CN107619625A - A kind of environmentally friendly showering finish paint of high comprehensive performance and preparation method thereof - Google Patents
A kind of environmentally friendly showering finish paint of high comprehensive performance and preparation method thereof Download PDFInfo
- Publication number
- CN107619625A CN107619625A CN201710627583.4A CN201710627583A CN107619625A CN 107619625 A CN107619625 A CN 107619625A CN 201710627583 A CN201710627583 A CN 201710627583A CN 107619625 A CN107619625 A CN 107619625A
- Authority
- CN
- China
- Prior art keywords
- finish paint
- environmentally friendly
- comprehensive performance
- high comprehensive
- showering finish
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to a kind of coating.A kind of environmentally friendly showering finish paint of high comprehensive performance, is made up of, the varnish is made up of the component of following mass percent varnish and diluent:Hydroxyl alkyd resinses 10 ~ 20%, aldehyde ketone resin 20 ~ 25%, amino resins 3 5%, 1/4 second nitrocotton 25 ~ 35%, auxiliary agent 5.5% ~ 15%, solvent 25 ~ 35%.For the present invention by screening suitable resin system and dicyandiamide solution, prepared showering finish paint has excellent dryness, glossiness, richness, adhesive force.
Description
Technical field
The present invention relates to a kind of coating.
Background technology
Loss is big when showering finish paint generally existing in the market is constructed, the easy lifting of paint film, the shortcomings of easily turning white.
The content of the invention
Based on this, the technical problems to be solved by the invention are to provide a kind of good environmentally friendly showering finish paint of combination property,
Its preparation method is also provided.
A kind of environmentally friendly showering finish paint of high comprehensive performance, is made up of, the varnish is by following quality varnish and diluent
The component composition of percentage:Hydroxyl alkyd resinses 10 ~ 20%, aldehyde ketone resin 20 ~ 25%, amino resins 3-5%, 1/4 second nitrocotton
25 ~ 35%, auxiliary agent 5.5% ~ 15%, solvent 25 ~ 35%.Resin in the formula is to the dryness of paint film, gloss, richness, solid
Part content is significantly improved, and product is also had clear improvement to the adhesive force of ground, can also improve hardness of paint film.
Further, the solvent 100% is counted by mass percentage, by butyl glycol ether 2-10%, acetone 5-10%, methyl
Pentanone alcohol 10-20%, isopropanol 20-30%, isobutanol 25-35%, ethyl acetate 15-30% compositions.Above-mentioned solvent formula is special
For the dicyandiamide solution different from conventional spray paint technique of showering finish paint research and development, solves the problems, such as conventional spray paint finish paint because of solvent
The problem of caused paint film easily turns white, lifting, bad levelling, also solve the easy stream pendant caused by showering is constructed, paint film
The problem of thickness bad control.
Further, the solvent 100% is counted by mass percentage, by ethylene glycol monomethyl ether 5%, acetone 5%, methylpentanone
Alcohol 10%, isopropanol 30%, isobutanol 35%, ethyl acetate 15% form.
Further, the auxiliary agent is plasticizer 2 ~ 5%, levelling agent 0.5 ~ 1.5%, adhesion promoter 3-5%.
Further, the diluent is based on percent by volume 100%, by ethyl acetate 20-30%, methyl iso-butyl ketone (MIBK) 5-
10%, methylpentanolone 10-20%, isopropanol 20-30%, isobutanol 20-30% are formed.
The preparation method of above-mentioned environmental protection coating material is:First solvent is mixed, is slowly added into while stirring with dispersion machine 1/4 second
Nitrocotton, side adds hydroxyl alkyd resinses and aldehyde ketone resin while stirring after nitrocotton dissolving completely in 1/4 second, treats hydroxyl alkyd
After resin and aldehyde ketone resin dissolve well, auxiliary agent is sequentially added while stirring, is stirred.
The present invention has the advantages that:
For the present invention by screening suitable resin system and dicyandiamide solution, prepared showering finish paint has excellent dryness, light
Damp degree, richness, adhesive force.
Embodiment
With reference to embodiment, the present invention will be described in detail.
Above example uses following preparation technology:First solvent is mixed, is slowly added into while stirring with dispersion machine 1/4 second
Nitrocotton, side adds hydroxyl alkyd resinses and aldehyde ketone resin while stirring after nitrocotton dissolving completely in 1/4 second, treats hydroxyl alkyd
After resin and aldehyde ketone resin dissolve well, auxiliary agent is sequentially added while stirring, is stirred.
Varnish prepared by above three embodiment, with diluent with 1:3 volume ratio mixing, obtains being directly used in construction
Finished product finish paint.The formula of diluent, based on percent by volume 100%, by ethyl acetate 20%, methyl iso-butyl ketone (MIBK) 10%, methyl
Pentanone alcohol 10%, isopropanol 30%, isobutanol 30% form.
As shown in upper table, the advantages such as finish paint of the invention has good surface effect, hardness, adhesive force, dryness good.
Claims (6)
1. a kind of environmentally friendly showering finish paint of high comprehensive performance, is made up of varnish and diluent, it is characterised in that:The varnish by
The component composition of following mass percent:Hydroxyl alkyd resinses 10 ~ 20%, aldehyde ketone resin 20 ~ 25%, amino resins 3-5%, 1/4
Second nitrocotton 25 ~ 35%, auxiliary agent 5.5% ~ 15%, solvent 25 ~ 35%.
2. the environmentally friendly showering finish paint of high comprehensive performance according to claim 1, it is characterised in that:The solvent presses quality
Percentage 100% is counted, by butyl glycol ether 2-10%, acetone 5-10%, methylpentanolone 10-20%, isopropanol 20-30%, isobutanol
25-35%, ethyl acetate 15-30% are formed.
3. the environmentally friendly showering finish paint of high comprehensive performance according to claim 2, it is characterised in that:The solvent presses quality
Percentage 100% is counted, by ethylene glycol monomethyl ether 5%, acetone 5%, methylpentanolone 10%, isopropanol 30%, isobutanol 35%, ethyl acetate
15% composition.
4. the environmentally friendly showering finish paint of high comprehensive performance according to claim 1, it is characterised in that:The auxiliary agent is plasticising
Agent 2 ~ 5%, levelling agent 0.5 ~ 1.5%, adhesion promoter 3-5%.
5. the environmentally friendly showering finish paint of high comprehensive performance according to claim 1, it is characterised in that:The diluent presses body
Product percentage 100% is counted, by ethyl acetate 20-30%, methyl iso-butyl ketone (MIBK) 5-10%, methylpentanolone 10-20%, isopropanol 20-
30%, isobutanol 20-30% are formed.
A kind of 6. preparation method of the environmentally friendly showering finish paint described in claim 1 ~ 4 any one, it is characterised in that the varnish
Preparation technology be:First solvent is mixed, is slowly added into 1/4 second nitrocotton while stirring with dispersion machine, treats that 1/4 second nitrocotton is molten
Solution completely after while stirring side add hydroxyl alkyd resinses and aldehyde ketone resin, treat hydroxyl alkyd resinses and aldehyde ketone resin dissolve it is good with
Afterwards, auxiliary agent is sequentially added while stirring, is stirred.