CN107629564A - 一种高氯化聚乙烯防腐涂料及其生产方法 - Google Patents

一种高氯化聚乙烯防腐涂料及其生产方法 Download PDF

Info

Publication number
CN107629564A
CN107629564A CN201710961481.6A CN201710961481A CN107629564A CN 107629564 A CN107629564 A CN 107629564A CN 201710961481 A CN201710961481 A CN 201710961481A CN 107629564 A CN107629564 A CN 107629564A
Authority
CN
China
Prior art keywords
parts
chlorinated polyethylene
corrosive paint
high chlorinated
highly
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710961481.6A
Other languages
English (en)
Inventor
杨松林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU XIN'AN NEW MATERIALS TECHNOLOGY Co Ltd
Original Assignee
JIANGSU XIN'AN NEW MATERIALS TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU XIN'AN NEW MATERIALS TECHNOLOGY Co Ltd filed Critical JIANGSU XIN'AN NEW MATERIALS TECHNOLOGY Co Ltd
Priority to CN201710961481.6A priority Critical patent/CN107629564A/zh
Publication of CN107629564A publication Critical patent/CN107629564A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种高氯化聚乙烯防腐涂料，由以下原料按照重量份组成：高氯化聚乙烯：30‑40份；丙二醇二醋酸酯：40‑50份；钛白粉：25‑35份；防锈颜料：5‑10份；溶剂：20‑30份；滑石粉20‑40份；助剂：2‑5份；一种高氯化聚乙烯防腐涂料的生产方法，该高氯化聚乙烯防腐涂料的生产方法包括以下步骤：S1；常压下搅拌；S2：研磨；S3包装。高氯化聚乙烯防腐漆是采用高氯化聚乙烯(HCPE)树脂为防腐基料、经物理加工，配以高级防腐颜料，溶剂、防锈颜料、填料和助剂，经聚合反应而形成。产品可分为底漆和面漆两大类。

Description

一种高氯化聚乙烯防腐涂料及其生产方法
技术领域
本发明涉及高氯化聚乙烯防腐涂料技术领域，具体为一种高氯化聚乙烯防腐涂料及其生产方法。
背景技术
高氯化聚乙烯防腐涂料的成膜物质具有化学的惰性，阻燃、封闭性好。对大气、水份及石油类都具有良好的抵御性，具有优异的户外耐候性，涂膜坚韧、耐温性佳、防霉变、附着力强，干燥迅速，单组分包装，不需在施工现场临时调配。维修方便，新旧涂层之间有互溶作用，故维修时不必去掉牢固的就涂膜。贮存期长，不结皮、不结块。高氯化聚乙烯防腐涂料适用于船舶、港口、铁路设施，海上采油平台，公路桥梁、石油、化工、冶炼、钢铁设备，集装箱、管道、木材表面及混凝土表面，厂房构筑物的保护。使其免受大气、海水、酸类、碱类、盐类、油类、化学气体等腐蚀介质的侵蚀。
发明内容
本发明的目的是为了解决现有技术中存在的缺点，而提出的一种高氯化聚乙烯防腐涂料及其生产方法。
为实现上述目的，本发明提供如下技术方案：
一种高氯化聚乙烯防腐涂料，由以下原料按照重量份组成：
高氯化聚乙烯：30份；
丙二醇二醋酸酯：40份；
钛白粉：25份；
防锈颜料：5份；
溶剂：20份；
滑石粉：20份；
助剂：2份；
优选的，所述高氯化聚乙烯。
优选的，所述钛白粉粒径为400目。
优选的，一种高氯化聚乙烯防腐涂料的生产方法，其特征在于：该高氯化聚乙烯防腐涂料的生产方法包括以下步骤：
S1：常压下搅拌：高氯化聚乙烯：30份；丙二醇二醋酸酯：40份；钛白粉：25份；防锈颜料：5份；溶剂：20份；滑石粉20份；助剂：2份；搅拌三十分钟到五十分钟；
S2：进研磨机研磨至细度30um；
S3：包装：将S2的产物按照规格要求进行包装。
本发明提供的一种高氯化聚乙烯防腐涂料，该高氯化聚乙烯防腐涂料不仅具有较好的防腐性能，而且是一种成本低廉，性能优异，功能全面的高氯化聚乙烯防腐涂料。
具体实施方式
基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
一种高氯化聚乙烯防腐涂料，由以下原料按照重量份组成：
高氯化聚乙烯：32份；
丙二醇二醋酸酯：41份；
钛白粉：26份；
防锈颜料：6份；
溶剂：21份；
滑石粉：22份；
助剂：2份；
优选的，所述高氯化聚乙烯。
优选的，所述钛白粉粒径为400目。
一种高氯化聚乙烯防腐涂料的生产方法，该高氯化聚乙烯防腐涂料的生产方法包括以下步骤：
S1：常压下搅拌高氯化聚乙烯：32份；丙二醇二醋酸酯：41份；钛白粉：26份；防锈颜料：6份；溶剂：21份；滑石粉22份；助剂：2份；搅拌三十分钟到五十分钟；
S2：进研磨机研磨至细度30um；
S3：包装：将S2的产物按照规格要求进行包装。
实施例2
一种高氯化聚乙烯防腐涂料，由以下原料按照重量份组成：
高氯化聚乙烯：33份；
丙二醇二醋酸酯：44份；
钛白粉：28份；
防锈颜料：7份；
溶剂：25份；
滑石粉：28份；
助剂：3份；
优选的，所述高氯化聚乙烯。
优选的，所述钛白粉粒径为400目。
一种高氯化聚乙烯防腐涂料的生产方法，该高氯化聚乙烯防腐涂料的生产方法包括以下步骤：
S1：常压下搅拌：高氯化聚乙烯：33份；丙二醇二醋酸酯：44份；
钛白粉：28份；防锈颜料：7份；溶剂：25份；滑石粉28份；助剂：3份；搅拌三十分钟到五十分钟；
S2：进研磨机研磨至细度30um；
S3：包装：将S2的产物按照规格要求进行包装。
实施例3
一种高氯化聚乙烯防腐涂料，该高氯化聚乙烯防腐涂料的配方由包含以下重量份的组分制成：
高氯化聚乙烯：40份；
丙二醇二醋酸酯：50份；
钛白粉：35份；
防锈颜料：10份；
溶剂：30份；
滑石粉：40份；
助剂：5份；
优选的，所述高氯化聚乙烯。
优选的，所述钛白粉粒径为400目。
一种高氯化聚乙烯防腐涂料的生产方法，该高氯化聚乙烯防腐涂料的生产方法包括以下步骤：
S1：常压下搅拌：高氯化聚乙烯：40份；丙二醇二醋酸酯：50份；
钛白粉：35份；防锈颜料：10份；溶剂：30份；滑石粉40份；助剂：5份；搅拌三十分钟到五十分钟；
S2：进研磨机研磨至细度30um；
S3：包装：将S2的产物按照规格要求进行包装。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。

Claims (6)

1.一种高氯化聚乙烯防腐涂料，其特征在于：由以下原料按照重量份组成：
高氯化聚乙烯：30-40份；
丙二醇二醋酸酯：40-50份；
钛白粉：25-35份；
防锈颜料：5-10份；
溶剂：20-30份；
滑石粉：20-40份；
助剂：2-5份。
2.根据权利要求1所述的一种高氯化聚乙烯防腐涂料，其特征在于：由以下原料按照重量份组成：
高氯化聚乙烯：30份；
丙二醇二醋酸酯：40份；
钛白粉：25份；
防锈颜料：5份；
溶剂：20份；
滑石粉：20份；
助剂：2份。
3.根据权利要求1所述的一种高氯化聚乙烯防腐涂料，其特征在于：所述高氯化聚乙烯。
4.根据权利要求1所述的一种高氯化聚乙烯防腐涂料，其特征在于：所述钛白粉粒径为400目。
5.根据权利要求1所述的一种高氯化聚乙烯防腐涂料，其特征在于：防锈颜料粒径为500目。
6.一种如权利要求1所述高氯化聚乙烯防腐涂料的生产方法，其特征在于：该高氯化聚乙烯防腐涂料的生产方法包括以下步骤：
S1：常压下搅拌：高氯化聚乙烯：30份；丙二醇二醋酸酯：40份；钛白粉：25份；防锈颜料：5份；溶剂：20份；滑石粉20份；助剂：2份；搅拌三十分钟到五十分钟；
S2：进研磨机研磨至细度30um；
S3：包装：将S2的产物按照规格要求进行包装。
CN201710961481.6A 2017-10-17 2017-10-17 一种高氯化聚乙烯防腐涂料及其生产方法 Pending CN107629564A (zh)