CN107629359A - A kind of abrasion resistant fire blocking cable jacket material - Google Patents
A kind of abrasion resistant fire blocking cable jacket material Download PDFInfo
- Publication number
- CN107629359A CN107629359A CN201710952903.3A CN201710952903A CN107629359A CN 107629359 A CN107629359 A CN 107629359A CN 201710952903 A CN201710952903 A CN 201710952903A CN 107629359 A CN107629359 A CN 107629359A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- abrasion resistant
- butadiene
- cable jacket
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of abrasion resistant fire blocking cable jacket material, and its raw material includes by weight：75 80 parts of polyvinyl chloride resin, 15 22 parts of trichloroactic acid ethylene copolymer, 13 18 parts of Kynoar, 8 12 parts of neoprene, 13 15 parts of nitrile rubber, 58 parts of butadiene-styrene rubber, 39 parts of butadiene rubber, 10 12 parts of glass fibre, 8 14 parts of carboxymethyl cellulose, 13 parts of carbon black, 13 parts of white carbon, 1.5 2 parts of talcum powder, 0.5 1.8 parts of zinc oxide, 1.5 2 parts of magnesia, 58 parts of nano-calcium carbonate, 58 parts of nano silica fume, 57 parts of nanometer Xuancheng stone, 6 12 parts of insect-and mouse-preventing auxiliary agent, 5 10 parts of sulphur, 5 10 parts of three-level stearic acid, 6 12 parts of pitch, 14 16 parts of composite flame-retardant agent, 15 19 parts of filler, 13 parts of plasticizer；The present invention is with polyvinyl chloride resin; butadiene-styrene rubber, nitrile rubber, ethylene propylene diene rubber; neoprene; the mixture of butadiene rubber is base-material, its excellent fireproof performance, is aided with other each raw materials; including composite flame-retardant agent; age resister, can be remarkably reinforced the ageing resistance and anti-flammability of cable, increase the service life of cable significantly.
Description
Technical field
The present invention relates to CABLE MATERIALS, and in particular to a kind of abrasion resistant fire blocking cable jacket material.
Background technology
With developing rapidly for economy, electric wire is widely used in industry-by-industry, field.Cable, lead to
It is often by several or the cable of similar rope that several groups of wires (every group at least two) are twisted, between every group of wire mutually absolutely
Edge, and be often twisted into around a center, whole outside is surrounded by the cable cover(ing) of high-insulation.Cable has interior energization, outer exhausted
The feature of edge.
Into after modern society, because urban land is nervous, traffic pressure is big, the reason such as appearance of the city construction, and big city is universal
Using buried cable power transmission mode.Relative to aerial cable, buried cable, which has, takes up an area small, reliable, strong antijamming capability of transmitting electricity
The advantages that.
But the wearability of existing cable is poor, by easily being deformed with ground friction in transport and process of deployment
With different degrees of damage, meanwhile, buried cable is often bitten by biologies such as worm mouse, and fault occurs.In order to
Solves above-mentioned phenomenon, the wearability and the anti-characteristic that bites for improving cable turn into the current technical issues that need to address.
The content of the invention
In view of the shortcomings of the prior art, the invention provides a kind of abrasion resistant fire blocking cable jacket material, the anti-ageing of cable is strengthened
The property changed and anti-flammability.
To realize object above, the present invention is achieved by the following technical programs：A kind of abrasion resistant fire blocking cable jacket material,
Its raw material includes by weight：Polyvinyl chloride resin 75-80 parts, vinyl chloride-vinyl acetate copolymer 15-22 parts, Kynoar 13-
18 parts, neoprene 8-12 parts, nitrile rubber 13-15 parts, butadiene-styrene rubber 5-8 parts, butadiene rubber 3-9 parts, glass fibre 10-12
Part, carboxymethyl cellulose 8-14 parts, carbon black 1-3 parts, white carbon 1-3 parts, talcum powder 1.5-2 parts, zinc oxide 0.5-1.8 parts, oxygen
Change magnesium 1.5-2 parts, nano-calcium carbonate 5-8 parts, nano silica fume 5-8 parts, nanometer Xuancheng stone 5-7 parts, insect-and mouse-preventing auxiliary agent 6-12 parts,
Sulphur 5-10 parts, three-level stearic acid 5-10 parts, pitch 6-12 parts, composite flame-retardant agent 14-16 parts, filler 15-19 parts, plasticizer
1-3 parts.
Preferably, the composite flame-retardant agent is that weight part ratio is 1:2:5 silicon nitride, magnesium silicate, modified calcium carbonate.
Preferably, the filler is the one or more in carbon black, lignin and plant ash.
Preferably, the plasticizer is one kind in epoxy aliphatic acid methyl ester and chlorinated paraffin.
Preferably, the insect-and mouse-preventing auxiliary agent is the molten alkyl cuprammonium of ammonia, paracide, allicin, 4,5,9-trithiadodeca-1,6,11-triene 9-oxide and capsicum
Element presses 3:2:4:2:1 ratio mixes.
Preferably, the nitrile rubber is BMI modified butadiene acrylonitrile rubbers.
Preferably, the butadiene-styrene rubber is acrylic modified butadiene-styrene rubber.
Preferably, the butadiene rubber is Polystyrene butadiene rubber.
The invention provides a kind of abrasion resistant fire blocking cable jacket material, the present invention is with polyvinyl chloride resin, butadiene-styrene rubber, nitrile rubber,
Ethylene propylene diene rubber, neoprene, the mixture of butadiene rubber is base-material, its excellent fireproof performance, is aided with other each raw materials, bag
Composite flame-retardant agent is included, age resister, the ageing resistance and anti-flammability of cable can be remarkably reinforced, increase cable significantly uses the longevity
Life.
Embodiment
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described,
Obviously, described embodiment is only part of the embodiment of the present invention, rather than whole embodiments.Based in the present invention
Embodiment, the every other embodiment that those of ordinary skill in the art are obtained under the premise of creative work is not made, all
Belong to the scope of protection of the invention.
In description of the invention, it is also necessary to explanation, unless otherwise clear and definite regulation and limitation, term " setting ", " peace
Dress ", " connected ", " connection " should be interpreted broadly, for example, it may be fixedly connected or be detachably connected, or integratedly
Connection, can be mechanical connection or electrical connection, can be directly connected to or be connected by intermediary, can
To be the connection of two element internals.For the ordinary skill in the art, can understand as the case may be above-mentioned
The concrete meaning of term in the present invention.
Embodiment 1：
A kind of abrasion resistant fire blocking cable jacket material, its raw material include by weight：75 parts of polyvinyl chloride resin, vinyl chloride-acetate
5 parts of copolymer 1,13 parts of Kynoar, 8 parts of neoprene, 13 parts of nitrile rubber, 5 parts of butadiene-styrene rubber, 3 parts of butadiene rubber, glass
10 parts of glass fiber, 8 parts of carboxymethyl cellulose, 1 part of carbon black, 1 part of white carbon, 1.5 parts of talcum powder, 0.5 part of zinc oxide, magnesia
1.5 parts, 8 parts of nano-calcium carbonate, 5 parts of nano silica fume, 5 parts of nanometer Xuancheng stone, 12 parts of insect-and mouse-preventing auxiliary agent, 5 parts of sulphur, three-level is hard
5 parts of resin acid, 12 parts of pitch, 16 parts of composite flame-retardant agent, 15 parts of filler, 1 part of plasticizer.
Preferably, the composite flame-retardant agent is that weight part ratio is 1:2:5 silicon nitride, magnesium silicate, modified calcium carbonate.
Preferably, the filler is the one or more in carbon black, lignin and plant ash.
Preferably, the plasticizer is one kind in epoxy aliphatic acid methyl ester and chlorinated paraffin.
Preferably, the insect-and mouse-preventing auxiliary agent is the molten alkyl cuprammonium of ammonia, paracide, allicin, 4,5,9-trithiadodeca-1,6,11-triene 9-oxide and capsicum
Element presses 3:2:4:2:1 ratio mixes.
Preferably, the nitrile rubber is BMI modified butadiene acrylonitrile rubbers.
Preferably, the butadiene-styrene rubber is acrylic modified butadiene-styrene rubber.
Preferably, the butadiene rubber is Polystyrene butadiene rubber.
Embodiment 2：
A kind of abrasion resistant fire blocking cable jacket material, its raw material include by weight：80 parts of polyvinyl chloride resin, vinyl chloride-acetate
22 parts of copolymer, 13 parts of Kynoar, 8 parts of neoprene, 15 parts of nitrile rubber, 8 parts of butadiene-styrene rubber, 9 parts of butadiene rubber, glass
12 parts of glass fiber, 14 parts of carboxymethyl cellulose, 3 parts of carbon black, 3 parts of white carbon, 2 parts of talcum powder, 1.8 parts of zinc oxide, magnesia 2
Part, 8 parts of nano-calcium carbonate, 8 parts of nano silica fume, 7 parts of nanometer Xuancheng stone, 12 parts of insect-and mouse-preventing auxiliary agent, 10 parts of sulphur, three-level tristearin
10 parts of acid, 12 parts of pitch, 16 parts of composite flame-retardant agent, 19 parts of filler, 3 parts of plasticizer.
Preferably, the composite flame-retardant agent is that weight part ratio is 1:2:5 silicon nitride, magnesium silicate, modified calcium carbonate.
Preferably, the filler is the one or more in carbon black, lignin and plant ash.
Preferably, the plasticizer is one kind in epoxy aliphatic acid methyl ester and chlorinated paraffin.
Preferably, the insect-and mouse-preventing auxiliary agent is the molten alkyl cuprammonium of ammonia, paracide, allicin, 4,5,9-trithiadodeca-1,6,11-triene 9-oxide and capsicum
Element presses 3:2:4:2:1 ratio mixes.
Preferably, the nitrile rubber is BMI modified butadiene acrylonitrile rubbers.
Preferably, the butadiene-styrene rubber is acrylic modified butadiene-styrene rubber.
Preferably, the butadiene rubber is Polystyrene butadiene rubber.
Experiment
Apparatus for Pressure at high-temp condition：
Test temperature：80 DEG C ± 2 DEG C,
The load lower duration：The outside diameter of cable≤12.5mm, 4h；
The outside diameter of cable ＞ 12.5mm, 6h；
Cable jacket material made from embodiment 1,2 is tested, and contrasted with market common cable protective cover material row.Experiment
As a result it is as follows：
The invention provides a kind of abrasion resistant fire blocking cable jacket material, the present invention is with polyvinyl chloride resin, butadiene-styrene rubber, nitrile rubber,
Ethylene propylene diene rubber, neoprene, the mixture of butadiene rubber is base-material, its excellent fireproof performance, is aided with other each raw materials, bag
Composite flame-retardant agent is included, age resister, the ageing resistance and anti-flammability of cable can be remarkably reinforced, increase cable significantly uses the longevity
Life.
The above embodiments are merely illustrative of the technical solutions of the present invention, rather than its limitations；Although with reference to the foregoing embodiments
The present invention is described in detail, it will be understood by those within the art that：It still can be to foregoing each implementation
Technical scheme described in example is modified, or carries out equivalent substitution to which part technical characteristic；And these modification or
Replace, the essence of appropriate technical solution is departed from the spirit and scope of various embodiments of the present invention technical scheme.
Claims (8)
1. a kind of abrasion resistant fire blocking cable jacket material, it is characterised in that its raw material includes by weight：Polyvinyl chloride resin 75-80 parts, chlorine
Ethene-vinyl acetate copolymer 15-22 parts, Kynoar 13-18 parts, neoprene 8-12 parts, nitrile rubber 13-15 parts,
Butadiene-styrene rubber 5-8 parts, butadiene rubber 3-9 parts, glass fibre 10-12 parts, carboxymethyl cellulose 8-14 parts, carbon black 1-3 parts, hard charcoal
Black 1-3 parts, talcum powder 1.5-2 parts, zinc oxide 0.5-1.8 parts, magnesia 1.5-2 parts, nano-calcium carbonate 5-8 parts, nano silica fume
5-8 parts, nanometer Xuancheng stone 5-7 parts, insect-and mouse-preventing auxiliary agent 6-12 parts, sulphur 5-10 parts, three-level stearic acid 5-10 parts, pitch 6-12
Part, composite flame-retardant agent 14-16 parts, filler 15-19 parts, plasticizer 1-3 parts.
2. abrasion resistant fire blocking cable jacket material according to claim 1, it is characterised in that：The composite flame-retardant agent is parts by weight
Than for 1:2:5 silicon nitride, magnesium silicate, modified calcium carbonate.
3. abrasion resistant fire blocking cable jacket material according to claim 1, it is characterised in that：The filler is carbon black, wooden
One or more in element and plant ash.
4. abrasion resistant fire blocking cable jacket material according to claim 1, it is characterised in that：The plasticizer is epoxyfatty acid
One kind in methyl esters and chlorinated paraffin.
5. abrasion resistant fire blocking cable jacket material according to claim 1 or 2, it is characterised in that：The insect-and mouse-preventing auxiliary agent is
The molten alkyl cuprammonium of ammonia, paracide, allicin, 4,5,9-trithiadodeca-1,6,11-triene 9-oxide and capsaicine press 3:2:4:2:1 ratio mixes.
6. abrasion resistant fire blocking cable jacket material according to claim 1 or 2, it is characterised in that：The nitrile rubber changes for BMI
Property nitrile rubber.
7. abrasion resistant fire blocking cable jacket material according to claim 1 or 2, it is characterised in that：The butadiene-styrene rubber is methyl
Acrylic acid modified butadiene-styrene rubber.
8. abrasion resistant fire blocking cable jacket material according to claim 1 or 2, it is characterised in that：The butadiene rubber is polyphenyl
Ethylene modified butadiene rubber.