CN107670847A - 一种锂辉石矿浮选捕收剂的制备方法及其应用 - Google Patents
一种锂辉石矿浮选捕收剂的制备方法及其应用 Download PDFInfo
- Publication number
- CN107670847A CN107670847A CN201710942260.4A CN201710942260A CN107670847A CN 107670847 A CN107670847 A CN 107670847A CN 201710942260 A CN201710942260 A CN 201710942260A CN 107670847 A CN107670847 A CN 107670847A
- Authority
- CN
- China
- Prior art keywords
- ore deposit
- product
- flotation collector
- spodumene
- mass ratio
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明提供一种锂辉石矿浮选捕收剂的制备方法及其应用,属于选矿技术领域。该制备方法包括如下步骤:(1)将地沟油、甲醇和浓硫酸按质量比地沟油:甲醇:浓硫酸=1.0~1.2:1.1~1.8:0.05~0.09混合,60~90℃下搅拌反应5~12小时,得产物1;(2)将盐酸羟胺、水和氢氧化钠按质量比盐酸羟胺:水:氢氧化钠=1.0~1.3:6.4~9.3:1.9~2.4混合,20~30℃下搅拌反应1~3小时,得产物2;(3)将产物1按质量比产物1:产物2=1.0~1.2:0.28~0.48加入产物2中,40~60℃下搅拌反应4~6小时,即得捕收剂。本发明制备的捕收剂用于浮选锂辉石矿时,解决了已有浮选捕收剂用量大、成本高、受低温度影响大、泡沫多、选择性差,精矿品位、回收率指标不理想的问题。
Description
技术领域
本发明涉及选矿技术领域,特别是指一种锂辉石矿浮选捕收剂的制备方法及其应用。
背景技术
金属锂用于电池、航空、核工业、陶瓷和润滑等多个领域,具有不可替代的作用。我国是锂资源大国,锂资源主要为盐湖卤水和含锂矿石。卤水资源主要分布于青海和西藏,矿石锂资源主要分布于四川、新疆、湖南、湖北和江西等。由于受到自然环境变化导致原料成分不稳定、镁离子含量高等因素的影响,从卤水中提取金属锂的工艺发展受到制约,从矿石中回收锂资源仍然处于重要的地位。浮选工艺是锂辉石矿最主要的选别方法,目前,锂辉石矿的浮选主要采用脂肪酸类捕收剂,但常用的脂肪酸类捕收剂的缺点是选择性差、用量大、在常温下的可溶性和分散性差,浮选过程中往往需要对矿浆进行加温才能达到较好的分选效果。因此,研究开发新型高效的浮选捕收剂对于锂辉石矿资源的开发利用和相关工业的可持续发展具有十分重大的意义。
发明内容
本发明针对现有锂辉石矿浮选中存在的捕收剂选择性差、用量大、在常温下的可溶性和分散性差等问题,提供一种锂辉石矿浮选捕收剂的制备方法及其应用。
该制备方法包括如下步骤:
(1)将地沟油、甲醇和浓硫酸按质量比地沟油:甲醇:浓硫酸=1.0~1.2:1.1~1.8:0.05~0.09混合,在60~90℃下搅拌反应5~12小时,得产物1;
(2)将盐酸羟胺、水和氢氧化钠按质量比盐酸羟胺:水:氢氧化钠=1.0~1.3:6.4~9.3:1.9~2.4混合,在20~30℃下搅拌反应1~3小时,得产物2;
(3)将产物1按质量比产物1:产物2=1.0~1.2:0.28~0.48加入产物2中,在40~60℃下搅拌反应4~6小时,即得锂辉石矿浮选捕收剂。
利用上述制得捕收剂进行锂辉石矿浮选的过程如下:
首先,将原矿锂辉石矿石磨矿至单体解离,然后加入抑制剂,再加入活化剂,再加步骤(3)中所得捕收剂对锂辉石矿进行捕收,其中,捕收剂总用量为:400~4000g/t。
其中,浮选矿浆pH值为8~14,通过氢氧化钠调节矿浆pH值。
所用抑制剂为碳酸钠,碳酸钠总用量为600~6000g/t。
所用活化剂为氯化钙,氯化钙总用量为100~1000g/t。
上述浮选过程中,所用的捕收剂采用原液添加。
本发明的上述技术方案的有益效果如下:
上述方案中,原料来源广泛、生产工艺简单、分散性好、矿浆温度适用范围广,具体优点如下:
(1)原料地沟油来源广泛,成本低廉,生产工艺能够充分利用威胁环境和食品安全的地沟油,实现了污染治理和综合利用的双重效果;
(2)生产工艺简单,属于绿色环保工艺,易于实现工业化,有广阔的应用前景;
(3)该捕收剂选择性好,易溶于水,分散性好,受温度影响小,在常温下有比较好的分选效果,能够达到优良的浮选指标。
具体实施方式
为使本发明要解决的技术问题、技术方案和优点更加清楚,下面将结合具体实施例进行详细描述。
本发明针对现有的锂辉石矿浮选中存在的捕收剂选择性差、用量大、在常温下的可溶性和分散性差等问题,提供一种锂辉石矿浮选捕收剂的制备方法及其应用。
实施例1
本发明所述的锂辉石矿浮选捕收剂的制备方法的一个实例,包括以下步骤:
(1)将地沟油、甲醇和浓硫酸按质量比地沟油:甲醇:浓硫酸=1.0:1.1:0.05混合,在60℃下搅拌反应5小时,得产物1;
(2)将盐酸羟胺、水和氢氧化钠按质量比盐酸羟胺:水:氢氧化钠=1.0:6.4:1.9混合,在20℃下搅拌反应1小时,得产物2;
(3)将产物1按质量比产物1:产物2=1.0:0.28加入产物2中,在40℃下搅拌反应4小时,即得锂辉石矿浮选捕收剂。
实施例2
本发明所述的锂辉石矿浮选捕收剂的制备方法的另一个实例,包括以下步骤:
(1)将地沟油、甲醇和浓硫酸按质量比地沟油:甲醇:浓硫酸=1.2:1.8:0.09混合,90℃下搅拌反应12小时,得产物1;
(2)将盐酸羟胺、水和氢氧化钠按质量比盐酸羟胺:水:氢氧化钠=1.3:9.3:2.4混合,在30℃下搅拌反应3小时,得产物2;
(3)将产物1按质量比产物1:产物2=1.2:0.48加入产物2中,60℃下搅拌反应6小时,即得锂辉石矿浮选捕收剂。
实施例3
本实施例为所述锂辉石矿浮选捕收剂在浮选锂辉石矿中的应用实例。
某锂辉石矿矿样,原矿含Li2O 1.46%,将矿石磨矿至矿物单体解离后加入氢氧化钠调矿浆pH值为10,然后加入碳酸钠1200g/t作抑制剂,再加入氯化钙150g/t作活化剂,再加实施例1中制得的捕收剂800g/t对锂辉石矿进行粗选浮选,扫选加入碳酸钠300g/t,氯化钙50g/t,捕收剂320g/t,一次精选加入碳酸钠300g/t,二次精选加入碳酸钠300g/t,三次精选加入碳酸钠200g/t。结果表明采用以上药剂条件能够有效将锂辉石矿高效浮选,在给矿Li2O含量1.46%条件下,经过一次粗选一次扫选及三次精选,得到含Li2O 5.92%、回收率为81.56%浮选锂辉石精矿。
实施例4
本实施例为所述锂辉石矿浮选捕收剂在浮选锂辉石矿中的另一应用实例。
某锂辉石矿矿样,原矿含Li2O 0.85%,将矿石磨矿至矿物单体解离后加入氢氧化钠调矿浆pH值为10,然后加入碳酸钠900g/t作抑制剂,再加入氯化钙250g/t作活化剂,再加实施例1中制得的捕收剂1200g/t对锂辉石矿进行粗选浮选,扫选加入氯化钙100g/t,捕收剂450g/t,一次精选加入碳酸钠200g/t,二次精选加入碳酸钠100g/t。结果表明采用以上药剂条件能够有效将锂辉石矿高效浮选,在给矿Li2O含量0.85%条件下,经过一次粗选一次扫选及两次精选,得到含Li2O 4.87%、回收率为80.69%浮选锂辉石精矿。
以上所述是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明所述原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
Claims (5)
1.一种锂辉石矿浮选捕收剂的制备方法,其特征在于:包括如下步骤:
(1)将地沟油、甲醇和浓硫酸按质量比地沟油:甲醇:浓硫酸=1.0~1.2:1.1~1.8:0.05~0.09混合,在60~90℃下搅拌反应5~12小时,得产物1;
(2)将盐酸羟胺、水和氢氧化钠按质量比盐酸羟胺:水:氢氧化钠=1.0~1.3:6.4~9.3:1.9~2.4混合,在20~30℃下搅拌反应1~3小时,得产物2;
(3)将产物1按质量比产物1:产物2=1.0~1.2:0.28~0.48加入产物2中,在40~60℃下搅拌反应4~6小时,即得锂辉石矿浮选捕收剂。
2.根据权利要求1所述的锂辉石矿浮选捕收剂的应用,其特征在于:首先,将原矿锂辉石矿石磨矿至单体解离,然后加入抑制剂,再加入活化剂,再加步骤(3)中所得捕收剂对锂辉石矿进行捕收,其中,捕收剂总用量为:400~4000g/t。
3.根据权利要求2所述的锂辉石矿浮选捕收剂的应用,其特征在于:所述浮选矿浆pH值为8~14,通过氢氧化钠调节矿浆pH值。
4.根据权利要求2所述的锂辉石矿浮选捕收剂的应用,其特征在于:所述抑制剂为碳酸钠,碳酸钠总用量为600~6000g/t。
5.根据权利要求2所述的锂辉石矿浮选捕收剂的应用,其特征在于:所述活化剂为氯化钙,氯化钙总用量为100~1000g/t。