CN107616546A - The preparation method of the quick-fried pearl lapping of cigarette - Google Patents
The preparation method of the quick-fried pearl lapping of cigarette Download PDFInfo
- Publication number
- CN107616546A CN107616546A CN201710761556.6A CN201710761556A CN107616546A CN 107616546 A CN107616546 A CN 107616546A CN 201710761556 A CN201710761556 A CN 201710761556A CN 107616546 A CN107616546 A CN 107616546A
- Authority
- CN
- China
- Prior art keywords
- quick
- cigarette
- fried pearl
- lapping
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of preparation method of the quick-fried pearl lapping of cigarette, the method weighs sodium alginate, Arabic gum, carragheen, pulullan polysaccharide, G & W according to a certain percentage;After well mixed, heating makes dissolving;Filtering, ultrasonication remove bubble removing, and Temperature fall produces the lapping for preparing the quick-fried pearl of cigarette.The present invention has the advantages that raw material sources are abundant, simple to operate.It is applied to the manufacturing of the quick-fried pearl of cigarette using lapping as rubber matrix, the increase of rubber thickness can be made, product permeability, adhesion phenomenon are reduced, cracking pressure improves, and the requirement of the physical indexs such as diameter, thickness, weight is disclosure satisfy that, after storing a period of time, it is not in the phenomenon of permeability and hair mist, the exterior quality and production qualification rate of quick-fried pearl product are improved on the whole, effective guarantee cigarette quality, there is the value of actual production conversion and popularization and application.
Description
Technical field
The invention belongs to cigarette material preparing technical field, and in particular to a kind of preparation side of the quick-fried pearl lapping of cigarette
Method.
Background technology
Quick-fried pearl, also referred to as fragrance dripping pill, fragility capsule etc., refer to a kind of liquid being embedded in the form of capsule in cigarette filter
The small glue bead of body, by wrapping up the liquid flux of diverse fragrant flavour, it is pinched brokenly, made by smoker during cigarette smoking with hand extruding
Perfume liquid is flowed out in pearl, and flavor component is released under cigarette mainstream flue gas effect.Application of the quick-fried pearl in cigarette filter rod,
The adjustable of cigarette odor-absorbing is realized, flavouring humectation positive effect, the consumer for pursuing cigarette individual character note can be met, relaxed
Suitable sense, return sweet tea sense, the suction experience for the pleasants such as sense of promoting the production of body fluid;Quick-fried pearl has the powerful vision such as the sound, transparent visual simultaneously
Output, assign the function that cigarette product play one.In recent years, domestic existing many tobacco enterprises are researched and developed and manufacture quick-fried pearl volume
Cigarette, in terms of quick-fried pearl key technology barrier is broken through, achieve certain achievement.Chinese patent CN102108136A discloses one
Kind dripping pills of cigarette additive lapping and the application with its dripping pill and dripping pill that wrap up;Chinese patent CN103190702A is announced
It is a kind of that there are the soft capsule for improving cigarette sense organ humid keeping performance, preparation method and applications;Chinese patent CN105540073A
Disclose a kind of cigarette fragility capsule and preparation method thereof;Chinese patent CN103653230A disclose a kind of fragile soft capsule and
Its preparation method.With reference to practical condition, the present inventor is using prior art(Dropping preparation method produces dripping pill soft capsule, specifically
Method is according to Chinese patent CN102108136A " dripping pills of cigarette additive lapping and the dripping pill and dripping pill with its parcel
Using ")Found when preparing the quick-fried pearl of cigarette filter rod, producing quick-fried pearl using dropping preparation method has following defect:Dripping pill is after formation
Dry, easily rubbed in screening and filter stick telescopiny, extrude and fracture phenomena occurs, the oily perfume in soft capsule holds
Easily ooze out, the adhesion situation between dripping pill occur, after storing a period of time, dripping pill fragility reduces, and showing for hair mist occurs once in a while
As when pinching brokenly dripping pill with hand, it is difficult to hear " " clear and melodious sound, have a strong impact on dripping pill exterior quality and practical application effect
Fruit.This is probably due to rubber thinner thickness, caused by moisture content is unstable, the reason such as putrid and deteriorated occurs for rubber matrix.
The wall material raw material that conventional art prepares soft capsule is mostly gelatin, and it is mainly extracted from the skin, bone of some animals
Obtain.With generation of the European to rabid ox disease and the frightened and domestic toxic capsule event of aftosa, gelatin soft capsule occurs
Security hidden trouble, and can not by some special belief culture persons(Jew, Islamic Moslem)Or vegetarian receives.
In recent years, in order to solve the problems, such as gelatin soft capsule, people attempt capsule product of the exploitation using plant polysaccharides as lapping,
Carry out replacing gelatin soft capsule, and gradually welcome by masses.
Arabic gum, it is a kind of natural plant for extracting to obtain from the secretory product of African leguminous plant, mainly
Including pectinose, galactolipin, glucuronic acid etc..Arabic gum is the most cheap in the world and wide variety of parent at present
One of hydrocolloid, through frequently as naturally occurring emulsifying agent, stabilizer, suspending agent, thickener, adhesive, film forming agent, being widely used in drinking
In the food such as material, essence, chocolate, candy, margarine.
Carragheen, it is a kind of high molecular weight hydrophilic polysaccharide for extracting to obtain from marine red alga, its chemical constitution is by D-
The linear polysaccharide compound that galactolipin and 3,6- dehydration-D- galactose residues are formed, also known as Eucheuma glue, agar glue,
Antler glue, carrageenan.Carragheen, which is dissolved in hot water, can form viscous transparent or slight milky easy fluent solution, eat
Thickener, gelling agent and stabilizer etc. are generally used as in product industry.
Sodium alginate also known as sodium alginate, seaweed gel, algin are a kind of using sea-tangle, marine alga as made of raw material extraction
Natural chain lock shape macromolecule polysaccharide polymer.Due to sodium alginate have unique thickening property, hydrophily, stability, gelling,
The characteristics such as film forming, are widely used in food industry, and have good biocompatibility and degradability, cheap,
The effect of with slowing down food water loss and suppressing microorganism pollution.
Pulullan polysaccharide is also known as pullulan, for a kind of similar as caused by fermenting Aureobasidium pullulans glucan, xanthan
The extracellular water solubility cement polysaccharide of glue is the maltotriose recurring unit by α-Isosorbide-5-Nitrae glucosides key connection through α -1, the polymerization of 6 glycosidic bonds
The straight-chain polysaccharide formed, molecular weight is typically 4.8 × 104-2.2×106Between(Commodity pulullan polysaccharide mean molecule quantity is
200000, about it is made up of 480 maltotrioses).The film forming of pulullan polysaccharide, barrier, plasticity, viscosity are relatively strong, and
And with good characteristics such as soluble in water, nontoxic, colorless and odorless, additionally there is certain fresh-keeping, preservative efficacy, extensively
It is general to be applied in candy, chocolate-coated, diaphragm, compound seasoner and fruit-vegetable juice beverage.
Reported according to documents and materials, in different materials described above, application of the pulullan polysaccharide in soft capsule preparation
Effect is ideal.The present invention is by materials such as Arabic gum, carragheen, sodium alginate, pulullan polysaccharides according to certain quality
Ratio rationally compounds, it is intended to develop it is a kind of using plant polysaccharides as the quick-fried pearl lapping of the cigarette of body material, it is existing to solve
There is produced problem in production technology.
The content of the invention
The purpose of the present invention is in view of the shortcomings of the prior art, there is provided a kind of lapping for being used to prepare the quick-fried pearl of cigarette,
Have the advantages that raw material sources are abundant, simple to operate, practical, be applied to the lapping as rubber matrix
In the manufacturing of the quick-fried pearl of cigarette, the increase of rubber thickness, product permeability, adhesion phenomenon are reduced, and cracking pressure improves, and disclosure satisfy that
The physical indexs such as diameter, thickness, weight requirement, store a period of time after, be not in permeability and hair mist phenomenon, dripping pill fragility
Increase, when pinching brokenly dripping pill with hand, you can hear " " clear and melodious sound, improve exterior quality and the life of quick-fried pearl product on the whole
Qualification rate is produced, effective guarantee cigarette quality, there is the value of actual production conversion and popularization and application.
To achieve the above object, a kind of lapping for being used to prepare the quick-fried pearl of cigarette provided by the invention, it includes as follows
Step:
(1)Sodium alginate 1.0~2.0% is weighed according to percentage by weight, Arabic gum 0.5~1.0%, carragheen 0.5~1.0%,
Pulullan polysaccharide 15~20%, glycerine 3~6%, water surplus;
(2)After above material is well mixed, it is placed in heating container, is warming up to 70~80 DEG C under constant agitation, protect
Temperature 0.5~1 hour, makes mixture fully dissolve;
(3)By step(2)In material filtering after, remove bubble removing through ultrasonication, Temperature fall is transferred to 50~60 DEG C
It is standby in heat-preserving container, the lapping as of the present invention for being used to prepare the quick-fried pearl of cigarette.
Preferably, the viscosity of described sodium alginate is 150~300mPas.
Preferably, described carragheen is κ type carragheens.
Preferably, the molecular weight of described pulullan polysaccharide is 15~250,000.
The advantage of the invention is that:
(1)The present invention is using pulullan polysaccharide as main wall material raw material, reasonable compounding Arabic gum, carragheen, sodium alginate, sweet
The materials such as oil, develop a kind of using plant polysaccharides as the quick-fried pearl lapping of the cigarette of body material.Pulullan polysaccharide has pole
Good dissolubility, film forming, plasticity, viscosity, heat sealability and barrier.As the lapping of dripping pill, rubber can be ensured
Moisture content is stable, increases rubber thickness, while has certain preservative efficacy, avoids rubber that mildew phenomena occurs.
(2)The present invention has the advantages that raw material sources are abundant, simple to operate, practical, by the lapping
It is applied to as rubber matrix in the manufacturing of the quick-fried pearl of cigarette, the increase of rubber thickness, product permeability, adhesion phenomenon are reduced, and are broken
Broken pressure improves, and disclosure satisfy that the requirement of the physical indexs such as diameter, thickness, weight, after storing a period of time, be not in permeability and
Send out mist phenomenon, dripping pill fragility increase, when pinching brokenly dripping pill with hand, you can hear " " clear and melodious sound, improve on the whole quick-fried
The exterior quality of pearl product and production qualification rate, effective guarantee cigarette quality, there are actual production conversion and popularization and application
Value.
Embodiment
Below in conjunction with specific embodiment, the present invention is described in further detail.
Embodiment one
(1)Sodium alginate 2.0% is weighed according to percentage by weight, Arabic gum 1.0%, carragheen 0.5%, pulullan polysaccharide 15%,
Glycerine 5.5%, water 76%.
(2)After above material is well mixed, it is placed in heating container, is warming up to 75 DEG C under constant agitation, protect
Warm 50min, makes mixture fully dissolve.
(3)By step(2)In material filtering after through ultrasonication remove bubble removing, Temperature fall is transferred to 60 DEG C
It is standby in heat-preserving container, the lapping as of the present invention for being used to prepare the quick-fried pearl of cigarette.
The viscosity of described sodium alginate is 150~300mPas.
Described carragheen is κ type carragheens.
The molecular weight of described pulullan polysaccharide is 15~250,000.
Embodiment two:
(1)Sodium alginate 1.0% is weighed according to percentage by weight, Arabic gum 0.5%, carragheen 0.5%, pulullan polysaccharide 17%,
Glycerine 4%, water 77%.
(2)After above material is well mixed, it is placed in heating container, is warming up to 70 DEG C under constant agitation, protect
Temperature 1 hour, makes mixture fully dissolve.
(3)By step(2)In material filtering after through ultrasonication remove bubble removing, Temperature fall is transferred to 55 DEG C
It is standby in heat-preserving container, the lapping as of the present invention for being used to prepare the quick-fried pearl of cigarette.
The viscosity of described sodium alginate is 150~300mPas.
Described carragheen is κ type carragheens.
The molecular weight of described pulullan polysaccharide is 15~250,000.
Embodiment three:
(1)Sodium alginate 1.5% is weighed according to percentage by weight, Arabic gum 0.6%, carragheen 0.4%, pulullan polysaccharide 20%,
Glycerine 4.5%, water 73%.
(2)After above material is well mixed, it is placed in heating container, is warming up to 70 DEG C under constant agitation, protect
Warm 1h, makes mixture fully dissolve.
(3)By step(2)In material filtering after through ultrasonication remove bubble removing, Temperature fall is transferred to 55 DEG C
It is standby in heat-preserving container, the lapping as of the present invention for being used to prepare the quick-fried pearl of cigarette.
The viscosity of described sodium alginate is 150~300mPas.
Described carragheen is κ type carragheens.
The molecular weight of described pulullan polysaccharide is 15~250,000.
Example IV:
(1)Sodium alginate 1.3%, Arabic gum 0.7%, carragheen 0.5%, pulullan polysaccharide are weighed according to percentage by weight
16.5%, glycerine 5.5%, water 75.5%.
(2)After above material is well mixed, it is placed in heating container, is warming up to 80 DEG C under constant agitation, protect
Warm 40min, makes mixture fully dissolve.
(3)By step(2)In material filtering after through ultrasonication remove bubble removing, Temperature fall is transferred to 55 DEG C
It is standby in heat-preserving container, the lapping as of the present invention for being used to prepare the quick-fried pearl of cigarette.
The viscosity of described sodium alginate is 150~300mPas.
Described carragheen is κ type carragheens.
The molecular weight of described pulullan polysaccharide is 15~250,000.
Concrete application:
The present invention is with reference to Chinese invention patent CN102108136A(Dripping pills of cigarette additive lapping and the dripping pill with its parcel
And the application of dripping pill)Described in method, using DWJSYJ-I types pill dripping machine by liquor drop drop is made, then drop onto paraffin
Dripping pill is made in oil coolant, through sieving, drying, arranging and produce cigarette with quick-fried pearl product.Used pill dripping machine be prior art
Have, the present invention borrows it and completes sample trial-production.
It is constant from the content core containing certain odor additive, fixed dripping pill preparation technology, by above example
Lapping in 1-4 serves as rubber matrix, prepares the quick-fried pearl product of cigarette.Make discovery from observation, products obtained therefrom is uniform in size, circle
Degree is preferable, and breakage rate is low, almost without dripping pill permeability and adhesion phenomenon, and after storing a period of time, does not find mist and permeability
Situation.Compared with control sample, dripping pill fragility increase, with hand slightly firmly can pinch brokenly dripping pill, while hear " " it is clear and melodious
Sound, the exterior quality and production qualification rate of quick-fried pearl product are improved on the whole.Further determine particle diameter, the rubber of dripping pill
The physical indexs such as thickness, weight, cracking pressure, moisture content.As shown in Table 1, rubber thickness increase, particle diameter, weight and contains
In allowed band, cracking pressure substantially increases water rate.
The physical index of the quick-fried pearl product of table 1
Claims (4)
1. the preparation method of the quick-fried pearl lapping of cigarette, comprises the following steps:
(1)Sodium alginate 1.0~2.0% is weighed according to percentage by weight, Arabic gum 0.5~1.0%, carragheen 0.5~1.0%,
Pulullan polysaccharide 15~20%, glycerine 3~6%, water surplus;
(2)After above material is well mixed, it is placed in heating container, is warming up to 70~80 DEG C under constant agitation, protect
Temperature 0.5~1 hour, makes mixture fully dissolve;
(3)By step(2)In material filtering after, remove bubble removing through ultrasonication, Temperature fall is transferred to 50~60 DEG C
It is standby in heat-preserving container, the lapping as of the present invention for being used to prepare the quick-fried pearl of cigarette.
2. the preparation method of the quick-fried pearl lapping of cigarette according to claim 1, it is characterised in that:The sodium alginate
Viscosity is 150~300mPas.
3. the preparation method of the quick-fried pearl lapping of cigarette according to claim 1, it is characterised in that:The carragheen is κ
Type carragheen.
4. the preparation method of the quick-fried pearl lapping of cigarette according to claim 1, it is characterised in that:The pulullan polysaccharide
Molecular weight be 15~250,000.