CN107611221A - 提高锑化物基ⅱ类超晶格材料质量的方法 - Google Patents
提高锑化物基ⅱ类超晶格材料质量的方法 Download PDFInfo
- Publication number
- CN107611221A CN107611221A CN201710834227.XA CN201710834227A CN107611221A CN 107611221 A CN107611221 A CN 107611221A CN 201710834227 A CN201710834227 A CN 201710834227A CN 107611221 A CN107611221 A CN 107611221A
- Authority
- CN
- China
- Prior art keywords
- crystal lattice
- quality
- growth
- super crystal
- improving
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提高锑化物基Ⅱ类超晶格材料质量的方法,步骤一:在高真空腔室中,执行材料的生长;步骤二:对于需要提高材料质量的部分,在生长过程进行到该部分时,开启原子氢源的束流覆盖材料表面,原子氢源的激发功率为50‑200W,期间的真空度为1×10‑8‑1×10‑6Torr;步骤三:高质量材料的部分生长完毕后,关闭原子氢源,之后可继续执行后续的材料生长工艺。本发明以原子氢来辅助超晶格材料的分子束外延生长过程,有效地提高了样品的载流子迁移率,这表明本发明的方法钝化了材料中的杂质、抑制了缺陷的形成,可得到高质量的Ⅱ类超晶格材料。
Description
技术领域
本发明属于半导体材料与器件技术领域,具体是一种提高锑化物基Ⅱ类超晶格材料质量的方法,它可被应用于锑化物基Ⅱ类超晶格相关材料的高质量制备。
背景技术
基于Ⅲ-Ⅴ族半导体的锑化物基Ⅱ类超晶格材料是一种新型的红外探测器材料,能同时满足第三代红外探测器对高探测率、大面阵、多波段、低功耗、低成本等要求,因此成为了第三代红外探测器材料的最佳选择而被国际上广泛看好。
锑化物基Ⅱ类超晶格是由两种或以上的基于InAs、GaSb的二元或多元化合物半导体薄层,按一定的设计顺序周期性地重复沉积而成。在超晶格材料(尤其是p-i-n结构探测器件的i层)中,杂质与缺陷会散射载流子、影响少子寿命,对其电学性能影响显著。另一方面,由于在超晶格的生长过程中腔室里的As分压和Sb分压较高,在这两种Ⅴ族源频繁交替切换的过程中,生长的超晶格各层之间的界面容易发生As、Sb元素互混,降低两种材料界面处的纯度,从而降低界面质量。因此,要提高锑化物基Ⅱ类超晶格红外探测器的探测率、良品率和稳定性,必须设法在超晶格材料的生长过程中提高其纯度及界面质量。
发明内容
本发明的目的是提供一种提高锑化物基Ⅱ类超晶格材料质量的方法,采用原子氢来辅助超晶格材料的分子束外延生长过程,可提高材料纯度与界面质量。
本发明通过如下技术方案实现上述目的:
提高锑化物基Ⅱ类超晶格材料质量的方法,包括以下步骤:
步骤一:在高真空腔室中,执行材料的生长;
步骤二:对于需要提高材料质量的部分,在生长过程进行到该部分时,开启原子氢源的束流覆盖材料表面,原子氢源的激发功率为50-200W,期间的真空度为1×10-8-1×10- 6Torr;
步骤三:高质量材料的部分生长完毕后,关闭原子氢源,之后可继续执行后续的材料生长工艺。
进一步的,所述步骤一中的材料为锑化物基Ⅱ类超晶格相关的Ⅲ-Ⅴ族锑化物及砷化物材料。
进一步的,所述步骤一中的材料生长方法为分子束外延。
进一步的,所述步骤一中的高真空腔室,其本底真空度高于1×10-9Torr。
与现有技术相比,本发明提高锑化物基Ⅱ类超晶格材料质量的方法的有益效果是:1)在生长过程中引入原子氢可即时钝化杂质,提高载流子迁移率,并且材料经过热退火后性能不退化;2)原子氢有助于外延生长时材料逐层在二维平面成核,促进了超晶格材料的二维生长模式,从而提升外延原子层的平整度并抑制缺陷、位错、层错的形成,提高外延材料质量;3)在生长过程中引入原子氢时,可以使用更低的As分压和Sb分压,减弱界面Ⅴ族元素互混现象,易于得到界面质量更好的超晶格材料。
具体实施方式
下面用实施例对本发明的技术方案作进一步的说明。
本发明的提高锑化物基Ⅱ类超晶格材料质量的方法可应用于锑化物基Ⅱ类超晶格相关材料的生长工艺。为了更明显地表现本发明的使用效果,下面对本发明的一个优选实施例进行详细描述,本实施例选择了生长锑化物基Ⅱ类超晶格InAs/GaSb中的InAs以展示应用本发明后的材料生长结果。本实施例的步骤包括:
步骤一:在本底真空度为5×10-10Torr的高真空腔室中,以GaAs为衬底,采用分子束外延方法生长InAs材料;
步骤二:生长开始时,同步开启原子氢源的束流覆盖材料表面,原子氢源的激发功率为150W,期间的真空度为2×10-7Torr;
步骤三:在开启原子氢源的状态下生长6微米InAs之后,关闭原子氢源。
作为对比例,另取GaAs衬底生长InAs材料,重复执行上述步骤,不同之处仅在于:在步骤二、三中,不开启原子氢源,生长过程中真空度为5×10-9Torr。
实施例和对比例各生长了6微米厚的InAs材料,测得77K温度下对比例样品的载流子迁移率为62000cm2/V·s,而实施例样品的载流子迁移率可达98000cm2/V·s,并且经过400摄氏度的热退火之后,实施例样品的载流子迁移率不变。
对比可见,采用本发明的方法,以原子氢来辅助超晶格材料的分子束外延生长过程,有效地提高了样品的载流子迁移率,这表明本发明的方法钝化了材料中的杂质、抑制了缺陷的形成,可得到高质量的Ⅱ类超晶格材料。
以上所述的仅是本发明的一种实施方式。对于本领域的普通技术人员来说,在不脱离本发明创造构思的前提下,还可以做出若干变形和改进,这些都属于本发明的保护范围。
Claims (4)
1.提高锑化物基Ⅱ类超晶格材料质量的方法,其特征在于,包括以下步骤:
步骤一:在高真空腔室中,执行材料的生长;
步骤二:对于需要提高材料质量的部分,在生长过程进行到该部分时,开启原子氢源的束流覆盖材料表面,原子氢源的激发功率为50-200W,期间的真空度为1×10-8-1×10- 6Torr;
步骤三:高质量材料的部分生长完毕后,关闭原子氢源,之后可继续执行后续的材料生长工艺。
2.根据权利要求1所述的提高锑化物基Ⅱ类超晶格材料质量的方法,其特征在于:所述步骤一中的材料为锑化物基Ⅱ类超晶格相关的Ⅲ-Ⅴ族锑化物及砷化物材料。
3.根据权利要求1所述的提高锑化物基Ⅱ类超晶格材料质量的方法,其特征在于:所述步骤一中的材料生长方法为分子束外延。
4.根据权利要求1所述的提高锑化物基Ⅱ类超晶格材料质量的方法,其特征在于:所述步骤一中的高真空腔室,其本底真空度高于1×10-9Torr。