acid
Sodium 2-4 parts, butanediol 2-4 parts, aluminium hydroxide 3-6 parts, curing agent 2-6 parts;
Above-mentioned raw materials are well mixed that compound, the production of Electrostatic Absorption film are warming up to 120 degrees Celsius with the surface of mould,
Then it is 120-350 μm in the surface of mould, thickness by compound uniform adhesion by organic silica gel, then hot pressing is uniform, heat
It is 355 degrees Celsius to press temperature.
Each component preferred weight ratio is:10 parts of polyhexamethylene sebacamide, 15 parts of butadiene-styrene rubber, 6 parts of boric acid, 2 parts of sodium carbonate,
22 parts of butanediol, 32 parts of aluminium hydroxide, 2 parts of curing agent.
The curing agent is amine curing agent.
The curing agent is aromatic polyvalent amine curing agent.
The beneficial effects of the invention are as follows:
The remarkable result of the present invention is to be easier to be stripped in the production of Electrostatic Absorption film.
Embodiment
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, tie below
Specific embodiment is closed, the present invention is expanded on further, but following embodiments are only the preferred embodiments of the present invention, and it is not all.
Based on the embodiment in embodiment, those skilled in the art obtain other realities on the premise of creative work is not made
Example is applied, belongs to protection scope of the present invention.Experimental method in following embodiments, it is conventional method unless otherwise specified,
Material used, reagent etc., unless otherwise specified, are commercially obtained in following embodiments.
Embodiment 1
A kind of preparation method of Electrostatic Absorption film production mould surfacing, include the active princlple of following parts by weight:It is poly-
10 parts of hexamethylene sebacamide, 15 parts of butadiene-styrene rubber, 6 parts of boric acid, 2 parts of sodium carbonate, 22 parts of butanediol, 32 parts of aluminium hydroxide, fragrance
3 parts of the polynary amine curing agent of race.
Above-mentioned raw materials are well mixed that compound, the production of Electrostatic Absorption film are warming up to 120 degrees Celsius with the surface of mould,
Then it is 120-350 μm in the surface of mould, thickness by compound uniform adhesion by organic silica gel, then hot pressing is uniform, heat
It is 355 degrees Celsius to press temperature.
Embodiment 2
The present embodiment is same as Example 1 in addition to following characteristics:
A kind of preparation method of Electrostatic Absorption film production mould surfacing, include the active princlple of following parts by weight:It is poly-
16 parts of hexamethylene sebacamide, 18 parts of butadiene-styrene rubber, 4 parts of boric acid, 2 parts of sodium carbonate, 3 parts of butanediol, 3 parts of aluminium hydroxide, aromatic series
Polynary 4 parts of amine curing agent.
Above-mentioned raw materials are well mixed that compound, the production of Electrostatic Absorption film are warming up to 120 degrees Celsius with the surface of mould,
Then it is 120-350 μm in the surface of mould, thickness by compound uniform adhesion by organic silica gel, then hot pressing is uniform, heat
It is 355 degrees Celsius to press temperature.
General principle, principal character and the advantages of the present invention of the present invention has been shown and described above.The technology of the industry
For personnel it should be appreciated that the present invention is not limited to the above embodiments, that described in above-described embodiment and specification is only the present invention
Preference, be not intended to limit the present invention, without departing from the spirit and scope of the present invention, the present invention also have it is various
Changes and improvements, these changes and improvements all fall within the protetion scope of the claimed invention.The claimed scope of the invention is by institute
Attached claims and its equivalent thereof.
Claims (4)
1. a kind of preparation method of Electrostatic Absorption film production mould surfacing, it is characterised in that comprise the following steps:
Following component is taken by weight:Polyhexamethylene sebacamide 5-20 parts, butadiene-styrene rubber 5-20 parts, boric acid 2-8 parts, sodium carbonate 2-
4 parts, butanediol 2-4 parts, aluminium hydroxide 3-6 parts, curing agent 2-6 parts;
Above-mentioned raw materials are well mixed that compound, the production of Electrostatic Absorption film are warming up to 120 degrees Celsius with the surface of mould, then
By organic silica gel by compound uniform adhesion on the surface of mould, thickness is 120-350 μm, and then hot pressing is uniform, hot pressing temperature
Spend for 355 degrees Celsius.
2. the preparation method of Electrostatic Absorption film production mould surfacing according to claim 1, it is characterised in that each group
Part preferred weight ratio is:10 parts of polyhexamethylene sebacamide, 15 parts of butadiene-styrene rubber, 6 parts of boric acid, 2 parts of sodium carbonate, 22 parts of butanediol,
32 parts of aluminium hydroxide, 2 parts of curing agent.
3. the preparation method of Electrostatic Absorption film production mould surfacing according to claim 1 or 2, it is characterised in that
The curing agent is amine curing agent.
4. the preparation method of Electrostatic Absorption film production mould surfacing according to claim 3, it is characterised in that described
Curing agent is aromatic polyvalent amine curing agent.