CN107652584A - A kind of fibre-reinforced plastic material - Google Patents
A kind of fibre-reinforced plastic material Download PDFInfo
- Publication number
- CN107652584A CN107652584A CN201711046689.1A CN201711046689A CN107652584A CN 107652584 A CN107652584 A CN 107652584A CN 201711046689 A CN201711046689 A CN 201711046689A CN 107652584 A CN107652584 A CN 107652584A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- fibre
- reinforced plastic
- plastic material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to a kind of fibre-reinforced plastic material, include the raw material of following parts by weight:The parts by weight of polyvinyl chloride 100 150, the parts by weight of polyurethane 20 30, the parts by weight of calcium silicates 10 25, the parts by weight of glass fibre 5 10, the parts by weight of polypropylene fibre 24, the parts by weight of lignin fibre 58.The beneficial effects of the invention are as follows provide a kind of fibre-reinforced plastic material.
Description
Technical field
The present invention relates to Material Field, specifically, is related to a kind of fibre-reinforced plastic material.
Background technology
21 century, the exploitation of advanced composite material (ACM) will enter the period of rapid development, therefore composite with application
It is particularly significant with the exploitation of reinforcement.It is every that the group for improving intensity, improving performance effect is played in polymer matrix composite
Divide and be properly termed as reinforcing material.Kind using epoxy resin as the composite tencel shape reinforcing material of matrix has:
Glass fibre, carbon fiber, ultrahigh relative molecular weight polyethylene fiber, Nomex (aramid fiber) fiber, pbo fiber, boron fibre
Deng.
Intensity is also a highly important index for plastic material, so how to obtain a kind of fibre-reinforced
Plastic material is that current needs solve.
The content of the invention
The technical problems to be solved by the invention are to provide a kind of fibre-reinforced plastic material.
The technical scheme that the present invention solves above-mentioned technical problem is as follows:
A kind of fibre-reinforced plastic material, include the raw material of following parts by weight:Polyvinyl chloride 100-150 parts by weight,
Polyurethane 20-30 parts by weight, calcium silicates 10-25 parts by weight, glass fibre 5-10 parts by weight, polypropylene fibre 2-4 parts by weight, wood
Quality fiber 5-8 parts by weight.
The beneficial effects of the invention are as follows:A kind of fibre-reinforced plastic material is provided.
On the basis of above-mentioned technical proposal, the present invention can also do following improvement:
Further, the fibre-reinforced plastic material, the raw material of following parts by weight is included:The weight of polyvinyl chloride 100
Part, the parts by weight of polyurethane 20, the parts by weight of calcium silicates 10, the parts by weight of glass fibre 5, the parts by weight of polypropylene fibre 2, lignin fibre
5 parts by weight.
Further, the fibre-reinforced plastic material, the raw material of following parts by weight is included:The weight of polyvinyl chloride 150
Part, the parts by weight of polyurethane 30, the parts by weight of calcium silicates 25, the parts by weight of glass fibre 10, the parts by weight of polypropylene fibre 4, lignin are fine
Tie up 8 parts by weight.
Further, a kind of fibre-reinforced plastic material, the raw material of following parts by weight is included:Polyvinyl chloride 120
Parts by weight, the parts by weight of polyurethane 27, the parts by weight of calcium silicates 19, the parts by weight of glass fibre 8, the parts by weight of polypropylene fibre 3, lignin
The parts by weight of fiber 6.
Further, the preparation method of the fibre-reinforced plastic material comprises the following steps:
1) raw material is on the waiting list in proportion, is mixed, is obtained mixture;
2) mixture is subjected to extruding pelletization, obtains semi-finished product;
3) semi-finished product are molded, are extruded or are molded, obtain the fibre-reinforced plastic material.
Embodiment
The principle and feature of the present invention are described with reference to embodiments, the given examples are served only to explain the present invention,
It is not intended to limit the scope of the present invention.
Embodiment 1
Fibre-reinforced plastic material, include the raw material of following parts by weight:The parts by weight of polyvinyl chloride 100, polyurethane 20
Parts by weight, the parts by weight of calcium silicates 10, the parts by weight of glass fibre 5, the parts by weight of polypropylene fibre 2, the parts by weight of lignin fibre 5.
The preparation method of the fibre-reinforced plastic material comprises the following steps:
1) raw material is on the waiting list in proportion, is mixed, is obtained mixture;
2) mixture is subjected to extruding pelletization, obtains semi-finished product;
3) semi-finished product are molded, are extruded or are molded, obtain the fibre-reinforced plastic material.
Embodiment 2
Fibre-reinforced plastic material, include the raw material of following parts by weight:The parts by weight of polyvinyl chloride 150, polyurethane 30
Parts by weight, the parts by weight of calcium silicates 25, the parts by weight of glass fibre 10, the parts by weight of polypropylene fibre 4, the parts by weight of lignin fibre 8.
The preparation method of the fibre-reinforced plastic material comprises the following steps:
1) raw material is on the waiting list in proportion, is mixed, is obtained mixture;
2) mixture is subjected to extruding pelletization, obtains semi-finished product;
3) semi-finished product are molded, are extruded or are molded, obtain the fibre-reinforced plastic material.
Embodiment 3
A kind of fibre-reinforced plastic material, include the raw material of following parts by weight:The parts by weight of polyvinyl chloride 120, poly- ammonia
The parts by weight of ester 27, the parts by weight of calcium silicates 19, the parts by weight of glass fibre 8, the parts by weight of polypropylene fibre 3, the weight of lignin fibre 6
Part.
The preparation method of the fibre-reinforced plastic material comprises the following steps:
1) raw material is on the waiting list in proportion, is mixed, is obtained mixture;
2) mixture is subjected to extruding pelletization, obtains semi-finished product;
3) semi-finished product are molded, are extruded or are molded, obtain the fibre-reinforced plastic material.
Comparative example 1
Common commercially available plastic material.
The sample in embodiment 1-3 and comparative example 1 is tested respectively according to ASTM D790 standard, by comparative example 1
The ductility result of middle sample is radix, and the intensity results of sample and the ratio of radix see the table below in embodiment 1-3:
Ratio | |
Embodiment 1 | 1.81 |
Embodiment 2 | 1.78 |
Embodiment 3 | 1.77 |
Comparative example 1 | 1 |
The foregoing is only presently preferred embodiments of the present invention, be not intended to limit the invention, it is all the present invention spirit and
Within principle, any modification, equivalent substitution and improvements made etc., it should be included in the scope of the protection.
Claims (5)
1. a kind of fibre-reinforced plastic material, it is characterised in that include the raw material of following parts by weight:Polyvinyl chloride 100-
150 parts by weight, polyurethane 20-30 parts by weight, calcium silicates 10-25 parts by weight, glass fibre 5-10 parts by weight, polypropylene fibre 2-
4 parts by weight, lignin fibre 5-8 parts by weight.
2. a kind of fibre-reinforced plastic material according to claim 1, it is characterised in that include the original of following parts by weight
Material:The parts by weight of polyvinyl chloride 100, the parts by weight of polyurethane 20, the parts by weight of calcium silicates 10, the parts by weight of glass fibre 5, polypropylene fibre
2 parts by weight, the parts by weight of lignin fibre 5.
3. a kind of fibre-reinforced plastic material according to claim 1, it is characterised in that include the original of following parts by weight
Material:The parts by weight of polyvinyl chloride 150, the parts by weight of polyurethane 30, the parts by weight of calcium silicates 25, the parts by weight of glass fibre 10, polypropylene are fine
Tie up 4 parts by weight, the parts by weight of lignin fibre 8.
4. a kind of fibre-reinforced plastic material according to claim 1, it is characterised in that include the original of following parts by weight
Material:The parts by weight of polyvinyl chloride 120, the parts by weight of polyurethane 27, the parts by weight of calcium silicates 19, the parts by weight of glass fibre 8, polypropylene fibre
3 parts by weight, the parts by weight of lignin fibre 6.
5. according to a kind of any fibre-reinforced plastic materials of claim 1-4, it is characterised in that its preparation method includes
Following steps:
1) raw material is on the waiting list in proportion, is mixed, is obtained mixture;
2) mixture is subjected to extruding pelletization, obtains semi-finished product;
3) semi-finished product are molded, are extruded or are molded, obtain the fibre-reinforced plastic material.