CN107630241A - Can continuous production anti-finger print steel plate processing method - Google Patents
Can continuous production anti-finger print steel plate processing method Download PDFInfo
- Publication number
- CN107630241A CN107630241A CN201710886878.3A CN201710886878A CN107630241A CN 107630241 A CN107630241 A CN 107630241A CN 201710886878 A CN201710886878 A CN 201710886878A CN 107630241 A CN107630241 A CN 107630241A
- Authority
- CN
- China
- Prior art keywords
- steel plate
- finger print
- continuous production
- processing method
- print steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses it is a kind of can continuous production anti-finger print steel plate processing method, including:(1)Substrate sheet prepares:Coil of strip uncoiling → aligning → shearing → welding → pre- degreasing degreasing;(2)The step of preceding storing;(3)Pre-electroplating treatment:Pickling → electrolytic cleaned → washing → pickling → washing;(4)Plating and post processing:An iron plating → time electrogalvanizing → second time electroplating zinc → electrogalvanizing → pickling → washing three times;(5)Fingerprint-resistant coating is applied, and anti-finger print steel plate is obtained after drying, cooling;(6)The step of storing afterwards;(7)Wound after quality inspection, oiling.The present invention realizes the continuous production to anti-finger print steel plate, and not only surface quality is good for the anti-finger print steel plate produced through the present invention, and service life is grown.
Description
Technical field
The present invention relates to Plate Production field, more particularly, to it is a kind of can continuous production anti-finger print steel plate processing method.
Background technology
In process, coil of strip needs constantly upper volume, uncoiling and winding, last volume to anti-finger print steel plate, if upper and lower
Occur during volume it is unexpected, cause can not smoothly upper and lower volume, then need to interrupt producing, and so can be to electroplating and being coated with rank
The plate quality of section has an impact.
And anti-finger print steel plate both domestic and external is all to use zinc sulfate mono-salt electrolytic galvanized sheet as substrate at present, but zinc layers are brilliant
Body is thick, and in layer structure, crystallization is coarse, loose, porosity is high, covering power is poor, it is electroplated after surface of steel plate zinc layers it is thick
Spend uneven, surface has defect, directly affects the uniformity of coating, and then influences its service life.And if in order that
The thickness of zinc layers more uniformly can first plate one layer of nickel, then add production cost.
The content of the invention
The present invention it is above-mentioned in order to overcome the shortcomings of, there is provided it is a kind of can ensure plate surface quality can continuous production it is resistance to
The processing method of finger print steel plate, including:
(1)Substrate sheet prepares:Coil of strip uncoiling → aligning → shearing → welding → pre- degreasing degreasing;
(2)The step of preceding storing;
(3)Pre-electroplating treatment:Pickling → electrolytic cleaned → washing → pickling → washing;
(4)Plating and post processing:An iron plating → time electrogalvanizing → second time electroplating zinc → electrogalvanizing → pickling → washing three times;
(5)Fingerprint-resistant coating is applied, and anti-finger print steel plate is obtained after drying, cooling;
(6)The step of storing afterwards;
(7)Wound after quality inspection, oiling.
The present invention can continuous production anti-finger print steel plate processing method, step(1)In pass through width notcher butt welding after welding
The both ends of seam are sheared, to avoid scraping rear machine.
The present invention can continuous production anti-finger print steel plate processing method, step(2)And step(7)By at least one set of storing
Roller carries out storing, and every group of storing roller includes a quiet roller and a dynamic roller, and steel plate sequentially passes through quiet roller and dynamic roller, by the shifting for moving roller
It is dynamic to increase/reduce it the distance between with quiet roller, pass through regulation in the gap of blanking after feeding and winding before coil of strip uncoiling
Dynamic the distance between roller and quiet roller can ensure the continuous production of anti-finger print steel plate.
The present invention can continuous production anti-finger print steel plate processing method, step(3)And step(4)In pickling using dense
The sulfuric acid solution for 6%-10% is spent, electrolytic cleaned uses the electrolytic cleaned agent of Yixing Hao Tian Chemical Co., Ltd.s production, and washing is adopted
It is neutral with three stage countercurrent cold water wash to pH value.
The present invention can continuous production anti-finger print steel plate processing method, step(4)Every liter of plating solution in the plating solution of middle iron plating
Including 400-500g ferrous sulfate, 150-200g potassium sulfates, 1-3g manganese sulfates, 1-3g oxalic acid, remaining is water;The plating of electrogalvanizing
Every liter of plating solution includes 60-75g zinc and 1-10g sulfuric acid in liquid, and remaining is water.
The present invention can continuous production anti-finger print steel plate processing method, during iron plating, pH value 1.8-2.2, temperature 40-
50 DEG C, current density 3-7A/dm2;During electrogalvanizing, pH value 2.5-4.5, temperature is 55-60 DEG C, current density 50-
70A/dm2。
The present invention can continuous production anti-finger print steel plate processing method, carried out after each washing by extracting roller group
Extract.
The present invention can continuous production anti-finger print steel plate processing method, step(5)Middle fingerprint-resistant coating can use ippon to apply
Material(China)Co., Ltd's production, it can also use the fingerprint-resistant coating for including following parts by weight of component:Thermoset acrylics tree
Fat 45-58 parts, nano silicon 4.5-9 parts, nano zirconium dioxide 1.5-3 parts, polytetrafluoroethylene (PTFE) 8-15 parts, Tissuemat E 3-
10 parts, the 0.8-1.5 of inorganic salts containing zirconium parts, silane coupler 3-5 parts, auxiliary agent 0.8-2 parts and deionized water 20-35 parts.
The present invention can continuous production anti-finger print steel plate processing method, the inorganic salts containing zirconium are Potassium Zirconium Fluoride, silane
Coupling agent is aminopropyl triethoxysilane or isobutyl triethoxy silane, and auxiliary agent is silicone oil.
The present invention can continuous production anti-finger print steel plate processing method, step(5)In drying temperature be 120 DEG C.
The beneficial effects of the invention are as follows:
The step of in the present invention by adding storing after uncoiling and before winding, it can effectively ensure the continuity of production, and
And by a plating iron and three times zinc-plated surface of steel plate that can make after plating almost zero defect, it ensure that the uniform of follow-up coating
Degree and surface smoothness, while production cost is relatively low.
The present invention realizes the continuous production to anti-finger print steel plate, and the anti-finger print steel plate produced through the present invention is not
But surface quality is good, and service life is grown.
Brief description of the drawings
Examples of the present invention will be described by way of reference to the accompanying drawings, wherein:
Fig. 1 is the schematic diagram of two groups of storing rollers.
Embodiment
In conjunction with the accompanying drawings, the present invention is further explained in detail.These accompanying drawings are simplified schematic diagram, only with
Illustration illustrates the basic structure of the present invention, therefore it only shows the composition relevant with the present invention.
It is a kind of can continuous production anti-finger print steel plate processing method, including:
(1)Substrate sheet prepares:Coil of strip uncoiling → aligning → shearing → welding → pre- degreasing degreasing;
(2)The step of preceding storing;
(3)Pre-electroplating treatment:Pickling → electrolytic cleaned → washing → pickling → washing;
(4)Plating and post processing:An iron plating → time electrogalvanizing → second time electroplating zinc → electrogalvanizing → pickling → washing three times;
(5)Fingerprint-resistant coating is applied through roll coater, and is dried at 120 DEG C, then anti-finger print steel plate is obtained after wind cools down;
(6)The step of storing afterwards;
(7)Wound after quality inspection, oiling.
Above-mentioned steps(1)In the both ends of weld seam are sheared by width notcher after welding, to avoid to rear machine
Scrape, pre- degreasing degreasing uses sodium hydroxide solution of the concentration for 10%-15%.
Step(2)And step(7)Storing is carried out by two groups of storing rollers, as shown in figure 1, every group of storing roller is quiet including one
Roller 1 and one moves roller 2, and two quiet rollers are in side, and for two dynamic rollers in opposite side, steel plate is S-shaped to sequentially pass through quiet roller → dynamic roller → quiet
Roller → dynamic roller sequentially passes through dynamic roller → quiet roller → dynamic roller → quiet roller, and forward and backward storing can ensure the storage for having more than 200m, and
Movement by moving roller can increase/reduce it the distance between with quiet roller, before coil of strip uncoiling after feeding and winding between blanking
In gap, the continuous production of anti-finger print steel plate can be ensured by adjusting dynamic the distance between roller and quiet roller.
If being provided with several groups of storing rollers to reduce the floor space of factory building, but storing roller is more more, and steel plate is defeated
Steering when sending is more, then easily causes steel plate to shift and rectified a deviation, it is necessary to be set in each turning point, is not only added to
This, and if have small skew in each turning point, after processing the phase can just be found, then the adjustment of the skew needs
Long period, influence to produce, step(2)And step(7)It is middle to use two groups of storing rollers to be set to be optimal.
Step(3)And step(4)In pickling use sulfuric acid solution of the concentration for 6%-10%, electrolytic cleaned uses Yixing
The electrolytic cleaned agent of Hao Tian Chemical Co., Ltd.s production, washing use three stage countercurrent cold water washes to pH value for neutrality, and
Extracted every time after washing by extracting roller group.
Step(4)Every liter of plating solution includes 400-500g ferrous sulfate, 150-200g potassium sulfates, 1- in the plating solution of middle iron plating
3g manganese sulfates, 1-3g oxalic acid, remaining is water;During iron plating, pH value 1.8-2.2, temperature is 40-50 DEG C, current density 3-
7A/dm2.The sulfuric acid that every liter of plating solution includes 60-75g zinc in the plating solution of electrogalvanizing and 1-10g concentration is 98%, remaining is water;Plating
During zinc, pH value 2.5-4.5, temperature is 55-60 DEG C, current density 50-70A/dm2.
Step(5)Middle fingerprint-resistant coating can use ippon coating(China)Co., Ltd production, can also use including with
The fingerprint-resistant coating of lower parts by weight of component:Thermosetting acrylic resin 45-58 parts, nano silicon 4.5-9 parts, nano-silica
Change zirconium 1.5-3 parts, polytetrafluoroethylene (PTFE) 8-15 parts, Tissuemat E 3-10 parts, the 0.8-1.5 of inorganic salts containing zirconium parts, silane coupler 3-5
Part, auxiliary agent 0.8-2 parts and deionized water 20-35 parts.Above-mentioned inorganic salts containing zirconium are Potassium Zirconium Fluoride, and silane coupler is aminopropyl
Triethoxysilane or isobutyl triethoxy silane, auxiliary agent are silicone oil.
The step of in the present invention by adding storing after uncoiling and before winding, it can effectively ensure the continuous of production
Property, and the zinc-plated Surface Defects in Steel Plate that can make after plating below 0.0009%, reaches in every square meter by a plating iron and three times
Nearly defect-free degree has been arrived, ensure that the uniformity and surface smoothness of follow-up coating, while production cost is relatively low.
The present invention realizes the continuous production to anti-finger print steel plate, and the anti-finger print steel plate produced through the present invention is not
But surface quality is good, and service life is grown.
Above-mentioned according to the present invention is enlightenment, by above-mentioned description, relevant staff completely can without departing from
In the range of this invention technological thought, various changes and amendments are carried out.The technical scope of this invention is not limited to
In the content on specification, it is necessary to determine its technical scope according to right.
Claims (10)
1. it is a kind of can continuous production anti-finger print steel plate processing method, it is characterised in that including:
(1)Substrate sheet prepares:Coil of strip uncoiling → aligning → shearing → welding → pre- degreasing degreasing;
(2)The step of preceding storing;
(3)Pre-electroplating treatment:Pickling → electrolytic cleaned → washing → pickling → washing;
(4)Plating and post processing:An iron plating → time electrogalvanizing → second time electroplating zinc → electrogalvanizing → pickling → washing three times;
(5)Fingerprint-resistant coating is applied, and anti-finger print steel plate is obtained after drying, cooling;
(6)The step of storing afterwards;
(7)Wound after quality inspection, oiling.
2. it is according to claim 1 can continuous production anti-finger print steel plate processing method, it is characterised in that step(1)In
The both ends of weld seam are sheared by width notcher after welding.
3. it is according to claim 1 can continuous production anti-finger print steel plate processing method, it is characterised in that step(2)With
Step(7)Storing is carried out by least one set of storing roller, every group of storing roller includes a quiet roller and a dynamic roller, and steel plate sequentially passes through
Quiet roller and dynamic roller.
4. it is according to claim 1 can continuous production anti-finger print steel plate processing method, it is characterised in that step(3)With
Step(4)In pickling use sulfuric acid solution of the concentration for 6%-10%, washing use three stage countercurrent cold water washes to pH value for
It is neutral.
5. it is according to claim 1 can continuous production anti-finger print steel plate processing method, it is characterised in that step(4)In
Every liter of plating solution includes 400-500g ferrous sulfate, 150-200g potassium sulfates, 1-3g manganese sulfates, 1-3g grass in the plating solution of iron plating
Acid, remaining is water;Every liter of plating solution includes 60-75g zinc and 1-10g sulfuric acid in the plating solution of electrogalvanizing, and remaining is water.
6. it is according to claim 5 can continuous production anti-finger print steel plate processing method, it is characterised in that during iron plating,
PH value is 1.8-2.2, and temperature is 40-50 DEG C, current density 3-7A/dm2;During electrogalvanizing, pH value 2.5-4.5, temperature
For 55-60 DEG C, current density 50-70A/dm2.
7. it is according to claim 1 can continuous production anti-finger print steel plate processing method, it is characterised in that washing every time
Extracted afterwards by extracting roller group.
8. it is according to claim 1 can continuous production anti-finger print steel plate processing method, it is characterised in that step(5)In
Fingerprint-resistant coating includes the component of following parts by weight:
Thermosetting acrylic resin 45-58 parts
Nano silicon 4.5-9 parts
Nano zirconium dioxide 1.5-3 parts
Polytetrafluoroethylene (PTFE) 8-15 parts
Tissuemat E 3-10 parts
The 0.8-1.5 parts of inorganic salts containing zirconium
Silane coupler 3-5 parts
Auxiliary agent 0.8-2 parts
Deionized water 20-35 parts.
9. it is according to claim 8 can continuous production anti-finger print steel plate processing method, it is characterised in that it is described containing zirconium without
Machine salt is Potassium Zirconium Fluoride, and silane coupler is aminopropyl triethoxysilane or isobutyl triethoxy silane, and auxiliary agent is silicon
Oil.
10. it is according to claim 1 can continuous production anti-finger print steel plate processing method, it is characterised in that step(5)In
Drying temperature be 120 DEG C.