CN1076037C - Thixotropic ink oil for screen printed applique paper - Google Patents
Thixotropic ink oil for screen printed applique paper Download PDFInfo
- Publication number
- CN1076037C CN1076037C CN98102794A CN98102794A CN1076037C CN 1076037 C CN1076037 C CN 1076037C CN 98102794 A CN98102794 A CN 98102794A CN 98102794 A CN98102794 A CN 98102794A CN 1076037 C CN1076037 C CN 1076037C
- Authority
- CN
- China
- Prior art keywords
- ink
- thixotropic
- printing
- oil
- butyl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to ink compounding oil for printing ink, particularly to thixotropic ink compounding oil for printing ink for decals of screen printing. The present invention provides the novel cheaper thixotropic ink compounding oil for printing ink for decals of screen printing, which is both suitable for applique paper with large films and applique paper with small films. The ink compounding oil is formed by adding a thixotropic agent and a diluent agent into film forming substances, wherein the film forming substances are an acrylic ester(co)polymer blend formed by randomly polymerizing four kinds of monomers such as methyl methacrylate, ethyl acrylate, butyl acrylate and butyl methacrylate. Use results indicate that the ink compounding oil of the present invention has good printing adaptability, screen lines and screen points can be clearly reduced, and screens can not be blocked. The adhesive force of an ink layer is good, and colors are firm and can not shed easily. A decoration baking effect is good, and colors are brilliant.
Description
The invention relates to stand linseed oil, particularly about a kind of invention of thixotropic ink oil for screen printed applique paper.
People have passed by and have printed to a long historical process of modernized silk screen printing from Freehandhand-drawing, spraying decoration, stamp the trailing of pottery, enamel, glass etc.The method of utilizing the modern typography to decorate implements has directly and indirect two kinds.So-called decorative method indirectly is earlier pattern to be printed on paper or the plastic film, it is attached to during use on the implements that need to decorate again.Print afterwards earlier and paste, the origin of Here it is transfer paste marble paper.Because meticulous true to nature, easy to use more flexible than the pattern that prints on implements in printing on the paper substrate, so industry such as pottery generally all adopts transfer paste marble paper decorative method.
At present, the decal paper that uses at ceramic industry roughly has two classes: big film marble paper (the polyvinyl butyral acetal marble paper is called for short the P.V.B marble paper) and membranelle marble paper (moving colored film marble paper).The characteristics of big film marble paper are that applique is convenient, cheap.But no matter the printing ink that import or homemade thixotropic ink oil are made, the easy explosion of ink film comes off after the easy adhesion of big film marble paper of printing, the long storage.The clear 62-334250 of Japanese Patent discloses a kind of transfer paste marble paper thixotropy ink adhesive resin combination, only be applicable to the membranelle marble paper by its stand linseed oil of making, and price is more expensive.
The object of the present invention is to provide a kind of new thixotropic ink oil for screen printed applique paper, can be used for the membranelle marble paper and can be used for big film marble paper again.
Another object of the present invention is: under the prerequisite that ensures printability and burning till property, make every effort to reduce the cost of stand linseed oil.
Printing ink is a kind of stable colloidal dispersion system, and its host is by forming as the pigment of disperse phase with as the stand linseed oil of external phase.Stand linseed oil is the dispersion medium in the printing ink host, is the carrier of pigment particles.The printability of printing ink and the property relationship of stand linseed oil are very close.That is to say that the ink performance beyond the color is subjected to the domination of stand linseed oil.The performance of stand linseed oil is then relevant with its formation.
In order to reach purpose of the present invention, at first having researched and developed with methyl methacrylate, ethyl propenoate, butyl acrylate and four kinds of monomers of butyl methacrylate is raw material, with the benzoyl peroxide is initiator, under 90 ℃ of conditions, carry out solution method random copolymerization, obtain a kind of mixture that contains multiple acrylate copolymer.Then based on this mixture, add thixotropic agent, thinner, the elaborate combination prescription has modulated a kind of thixotropic ink oil for screen printed applique paper.Transfer China ink to go up the machine print result through applique paper plant and show, stand linseed oil of the present invention not only is applicable to big film marble paper but also is applicable to the membranelle marble paper that printability, anti-stick page or leaf property, anti-deciduous and burning till property are all good.
Stand linseed oil of the present invention is made up of aforesaid propylene acid ester copolymer 100 weight parts, thixotropic agent 10～30 weight parts and thinner 200～250 weight parts.
Adding thixotropic agent is in order to make the printing ink of making have thixotropy, to adapt to the requirement of silk screen printing.All in principle can give thixotropic Wax can be as thixotropic agent.What the present invention used is synthetic wax.
The used thinner of the present invention is the mixture of n-Butyl lactate, turps, Terpineol 350, white oil of camphor composition.Its consumption is as the criterion with viscosity and the TI value that satisfies stand linseed oil.This thinner is more cheap than a large amount of formula systems of naphthane that use.
The viscosity of thixotropic ink oil of the present invention (25 ℃) is 1.90～5.50Pas; It is 2.50～3.50 that thixotropy is estimated the TI value.
So-called thixotropy is estimated the TI value and is meant: under 25 ℃ of conditions, record the viscosity number η under 90 rev/mins respectively
90With 360 rev/mins under viscosity number η
360Ratio, promptly thixotropy is estimated TI value=η
90/ η
360
The advantage that the present invention is had compared to existing technology is:
1. stand linseed oil of the present invention not only had been applicable to big film marble paper but also had been applicable to the silk screen printing of membranelle marble paper.These two kinds of marble papers can both be used for the decoration of high-grade ceramic.
2. compare with the import stand linseed oil, cheap.
3. solved the problem that the easy adhesion of big film marble paper, the easy explosion of ink film come off, membranelle marble paper quality and external product are suitable.
4. modulation printing ink can be directly used in, and in printing process, thinner need be do not added, easy to use, help the production scene quality control.
Relevant producer uses the back consistently to think in batches: stand linseed oil printability of the present invention is good, and figure line, site reduction are clear, not network blocking.China ink layer sticking power is good, the color fast difficult drop-off, and decoration firing is effective, bright in color.Needn't mix thinning oil during use, be convenient to the production scene quality control.
The invention will be further described below by embodiment.Because esters of acrylic acid can be with the arbitrary proportion copolymerization, so the restriction of 4 kinds of monomer ratios that the present invention is not provided.
Embodiment 1
Be blown in the four-hole boiling flask of pipe in that agitator, reflux exchanger, nitrogen are housed, add n-Butyl lactate 60 grams, be warmed up to 90 ℃.Temperature is controlled under 90 ℃ of conditions, and the limit fed the nitrogen limit and dripped methyl methacrylate 52 grams in 4 hours, butyl methacrylate 30 grams, and ethyl propenoate 10 grams, butyl acrylate 8 grams, benzoyl peroxide 0.2 gram is dissolved in the aforesaid propylene acid esters in advance.Drip off afterreaction 2 hours, and in 2 hours, dripped 0.03 gram (being dissolved in the 20 gram n-Butyl lactates) benzoyl peroxide subsequently, continue reaction 2 hours after dripping off again, obtain solid content and be 55% resin solution.
Above-mentioned 180 gram resin solutions and n-Butyl lactates, 5 grams, Terpineol 350 40 grams, turps 60 grams and white oil of camphor 45 grams, organobentonite 23 are restrained, after fully disperseing with high speed dispersor (more than the 3000r/min), grind just to have made through three-roller again and have thixotropic stand linseed oil.
Sample viscosity after measured is 4.87Pas (25 ℃); Thixotropy TI value is 3.34.
Embodiment 2
Use the device identical, add n-Butyl lactate 60 and restrain, be warmed up to 90 ℃ with embodiment 1.Temperature is controlled under 90 ℃ of conditions, and the limit fed the nitrogen limit and dripped methyl methacrylate 18 grams in 4 hours, butyl methacrylate 15 grams, and ethyl propenoate 27 grams, butyl acrylate 40 grams, benzoyl peroxide 0.2 gram is dissolved in the aforesaid propylene acid esters in advance.Drip off afterreaction 2 hours, and in 2 hours, dripped 0.03 gram (being dissolved in the 20 gram n-Butyl lactates) benzoyl peroxide subsequently, continue reaction 2 hours after dripping off again, obtain solid content and be 55% resin solution.
With above-mentioned 180 gram resin solutions and n-Butyl lactates, 10 grams, Terpineol 350 70 grams, turps 45 grams and white oil of camphor 30 grams, fatty polyamide 12 grams, after fully disperseing with high speed dispersor, just made through the three-roller grinding again and had thixotropic stand linseed oil.
Sample viscosity after measured is 2.38Pas (25 ℃); Thixotropy TI value is 2.56.
Claims (4)
1. thixotropic ink oil for screen printed applique paper, its component and content are:
100 parts of acrylate copolymers
10～30 parts of thixotropic agent
200～250 parts of parts of thinner refer to weight part; Acrylate copolymer carries out solution method random copolymerization by methyl methacrylate, ethyl propenoate, butyl acrylate and four kinds of monomers of butyl methacrylate and makes.
2. according to the described stand linseed oil of claim 1, it is characterized in that acrylate copolymer is is raw material with methyl methacrylate, ethyl propenoate, butyl acrylate and butyl methacrylate, with the benzoyl peroxide is initiator, carries out under 90 ℃ of conditions that solution method random copolymerization makes.
3. according to the described stand linseed oil of claim 1, it is characterized in that thinner is the mixture of n-Butyl lactate, Terpineol 350, turps and white oil of camphor.
4. according to the described stand linseed oil of claim 1, it is characterized in that it is 2.50～3.50 that thixotropy is estimated the TI value.