CN107644704A - A kind of adhesive tape for FFC stiffening plates and preparation method thereof - Google Patents
A kind of adhesive tape for FFC stiffening plates and preparation method thereof Download PDFInfo
- Publication number
- CN107644704A CN107644704A CN201610571203.5A CN201610571203A CN107644704A CN 107644704 A CN107644704 A CN 107644704A CN 201610571203 A CN201610571203 A CN 201610571203A CN 107644704 A CN107644704 A CN 107644704A
- Authority
- CN
- China
- Prior art keywords
- ffc
- adhesive tape
- melten gel
- resin film
- gel coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of preparation method of the adhesive tape for FFC stiffening plates, it comprises the following steps：Colored paint is coated on to the whole surface of resin film, forms colored paint layer；Colloidal sol is coated on to the surface middle part of the colored paint layer, forms melten gel coating；One end of FFC wire rods is pressed on to the surface of the melten gel coating, using FFC pressing machines, temperature at 180 DEG C, thermocompression forming is carried out under 0.5 ~ 0.8Pa pressure, obtains the adhesive tape for being used for stiffening plate.Compared with prior art, the present invention has following beneficial effect：1st, surface district portion gluing, it is without the use of adhesive tape isolated part size when being fitted in FFC soft arranging wire product ports by heating, the handle position after the shaping of FFC soft arranging wires can be met, saved FFC soft arranging wire production costs；2nd, human cost is saved, save material cost, effective to improve production efficiency.
Description
Technical field
The present invention relates to a kind of preparation method of the adhesive tape for FFC stiffening plates, belong to technical field of electronic equipment.
Background technology
Flexible flat cable, abbreviation FFC (Flexible Flat Cable), it is a kind of with PET insulating materials and very thin
Tin plating flat copper wire, the new types of data cable that pressing forms is produced by high-tech automation equipment, had soft, arbitrarily curved
Tortuous folded, thickness of thin, small volume, connect the advantages that simple, convenient disassembly, easily solution electromagnetic shielding (EMI).
Such product of the prior art need to be used when being fitted in FFC soft arranging wire product ports by heating adhesive tape every
From portion size, the handle position after the shaping of FFC soft arranging wires can be met.
The content of the invention
It is an object of the invention to provide a kind of preparation method of the adhesive tape for FFC stiffening plates, to solve prior art
In the presence of above mentioned problem.
The present invention is achieved by the following technical solutions：
The invention provides a kind of preparation method of the adhesive tape for FFC stiffening plates, it comprises the following steps：
Colored paint is coated on to the whole surface of resin film, forms colored paint layer；
Colloidal sol is coated on to the surface middle part of the colored paint layer, forms melten gel coating；
One end of FFC wire rods is pressed on to the surface of the melten gel coating, using FFC pressing machines, temperature at 180 DEG C,
Thermocompression forming is carried out under 0.5~0.8Pa pressure, obtains the adhesive tape for being used for stiffening plate.
Preferably, the ratio between thickness of the resin film, colored paint layer and melten gel coating is 80：0.5：19.5.
Preferably, the length of the melten gel coating is the 30~40% of resin film length.
Preferably, the length of the melten gel coating is the 37.5% of resin film length.
Preferably, the resin film is PET film.
Compared with prior art, the present invention has following beneficial effect：
1st, surface district portion gluing, isolate when being fitted in FFC soft arranging wire product ports by heating without the use of adhesive tape
Portion size, the handle position after the shaping of FFC soft arranging wires can be met, saved FFC soft arranging wire production costs；
2nd, human cost is saved, save material cost, effective to improve production efficiency.
Brief description of the drawings
Fig. 1 is the structural representation of the adhesive tape for FFC stiffening plates of the present invention.
Embodiment
With reference to specific embodiment, the present invention is described in detail.Following examples will be helpful to the technology of this area
Personnel further understand the present invention, but the invention is not limited in any way.It should be pointed out that the ordinary skill to this area
For personnel, without departing from the inventive concept of the premise, various modifications and improvements can be made.These belong to the present invention
Protection domain.
As shown in figure 1, a kind of adhesive tape for FFC stiffening plates, it includes：Resin film 1, colored paint layer 2 and melten gel coating 3,
Colored paint layer 2 is all covered in the surface of resin film 1, and melten gel coating 3 is covered in the surface middle part of colored paint layer 2.
The length of melten gel coating 3 is the 30~40% of the length of resin film 1.
The length of melten gel coating 3 is the 37.5% of the length of resin film 1.
The ratio between thickness of resin film 1, colored paint layer 2 and melten gel coating 3 is 80：0.5：19.5.
Resin film 1 is PET film.
The invention provides a kind of preparation method of the adhesive tape for FFC stiffening plates, it comprises the following steps：
Colored paint is coated on to the whole surface of resin film, forms colored paint layer；
Colloidal sol is coated on to the surface middle part of the colored paint layer, forms melten gel coating；
One end of FFC wire rods is pressed on to the surface of the melten gel coating, using FFC pressing machines, temperature at 180 DEG C,
Thermocompression forming is carried out under 0.5~0.8Pa pressure, obtains the adhesive tape for being used for stiffening plate.
Preferably, the ratio between thickness of the resin film, colored paint layer and melten gel coating is 80：0.5：19.5.
Preferably, the length of the melten gel coating is the 30~40% of resin film length.
Preferably, the length of the melten gel coating is the 37.5% of resin film length.
Preferably, the resin film is PET film.
Compared with prior art, the present invention has following beneficial effect：
1st, surface district portion gluing, isolate when being fitted in FFC soft arranging wire product ports by heating without the use of adhesive tape
Portion size, the handle position after the shaping of FFC soft arranging wires can be met, saved FFC soft arranging wire production costs；
2nd, human cost is saved, save material cost, effective to improve production efficiency.
The specific embodiment of the present invention is described above.It is to be appreciated that the invention is not limited in above-mentioned
Particular implementation, those skilled in the art can make various deformations or amendments within the scope of the claims, this not shadow
Ring the substantive content of the present invention.
Claims (10)
- A kind of 1. adhesive tape for FFC stiffening plates, it is characterised in that including：Resin film, colored paint layer and melten gel coating, the color Enamelled coating is all covered in the surface of resin film, and the melten gel coating is covered in the surface middle part of colored paint layer.
- 2. it is used for the adhesive tape of FFC stiffening plates as claimed in claim 1, it is characterised in that the length of the melten gel coating is tree The 30 ~ 40% of adipose membrane length.
- 3. it is used for the adhesive tape of FFC stiffening plates as claimed in claim 2, it is characterised in that the length of the melten gel coating is tree The 37.5% of adipose membrane length.
- 4. it is used for the adhesive tape of FFC stiffening plates as claimed in claim 1, it is characterised in that the resin film, colored paint layer and melten gel The ratio between thickness of coating is 80：0.5：19.5.
- 5. it is used for the adhesive tape of FFC stiffening plates as claimed in claim 1, it is characterised in that the resin film is PET film.
- 6. a kind of preparation method of the adhesive tape as claimed in claim 1 for FFC stiffening plates, it is characterised in that including as follows Step：Colored paint is coated on to the whole surface of resin film, forms colored paint layer；Colloidal sol is coated on to the surface middle part of the colored paint layer, forms melten gel coating；One end of FFC wire rods is pressed on to the surface of the melten gel coating, using FFC pressing machines, temperature at 180 DEG C, 0.5 ~ Thermocompression forming is carried out under 0.8Pa pressure, obtains the adhesive tape for being used for stiffening plate.
- 7. it is used for the preparation method of the adhesive tape of FFC stiffening plates as claimed in claim 6, it is characterised in that the resin film, color The ratio between thickness of enamelled coating and melten gel coating is 80：0.5：19.5.
- 8. it is used for the preparation method of the adhesive tape of FFC stiffening plates as claimed in claim 6, it is characterised in that the melten gel coating Length be resin film length 30 ~ 40%.
- 9. it is used for the preparation method of the adhesive tape of FFC stiffening plates as claimed in claim 6, it is characterised in that the melten gel coating Length be resin film length 37.5%.
- 10. as claimed in claim 6 for FFC stiffening plates adhesive tape preparation method, it is characterised in that the resin film is PET film.