CN107623108A - A kind of solidifying lead acid battery polar plate drying process - Google Patents
A kind of solidifying lead acid battery polar plate drying process Download PDFInfo
- Publication number
- CN107623108A CN107623108A CN201710881706.7A CN201710881706A CN107623108A CN 107623108 A CN107623108 A CN 107623108A CN 201710881706 A CN201710881706 A CN 201710881706A CN 107623108 A CN107623108 A CN 107623108A
- Authority
- CN
- China
- Prior art keywords
- solidification
- stage
- plate
- drying process
- relative humidity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of solidifying lead acid battery polar plate drying process, it is related to accumulator plate preparing technical field.Including curing schedule and drying steps；Wherein cure stage includes three phases, and drying steps include two stages.The present invention is heated up by staged, rises in cure stage temperature early stage slow, avoids that lead plaster dehydration is too fast to cause pole plate to ftracture；And by keeping the relative humidity in curing room, free lead oxidation and the heat humidity needed for grid corrosion are ensure that, accelerated oxidation, the good corrosion layer of forming properties, connection is provided to solidify the skeleton of lead plaster, improves polar plate solidification quality.
Description
Technical field
The invention belongs to accumulator plate preparing technical field, is dried more particularly to a kind of solidifying lead acid battery polar plate
Technique.
Background technology
Curing process is process extremely crucial together during lead-acid storage battery production.Pole plate, after the completion of coating
Curing room is sent to be solidified.Solidifying lead acid battery polar plate is a physical change and electrochemical corrosion course, and its effect is
The hardening and corrosion of lead plaster are completed, allows being further oxidized to as lead monoxide of free lead in lead plaster, while allows lead plaster and grid
Between react and be combined as a whole, so as to reach the purpose of good mechanical strength and electrical property.So polar plate solidification is good
Bad overall performance and the life-span for being directly connected to pole plate.The solidification drying of green plate is in polar plate of lead acid storage battery manufacturing process
One of critical process, it directly influences the mechanical strength and electrical property of pole plate after chemical conversion complexity, chemical conversion, is related to plumbic acid
The amount of capacity and life-span length of battery.So the solidification process of the green plate after filling can not adopt a casual attitude；Polar plate solidification
Drying process is exactly the pole plate for scribbling wet cream, under high humidity and certain temperature, makes moisture evaporation in pole plate, and makes to send out in wet cream
Raw some changes, last wet pole plate turns into the green plate for having some strength to dry, for follow-up processing.
The content of the invention
It is an object of the invention to provide a kind of solidifying lead acid battery polar plate drying process, heated up by staged,
Cure stage temperature early stage rises slow, avoids that lead plaster dehydration is too fast to cause pole plate to ftracture；And by keeping in curing room
Relative humidity, it ensure that free lead oxidation and the heat humidity needed for grid corrosion, accelerated oxidation, the good corruption of forming properties
Layer is lost, connection is provided to solidify the skeleton of lead plaster, improves polar plate solidification quality.
In order to solve the above technical problems, the present invention is achieved by the following technical solutions：
The present invention is a kind of solidifying lead acid battery polar plate drying process, is comprised the following steps：
Step 1：Cure stage
The a first stage：By curing room temperature control at 35 DEG C -40 DEG C, then relative humidity control is put pole plate 90%
In solidifying 5h in curing room；
B second stage：Solidification indoor temperature is improved to 50 DEG C -65 DEG C, relative humidity in 2h and is down to 70%, then will
Pole plate continues to solidify 7h；
The c phase IIIs：Solidification indoor temperature is improved to 70 DEG C -80 DEG C, relative humidity in 5h and is down to 45%, then will
Pole plate continues to solidify 10h；
Step 2：Drying stage
The a first stage：Solidification indoor temperature is improved to 75 DEG C, relative humidity in 4h and is down to 20%, then by pole plate
Continue to dry 18h；
B second stage：Solidification indoor temperature is improved to 90 DEG C, relative humidity in 5h and is down to 5%, then by pole plate after
It is continuous to dry 25h.
Further, the positive plate lead paste free lead content after the solidification is less than 3%；Negative plate lead after the solidification
Cream free lead content is less than 5%.
Further, the curing schedule first stage temperature uniformly slowly rises, temperature lifting per hour 1 in the stage
℃。
Further, the moisture of the positive plate after the solidification and negative plate is respectively less than 0.5%.
Further, in the solidification and drying process, temperature error≤± 1.5 DEG C, relative humidity deviation≤±
1.5%.
The invention has the advantages that：
The present invention is heated up by staged, rises in cure stage temperature early stage slow, avoids that lead plaster dehydration is too fast to be led
Cause pole plate cracking；And by keeping the relative humidity in curing room, it ensure that free lead oxidation and the heat needed for grid corrosion
Individual humidity, accelerated oxidation, the good corrosion layer of forming properties, connection is provided to solidify the skeleton of lead plaster, pole plate is improved and consolidates
Change quality.
Certainly, any product for implementing the present invention it is not absolutely required to reach all the above advantage simultaneously.
Embodiment
The present invention is a kind of solidifying lead acid battery polar plate drying process, is comprised the following steps：
Step 1：Cure stage
The a first stage：By curing room temperature control at 35 DEG C -40 DEG C, then relative humidity control is put pole plate 90%
In solidifying 5h in curing room；
B second stage：Solidification indoor temperature is improved to 50 DEG C -65 DEG C, relative humidity in 2h and is down to 70%, then will
Pole plate continues to solidify 7h；
The c phase IIIs：Solidification indoor temperature is improved to 70 DEG C -80 DEG C, relative humidity in 5h and is down to 45%, then will
Pole plate continues to solidify 10h；
Step 2：Drying stage
The a first stage：Solidification indoor temperature is improved to 75 DEG C, relative humidity in 4h and is down to 20%, then by pole plate
Continue to dry 18h；
B second stage：Solidification indoor temperature is improved to 90 DEG C, relative humidity in 5h and is down to 5%, then by pole plate after
It is continuous to dry 25h.
Wherein, the positive plate lead paste free lead content after solidification is less than 3%；Negative plate lead plaster free lead content after solidification
Less than 5%.
Wherein, curing schedule first stage temperature uniformly slowly rises, and temperature lifts 1 DEG C per hour in the stage.
Wherein, the moisture of the positive plate after solidification and negative plate is respectively less than 0.5%.
Wherein, in solidification and drying process, temperature error≤± 1.5 DEG C, relative humidity deviation≤± 1.5%.
Wherein, solidify indoor relative humidity to control by atomizing humidifying performance shower nozzle and vapor shower nozzle；Temperature passes through electrical heating
System and ventilating system control；Ventilating system includes supply fan and exhaust fan.
If surrounding, ground and top are evenly distributed with dry temperature sensor and humidity sensor in curing room；Switch board leads to
Temperature and relative humidity in excess temperature sensor and humidity sensor sensing curing room, so as to be adjusted in time.
In the description of this specification, the description of reference term " one embodiment ", " example ", " specific example " etc. means
At least one implementation of the present invention is contained in reference to specific features, structure, material or the feature that the embodiment or example describe
In example or example.In this manual, identical embodiment or example are not necessarily referring to the schematic representation of above-mentioned term.
Moreover, specific features, structure, material or the feature of description can close in any one or more embodiments or example
Suitable mode combines.
Present invention disclosed above preferred embodiment is only intended to help and illustrates the present invention.Preferred embodiment is not detailed
All details are described, it is only described embodiment also not limit the invention.Obviously, according to the content of this specification,
It can make many modifications and variations.This specification is chosen and specifically describes these embodiments, is to preferably explain the present invention
Principle and practical application so that skilled artisan can be best understood by and utilize the present invention.The present invention is only
Limited by claims and its four corner and equivalent.
Claims (5)
1. a kind of solidifying lead acid battery polar plate drying process, it is characterised in that comprise the following steps：
Step 1：Cure stage
The a first stage：By curing room temperature control at 35 DEG C -40 DEG C, then pole plate is placed in solid 90% by relative humidity control
Change indoor solidification 5h；
B second stage：Solidification indoor temperature is improved to 50 DEG C -65 DEG C, relative humidity in 2h and is down to 70%, then by pole plate
Continue to solidify 7h；
The c phase IIIs：Solidification indoor temperature is improved to 70 DEG C -80 DEG C, relative humidity in 5h and is down to 45%, then by pole plate
Continue to solidify 10h；
Step 2：Drying stage
The a first stage：Solidification indoor temperature is improved to 75 DEG C, relative humidity in 4h and is down to 20%, then continues pole plate
Dry 18h；
B second stage：Solidification indoor temperature is improved to 90 DEG C, relative humidity in 5h and is down to 5%, then continues to do by pole plate
Dry 25h.
2. a kind of solidifying lead acid battery polar plate drying process according to claim 1, it is characterised in that after the solidification
Positive plate lead paste free lead content be less than 3%；Negative plate lead plaster free lead content after the solidification is less than 5%.
A kind of 3. solidifying lead acid battery polar plate drying process according to claim 1, it is characterised in that the solidification step
Rapid first stage temperature uniformly slowly rises, and temperature lifts 1 DEG C per hour in the stage.
4. a kind of solidifying lead acid battery polar plate drying process according to claim 1, it is characterised in that after the solidification
Positive plate and the moisture of negative plate be respectively less than 0.5%.
A kind of 5. solidifying lead acid battery polar plate drying process according to claim 1, it is characterised in that it is described solidification and
In drying process, temperature error≤± 1.5 DEG C, relative humidity deviation≤± 1.5%.