CN109810564A - A kind of compound copper pate printing ink and preparation method thereof suitable for pearl cotton plates printing - Google Patents
A kind of compound copper pate printing ink and preparation method thereof suitable for pearl cotton plates printing Download PDFInfo
- Publication number
- CN109810564A CN109810564A CN201811647020.2A CN201811647020A CN109810564A CN 109810564 A CN109810564 A CN 109810564A CN 201811647020 A CN201811647020 A CN 201811647020A CN 109810564 A CN109810564 A CN 109810564A
- Authority
- CN
- China
- Prior art keywords
- printing
- pate
- ink
- copper
- printing ink
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to pearl cotton plates printing technologies, more particularly to a kind of compound copper pate printing ink and preparation method thereof suitable for pearl cotton plates printing, compound copper pate printing ink by mass percent meter copper pate printing ink 46-65%, ink for screen printing 3-13% and copperplate water 32-44% are mixed, wherein copper pate printing ink is by isopropanol, ethyl acetate, polyamide, pigment A and nitrocotton composition, ink for screen printing is by isophorone, dibasic acid dimethyl ester, cyclohexanone, polyester resin and pigment B composition, pass through the synergistic effect of the above component, so that prepared compound copper pate printing ink is not faded when being printed using copperplate machine copper, glossiness is good, pattern is apparent, and guarantee printing quality, stability is good, it can satisfy the needs of scale industrial production.
Description
Technical field
The present invention relates to pearl cotton plates printing technologies, and in particular to a kind of answering suitable for pearl cotton plates printing
Close copper pate printing ink and preparation method thereof.
Background technique
Pearl cotton is a kind of packaging material of novel environment friendly, have water proof is moisture-proof, shockproof, sound insulation, heat preservation, plasticity are good,
Many advantages, such as toughness is strong is widely used in the packaging of the various products such as computer, TV, sound equipment.
Printing for pearl cotton plates, traditional approach mainly use silk-screen printing (abbreviation silk-screen), and silk-screen is first material
Material is cut into required size with cutting machine, adjusts ink for screen printing, then printed one by one with screen printing device (or manually one
One print), one has been printed, has been taken out, then has put one and enters to print, and has needed often cleaning screen printing net plate, and dry in the air one by one
Dry, production efficiency is low (about 6000/day/3 people), and the clarity of printed patterns is unstable, and of poor quality, product qualification rate is not high
(general yields 92%).
As technological improvement, the prior art is by the way of copperplate printing, i.e., real on copperplate machine using copper pate printing ink
Existing continuous printing, although comparing silk screen printing process, copperplate printing improves production efficiency, at present for used in copperplate machine
Simple copper pate printing ink, it may appear that it fades, the problem that printed patterns are unclear, there is no guarantee that steadily product quality, and silk
Printing ink is denseer and rate of drying is fast, can not use on copperplate machine, therefore be unable to satisfy the needs of scale industrial production.
Summary of the invention
It is an object of the invention to aiming at the shortcomings in the prior art, and provide a kind of suitable for pearl cotton plates printing
Compound copper pate printing ink and preparation method thereof, be not in when carrying out copperplate printing using the compound copper pate printing ink fade, pattern not
Clear problem, printing quality is good and stability is good.
A kind of compound copper pate printing ink suitable for pearl cotton plates printing is provided, by the raw material system of following mass percent
At: copper pate printing ink 46-65%, ink for screen printing 3-13% and copperplate water 32-44%；Wherein:
The copper pate printing ink is made of raw material from the following weight:
The ink for screen printing is made of raw material from the following weight:
The copperplate water is made of raw material from the following weight:
In above-mentioned technical proposal, a kind of compound copper pate printing ink suitable for pearl cotton plates printing, by following matter
The raw material of amount percentage is made: copper pate printing ink 56%, ink for screen printing 6% and copperplate water 38%.
In above-mentioned technical proposal, the polyester resin is polyester resin ES-320 and polyester resin ES-360 according to mass ratio
(1-3): the mixture of (2-3) compounding.
In above-mentioned technical proposal, the pigment A and pigment B are carbon black, Pigment white 6, pigment Yellow 14, pigment red 4 8:2, face
At least one of material basket 15:4, pigment Green 7, pigment orange 13 and pigment Violet 23.
The present invention also provides a kind of above-mentioned preparation methods of the compound copper pate printing ink suitable for pearl cotton plates printing, including
Following steps:
Step a, copper pate printing ink is configured:
By formula ratio, isopropanol and ethyl acetate are added in stirring container A, polyamide is added while stirring, so
Pigment A and after mixing evenly is added afterwards, is slow added into nitrocotton, after mixing evenly, obtains copper pate printing ink；
Step b, ink for screen printing is prepared:
By formula ratio, isophorone, dibasic acid dimethyl ester and cyclohexanone are added in stirring container B, are added while stirring
Then polyester resin is added pigment B and obtains ink for screen printing after mixing evenly；
Step c, copperplate water is prepared:
By formula ratio, after mixing by toluene, isopropanol, dehydrated alcohol and ethyl acetate, copperplate water is obtained；
Step d, compound copper pate printing ink is prepared:
By formula ratio, the copperplate water of preparation is added in stirring container C, stirring a period of time is opened, copper is then added
Printing ink is simultaneously sufficiently mixed uniformly, and ink for screen printing is then added while stirring, after mixing evenly to get oily to the compound copperplate
Ink.
Beneficial effects of the present invention:
A kind of compound copper pate printing ink suitable for pearl cotton plates printing of the invention, by copperplate by mass percentage
Ink 46-65%, ink for screen printing 3-13% and copperplate water 32-44% are mixed, in which: copper pate printing ink is by isopropanol, acetic acid
Ethyl ester, polyamide, pigment A and nitrocotton composition, ink for screen printing is by isophorone, dibasic acid dimethyl ester, cyclohexanone, polyester
Resin and pigment B composition, copperplate water are made of toluene, isopropanol, dehydrated alcohol and ethyl acetate；Binary acid in ink for screen printing
Diformazan, which plays the role of good stability, promotion gloss and smoothness, cyclohexanone, can promote the glossiness of ink, also have dispersing agent
Effect, the nitrocotton in copper pate printing ink plays the adhesive effect of adhesive, and is conducive to promote print speed printing speed, and copperplate water is advantageous
In the compatibility for improving resin binder, by the synergistic effect of the above component, so that final prepared compound copper pate printing ink
It does not fade when being printed using copperplate machine copper, glossiness is good, and pattern is apparent, and guarantees printing quality, and stability is good, prepares work
Skill is simple, can satisfy the needs of scale industrial production.
Specific embodiment
The invention will be further described with the following Examples.
Embodiment 1:
The present embodiment it is a kind of suitable for pearl cotton plates printing compound copper pate printing ink the preparation method is as follows:
Step a, copper pate printing ink is configured:
By weight, 5 parts of isopropanols and 22 parts of ethyl acetate are added in stirring container A, 10 parts is added while stirring
Polyamide, is then added 6 parts of pigment carbon blacks, 4 parts of pigment Yellow 14s and 5 parts of pigment blue 15s: 4 and after mixing evenly, then slowly
10 parts of nitrocottons are added and obtain copper pate printing ink after mixing evenly；
Step b, ink for screen printing is prepared:
By weight, 20 parts of isophorones, 18 parts of dibasic acid dimethyl esters and 5 parts of cyclohexanones are added in stirring container B,
25 parts of polyester resin are added while stirring, 2 parts of pigment Green 7s, 6 parts of pigment orange 13s and 2 parts of pigment Violet 23s are then added, stir evenly
Afterwards, ink for screen printing is obtained；
Step c, copperplate water is prepared:
By weight, after mixing by 65 parts of toluene, 20 parts of isopropanols, 3 parts of dehydrated alcohols and 15 parts of ethyl acetates,
Obtain copperplate water；
Step d, compound copper pate printing ink is prepared:
By mass percentage, 38% copperplate water of preparation is added in stirring container C, opens stirring a period of time,
Then 56% copper pate printing ink is added and is sufficiently mixed uniformly, 6% ink for screen printing is then added while stirring, after mixing evenly, i.e.,
Obtain the compound copper pate printing ink.
In the present embodiment, polyester resin is that polyester resin ES-320 and polyester resin ES-360 is compounded according to mass ratio 2:3
Mixture.
Embodiment 2:
The present embodiment it is a kind of suitable for pearl cotton plates printing compound copper pate printing ink the preparation method is as follows:
Step a, copper pate printing ink is configured:
By weight, 8 parts of isopropanols and 26 parts of ethyl acetate are added in stirring container A, 18 parts is added while stirring
Polyamide, is then added 2 parts of pigment red 4 8:2,4 parts of pigment blue 15s: 4,3 parts of pigment Green 7s and 1 part of pigment orange 13 and stirring
After uniformly, it is slow added into 16 parts of nitrocottons and obtains copper pate printing ink after mixing evenly；
Step b, ink for screen printing is prepared:
By weight, stirring container B is added in 15 parts of isophorones, 22 parts of dibasic acid dimethyl esters and 12 parts of cyclohexanones
In, 28 parts of polyester resin are added while stirring, 3 parts of Pigment whites, 6,5 parts of pigment Yellow 14s and 6 parts of pigment red 4 8:2 are then added, stir
After mixing uniformly, ink for screen printing is obtained；
Step c, copperplate water is prepared:
By weight, after mixing by 58 parts of toluene, 15 parts of isopropanols, 5 parts of dehydrated alcohols and 12 parts of ethyl acetates,
Obtain copperplate water；
Step d, compound copper pate printing ink is prepared:
By mass percentage, 32% copperplate water of preparation is added in stirring container C, opens stirring a period of time,
Then 65% copper pate printing ink is added and is sufficiently mixed uniformly, 3% ink for screen printing is then added while stirring, after mixing evenly, i.e.,
Obtain the compound copper pate printing ink.
In the present embodiment, polyester resin is that polyester resin ES-320 and polyester resin ES-360 is compounded according to mass ratio 1:2
Mixture.
Embodiment 3:
The present embodiment it is a kind of suitable for pearl cotton plates printing compound copper pate printing ink the preparation method is as follows:
Step a, copper pate printing ink is configured:
By weight, 10 parts of isopropanols and 20 parts of ethyl acetate are added in stirring container A, 15 parts is added while stirring
Then polyamide is added 10 parts of pigment Yellow 14s, 16 parts of pigment red 4 8:2 and 4 parts of pigment Violet 23s and after mixing evenly, then delays
Slowly 13 parts of nitrocottons are added and obtain copper pate printing ink after mixing evenly；
Step b, ink for screen printing is prepared:
By weight, stirring container B is added in 25 parts of isophorones, 15 parts of dibasic acid dimethyl esters and 15 parts of cyclohexanones
In, 32 parts of polyester resin are added while stirring, 15 parts of carbon blacks, 5 parts of Pigment whites 6 are then added, after mixing evenly, obtain silk-screen oil
Ink；
Step c, copperplate water is prepared:
By weight, after mixing by 55 parts of toluene, 22 parts of isopropanols, 6 parts of dehydrated alcohols and 16 parts of ethyl acetates,
Obtain copperplate water；
Step d, compound copper pate printing ink is prepared:
By mass percentage, 44% copperplate water of preparation is added in stirring container C, opens stirring a period of time,
Then 46% copper pate printing ink is added and is sufficiently mixed uniformly, 10% ink for screen printing is then added while stirring, after mixing evenly, i.e.,
Obtain the compound copper pate printing ink.
In the present embodiment, polyester resin is that polyester resin ES-320 and polyester resin ES-360 is compounded according to mass ratio 1:1
Mixture.
Embodiment 4:
The present embodiment it is a kind of suitable for pearl cotton plates printing compound copper pate printing ink the preparation method is as follows:
Step a, copper pate printing ink is configured:
By weight, 6 parts of isopropanols and 30 parts of ethyl acetate are added in stirring container A, 20 parts is added while stirring
Polyamide, is then added 3 parts of carbon blacks, 12 parts of pigment blue 15s: 4,8 parts of pigment Green 7s and 1 part of pigment orange 13 and stirring evenly
Afterwards, 20 parts of nitrocottons are slow added into and obtain copper pate printing ink after mixing evenly；
Step b, ink for screen printing is prepared:
By weight, stirring container B is added in 23 parts of isophorones, 25 parts of dibasic acid dimethyl esters and 10 parts of cyclohexanones
In, 35 parts of polyester resin are added while stirring, then 8 parts of pigment red 4 8:2 of addition and 10 parts of pigment blue 15s: 4, after mixing evenly,
Obtain ink for screen printing；
Step c, copperplate water is prepared:
By weight, after mixing by 62 parts of toluene, 25 parts of isopropanols, 8 parts of dehydrated alcohols and 18 parts of ethyl acetates,
Obtain copperplate water；
Step d, compound copper pate printing ink is prepared:
By mass percentage, 35% copperplate water of preparation is added in stirring container C, opens stirring a period of time,
Then 52% copper pate printing ink is added and is sufficiently mixed uniformly, 13% ink for screen printing is then added while stirring, after mixing evenly, i.e.,
Obtain the compound copper pate printing ink.
In the present embodiment, polyester resin is that polyester resin ES-320 and polyester resin ES-360 is compounded according to mass ratio 3:2
Mixture.
Finally it should be noted that the above embodiments are merely illustrative of the technical solutions of the present invention, rather than the present invention is protected
The limitation of range is protected, although explaining in detail referring to preferred embodiment to the present invention, those skilled in the art are answered
Work as understanding, it can be with modification or equivalent replacement of the technical solution of the present invention are made, without departing from the reality of technical solution of the present invention
Matter and range.
Claims (5)
1. a kind of compound copper pate printing ink suitable for pearl cotton plates printing, it is characterised in that: by the original of following mass percent
Material is made: copper pate printing ink 46-65%, ink for screen printing 3-13% and copperplate water 32-44%；Wherein:
The copper pate printing ink is made of raw material from the following weight:
The ink for screen printing is made of raw material from the following weight:
The copperplate water is made of raw material from the following weight:
。
2. a kind of compound copper pate printing ink suitable for pearl cotton plates printing according to claim 1, it is characterised in that: by
The raw material of following mass percent is made: copper pate printing ink 56%, ink for screen printing 6% and copperplate water 38%.
3. a kind of compound copper pate printing ink suitable for pearl cotton plates printing according to claim 1 or 2, feature exist
In: the polyester resin is polyester resin ES-320 and polyester resin ES-360 according to mass ratio (1-3): (2-3) compounding is mixed
Close object.
4. a kind of compound copper pate printing ink suitable for pearl cotton plates printing according to claim 1 or 2, feature exist
In: the pigment A and pigment B is carbon black, Pigment white 6, pigment Yellow 14, pigment red 4 8:2, pigment blue 15: 4, pigment Green 7, pigment
Orange at least one of 13 and pigment Violet 23.
5. a kind of system of compound copper pate printing ink suitable for pearl cotton plates printing as described in Claims 1-4 any one
Preparation Method, it is characterised in that: the following steps are included:
Step a, copper pate printing ink is configured:
By formula ratios, isopropanol and ethyl acetate are added in stirring container A, polyamide is added while stirring, then plus
Enter pigment A and after mixing evenly, is slow added into nitrocotton, after mixing evenly, obtains copper pate printing ink；
Step b, ink for screen printing is prepared:
By formula ratio, isophorone, dibasic acid dimethyl ester and cyclohexanone are added in stirring container B, polyester is added while stirring
Then resin is added pigment B and obtains ink for screen printing after mixing evenly；
Step c, copperplate water is prepared:
By formula ratio, after mixing by toluene, isopropanol, dehydrated alcohol and ethyl acetate, copperplate water is obtained；
Step d, compound copper pate printing ink is prepared:
By formula ratio, the copperplate water of preparation is added in stirring container A, is sufficiently mixed copperplate water and copper pate printing ink uniformly,
Then ink for screen printing is added while stirring, after mixing evenly to get arrive the compound copper pate printing ink.