CN107651919A - A kind of regeneration brick aggregate concrete and preparation method thereof - Google Patents
A kind of regeneration brick aggregate concrete and preparation method thereof Download PDFInfo
- Publication number
- CN107651919A CN107651919A CN201710916061.6A CN201710916061A CN107651919A CN 107651919 A CN107651919 A CN 107651919A CN 201710916061 A CN201710916061 A CN 201710916061A CN 107651919 A CN107651919 A CN 107651919A
- Authority
- CN
- China
- Prior art keywords
- regeneration brick
- aggregate
- regeneration
- concrete
- aggregate concrete
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of regeneration brick aggregate concrete and preparation method thereof, the concrete includes following components by quality:64~90 parts of regeneration brick coarse aggregate, 48~80 parts of regeneration brick fine aggregate, 36~42 parts of cement, 1.8~2.2 parts of silicon ash, 11~17 parts of water, 0.2~1.0 part of high-performance water reducing agent, its preparation method is as follows:1) regeneration brick coarse aggregate and regeneration brick fine aggregate are weighed in proportion, are uniformly mixed to obtain regeneration brick aggregate;2) after being in proportion well mixed cement and silicon ash, add in regeneration brick aggregate, be uniformly mixed to obtain compound;3) water is weighed in proportion and high-performance water reducing agent is added in compound, and described regeneration brick aggregate concrete is obtained after being uniformly mixed.The regeneration brick aggregate concrete has preferable workability, and cohesiveness is preferable, has more preferable heat insulating effect compared with normal concrete, and anti-seismic performance gets a promotion with fire resistance.
Description
Technical field
The present invention relates to a kind of regeneration brick aggregate concrete and preparation method thereof, belong to building material field.
Background technology
Regeneration brick aggregate concrete refers to crush common brick as aggregate using building castoff, and by adding binder materials, outer
A kind of construction material for adding agent to be mixed with out with water.The material has insulation, lightweight etc. compared with conventional concrete
Feature, and can help solve the problems, such as that sand and stone resources increasingly with recovery process to surrounding environment destroy by scarcity, with China
Sustainable development policies be consistent.Part substitution sandstone is generally intended only as regeneration brick aggregate concrete to carry out at present
Use so that the insulation of brick aggregate concrete and it is light the characteristics of fail to give full play to.
Prepare regeneration brick aggregate concrete as thick, fine aggregate using discarded clay brick and meet low-carbon, circular economy concept
Novel green construction material.Regeneration brick aggregate concrete has following characteristics:Compared with conventional concrete, regeneration brick aggregate concrete
Effect with more preferable insulation, while the deadweight of regeneration brick aggregate concrete is also greatly lowered, and alleviates basis
Payload values, be advantageous to carry out basement process, while also can be improved the anti-seismic performance of building, secondly raw material resources is rich
Richness, cost are low.Aggregate used in regeneration brick aggregate concrete is building castoff clay brick, with constantly pushing away for China's urbanization
Enter, can all produce substantial amounts of building waste every year, to prepare the raw material that regeneration brick aggregate concrete provides abundance.
The content of the invention
Technical problem:It is an object of the invention to provide a kind of regeneration brick aggregate concrete and preparation method thereof, regeneration brick
Aggregate concrete has preferable workability and has the characteristics of insulation and lightweight, disclosure satisfy that compression strength and items make
Use performance.
Technical scheme:The invention provides a kind of regeneration brick aggregate concrete, the proportioning of the regeneration brick aggregate concrete with
Mass parts meter includes:
Wherein:
The particle diameter of described regeneration brick coarse aggregate is 4.75~9.5mm, and the particle diameter of described regeneration brick fine aggregate is less than
4.75mm。
Described regeneration brick aggregate is that regeneration brick coarse aggregate is mixed to get with regeneration brick fine aggregate, common brick in regeneration brick aggregate
Content be 60wt%~80wt%, total content 20wt%~40wt% of broken regeneration concrete and regeneration mortar.
Described cement is portland cement, Portland cement, the slag silicon of defined in GB175-2011 table standards
Acid salt cement, Portland pozzolana cement, Portland fly ash cement or composite Portland cement.
Described silicon ash is to meet the silicon ash of defined in GBT27690-2011 standards.
Described high-performance water reducing agent is the high-performance water reducing agent for meeting defined in GB8076-2008 standards.
Present invention also offers a kind of preparation method of regeneration brick aggregate concrete, comprise the following steps:
1) regeneration brick coarse aggregate and regeneration brick fine aggregate are weighed in proportion, are uniformly mixed to obtain regeneration brick aggregate;
2) after being in proportion well mixed cement and silicon ash, add in the regeneration brick aggregate that step 1) obtains, be stirred
Uniformly obtain compound;
3) water is weighed in proportion and high-performance water reducing agent is added in the compound that step 2) obtains, after being uniformly mixed
To described regeneration brick aggregate concrete.
Wherein:
Regeneration brick coarse aggregate and regeneration brick fine aggregate described in step 1) are prewetted 20~30h in advance;
It is described be stirred during stir speed (S.S.) be 20~40r/min;
The when a length of 20~60s being stirred described in step 1);
The when a length of 20~60s being stirred described in step 2);
The when a length of 2~5min being stirred described in step 3).
Beneficial effect:
Compared with prior art, the present invention has following advantages:
1st, the present invention can be used for clay brick as coarse-fine aggregate to prepare regeneration brick aggregate concrete to be a kind of, utilize its system
Thermal and insulating performance for the regeneration brick aggregate concrete gone out is more excellent, and the density of itself substantially reduces, its strength grade
Reach C30 and more than, density rating can be up to 1800;
2nd, present invention selection partly substitutes cement to lift the cohesiveness of brick aggregate concrete using silicon ash, makes slurry more
Be wrapped in brick aggregate surface well, avoid due to the density contrast between brick aggregate and slurry is larger and caused by segregation phenomenon;
3rd, water-cement ratio is reduced while the present invention is selected using high-performance water reducing agent to ensure mobility so that brick aggregate
Concrete can reach higher intensity;The use of silicon ash is also made that tribute for the strength enhancing of regeneration brick aggregate concrete simultaneously
Offer.
Embodiment
In order to be better understood from the present invention, below the invention will be further described, but it is not intended that the present invention is only suitable
For Examples below, person skilled in art the present invention is made according to the content of the invention described above some nonessential change
Enter and adjust, still fall within protection scope of the present invention.
By the present invention in that substitute natural resources sandstone with building castoff regeneration brick aggregate, by adjusting cement, silicon ash
It can be used for preparing with insulation and meet the regeneration brick aggregate coagulation of strength demand to make with the dosage of additive
Soil, this is all significant to recycling for building castoff.
Example 1:
A kind of regeneration brick aggregate concrete, the proportioning of the regeneration brick aggregate concrete include in mass:
The preparation process of the regeneration brick aggregate concrete is as follows:
Regeneration brick coarse aggregate and regeneration brick fine aggregate are prewetted 24h in advance respectively, is subsequently placed in mixer, is in speed
30s is stirred under conditions of 30r/min, is added after being afterwards well mixed cement and silicon ash in advance in forced stirrer and continues to stir
30s, finally water and polycarboxylate high performance water-reducing agent are added in mixer simultaneously after stirring 3min and can obtain regeneration brick bone
Expect concrete.
Example 2:
A kind of regeneration brick aggregate concrete, the proportioning of the regeneration brick aggregate concrete include in mass:
The preparation process of the regeneration brick aggregate concrete is as follows:
Regeneration brick coarse aggregate and regeneration brick fine aggregate are prewetted 20h in advance respectively, is subsequently placed in mixer, is in speed
20s is stirred under conditions of 40r/min, is added after being afterwards well mixed cement and silicon ash in advance in mixer and continues to stir 20s,
Finally water and polycarboxylate high performance water-reducing agent are added in mixer simultaneously to stir and can obtain regeneration brick aggregate after 2min and mix
Solidifying soil.
Example 3:
A kind of regeneration brick aggregate concrete, the proportioning of the regeneration brick aggregate concrete include in mass:
The preparation process of the regeneration brick aggregate concrete is as follows:
Regeneration brick coarse aggregate and regeneration brick fine aggregate are prewetted 30h in advance respectively, is subsequently placed in mixer, is in speed
60s is stirred under conditions of 20r/min, is added after being afterwards well mixed cement and silicon ash in advance in mixer and continues to stir 60s,
Finally water and polycarboxylate high performance water-reducing agent are added in mixer simultaneously to stir and can obtain regeneration brick aggregate after 5min and mix
Solidifying soil.
Example 4:
A kind of regeneration brick aggregate concrete, the proportioning of the regeneration brick aggregate concrete include in mass:
The preparation process of the regeneration brick aggregate concrete is as follows:
Regeneration brick coarse aggregate and regeneration brick fine aggregate are prewetted 28h in advance respectively, is subsequently placed in mixer, is in speed
50s is stirred under conditions of 25r/min, is added after being afterwards well mixed cement and silicon ash in advance in mixer and continues to stir 40s,
Finally water and polycarboxylate high performance water-reducing agent are added in mixer simultaneously to stir and can obtain regeneration brick aggregate after 4min and mix
Solidifying soil.
Example 5:
A kind of regeneration brick aggregate concrete, the proportioning of the regeneration brick aggregate concrete include in mass:
The preparation process of the regeneration brick aggregate concrete is as follows:
Regeneration brick coarse aggregate and regeneration brick fine aggregate are prewetted 22h in advance respectively, is subsequently placed in mixer, is in speed
40s is stirred under conditions of 35r/min, is added after being afterwards well mixed cement and silicon ash in advance in mixer and continues to stir 30s,
Finally water and polycarboxylate high performance water-reducing agent are added in mixer simultaneously to stir and can obtain regeneration brick aggregate after 3min and mix
Solidifying soil.
The performance test of regeneration brick aggregate concrete
Reference standard JGJ 51-2002《The attached provision explanation of lightweight aggregate concrete technology code》Respectively to being prepared in embodiment
Compression strength, dry apparent density and the thermal conductivity factor of regeneration brick aggregate concrete tested, test acquired results are shown in Table 1.
The regeneration brick aggregate concrete the performance test results of table 1
Claims (10)
- A kind of 1. regeneration brick aggregate concrete, it is characterised in that:The proportioning of the regeneration brick aggregate concrete in terms of mass parts including:
- A kind of 2. regeneration brick aggregate concrete as claimed in claim 1, it is characterised in that:The grain of described regeneration brick coarse aggregate Footpath is 4.75~9.5mm, and the particle diameter of described regeneration brick fine aggregate is less than 4.75mm.
- A kind of 3. regeneration brick aggregate concrete as claimed in claim 1, it is characterised in that:Described regeneration brick aggregate is regeneration Brick coarse aggregate is mixed to get with regeneration brick fine aggregate, and the content of common brick is 60wt%~80wt%, broken in regeneration brick aggregate The total content of regeneration concrete and regeneration mortar is 20wt%~40wt%.
- A kind of 4. regeneration brick aggregate concrete as claimed in claim 1, it is characterised in that:Described cement is GB175-2011 The portland cement of defined, Portland cement, portland slag cement, Portland pozzolana cement, powder in standard Coal ash portland cement or composite Portland cement.
- A kind of 5. regeneration brick aggregate concrete as claimed in claim 1, it is characterised in that:Described silicon ash is satisfaction The silicon ash of defined in GBT27690-2011 standards.
- A kind of 6. regeneration brick aggregate concrete as claimed in claim 1, it is characterised in that:Described high-performance water reducing agent meets The high-performance water reducing agent of defined in GB8076-2008 standards.
- A kind of 7. preparation method of regeneration brick aggregate concrete as claimed in claim 1, it is characterised in that:The preparation method bag Include following steps:1) regeneration brick coarse aggregate and regeneration brick fine aggregate are weighed in proportion, are uniformly mixed to obtain regeneration brick aggregate;2) after being in proportion well mixed cement and silicon ash, add in the regeneration brick aggregate that step 1) obtains, be uniformly mixed Obtain compound;3) water is weighed in proportion and high-performance water reducing agent is added in the compound that step 2) obtains, and institute is obtained after being uniformly mixed The regeneration brick aggregate concrete stated.
- A kind of 8. preparation method of regeneration brick aggregate concrete as claimed in claim 7, it is characterised in that:Described in step 1) Regeneration brick coarse aggregate and regeneration brick fine aggregate are prewetted 20~30h in advance.
- A kind of 9. preparation method of regeneration brick aggregate concrete as claimed in claim 7, it is characterised in that:Described stirring mixes Stir speed (S.S.) is 20~40r/min during conjunction.
- A kind of 10. preparation method of regeneration brick aggregate concrete as claimed in claim 7, it is characterised in that:Step 1) is described The when a length of 20~60s being stirred, the when a length of 30s20~60s being stirred described in step 2), described in step 3) The when a length of 2~5min being stirred.