CN107629360A - 一种改进pvc绝缘材料阻燃性能的配方及其加工工艺 - Google Patents
一种改进pvc绝缘材料阻燃性能的配方及其加工工艺 Download PDFInfo
- Publication number
- CN107629360A CN107629360A CN201710997795.1A CN201710997795A CN107629360A CN 107629360 A CN107629360 A CN 107629360A CN 201710997795 A CN201710997795 A CN 201710997795A CN 107629360 A CN107629360 A CN 107629360A
- Authority
- CN
- China
- Prior art keywords
- parts
- formula
- insulating materials
- mixed
- processing technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种改进PVC绝缘材料阻燃性能的配方，所述配方按重量份含有如下组分：PVC树脂100份，氯化石蜡30‑40份，环氧化油5‑12份，氧化钙1‑5份，氧化镁1‑5份，三碱式硫酸铅1‑5份，石蜡2‑5份。并提供了本发明的配方的加工工艺。按本发明配方制得的绝缘材料的阻燃性能优异。
Description
技术领域
本发明公开了一种改进PVC绝缘材料阻燃性能的配方及其加工工艺。
背景技术
PVC即聚氯乙烯，是由氯乙烯在引发剂作用下聚合而成的热塑性树脂，是氯乙烯的均聚物。PVC是通用型树脂，价格低廉、加工方便，它和助剂配合制得制品具有重量轻、强度高，耐化学药品性好，电绝缘性能和耐老化性能、防水防腐性能皆优，是电线电缆较理想的包覆材料。
通常，未加增塑剂的PVC(PVC-U)制品具有良好的阻燃性能，但掺入大量增塑剂的软质PVC却易燃。同时，无论是硬质PVC还是软质PVC在燃烧过程中都会产生大量烟雾，其最大烟密度(Dm)高达720(以Rohm&HassXP-2烟箱测定)，在塑料中名列榜首。据统计，火灾中死亡人数的82.5％是被燃烧时产生的有毒气体窒息而死。因此，对PVC的阻燃抑烟研究引起人们极大的关注。
发明内容
本发明解决其技术问题所采用的技术方案是：一种改进PVC绝缘材料阻燃性能的配方，所述配方按重量份含有如下组分：PVC树脂100份，氯化石蜡30-40份，环氧化油5-12份，氧化钙1-5份，氧化镁1-5份，三碱式硫酸铅1-5份，石蜡2-5份。
本发明的目的之一还在于提供本发明所述配方的加工工艺，包括如下步骤：
(1)按组成原料的重量份称取各原料，将所有原料加入混合机中混合均匀，控制混合机温度在85℃下先低速混合20min，然后再高速混合5min，然后在170℃下进行一次塑化，切粒，风冷；
(2)将步骤(1)的风冷料在120℃下进行二次塑化，切粒、风冷、检测后包装。
本发明的有益效果是：本发明制得的绝缘材料阻燃性能显著增加，并且绝缘性能依然很好。
具体实施方式
具体实施例：一种改进PVC绝缘材料阻燃性能的配方，所述配方按重量份含有如下组分：PVC树脂100份，氯化石蜡30-40份，环氧化油5-12份，氧化钙1-5份，氧化镁1-5份，三碱式硫酸铅1-5份，石蜡2-5份。
本发明还在于提供本发明所述配方的加工工艺，包括如下步骤：
(1)按组成原料的重量份称取各原料，将所有原料加入混合机中混合均匀，控制混合机温度在85℃下先低速混合20min，然后再高速混合5min，然后在170℃下进行一次塑化，切粒，风冷；
(2)将步骤(1)的风冷料在120℃下进行二次塑化，切粒、风冷、检测后包装。
本发明的有益效果是：本发明制得的绝缘材料阻燃性能显著增加，并且绝缘性能依然很好。
显然，上述实施例仅仅是为清楚地说明所作的举例，而并非对实施方式的限定。对于所属领域的普通技术人员来说，在上述说明的基础上还可以做出其它不同形式的变化或变动。这里无需也无法对所有的实施方式予以穷举。而由此所引伸出的显而易见的变化或变动仍处于本发明创造的保护范围之中。
Claims (2)
1.一种改进PVC绝缘材料阻燃性能的配方，其特征是：由下述重量份混合而成：PVC树脂100份，氯化石蜡30-40份，环氧化油5-12份，氧化钙1-5份，氧化镁1-5份，三碱式硫酸铅1-5份，石蜡2-5份。
2.根据权利要求1所述配方的加工工艺，其特征在于，包括如下步骤：
(1)按组成原料的重量份称取各原料，将所有原料加入混合机中混合均匀，控制混合机温度在85℃下先低速混合20min，然后再高速混合5min，然后在170℃下进行一次塑化，切粒，风冷；
(2)将步骤(1)的风冷料在120℃下进行二次塑化，切粒、风冷、检测后包装。