CN107641808A - A kind of aluminium Special cleaning brightener and preparation method thereof - Google Patents
A kind of aluminium Special cleaning brightener and preparation method thereof Download PDFInfo
- Publication number
- CN107641808A CN107641808A CN201610579055.1A CN201610579055A CN107641808A CN 107641808 A CN107641808 A CN 107641808A CN 201610579055 A CN201610579055 A CN 201610579055A CN 107641808 A CN107641808 A CN 107641808A
- Authority
- CN
- China
- Prior art keywords
- aluminium
- product
- stirred
- brightener
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of aluminium Special cleaning brightener and preparation method thereof, its component, which is formed, is respectively：Ammonium citrate 5~10%, PBTCA (tricarboxylic acids) 30~40%, EN 90 (isomerous tridecanol polyoxyethylene ether) 3~5%, APG (APG) 3~5%, remaining add water to 100%.This product is from raw material based on the industrial chemicals for the green fully biodegradable for comparing forward position, to environment Huan Bao ﹑ safety.The present invention has quick cleaning performance, pass through the inner surface of bleeding agent rapid osmotic to greasy dirt, quickly greasy dirt is removed rapidly from workpiece surface by principles such as Rong Xie ﹑ Bao Li ﹑ emulsifications, while the organic acid used is very soft, the problems such as discoloration to surface of workpiece without any Fu Shi ﹑.
Description
Technical field
The invention belongs to clean field, it is related to the cleaning and polishing of aluminium, especially a kind of aluminium Special cleaning brightener
And preparation method thereof.
Background technology
In the fast development of modern manufacturing industry, with the popularization and use of aluminium, aluminium among our life with
And extremely important role is played in expanding economy, such as：Popularization of engine Wai Ke ﹑ aluminium material electric wires of automobile etc.
Deng.But the problem of various can be run into the process of aluminium material, most important of which is exactly to be processed in raw material
During or the transport of aluminium workpiece product in because it is various the reason for aluminium material surface can be caused dirt occur, it is dirty
The species of thing is a lot, such as：You Wu ﹑ Hui Chen ﹑ dust etc., the great puzzlement that use or conveyer belt to product come, institute
To need cleaning to seem particularly important, but aluminium belongs to amphoteric metal, very fragile, meets acid or chance alkali all can be rotten rapidly
Erosion, even if exposed also result in generation oxide skin in atmosphere, the use of workpiece and attractive in appearance is influenceed, so difficult for this industry
There are various aluminum material cleaning agents in topic, in the market, including alkaline Qing Xi Ji ﹑ neutral cleaners and acid cleaning
Agent etc., although neutral aluminum material cleaning agent will not cause to corrode to aluminium, because the stubbornness of greasy dirt or dust is difficult clear
Wash thoroughly, washing ability is not outstanding enough, can only be confined to the cleaning that workpiece surface is not very dirty workpiece and use, acid or alkali
Property aluminum material cleaning agent open market on using strong acid or highly basic, and add aluminium corrosion inhibiter and surfactant and carry out
Compounding, although cleansing power disclosure satisfy that requirement, can be caused in itself as a result of strong acid or highly basic to aluminium
The appearance for a series of problems, such as certain corrosion, some meetings cause aluminium to change colour, and serious meeting causes aluminium to black.
The content of the invention
It is an object of the invention to overcome the deficiencies of the prior art and provide a kind of aluminium Special cleaning brightener and its preparation
Method, it is environment-friendly type water based cleaning agent by the aluminium brightening agent for washing prepared by this method, without strong sour ﹑ highly basic and a huge sum of money
The materials such as category.
The present invention realizes that the technical scheme of purpose is：
A kind of aluminium Special cleaning brightener, its constituent and weight percentage ranges are respectively：
Water surplus.
Moreover, the solution concentration and content of impurities of described each constituent are respectively following scope：
A kind of preparation method of aluminium Special cleaning brightener, step are：
(1) start product special equipment stirring axe first, and check that the equipment operation is normal, device interior keep cleaning and
Dry, with standby；
(2) claim ammonium citrate according to proportioning with clean porcelain enamel barrel, add at normal temperatures a small amount of distilled water be stirred it is molten
Solve operation, with pony mixer or manually be stirred, stirring 20-30 minutes to it is complete melt it is uniform after to pour into product special
In reactor；
(3) continue to add distilled water according to metered proportions in product special reactor, and start reactor and be stirred work
Industry；
(4) PBTCA (tricarboxylic acids) ﹑ EN-90 (isomerous tridecanol polyoxyethylene ether) and APG are sequentially added into reactor
(APG) and operation is stirred, mixing time is about 20-30 minutes, until product stirs, product is in
Existing water white transparency state can stop operation.
Advantages of the present invention and beneficial effect are：
1st, this simple science of loose aluminium Special cleaning brightener mechanism of action, by bleeding agent rapid osmotic to greasy dirt
Surface, quickly greasy dirt is removed rapidly from workpiece surface by principles such as Rong Xie ﹑ Bao Li ﹑ emulsifications, while the organic acid used is non-
Normal is soft, the problems such as discoloration to surface of workpiece without any Fu Shi ﹑.
2nd, this aluminium Special cleaning brightener is obvious using simple effects, can be cleaned, can met using various ways
The different duty requirements of curstomer's site, cleaning performance is obvious, and speed is fast, improves operating efficiency, non-foaming at high temperature under high pressure, can
Cleaning and bright effect are properly arrived at,
3rd, this aluminium Special cleaning brightener be especially be formulated using new organic environmental-protection raw material, biodegradable biology
Processing of the base bleeding agent through science is prepared, Environmental Safety, and this product is in faintly acid, raw materials used wide material sources, obtains and holds
Easily, usage amount is few.
Embodiment
Below by specific embodiment, the invention will be further described, and following examples are descriptive, is not limit
Qualitatively, it is impossible to which protection scope of the present invention is limited with this.
What it is firstly the need of explanation is：The various components that the embodiment of the present invention uses are commercially available prod.
Embodiment 1：
A kind of aluminium Special cleaning brightener, each component and its content, weight proportion are respectively：
A kind of preparation method of aluminium Special cleaning brightener, step are as follows：
(1) start product special equipment stirring axe first, and check that the equipment operation is normal, device interior keep cleaning and
Dry, with standby；
(2) claim ammonium citrate according to proportioning with clean porcelain enamel barrel, add at normal temperatures a small amount of distilled water be stirred it is molten
Solve operation, with pony mixer or manually be stirred, stirring 20-30 minutes to it is complete melt it is uniform after to pour into product special
In reactor；
(3) continue to add distilled water according to metered proportions in product special reactor, and start reactor and be stirred work
Industry；
(4) PBTCA (tricarboxylic acids) ﹑ EN-90 (isomerous tridecanol polyoxyethylene ether) and APG are sequentially added into reactor
(APG) and operation is stirred, mixing time is about 20-30 minutes, until product stirs, product is in
Existing water white transparency state can stop operation.
Embodiment 2：
A kind of aluminium Special cleaning brightener, each component and its content, weight proportion are respectively：
A kind of preparation method of aluminium Special cleaning brightener, step are as follows：
(1) start product special equipment stirring axe first, and check that the equipment operation is normal, device interior keep cleaning and
Dry, with standby；
(2) claim ammonium citrate according to proportioning with clean porcelain enamel barrel, add at normal temperatures a small amount of distilled water be stirred it is molten
Solve operation, with pony mixer or manually be stirred, stirring 20-30 minutes to it is complete melt it is uniform after to pour into product special
In reactor；
(3) continue to add distilled water according to metered proportions in product special reactor, and start reactor and be stirred work
Industry；
(4) PBTCA (tricarboxylic acids) ﹑ EN-90 (isomerous tridecanol polyoxyethylene ether) and APG are sequentially added into reactor
(APG) and operation is stirred, mixing time is about 20-30 minutes, until product stirs, product is in
Existing water white transparency state can stop operation.
Quality standard：
Outward appearance：It is colourless to light yellow transparent liquid
Density (20 DEG C), g/cm3:1.130±0.010
PH value (3% aqueous solution, 25 DEG C):1.0~2.0
Sugar amount value (20 DEG C):29±1.0
The bright mechanism of action of this aluminium Special cleaning：
The present invention has quick cleaning performance, by the inner surface of bleeding agent rapid osmotic to greasy dirt, is shelled by Rong Xie ﹑
The principles such as Li ﹑ emulsifications quickly remove rapidly greasy dirt from workpiece surface, while the organic acid used is very soft, to metal work
The problems such as part surface changes colour without any Fu Shi ﹑.
Claims (3)
- A kind of 1. aluminium Special cleaning brightener, it is characterised in that：Its constituent and weight percentage ranges are respectively：
- 2. aluminium Special cleaning brightener according to claim 1, it is characterised in that：The solution of described each constituent Concentration and content of impurities are respectively following scope：
- A kind of 3. preparation method of aluminium Special cleaning brightener as claimed in claim 1, it is characterised in that：Its preparation method The step of be：(1) starting product special equipment stirring axe first, and check that the equipment operation is normal, device interior keeps cleaning and dried, With standby；(2) claim ammonium citrate according to proportioning with clean porcelain enamel barrel, add a small amount of distilled water at normal temperatures and be stirred to dissolve and make Industry, with pony mixer or manually it is stirred, pouring into product Special reverse after stirring 20-30 minutes to complete melt uniformly should In kettle；(3) continue to add distilled water according to metered proportions in product special reactor, and start reactor and be stirred operation；(4) PBTCA (tricarboxylic acids) ﹑ EN-90 (isomerous tridecanol polyoxyethylene ether) and APG (alkyl are sequentially added into reactor Glucosides) and operation is stirred, mixing time is about 20-30 minutes, until product stirs, product presents colourless Pellucidity can stop operation.