CN107662439A - A kind of UV shifts refractive power figured plate glass technique - Google Patents
A kind of UV shifts refractive power figured plate glass technique Download PDFInfo
- Publication number
- CN107662439A CN107662439A CN201711036200.2A CN201711036200A CN107662439A CN 107662439 A CN107662439 A CN 107662439A CN 201711036200 A CN201711036200 A CN 201711036200A CN 107662439 A CN107662439 A CN 107662439A
- Authority
- CN
- China
- Prior art keywords
- glass
- refractive power
- glue
- figured plate
- transfers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of UV transfers refractive power figured plate glass technique, and compared with prior art, the present invention has following beneficial effect:The each procedure of processing shifted by UV, refractive power pattern is set to be presented on glass surface, refractive power effect is showed by the irradiation of LED lamplight, present invention application solves the silk-screen printing of traditional glass picture on surface or the low problem of numerial code spray drawing efficiency, processing technology is simple, equipment investment and operating process are all easily mastered, and very big progradation is played in the development to glass technology.
Description
Technical field
The present invention is a kind of UV transfers refractive power figured plate glass technique, belongs to glass UV transfer techniques.
Background technology
According to different product different demands, it is necessary to print corresponding pattern in product, and the complexity of pattern content
Difference, the requirement to production technology are also different.Complicated pattern, such as lines are intensive, pattern content is abundant etc., to work
The requirement of the process conditions of skill process and each step is more harsh, both affects production efficiency, more influence whether the quality of production.
The content of the invention
In view of the deficienciess of the prior art, it is an object of the present invention to provide a kind of UV to shift refractive power figured plate glass technique, with
Solve the problems, such as to propose in above-mentioned background technology.
To achieve these goals, the present invention is to realize by the following technical solutions:A kind of UV shifts refractive power pattern
Glass technology, including following operation:
Needs are done to the glass shifted to be cleaned up with cleaning agent, drying or drying makes its drying;
Glass surrounding carries out edge sealing with the outdoor omnipotent rubberizing paper of 0.15MM thickness;
The refractive power pattern film for needing to shift is cut into the square template smaller 10-15MM than that need to shift glass;
The glass surface for posting Protection glue is smeared into last layer primary coat with sponge or with coating roller;
The glass for carrying out primary coat is dried;
The glass rubberizing paper dried is placed in the template made of acrylic board upward and carries out secondary edge sealing, is turned what is cut out
Move film figure to be placed on glass downwards, wherein one side and glass gluing are fixed with U.S. line paper;
One layer is uniformly coated between glass and transfer membrane with special UV glue, ensures that film draw above case is substantially filled to glue
Water, transfer membrane is then fitted in glass surface, with frictioning of the hardness more than 85 degree, from the one side fixed with U.S. line paper in addition
Steadily scraped on one side, and ensured that glue is uniform, do not produce bubble;
The glass of glue will be uniformly scraped, be put into UV curing and solidified in the lump together with template;
Glass is taken out together with template behind UV machines, first taken out glass from template, then pastes glass surrounding
Good transfer membrane and gummed paper is torn successively, and glass is placed into four hour Temperature falls;
Printed with the glue above alcohol and rag cleaning glass, bubble bags protective packaging is filled after clean.
Further, cleaned up with cleaning agent will need to do the glass that shifts, drying or dry makes in its drying,
When being dried to glass with cleaning agent, by the way that glass is placed on into shady place wind of the environment temperature at 25-28 °C with cleaning agent
It is dry, when being dried to glass with cleaning agent, dried by the way that glass is placed in dryer with cleaning agent.
Further, in glass surrounding carries out edge sealing with the outdoor omnipotent rubberizing paper of 0.15MM thickness, edge sealing need to be smooth,
The junction compacting at four angles of glass, avoids glue from penetrating into.
Further, the refractive power pattern film for needing to shift is being cut into the square template smaller 10-15MM than that need to shift glass
In, refractive power film smooth need to not play fold.
Further, by smearing last layer primary coat with sponge or with coating roller in glass surface, UV glue and glass are increased
Adhesive force between glass, primary coat thickness is in 3-5 microns.
Further, in the glass for carrying out primary coat is dried, between 60-90 °C of drying temperature, the time 100-
150s。
Further, the glass of glue will be uniformly being scraped, is being put into the lump together with template in being solidified in UV curing,
The temperature of UV machines is between 70-90 °C, and for the energy in UV machines between 750-800 MJs, the time is the 20-30 seconds.
Beneficial effects of the present invention:A kind of UV transfer refractive power figured plate glass techniques of the present invention, pass through each of UV transfers
Procedure of processing, refractive power pattern is presented on glass surface, refractive power effect, present invention application are showed by the irradiation of LED lamplight
Solve the silk-screen printing of traditional glass picture on surface or the low problem of numerial code spray drawing efficiency, processing technology is simple, and equipment is thrown
Enter and operating process is all easily mastered, very big progradation is played in the development to glass technology.
Embodiment
To be easy to understand the technical means, the inventive features, the objects and the advantages of the present invention, with reference to
Embodiment, the present invention is expanded on further.
The present invention provides a kind of technical scheme:A kind of UV shifts refractive power figured plate glass technique, including following operation:
Needs are done to the glass shifted to be cleaned up with cleaning agent, drying or drying makes its drying;
Glass surrounding carries out edge sealing with the outdoor omnipotent rubberizing paper of 0.15MM thickness;
The refractive power pattern film for needing to shift is cut into the square template smaller 10-15MM than that need to shift glass;
The glass surface for posting Protection glue is smeared into last layer primary coat with sponge or with coating roller;
The glass for carrying out primary coat is dried;
The glass rubberizing paper dried is placed in the template made of acrylic board upward and carries out secondary edge sealing, is turned what is cut out
Move film figure to be placed on glass downwards, wherein one side and glass gluing are fixed with U.S. line paper;
One layer is uniformly coated between glass and transfer membrane with special UV glue, ensures that film draw above case is substantially filled to glue
Water, transfer membrane is then fitted in glass surface, with frictioning of the hardness more than 85 degree, from the one side fixed with U.S. line paper in addition
Steadily scraped on one side, and ensured that glue is uniform, do not produce bubble;
The glass of glue will be uniformly scraped, be put into UV curing and solidified in the lump together with template;
Glass is taken out together with template behind UV machines, first taken out glass from template, then pastes glass surrounding
Good transfer membrane and gummed paper is torn successively, and glass is placed into four hour Temperature falls;
Printed with the glue above alcohol and rag cleaning glass, bubble bags protective packaging is filled after clean.
Cleaned up will need to do the glass that shifts with cleaning agent, drying or dry makes during it dries, to glass use
When cleaning agent is dried, air-dried by the way that glass is placed on into environment temperature with cleaning agent in 25-28 °C of shady place, to glass
When glass is dried with cleaning agent, dried by the way that glass is placed in dryer with cleaning agent.
In glass surrounding carries out edge sealing with the outdoor omnipotent rubberizing paper of 0.15MM thickness, edge sealing needs smooth, four, glass
The junction compacting at angle, avoids glue from penetrating into.
It is cut into by the refractive power pattern film for needing to shift in the square template smaller 10-15MM than glass need to be shifted, refractive power film
Smooth it need to not play fold.
By smearing last layer primary coat with sponge or with coating roller in glass surface, increase attached between UV glue and glass
Put forth effort, primary coat thickness is in 3-5 microns.
In the glass for carrying out primary coat is dried, between 60-90 °C of drying temperature, 100-150s of time.
The glass of glue will be uniformly being scraped, be put into the lump together with template in being solidified in UV curing, the temperature of UV machines
Degree is between 70-90 °C, and for the energy in UV machines between 750-800 MJs, the time is the 20-30 seconds.
As one embodiment of the present of invention:A kind of UV transfer refractive power figured plate glass techniques of the present invention, are shifted by UV
Each procedure of processing, refractive power pattern is presented on glass surface, refractive power effect, this hair showed by the irradiation of LED lamplight
Bright application solves the silk-screen printing of traditional glass picture on surface or the low problem of numerial code spray drawing efficiency, and processing technology is simple,
Equipment investment and operating process are all easily mastered, and very big progradation is played in the development to glass technology.
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above, for this area skill
For art personnel, it is clear that the invention is not restricted to the details of above-mentioned one exemplary embodiment, and without departing substantially from the present invention spirit or
In the case of essential characteristic, the present invention can be realized in other specific forms.Which point therefore, no matter from the point of view of, all should incite somebody to action
Embodiment regards exemplary as, and be it is nonrestrictive, the scope of the present invention by appended claims rather than on state
Bright restriction, it is intended that all changes fallen in the implication and scope of the equivalency of claim are included in the present invention
It is interior.
Moreover, it will be appreciated that although the present specification is described in terms of embodiments, not each embodiment is only wrapped
Containing an independent technical scheme, this narrating mode of specification is only that those skilled in the art should for clarity
Using specification as an entirety, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
It is appreciated that other embodiment.
Claims (8)
1. a kind of UV shifts refractive power figured plate glass technique, it is characterised in that:Including following operation:
Needs are done to the glass shifted to be cleaned up with cleaning agent, drying or drying makes its drying;
Glass surrounding carries out edge sealing with the outdoor omnipotent rubberizing paper of 0.15MM thickness;
The refractive power pattern film for needing to shift is cut into the square template smaller 10-15MM than that need to shift glass;
The glass surface for posting Protection glue is smeared into last layer primary coat with sponge or with coating roller;
The glass for carrying out primary coat is dried;
The glass rubberizing paper dried is placed in the template made of acrylic board upward and carries out secondary edge sealing, is turned what is cut out
Move film figure to be placed on glass downwards, wherein one side and glass gluing are fixed with U.S. line paper;
One layer is uniformly coated between glass and transfer membrane with special UV glue, ensures that film draw above case is substantially filled to glue
Water, transfer membrane is then fitted in glass surface, with frictioning of the hardness more than 85 degree, from the one side fixed with U.S. line paper in addition
Steadily scraped on one side, and ensured that glue is uniform, do not produce bubble;
The glass of glue will be uniformly scraped, be put into UV curing and solidified in the lump together with template;
Glass is taken out together with template behind UV machines, first taken out glass from template, then pastes glass surrounding
Good transfer membrane and gummed paper is torn successively, and glass is placed into four hour Temperature falls;
Printed with the glue above alcohol and rag cleaning glass, bubble bags protective packaging is filled after clean.
A kind of 2. UV transfers refractive power figured plate glass technique according to claim 1, it is characterised in that:It will need to shift
Glass cleaned up with cleaning agent, dry or dry make its dry in, when being dried to glass with cleaning agent, pass through by
Glass is placed on environment temperature with cleaning agent and air-dried in 25-28 °C of shady place, when being dried to glass with cleaning agent, leads to
Cross glass being placed in dryer with cleaning agent and dry.
A kind of 3. UV transfers refractive power figured plate glass technique according to claim 1, it is characterised in that:Used in glass surrounding
The outdoor omnipotent rubberizing paper of 0.15MM thickness is carried out in edge sealing, and edge sealing need to be smooth, the junction compacting at four angles of glass, avoids glue
Water penetrates into.
A kind of 4. UV transfers refractive power figured plate glass technique according to claim 1, it is characterised in that:It will need what is shifted
Refractive power pattern film is cut into the square template smaller 10-15MM than that need to shift glass, and refractive power film smooth need to not play fold.
A kind of 5. UV transfers refractive power figured plate glass technique according to claim 1, it is characterised in that:By in glass surface
Last layer primary coat is smeared with sponge or with coating roller, increases the adhesive force between UV glue and glass, primary coat thickness is micro- in 3-5
Rice.
A kind of 6. UV transfers refractive power figured plate glass technique according to claim 1, it is characterised in that:Primary coat will carried out
During glass is dried, between 60-90 °C of drying temperature, 100-150s of time.
A kind of 7. UV transfers refractive power figured plate glass technique according to claim 1, it is characterised in that:With special UV glue
One layer is uniformly coated between glass and transfer membrane, ensures that film draw above case is substantially filled to glue, then pastes transfer membrane
Close in glass surface, with frictioning of the hardness more than 85 degree, steadily scraped to other one side from the one side fixed with U.S. line paper, ensured
Glue is uniform, does not produce in bubble, and UV glue compositions are:Prepolymer 40%, acrylate monomer 50%, sensitising agent 5%, auxiliary agent 4%,
Water-proofing agent 1%.
A kind of 8. UV transfers refractive power figured plate glass technique according to claim 1, it is characterised in that:Glue uniformly will scraped
The glass of water, it is put into the lump together with template in being solidified in UV curing, the temperature of UV machines is between 70-90 °C, in UV machines
Energy between 750-800 MJs, the time is the 20-30 seconds.