CN107653415A - A kind of microalloy high-carbon steel for pin cloth product - Google Patents
A kind of microalloy high-carbon steel for pin cloth product Download PDFInfo
- Publication number
- CN107653415A CN107653415A CN201710705320.0A CN201710705320A CN107653415A CN 107653415 A CN107653415 A CN 107653415A CN 201710705320 A CN201710705320 A CN 201710705320A CN 107653415 A CN107653415 A CN 107653415A
- Authority
- CN
- China
- Prior art keywords
- carbon steel
- pin cloth
- microalloy high
- cloth product
- microalloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of microalloy high-carbon steel for pin cloth product, it is characterised in that:The component and its weight/mass percentage composition of microalloy high-carbon steel be:C:0.60~0.75%、Si:0.20~0.30%、Mn:0.50~0.70%、Cr:< 0.15%, P:<0.020%、S:<0.010%, V:0.05~0.20%、Nb:0.010~0.035 %、Ni:0~0.50%、Mo:0~0.50%、Cu:0~0.40%.The present invention improves the eutectoid carbon content of material so that material is thinner in equal quenching temperature undertissue, and martensite hardness is higher, so as to improve the anti-soft abrasiye polishing machine of material by adding micro Nb and V in high-carbon steel.Meanwhile and because micro alloying element adds so that material remains to the cold-forming property for keeping ordinary carbon steel excellent.
Description
Technical field
The invention belongs to textile equipment processing technique field, and in particular to a kind of microalloy high-carbon for pin cloth product
Steel.
Background technology
Pin cloth product requires that material has preferable cold-formed performance with steel, has after Q-tempering preferably wear-resisting
Property and obdurability.The steel grade that pin cloth uses at present is mainly hard wire steel, such as 60#, 72B, 82B, and is developed in 70 ~ eighties
The micro alloyed steel to get up, such as 80WV materials.Ordinary carbon steel material cold-forming property is preferable, and remaining carbide is less after quenching, and C is former
Son improves the polishing machine between fiber and pin cloth in being dissolved into martensitic matrix, but because card clothing tooth top is smaller relatively thin, quenching
Crystallite dimension is easy to thick during heating, the risk of crown fracture when increase pin cloth works;And in 80WV 0.50 ~ 0.9% W content
Generally it is present in being dissolved state in steel, is not separated out with carbide form and play precipitation strength or crystal grain thinning, and W is former
Also there is segregation risk in steel-making in son, the cold drawn performance and uniformity of hardness of material can be caused necessarily to influence, processing characteristics
It is poor so that processing cost is higher.
The content of the invention
In order to solve the above problems.The present invention provides a kind of microalloy high-carbon steel for pin cloth product, it is characterised in that:
The component and its weight/mass percentage composition of microalloy high-carbon steel be:
C:0.60~0.75%、Si:0.20~0.30%、Mn:0.50~0.70%、Cr:< 0.15%, P:<0.020%、S:<0.010%,
V:0.05~0.20%、Nb:0.010~0.035 %、Ni:0~0.50%、Mo:0~0.50%、Cu:0~0.40%.
The present invention is advantageous in that:Addition and rational stoicheiometry material by micro alloying element
Existing good cold-forming property, Cr and V can enter cementite, form alloyed cementite;V can also form VC, play obvious
The effect for preventing crystal grain from growing up, the effect of precipitation strength and crystal grain refinement is brought using Nb, V element Carbide Precipitation, and Nb promotees
Enter the degeneration of eutectoid phase transformation, eliminate net carbide, promote the nodularization of cementite.Simultaneously Nb, V and C-shaped into NbC, VC may be used also
Material wear ability is improved to a certain extent, and there is excellent cold-forming property, easy nodularization using the microalloy high-carbon steel
Can, and martensite hardness is higher after heat treatment, organizes more tiny, the anti-soft abrasiye polishing machine of effective lift pins cloth.
Embodiment
In order to deepen the understanding of the present invention, below in conjunction with embodiment, the invention will be further described, the embodiment
It is only used for explaining the present invention, does not form the restriction to protection scope of the present invention.
Embodiment 1
A kind of microalloy high-carbon steel for pin cloth product, it is characterised in that:The component and its quality percentage of microalloy high-carbon steel
Content is:
C:0.62%、Si:0.22%、Mn:0.60%、Cr:0.010%、P: 0.009%、S:0.005%, V:0.07%、Nb:0.028
%、Ni:0.006%、Cu:0.06%、Mo:0.034 %.
Embodiment 2
A kind of microalloy high-carbon steel for pin cloth product, it is characterised in that:The component and its quality percentage of microalloy high-carbon steel
Content is:
C:0.65%、Si:0.26%、Mn:0.69%、Cr:0.024%、P: 0.010%、S:0.004%, V:0.10%、Nb:0.026
%、Ni:0.028%、Cu:0.05%、Mo:0.12 %.
Embodiment 3
A kind of microalloy high-carbon steel for pin cloth product, it is characterised in that:The component and its quality percentage of microalloy high-carbon steel
Content is:
C:0.70%、Si:0.26%、Mn:0.70%、Cr:0.120%、P: 0.007%、S:0.005%, V:0.15%、Nb:0.018
%、Ni:0.006%、Cu:0.051%、Mo:0.15 %.
Embodiment 4
A kind of microalloy high-carbon steel for pin cloth product, it is characterised in that:The component and its quality percentage of microalloy high-carbon steel
Content is:
C:0.73%、Si:0.25%、Mn:0.68%、Cr:0.10%、P: 0.011%、S:0.003%, V:0.18%、Nb:0.025 %、
Ni:0.020%、Cu:0.082%、Mo:0.04%.
Claims (2)
- A kind of 1. microalloy high-carbon steel for pin cloth product, it is characterised in that:The component and its quality hundred of microalloy high-carbon steel Point content is:C:0.60~0.75%、Si:0.20~0.30%、Mn:0.50~0.70%、Cr:< 0.15%, P:<0.020%、S:<0.010%, V:0.05~0.20%、Nb:0.010~0.035 %、Ni:0~0.50%、Mo:0~0.50%、Cu:0~0.40%.
- A kind of 2. microalloy high-carbon steel for pin cloth product according to claim 1, it is characterised in that:The chi of the V Very little is 9nm-11nm.