CN107604631A - A kind of refining white technique of silk floss satin - Google Patents
A kind of refining white technique of silk floss satin Download PDFInfo
- Publication number
- CN107604631A CN107604631A CN201710688539.4A CN201710688539A CN107604631A CN 107604631 A CN107604631 A CN 107604631A CN 201710688539 A CN201710688539 A CN 201710688539A CN 107604631 A CN107604631 A CN 107604631A
- Authority
- CN
- China
- Prior art keywords
- tons
- cylinder
- refining
- water
- satin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of white technique of refining of silk floss satin, and it includes following technological process：The first step, the ripe wrinkle print on green compact is evened up with stenter；Second step, preparation house, green compact are carried out with circle code, nail button loop；3rd step, degumming refining is carried out in cylinder is just refined in vain, 40 45 are done per cylinder, coupe is 45 50 meters, and specific practice is as follows, is first soaked with 5 tons of warm water cylinder, 30 40 minutes time, 30 40 DEG C of water temperature；Then cylinder just is refined with 5 tons of hot water, puts the 20kg of dispersant 15, the 8kg of soda ash 6, the 6kg of sodium silicate 4, the 1.5kg of sodium hydrosulfite 1 in water, water temperature control is at 96 98 DEG C, 90 100 minutes time.The product whiteness of the refining white technique processing of the silk floss satin is good, silk fabric face is clean, wrinkle-free print.
Description
Technical field：
It is especially a kind of white technique of refining of silk floss satin the present invention relates to dyeing and finishing field.
Background technology：
Contain substantial amounts of silk gum impurity in silk floss satin, wherein most be fibrous material silk gum inherently and oily wax,
Ash content, pigment etc., also it is stained with addition in slurry and the illuminating colour and operation, transportation that apply for identification twist direction
Various greasy dirts.These natural and artificial impurity presence, not only impair the intrinsic fine quality of silk floss satin, influence taking
Can, and make fabric be difficult to be contaminated material solution-wet and infiltration, hinder dyeing and finishing processing.Thus silk floss satin has to pass through refining and added
Work provides qualified semi-products to go the removal of impurity, for post-processing or directly obtains the white product of refining, but the existing white technique of refining comes out
Product whiteness is poor, silk fabric face is not clean enough, have impurity, or even there is also wrinkle print.
The content of the invention：
It is good, clean, the wrinkle-free print in silk fabric face the technical problem to be solved by the invention is to provide a kind of product whiteness of processing
The white technique of refining of silk floss satin.
The technical solution of the present invention is to provide a kind of white technique of refining of silk floss satin, and it includes following technological process：
The first step, the ripe wrinkle print on green compact is evened up with stenter；
Second step, preparation house, green compact are carried out with circle code, nail button loop；
3rd step, carries out degumming refining in vain in cylinder is just refined, and is 40-45 per cylinder, coupe is 45-50 rice, and specific practice is such as
Under, first soaked, green compact are impregnated with, minute time 30-40,30-40 DEG C of water temperature with 5 tons of warm water cylinder；Then just refined with 5 tons of hot water
Cylinder, dispersant 15-20kg, soda ash 6-8kg, sodium silicate 4-6kg, sodium hydrosulfite 1-1.5kg are put in water, water temperature is controlled at 96-98 DEG C,
Minute time 90-100；Then with 5 tons of hot water oxygen bleaching cylinders, hydrogen peroxide 20-25kg, sodium silicate 6-8kg are added, water temperature control exists
80-90 DEG C, minute time 110-120；With 5 tons of hot water freshening cylinders, dispersant 8-10kg, soda ash 1-2kg, sodium silicate 2- are added
The soft flat 1-2kg of 4kg, sodium hydrosulfite 0.5-1kg, silk, temperature control is at 96-98 DEG C, minute time 50-60；
4th step, rolled up by operation card number into big；
5th step, dried using blanket machine, shaped using stenter；
6th step, examine.
The present invention has advantages below compared to prior art：This technique by sericin removal, remove cotton seed hulls and oxygen bleaching flow,
So that the product whiteness of processing is good, silk fabric face is clean, wrinkle-free print.
Embodiment：
With reference to embodiment, the invention will be further described：
Embodiment
A kind of white technique of refining of silk floss satin, it includes following technological process：
The first step, the ripe wrinkle print on green compact is evened up with stenter；
Second step, preparation house, green compact are carried out with circle code, nail button loop, with the circle ink recorder circle of one meter in diameter into big volume, then with fastening with a rope, string, etc.
Rope hook is fixed to be hung on refining cloth holder again；
3rd step, carries out degumming refining in vain in cylinder is just refined, and is 40-45 per cylinder, coupe is 45-50 rice, and specific practice is such as
Under, first soaked, green compact are impregnated with, minute time 30-40,30-40 DEG C of water temperature with 5 tons of warm water cylinder；Then just refined with 5 tons of hot water
Cylinder, dispersant 15-20kg, soda ash 6-8kg, sodium silicate 4-6kg, sodium hydrosulfite 1-1.5kg are put in water, water temperature is controlled at 96-98 DEG C,
Minute time 90-100, carry out sericin removal processing；Then with 5 tons of hot water oxygen bleaching cylinders, hydrogen peroxide 20-25kg, sodium silicate 6- are added
8kg, water temperature control at 80-90 DEG C, minute time 110-120, carry out cotton seed hulls and handle；With 5 tons of hot water freshening cylinders, add and divide
The soft flat 1-2kg of powder 8-10kg, soda ash 1-2kg, sodium silicate 2-4kg, sodium hydrosulfite 0.5-1kg, silk, temperature control at 96-98 DEG C,
Minute time 50-60, to increase whiteness；
4th step, rolled up by operation card number into big；
5th step, dried using blanket machine, shaped using stenter；
6th step, examine.
Only preferred embodiments of the present invention are described above, but are not to be construed as limiting the scope of the invention.
Claims (1)
1. the white technique of refining of a kind of silk floss satin, it is characterised in that it includes following technological process：
The first step, the ripe wrinkle print on green compact is evened up with stenter；
Second step, preparation house, green compact are carried out with circle code, nail button loop；
3rd step, carries out degumming refining in vain in cylinder is just refined, and 40-45 is per cylinder, and coupe is 45-50 rice, and specific practice is as follows, first
Soaked, green compact are impregnated with, minute time 30-40,30-40 DEG C of water temperature with 5 tons of warm water cylinders；Then just cylinder is refined with 5 tons of hot water, in water
Put dispersant 15-20kg, soda ash 6-8kg, sodium silicate 4-6kg, sodium hydrosulfite 1-1.5kg, water temperature control is at 96-98 DEG C, time 90-
100 minutes；Then with 5 tons of hot water oxygen bleaching cylinders, hydrogen peroxide 20-25kg, sodium silicate 6-8kg are added, water temperature is controlled at 80-90 DEG C,
Minute time 110-120；With 5 tons of hot water freshening cylinders, dispersant 8-10kg, soda ash 1-2kg, sodium silicate 2-4kg, sodium hydrosulfite are added
The soft flat 1-2kg of 0.5-1kg, silk, temperature control is at 96-98 DEG C, minute time 50-60；
4th step, rolled up by operation card number into big；
5th step, dried using blanket machine, shaped using stenter；
6th step, examine.