CN107603384A - Kitchen water-water suit and its preparation method and application - Google Patents
Kitchen water-water suit and its preparation method and application Download PDFInfo
- Publication number
- CN107603384A CN107603384A CN201710811936.6A CN201710811936A CN107603384A CN 107603384 A CN107603384 A CN 107603384A CN 201710811936 A CN201710811936 A CN 201710811936A CN 107603384 A CN107603384 A CN 107603384A
- Authority
- CN
- China
- Prior art keywords
- water
- weight
- parts
- agent
- kitchen
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses kitchen water-water suit and its preparation method and application, wherein, water-water suit in kitchen includes：Protection glue, color-mixed base paint and continuous phase, Protection glue are made up of protection rubber powder, deionized water, thinner, mould inhibitor, bactericide and pH adjusting agent；Color-mixed base paint is made up of deionized water, mould inhibitor, dispersant, cellulose, antifreezing agent, filler, nano silicon, defoamer, pH adjusting agent, hardening agent, emulsion, coalescents, bactericide, wetting agent and Protection glue；Continuous phase deionized water, modified cellulose, hydrophobic auxiliary agent, emulsion, coalescents, antifreezing agent, pH adjusting agent and thickener composition, wherein, the Protection glue, the color-mixed base paint and the continuous phase are separately positioned in different containers.The kitchen water-water suit can effectively configure to obtain sealing wax, and the paint film of the sealing wax has unique scratch resistance capability, hardness and hydrophobicity, disclosure satisfy that kitchen to cabinet table surface high rigidity, the requirement of scratch resistance, water resistance.
Description
Technical field
The invention belongs to chemical field, in particular to kitchen water-water suit and its preparation method and application.
Background technology
With the development of building decoration industry, coatings industry also develops therewith there are various functions paintings on the market
Material.Natural marble is widely used because its color is ever-changing in building coating, but lithotome exploitation and application can cause
A series of problems, such as wasting of resources and awful weather, thus water-water is arisen at the historic moment, and water-water is one kind of multicolor finish, more should
For copying stone effect, it is suspended in by two or more water-based colored particle in water-based interlayer, by once spraying production
The one-component coating for skin of multicolour is given birth to, is a kind of water-based, nuisanceless, rich colored hilllock texture, high score
The product of daughter element structure.However, water-water is usually to be used as exterior coating application, interior is seldom related to.Therefore, by water-water
Materials application is of great significance to indoor tool.
The content of the invention
It is contemplated that at least solves one of technical problem in correlation technique to a certain extent.Therefore, the present invention
One purpose is to propose kitchen water-water suit and its preparation method and application, using water-water set in kitchen proposed by the present invention
Dress can effectively configure to obtain sealing wax, and the hardness of paint film formed using the sealing wax is extremely strong, has unique scratch resistance capability, and
Hydrophobicity is good, can substitute marble during applied to kitchen and meet kitchen to cabinet table surface high rigidity, scratch resistance, water resistance
It is required that decoration cost is low and green.
According to an aspect of the present invention, the present invention proposes a kind of kitchen water-water suit, including：
Protection glue, the Protection glue is by the protection rubber powder of 5-25 parts by weight, the deionized water of 75-90 parts by weight, 0.1-5 weights
Measure the pH adjusting agent group of the thinner of part, the mould inhibitor of 0.1-4 parts by weight, the bactericide of 0.1-3 parts by weight and 0.1-1 parts by weight
Into；
Color-mixed base paint, the color-mixed base paint by the deionized waters of 45-65 parts by weight, 0.1-0.5 parts by weight it is mould proof
Agent, the dispersant of 0.1-1 parts by weight, the cellulose of 0.5-1 parts by weight, the antifreezing agent of 0.5-1.5 parts by weight, 5-15 parts by weight
Filler, the nano silicon of 1-5 parts by weight, the defoamer of 0.5-1.5 parts by weight, the pH adjusting agent of 0.1-0.8 parts by weight, 1-
The hardening agent of 5 parts by weight, the emulsion of 15-45 parts by weight, 0.5-1.5 parts by weight coalescents, 0.1-1 parts by weight sterilization
The Protection glue composition of agent, the wetting agent of 0.2-1 parts by weight and 2-6 parts by weight；
Continuous phase, the continuous phase by the deionized waters of 5.5-7.5 parts by weight, 5-10 parts by weight modified cellulose,
The hydrophobic auxiliary agent of 0.1-0.5 parts by weight, the emulsion of 70-95 parts by weight, the coalescents of 3-10 parts by weight, 5-10 parts by weight it is anti-
Freeze the thickener composition of agent, the pH adjusting agent of 0.1-0.5 parts by weight and 0.1-0.8 parts by weight,
Wherein, the Protection glue, the color-mixed base paint and the continuous phase are separately positioned in different containers.
The kitchen water-water suit of the embodiment of the present invention includes Protection glue, color-mixed base paint and continuous phase, by using this
Inventing the kitchen water-water suit proposed can effectively configure to obtain sealing wax, and the paint film of the sealing wax has unique scratch resistance energy
Power, hardness are extremely strong and hydrophobicity is good, and the sealing wax applicability is wider, can substitute marble during applied to kitchen, meet kitchen pair
The requirement of cabinet table surface high rigidity, scratch resistance, water resistance, and then the exploitation of lithotome can be reduced, reduce decoration cost, it is green
Color environmental protection again.
In addition, water-water suit in kitchen according to the above embodiment of the present invention can also have technology additional as follows special
Sign：
In some embodiments of the invention, the protection rubber powder is made up of aluminium-magnesium silicate and lithium magnesium silicate.Thus, it is possible to
Make Protection glue that there is certain viscosity, and with excellent stability, thixotropy and adsorptivity etc., can during for configuring sealing wax
Effectively to prevent the precipitating of various suspended materials in sealing wax, product is closed, hardening etc., and then makes sealing wax uniform and stable.
In some embodiments of the invention, the thinner is sodium pyrophosphate.It is possible thereby to it is appropriate to have Protection glue
Viscosity.
In some embodiments of the invention, the mould inhibitor is tricresyl phosphate.It is possible thereby to effectively suppress mould
Growth, ensure kitchen water-water suit quality.
In some embodiments of the invention, the bactericide is MERGAL K9N.It is possible thereby to effectively kill kitchen water
The various microorganisms such as bacterium, mould in bag water jacket dress, and then addling for kitchen water-water suit is prevented, effectively extend its storage
And usage time.
In some embodiments of the invention, the pH adjusting agent is 2-amino-2-methyl-1-propanol and butylethanolamine
At least one of.Thus, it is possible to effectively adjust the pH value of kitchen water-water suit, there is kitchen water-water suit preferable
Stability.
In some embodiments of the invention, the dispersant is ROHM AND HAAS dispersant.It is possible thereby to effectively improve kitchen
Aqueous humor bag water jacket assembles the dispersion efficiency of each composition in the sealing wax for putting to obtain, and then gives full play to the covering potentiality of color stuffing.
In some embodiments of the invention, the filler is kaolin.It is possible thereby to further adjust kitchen water-water
Gloss, quality, suspension and viscosity of sealing wax that suit configuration obtains etc..
In some embodiments of the invention, the antifreezing agent is propane diols.Thus, it is possible to ensure that cryogenic conditions are gone to the kitchen
The normal use of water-water suit.
In some embodiments of the invention, the hardening agent is to be dissipated selected from aqueous silica dispersion, aluminum oxide moisture
At least one of body, the aqueous dispersion of titanium dioxide and ethylene glycol dispersion.Thus, it is possible to significantly improve kitchen water-water suit
Configure the hardness for the paint film that obtained sealing wax is formed.
In some embodiments of the invention, the cellulose is hydroxyethyl cellulose.Thus, it is possible to significantly improve kitchen
The adhesive strength for the sealing wax that water-water suit configuration obtains.
In some embodiments of the invention, the modified cellulose is organic modified bentonite.Thus, it is possible to make kitchen
The sealing wax that water-water suit configuration obtains has preferable thixotropy, effectively prevents the sedimentation of the composition such as color stuffing in sealing wax, enters
And make sealing wax that there is preferable levelability.
In some embodiments of the invention, the emulsion is silicone modified acrylic resin.Thus, it is possible to make kitchen Shui Bao
The sealing wax that water jacket assembling puts to obtain has preferable adhesive force, impact resistance, pliability, weatherability and Bao Se gloss retentions and dashed forward
Heat resistance gone out etc..
In some embodiments of the invention, the coalescents are Lauryl Alcohol ester.It is possible thereby to make emulsion or scattered
Body particulate forms the film of even compact, and improves the film forming under cryogenic conditions, improves what water-water suit configuration in kitchen obtained
The film forming efficiency of sealing wax.
In some embodiments of the invention, the thickener is ACRYSOL TT-935.It is possible thereby to it is effectively increased kitchen
The viscosity of obtained sealing wax is put in the assembling of aqueous humor bag water jacket, and effectively prevents paint solution from precipitating and being layered, and improves the wet film of an application
Thickness.
In some embodiments of the invention, the hydrophobic auxiliary agent is water-soluble nonionic surfactant.Thus, may be used
To effectively improve the hydrophobic performance for the sealing wax coating surface that kitchen water-water suit configuration obtains, moisture penetration is prevented, improves paint
Anti-stick, the antifouling property of film.
According to the second aspect of the invention, the invention also provides a kind of side for preparing above-mentioned kitchen water-water suit
Method, wherein,
The Protection glue is prepared according to the following steps：(1) deionized water is added in a reservoir, and in 600r/min's
Thinner, preservative, bactericide and the pH adjusting agent of predetermined ratio are sequentially added under stir speed (S.S.)；(2) in 1300-1500r/
The protection rubber powder of predetermined ratio is added under min stir speed (S.S.), 30min is stirred, to obtain Protection glue.
The color-mixed base paint is prepared according to the following steps：(1) deionized water is added in a reservoir, and in 300-
The mould inhibitor and dispersant of predetermined ratio are added under 500r/min stir speed (S.S.), improves rotating speed to 700-1000r/min stirrings
10min；(2) rotating speed is reduced to 300-500r/min, is added the cellulose stirring 5min of predetermined ratio, is sequentially added predetermined ratio
Antifreezing agent, filler, nano silicon and the defoamer of example；(3) rotating speed is improved to 500-900r/min, and is sequentially added predetermined
PH adjusting agent, hardening agent and the emulsion of ratio, rotating speed is improved to 1300-1500r/min stirrings 20min；(4) rotating speed is reduced extremely
700-1000r/min, and coalescents, defoamer, bactericide, wetting agent and the Protection glue of predetermined ratio are sequentially added,
To obtain color-mixed base paint.
The continuous phase is prepared according to the following steps：(1) deionized water is added in a reservoir, in 600-700r/min
Stir speed (S.S.) under sequentially add mould inhibitor, bactericidal agent modified cellulose, hydrophobic auxiliary agent and the emulsion of predetermined ratio, and stir
10min；(2) coalescents, antifreezing agent, defoamer and the pH adjusting agent of predetermined ratio are sequentially added, and stirs 5min；(3) add
Enter the thickener of predetermined ratio and stir 10min, to obtain continuous phase.
The method according to the above embodiment of the present invention for preparing kitchen water-water suit, can effectively be prepared respectively
Protection glue, color-mixed base paint and continuous phase, it can effectively configure to obtain sealing wax using kitchen water-water suit, and the sealing wax
Paint film has unique scratch resistance capability, hardness is extremely strong and hydrophobicity is good, and the sealing wax applicability is wider, can during applied to kitchen
Marble is substituted, meets kitchen to cabinet table surface high rigidity, the requirement of scratch resistance, water resistance, and then lithotome can be reduced
Exploitation, reduce decoration cost, green but it is environmentally friendly.
According to the third aspect of the present invention, the invention also provides a kind of sealing wax, the sealing wax is by the above-mentioned implementation of the present invention
Example Protection glue, the color-mixed base paint and the continuous phase are 3 according to mass ratio：4：3 are mixed to get.
Thus, it is possible to effectively configuration obtains paint film with unique scratch resistance capability, the water that hardness is extremely strong and hydrophobicity is good
Paint, and the sealing wax applicability is wider, can substitute marble during applied to kitchen, meets kitchen to cabinet table surface high rigidity, anti-
Scratch, the requirement of water resistance, and then the exploitation of lithotome can be reduced, reduce decoration cost, it is green and environmentally friendly.
According to the fourth aspect of the present invention, the invention also provides a kind of cabinet, including：Cabinet and lacquer painting, wherein, institute
It is wooden cabinet to state cabinet；The lacquer painting is formed by the way that the sealing wax of above-described embodiment is applied into the wooden cabinet surface.
Thus, it is possible to which the sealing wax of the above embodiment of the present invention is successfully applied into wooden cabinet, and meet kitchen to cabinet
The requirement of table top high rigidity, scratch resistance, water resistance, thus, it is possible to substitute artificial marble products, reduce decoration cost, green and ring
Protect.
Embodiment
Embodiments of the invention are described below in detail.The embodiments described below is exemplary, it is intended to for explaining this
Invention, and be not considered as limiting the invention.
According to an aspect of the present invention, the present invention proposes a kind of kitchen water-water suit, including：Protection glue, protection
Glue is by the protection rubber powder of 5-25 parts by weight, the deionized water of 75-90 parts by weight, the thinner of 0.1-5 parts by weight, 0.1-4 weight
The pH adjusting agent composition of the mould inhibitor of part, the bactericide of 0.1-3 parts by weight and 0.1-1 parts by weight；Color-mixed base paint, color-mixed base
Paint is by the deionized water of 45-65 parts by weight, the mould inhibitor of 0.1-0.5 parts by weight, the dispersant of 0.1-1 parts by weight, 0.5-1 weight
Part cellulose, the antifreezing agent of 0.5-1.5 parts by weight, the filler of 5-15 parts by weight, 1-5 parts by weight nano silicon,
The defoamer of 0.5-1.5 parts by weight, the pH adjusting agent of 0.1-0.8 parts by weight, the hardening agents of 1-5 parts by weight, 15-45 parts by weight
Emulsion, the coalescents of 0.5-1.5 parts by weight, the bactericide of 0.1-1 parts by weight, the wetting agent of 0.2-1 parts by weight and 2-6 weight
The Protection glue composition of part；Continuous phase, continuous phase by the deionized waters of 5.5-7.5 parts by weight, 5-10 parts by weight modified cellulose,
The hydrophobic auxiliary agent of 0.1-0.5 parts by weight, the emulsion of 70-95 parts by weight, the coalescents of 3-10 parts by weight, 5-10 parts by weight it is anti-
Freeze the thickener composition of agent, the pH adjusting agent of 0.1-0.5 parts by weight and 0.1-0.8 parts by weight, wherein, Protection glue, color-mixed base
Paint and continuous phase are separately positioned in different containers.
The kitchen water-water suit of the embodiment of the present invention includes Protection glue, color-mixed base paint and continuous phase, by using this
Inventing the kitchen water-water suit proposed can effectively configure to obtain sealing wax, and the paint film of the sealing wax has unique scratch resistance energy
Power, hardness are extremely strong and hydrophobicity is good, and the sealing wax applicability is wider, can substitute marble during applied to kitchen, meet kitchen pair
The requirement of cabinet table surface high rigidity, scratch resistance, water resistance, and then the exploitation of lithotome can be reduced, reduce decoration cost, it is green
Color environmental protection again.
Protection glue is described in detail below.
Protection glue
According to an embodiment of the invention, Protection glue is by the protection rubber powder of 5-25 parts by weight, the deionization of 75-90 parts by weight
Water, the thinner of 0.1-5 parts by weight, the mould inhibitor of 0.1-4 parts by weight, the bactericide of 0.1-3 parts by weight and 0.1-1 parts by weight
PH adjusting agent forms.Protection glue can effectively be prepared by using said components in the present invention.
According to a particular embodiment of the invention, protection rubber powder can be made up of aluminium-magnesium silicate and lithium magnesium silicate.Thus, it is possible to
Make Protection glue that there is certain viscosity, and with excellent stability, thixotropy and adsorptivity etc., can during for configuring sealing wax
Effectively to prevent the precipitating of various suspended materials in sealing wax, product is closed, hardening etc., and then makes sealing wax uniform and stable.Aluminium-magnesium silicate and
Lithium magnesium silicate is inorganic mineral, will not be destroyed and decompose by bacterium, heating and mechanical shearing, and long-term storage undergoes no deterioration, will not
Go mouldy, viscosity is not varied with temperature, and suspending stabilized colloid can be formed after water high speed is scattered, pH value is changed unwise
Sense, adsorption capacity is strong, prepares kitchen water-water Protection glue using aluminium-magnesium silicate and lithium magnesium silicate in the present invention, can effectively improve
Viscosity, thixotropy and the adsorptivity of the sealing wax configured using the Protection glue, make that there is certain toughness and lubricity, and effectively
Improve the cohesive force of sealing wax and matrix material.Meanwhile when being set with configuration sealing wax using kitchen water-water of the present invention, moreover it is possible to make silicic acid
Magnalium and lithium magnesium silicate play with organic colloid cellulose to act synergistically, and sealing wax is had more preferable viscosity and stability, sticky
Degree increases at double, reaches optimal performance, so can effectively prevent the precipitating of various suspended materials in sealing wax, product is closed, hardening etc.,
Make sealing wax uniform and stable.
According to a particular embodiment of the invention, can further be adjusted by adding a certain amount of thinner in the present invention
The viscosity of Protection glue.For example, according to the specific example of the present invention, thinner can be sodium pyrophosphate, it is possible thereby to make Protection glue
With appropriate viscosity.
According to a particular embodiment of the invention, it can be tricresyl phosphate that mould inhibitor, which is, by using phosphorus in the present invention
Sour front three phenolic ester can effectively suppress the growth of mould in Protection glue as mould inhibitor, ensure the quality of Protection glue, and then enter one
Step improves the quality for the sealing wax that kitchen water-water suit configuration of the present invention obtains.According to the specific example of the present invention, mould inhibitor can
With using the tricresyl phosphate mould inhibitor of model 786.
According to a particular embodiment of the invention, guarantor can effectively be killed by adding bactericide in Protection glue in the present invention
The various microorganisms such as bacterium, mould in shield glue, and then addling for Protection glue is prevented, effectively extend its storage and usage time,
And then further improve the quality of the sealing wax obtained by kitchen water-water of the present invention suit configuration.Specific according to the present invention is shown
Example, bactericide can be MERGAL K9N, thus, it is possible to further improve the bactericidal effect to Protection glue.
According to a particular embodiment of the invention, pH adjusting agent can be 2-amino-2-methyl-1-propanol and butylethanolamine
At least one of.The pH value of Protection glue can be effectively adjusted in the present invention by using above-mentioned pH adjusting agent, has Protection glue
There is preferable stability, and then make that there is preferable stability, example by the sealing wax that kitchen water-water of the present invention suit configuration obtains
Such as freeze-thaw stability.According to the specific example of the present invention, pH adjusting agent can select DOW Chemical model AMP-95 2-
The butylethanolamine of amino-2-methyl -1- propyl alcohol and Ai Wangde.
Color-mixed base paint is described in detail below.
Color-mixed base paint
According to an embodiment of the invention, color-mixed base paint is by the deionized waters of 45-65 parts by weight, 0.1-0.5 parts by weight
Mould inhibitor, the dispersant of 0.1-1 parts by weight, the cellulose of 0.5-1 parts by weight, the antifreezing agent of 0.5-1.5 parts by weight, 5-15 weight
Part filler, the nano silicon of 1-5 amount parts, the defoamer of 0.5-1.5 parts by weight, 0.1-0.8 parts by weight pH adjusting agent,
The hardening agent of 1-5 parts by weight, the emulsion of 15-45 parts by weight, 0.5-1.5 parts by weight coalescents, 0.1-1 parts by weight sterilization
The Protection glue composition of agent, the wetting agent of 0.2-1 parts by weight and 2-6 parts by weight.Thus, can by using said components in the present invention
So that color-mixed base paint is effectively prepared.
According to a particular embodiment of the invention, it can be tricresyl phosphate that mould inhibitor, which is, thus, by adopting in the present invention
The growth of mould in color-mixed base paint can effectively be suppressed by the use of tricresyl phosphate as mould inhibitor, ensure the product of color-mixed base paint
Matter, and then further improve the quality of the sealing wax obtained by kitchen water-water of the present invention suit configuration.According to the specific of the present invention
Example, mould inhibitor can use the tricresyl phosphate mould inhibitor of model 786.
According to a particular embodiment of the invention, dispersant can be ROHM AND HAAS dispersant.By using sieve in the present invention
Door Haas dispersant can effectively improve the dispersion efficiency of each composition in color-mixed base paint, and then improve by kitchen Shui Bao of the present invention
Water jacket assembles the dispersion efficiency of each composition in the sealing wax for putting to obtain, and gives full play to the covering potentiality of color stuffing.According to the present invention's
Specific example, dispersant can be ROHM AND HAAS dispersant 731A, and ROHM AND HAAS dispersant 731A hydrophobic structure makes it have
The incomparable water resistance of common sodium salt dispersant, and it is free of formaldehyde, using water as carrier, applicability is wider, has to all kinds of
The high dispersion efficiency of color stuffing, the covering potentiality of color stuffing can be given full play to, thus, by from Luo Menha in the present invention
This dispersant 731A can further improve the quality of the sealing wax obtained by kitchen water-water of the present invention suit configuration.
According to a particular embodiment of the invention, cellulose can be hydroxyethyl cellulose.It is fine by ethoxy in the present invention
Dimension element can further prevent in color-mixed base paint and the sealing wax that is prepared using the color-mixed base paint in heavy color stuffing
Sedimentation, introduce yield value and thixotropy for sealing wax components system, significantly improve the adhesion strength of sealing wax, so as to further improve
The performance of obtained sealing wax is prepared by kitchen water-water of the present invention suit.In addition, inventor also found, when utilization kitchen of the present invention
During water-water suit configuration sealing wax, hydroxyethyl cellulose can also cooperate with the aluminium-magnesium silicate in Protection glue and lithium magnesium silicate
Effect, further enhance the toughness of the sealing wax obtained by kitchen water-water of the present invention suit configuration and avoid heavy color stuffing
Sedimentation, makes the performance of sealing wax more excellent.According to the specific example of the present invention, cellulose can select model 250HBR ethoxy
The hydroxyethyl cellulose of cellulose or model HS10W.It is set with thus, it is possible to further improve using kitchen water-water of the present invention
The performance for the sealing wax being prepared.
According to a particular embodiment of the invention, antifreezing agent can be propane diols.By in color-mixed base paint in the present invention
The normal use of color-mixed base paint under cryogenic conditions can be ensured by adding antifreezing agent, and effectively be solved by kitchen water-water of the present invention
The problem of paint film freeze thawing cracking, hollowing, paint film and base material come off when the sealing wax that suit configuration obtains uses at low temperature, improves water
The freeze-thaw stability of paint.According to a particular embodiment of the invention, antifreezing agent can select the propane diols of emerging foreign Chemical Manufacture.By
This, can further improve the freeze-thaw stability of the sealing wax obtained by kitchen water-water of the present invention suit configuration.
According to a particular embodiment of the invention, filler can be kaolin, and inventor has found, by into color-mixed base paint
Kaolin is added as filler, production cost can be not only reduced, can also further improve by water-water set in kitchen of the present invention
The rheological characteristic and thixotropy of obtained sealing wax are put in assembling, and make sealing wax film more plentiful.Thus, by using height in the present invention
Ridge soil can further adjust as filler and be set with the gloss for configuring obtained sealing wax, quality by kitchen water-water of the present invention, hang
Buoyancy and viscosity etc..
According to a particular embodiment of the invention, the defoamer of 0.5-1.5 parts by weight can be incorporated in color-mixed base paint, is sent out
A person of good sense has found effectively help in color-mixed base paint each component disperse by being incorporated the defoamer of said ratio and formed surely
Fixed, bubble-free and the system without shrinkage cavity, so as to further improve the sealing wax obtained by kitchen water-water of the present invention suit configuration
Performance.According to the specific example of the present invention, defoamer can be Kening Co., Ltd model FoamStar A10 defoamer, should
Defoamer has the wetting action that traditional defoamer does not have, and addition is lower than traditional defoamer, thus, can not only enter one
Step improves, and effectively helps each component in color-mixed base paint disperse and forms stable, bubble-free and the system without shrinkage cavity, raising
The performance of the sealing wax obtained by kitchen water-water of the present invention suit configuration, moreover it is possible to cost-effective.
According to a particular embodiment of the invention, pH adjusting agent can be 2-amino-2-methyl-1-propanol and butylethanolamine
At least one of.The pH value of color-mixed base paint can be effectively adjusted in the present invention by using above-mentioned pH adjusting agent, makes toning
Base paint has preferable stability, and then makes to be had preferably surely by the sealing wax that kitchen water-water of the present invention suit configuration obtains
It is qualitative, such as freeze-thaw stability etc..According to the specific example of the present invention, pH adjusting agent can select DOW Chemical model AMP-
95 2-amino-2-methyl-1-propanol and Ai Wangde butylethanolamine.
According to a particular embodiment of the invention, hardening agent can be to be dissipated selected from aqueous silica dispersion, aluminum oxide moisture
At least one of body, the aqueous dispersion of titanium dioxide and ethylene glycol dispersion.In the present invention, by being incorporated in color-mixed base paint
Above-mentioned hardening agent, the hard of the paint film that the sealing wax obtained by kitchen water-water of the present invention suit configuration is formed can be effectively improved
Degree, and then can make the paint film that there is preferable hardness and scratch resistance capability.According to the specific example of the present invention, hardening agent can be with
The dispersion that the dispersion and the trade mark for being AERODISP for the trade mark are AERODISP G1220, thus, it is possible to further improve by
The hardness of paint film for the sealing wax that kitchen water-water suit configuration of the present invention obtains.
According to a particular embodiment of the invention, emulsion can be silicone modified acrylic resin.Have in the present invention by selecting
Emulsion of the machine silicone acrylic resin as color-mixed base paint, the sealing wax obtained by kitchen water-water of the present invention suit configuration can be made
With preferable adhesive force, impact resistance, pliability, weatherability and heat resistance of Bao Se gloss retentions and protrusion etc., Jin Erke
Further to improve the performance of sealing wax.
According to an embodiment of the invention, by being incorporated above-mentioned coalescents, Ke Yiyou in color-mixed base paint in the present invention
Effect makes emulsion or dispersion microparticle form the film of even compact, and improves the film forming under cryogenic conditions, and then effectively improves
The film forming efficiency of the sealing wax obtained by kitchen water-water of the present invention suit configuration.According to a particular embodiment of the invention, film forming helps
Agent can be Lauryl Alcohol ester, and from Lauryl Alcohol ester as coalescents in the present invention, not only dosage is few, moreover it is possible to makes toning base
Plinth paint has more good stability under different PH environment, and film forming is closely knit, and then can further improve by the present invention
The film forming efficiency for the sealing wax that kitchen water-water suit configuration obtains.
According to a particular embodiment of the invention, can effectively be killed in the present invention by adding bactericide in color-mixed base paint
Go out the various microorganisms such as bacterium in color-mixed base paint, mould, and then prevent addling for color-mixed base paint, effectively extend its storage
And usage time, and then further improve the quality of the sealing wax obtained by kitchen water-water of the present invention suit configuration.According to this hair
Bright specific example, bactericide can be MERGAL K9N, thus, it is possible to further improve the sterilization effect to color-mixed base paint
Fruit.
According to a particular embodiment of the invention, wetting agent can be modified anion surfactant.Thus, it is possible to effectively
Ground soaks to each component particle in color-mixed base paint, reduces the surface tension of particle, reaches excellent wetting effect, and then
The sealing wax obtained by kitchen water-water of the present invention suit configuration can further be improved to the wettability of ground, improve paint solution
Levelability, adhesive force and filming performance of the increase paint film to ground.
According to a particular embodiment of the invention, the Protection glue of certain content can be incorporated in color-mixed base paint.Thus, may be used
Further to improve the stability of each composition in color-mixed base paint, improving the thixotropy of base paint is easier base paint granulation,
And particle effect is more preferable, and then effectively improve the combination property of the sealing wax obtained by kitchen water-water of the present invention suit configuration.
Continuous phase is described in detail below.
Continuous phase
According to an embodiment of the invention, continuous phase is by the deionized water of 5.5-7.5 parts by weight, the modified fibre of 5-10 parts by weight
Tie up element, the hydrophobic auxiliary agent of 0.1-0.5 parts by weight, the emulsion of 70-95 parts by weight, the coalescents of 3-10 parts by weight, 5-10 weight
The thickener composition of the antifreezing agent of part, the pH adjusting agent of 0.1-0.5 parts by weight and 0.1-0.8 parts by weight.By adopting in the present invention
Continuous phase can effectively be prepared with said components.
According to a particular embodiment of the invention, modified cellulose can be organic modified bentonite.In the present invention by
Organic modified bentonite is added in continuous phase can significantly improve the thixotropy of continuous phase, and then can make by kitchen water of the present invention
The sealing wax that the assembling of bag water jacket puts to obtain has preferable thixotropy, effectively prevents the sedimentation of the composition such as color stuffing in sealing wax, and then
Make sealing wax that there is preferable levelability, improve the disposable rate of film build of sealing wax.
According to a particular embodiment of the invention, hydrophobic auxiliary agent can be water-soluble nonionic surfactant.Thus, may be used
To effectively improve the hydrophobic performance of the sealing wax coating surface obtained by kitchen water-water of the present invention suit configuration, prevent moisture from oozing
Thoroughly, anti-stick, the antifouling property of paint film are improved.
According to a particular embodiment of the invention, emulsion can be silicone modified acrylic resin.Have in the present invention by selecting
Emulsion of the machine silicone acrylic resin as continuous phase, it can make to be had by the sealing wax that kitchen water-water of the present invention suit configuration obtains
Preferable adhesive force, impact resistance, pliability, weatherability and heat resistance of Bao Se gloss retentions and protrusion etc., and then can enter
One step improves the combination property of sealing wax.
According to an embodiment of the invention, can effectively be made by being incorporated above-mentioned coalescents in continuous phase in the present invention
Emulsion or dispersion microparticle is formed the film of even compact, and improve the film forming under cryogenic conditions, and then effectively improve utilization
The film forming efficiency for the sealing wax that kitchen water-water suit configuration of the present invention obtains.According to a particular embodiment of the invention, coalescents
Can be Lauryl Alcohol ester, from Lauryl Alcohol ester as coalescents in the present invention, not only dosage is few, moreover it is possible to makes different
There is more good stability under PH environment, and film forming is closely knit, and then can further improve and utilize kitchen water-water of the present invention
The film forming efficiency for the sealing wax that suit configuration obtains.
According to a particular embodiment of the invention, antifreezing agent can be propane diols.By being added in continuous phase in the present invention
Antifreezing agent can ensure that cryogenic conditions are gone to the kitchen the normal use of water-water suit, and are effectively solved by kitchen water-water of the present invention
The problem of paint film freeze thawing cracking, hollowing, paint film and base material come off when the sealing wax that suit configuration obtains uses at low temperature, improves water
The freeze-thaw stability of paint.According to a particular embodiment of the invention, antifreezing agent can select the propane diols of emerging foreign Chemical Manufacture.By
This, the freeze-thaw stability that can further improve.
According to a particular embodiment of the invention, pH adjusting agent can be 2-amino-2-methyl-1-propanol and butylethanolamine
At least one of.The pH value of continuous phase can be effectively adjusted in the present invention by using above-mentioned pH adjusting agent, has continuous phase
There is preferable stability, and then make that there is preferable stability, example by the sealing wax that kitchen water-water of the present invention suit configuration obtains
Such as freeze-thaw stability.According to the specific example of the present invention, pH adjusting agent can select DOW Chemical model AMP-95 2-
The butylethanolamine of amino-2-methyl -1- propyl alcohol and Ai Wangde.
According to a particular embodiment of the invention, the present invention in by continuous phase add thickener can be effectively increased by
The viscosity for the sealing wax that kitchen water-water suit configuration of the present invention obtains, and effectively prevent that paint solution from precipitating and layering, raising once apply
The wet-film thickness of dress.According to the specific example of the present invention, thickener can be ACRYSOL TT-935, it is possible thereby to further carry
The film forming efficiency of the high sealing wax obtained by kitchen water-water of the present invention suit configuration.
According to the second aspect of the invention, the invention also provides a kind of side for preparing above-mentioned kitchen water-water suit
Method, wherein,
Protection glue is prepared according to the following steps：(1) deionized water is added in a reservoir, and in 600r/min stirring
Thinner, preservative, bactericide and the pH adjusting agent of predetermined ratio are sequentially added under speed；(2) 1300-1500r/min's
The protection rubber powder of predetermined ratio is added under stir speed (S.S.), 30min is stirred, to obtain Protection glue；
Color-mixed base paint is prepared according to the following steps：(1) deionized water is added in a reservoir, and in 300-500r/
The mould inhibitor and dispersant of predetermined ratio are added under min stir speed (S.S.), improves rotating speed to 700-1000r/min stirrings 10min；
(2) rotating speed is reduced to 300-500r/min, is added the cellulose stirring 5min of predetermined ratio, is sequentially added the anti-of predetermined ratio
Freeze agent, filler, nano silicon and defoamer；(3) rotating speed is improved to 500-900r/min, and sequentially adds predetermined ratio
PH adjusting agent, hardening agent and emulsion, rotating speed is improved to 1300-1500r/min stirrings 20min；(4) rotating speed is reduced to 700-
1000r/min, and coalescents, defoamer, bactericide, wetting agent and the Protection glue of predetermined ratio are sequentially added, to obtain
Color-mixed base paint；
Continuous phase is prepared according to the following steps：(1) deionized water is added in a reservoir, in stirring for 600-700r/min
The mould inhibitor that predetermined ratio is sequentially added under speed, bactericide, modified cellulose, hydrophobic auxiliary agent and emulsion are mixed, and is stirred
10min；(2) coalescents, antifreezing agent, defoamer and the pH adjusting agent of predetermined ratio are sequentially added, and stirs 5min；(3) add
Enter the thickener of predetermined ratio and stir 10min, to obtain continuous phase.
The method according to the above embodiment of the present invention for preparing kitchen water-water suit, can effectively be prepared respectively
Protection glue, color-mixed base paint and continuous phase, it can effectively configure to obtain sealing wax, and the sealing wax using above-mentioned kitchen water-water suit
Paint film there is unique scratch resistance capability, hardness is extremely strong and hydrophobicity is good, the sealing wax applicability is wider, energy during applied to kitchen
Marble is enough substituted, meets kitchen to cabinet table surface high rigidity, the requirement of scratch resistance, water resistance, and then natural stone can be reduced
The exploitation of material, decoration cost is reduced, it is green and environmentally friendly.
According to the third aspect of the present invention, the invention also provides a kind of sealing wax, the sealing wax is by the above-mentioned implementation of the present invention
Example Protection glue, color-mixed base paint and continuous phase are according to mass ratio 3：4：3 are mixed to get.
Inventor has found, when the composition of Protection glue in sealing wax is excessive, not only considerably increases sealing wax cost, can make sealing wax
Viscosity is too high, and so as to cause color point particle fragmentation, when the composition of Protection glue in sealing wax is very few, sealing wax viscosity is low, is unfavorable for coloured silk
That puts is dispersed, and during spraying application, easy sagging, coloured silk point intensity is also undesirable, when the content of Protection glue is sealing wax
When 30%, sealing wax modest viscosity, do not broken up again beneficial to coloured silk point uniform particle is scattered, spraying effect is good, moderate strength.Work as water
When color-mixed base paint content is excessive in paint, makes Protection glue is relative with continuous phase content to reduce, can substantially reduce the performance of sealing wax.
When the content of tinter is very few, spreading rate can substantially reduce, and increase cost, when the content of color-mixed base paint is 40%, sealing wax
Performance is optimal.When the content of continuous phase in sealing wax is excessive, viscosity is too high, is unfavorable for spraying and puts particle-stabilised deposit with coloured silk
, cost increase, when the content of continuous phase in sealing wax is very few, degradation, when the content of continuous phase is 30%, sealing wax
Various aspects of performance is optimal.It is 3 by controlling the proportioning of Protection glue, color-mixed base paint and continuous phase in the present invention：4：3, Ke Yiyou
Effect configuration, which obtains paint film, has unique scratch resistance capability, a sealing wax that hardness is extremely strong and hydrophobicity is good, and the sealing wax applicability compared with
Marble can be substituted when extensively, applied to kitchen, meets that kitchen to cabinet table surface high rigidity, the requirement of scratch resistance, water resistance, is entered
And the exploitation of lithotome can be reduced, reduce decoration cost, it is green and environmentally friendly.
It should be noted that above-mentioned excellent properties possessed by the sealing wax of the above embodiment of the present invention are to be based on invention human hair
Showed by Protection glue, color-mixed base paint and continuous phase according to mass ratio be 3：4：3 proportioning is put into the base paint for mixing up color
In Protection glue, dispersion impeller obtains purpose particle size with certain rotating speed, time, adds continuous phase, stirs and be obtained by mixing
Go out.
According to the fourth aspect of the present invention, the invention also provides a kind of cabinet, including：Cabinet and lacquer painting, wherein, cabinet
Body is wooden cabinet；Lacquer painting is formed by the way that the sealing wax of above-described embodiment is applied into wooden cabinet surface.
Thus, it is possible to which the sealing wax of the above embodiment of the present invention is successfully applied into wooden cabinet, and significantly improve wooden cabinet
The hardness and water resistance of body, wooden cabinet is set to have marmorean attractive in appearance and similar marmorean hardness and water resistance concurrently,
Thus it can not only meet kitchen to cabinet table surface high rigidity, the requirement of scratch resistance, water resistance, moreover it is possible to marble material is substituted,
Reaching reduces decoration cost and green effect.
Embodiment 1
(1) water-water suit in kitchen is formed by the component of following parts by weight respectively：
It is prepared by Protection glue：
It is prepared by basic colored paint：
Continuous phase：
Wherein, in Protection glue, protection rubber powder is made up of aluminium-magnesium silicate and lithium magnesium silicate；Thinner is sodium pyrophosphate；It is mould proof
Agent is the tricresyl phosphate mould inhibitor of model 786；Bactericide is MERGAL K9N；PH adjusting agent is the AMP- of DOW Chemical
95。
In color-mixed base paint, mould inhibitor is the tricresyl phosphate mould inhibitor of model 786；Dispersant is ROHM AND HAAS point
Powder 731A；Cellulose is model 250HBR hydroxyethyl cellulose and model HS10W hydroxyethyl cellulose；Antifreezing agent
For the propane diols of emerging foreign Chemical Manufacture；Filler can be kaolin；Defoamer is Kening Co., Ltd model FoamStar A10's
Defoamer；PH adjusting agent is Ai Wangde butylethanolamine；Hardening agent is the dispersion that the trade mark is AERODISP and the trade mark is
AERODISP G1220 dispersion；Emulsion is silicone modified acrylic resin；Coalescents are Lauryl Alcohol ester；Bactericide is
MERGAL K9N；Wetting agent is modified anion surfactant.
In continuous phase, modified cellulose is organic modified bentonite；Hydrophobic auxiliary agent is water-soluble nonionic surface-active
Agent；Emulsion is silicone modified acrylic resin；Coalescents are Lauryl Alcohol ester；Antifreezing agent is the propane diols of emerging foreign Chemical Manufacture；
PH adjusting agent is the AMP-95 and Ai Wangde of DOW Chemical butylethanolamine；Thickener is ACRYSOL TT-935.
(2) preparation method of kitchen water-water suit：
The preparation method of Protection glue is as follows：
1) deionized water is added in a reservoir, and the viscosity reduction of predetermined ratio is sequentially added under 600r/min stir speed (S.S.)
Agent, preservative, bactericide and pH adjusting agent；
2) the protection rubber powder of predetermined ratio is added under 1200r/min stir speed (S.S.), 30min is stirred, to be protected
Protect glue,
The preparation method of color-mixed base paint is as follows：
1) add deionized water in a reservoir, and add under 300r/min stir speed (S.S.) predetermined ratio mould inhibitor and
Dispersant, rotating speed is improved to 800r/min stirrings 10min；
2) rotating speed is reduced to 400r/min, is added the cellulose stirring 5min of predetermined ratio, is sequentially added predetermined ratio
Antifreezing agent, filler, nano silicon and defoamer；
3) rotating speed is improved to 700r/min, and sequentially adds pH adjusting agent, hardening agent and the emulsion of predetermined ratio, is improved and is turned
Speed to 1300r/min stir 20min；
4) rotating speed is reduced to 700r/min, and sequentially adds the coalescents of predetermined ratio, defoamer, bactericide, wetting
Agent and the Protection glue, to obtain color-mixed base paint,
The preparation method of continuous phase is as follows：
1) deionized water is added in a reservoir, and the mould proof of predetermined ratio is sequentially added under 600r/min stir speed (S.S.)
Agent, bactericide, modified cellulose, hydrophobic auxiliary agent and emulsion, and stir 10min；
2) coalescents, antifreezing agent, defoamer and the pH adjusting agent of predetermined ratio are sequentially added, and stirs 5min；
3) add the thickener of predetermined ratio and stir 10min, to obtain continuous phase.
(3) sealing wax formula and application：
By obtained Protection glue, color-mixed base paint and continuous phase prepared above according to mass ratio be 3：4：3 are mixed to get
Sealing wax.And by the sealing wax coated in the paint film on the wooden cabinet table surface in kitchen, forming similar marbling effect.
The paint film is remarkably improved the hardness and water resistance of wooden cabinet, wooden cabinet is had marmorean U.S. concurrently
See and similar marmorean hardness and water resistance, thus can not only meet kitchen to cabinet table surface high rigidity, scratch resistance, water-fast
Property requirement, moreover it is possible to substitute marble material, reaching reduces decoration cost and green effect.
Embodiment 2
(1) water-water suit in kitchen is formed by the component of following parts by weight respectively：Protection glue：
It is prepared by basic colored paint：
Continuous phase：
Wherein, in Protection glue, protection rubber powder is made up of aluminium-magnesium silicate and lithium magnesium silicate；Thinner is sodium pyrophosphate；It is mould proof
Agent is the tricresyl phosphate mould inhibitor of model 786；Bactericide is MERGAL K9N；PH adjusting agent is the AMP- of DOW Chemical
95 and Ai Wangde butylethanolamine.
In color-mixed base paint, mould inhibitor is the tricresyl phosphate mould inhibitor of model 786；Dispersant is ROHM AND HAAS point
Powder 731A；Cellulose is model 250HBR hydroxyethyl cellulose and model HS10W hydroxyethyl cellulose；Antifreezing agent
For the propane diols of emerging foreign Chemical Manufacture；Filler can be kaolin；Defoamer is Kening Co., Ltd model FoamStar A10's
Defoamer；PH adjusting agent is the AMP-95 and Ai Wangde of DOW Chemical butylethanolamine；Hardening agent is that the trade mark is AERODISP
Dispersion and the trade mark be AERODISP G1220 dispersion；Emulsion is silicone modified acrylic resin；Coalescents are 12
Carbon alcohol ester；Bactericide is MERGAL K9N；Wetting agent is modified anion surfactant.
In continuous phase, modified cellulose is organic modified bentonite；Hydrophobic auxiliary agent is water-soluble nonionic surface-active
Agent；Emulsion is silicone modified acrylic resin；Coalescents are Lauryl Alcohol ester；Antifreezing agent is the propane diols of emerging foreign Chemical Manufacture；
PH adjusting agent is the AMP-95 and Ai Wangde of DOW Chemical butylethanolamine；Thickener is ACRYSOL TT-935.
(2) preparation method of kitchen water-water suit：
The preparation method of Protection glue is as follows：
1) deionized water is added in a reservoir, and the viscosity reduction of predetermined ratio is sequentially added under 600r/min stir speed (S.S.)
Agent, preservative, bactericide and pH adjusting agent；
2) the protection rubber powder of predetermined ratio is added under 1300r/min stir speed (S.S.), 30min is stirred, to be protected
Protect glue,
The preparation method of color-mixed base paint is as follows：
1) add deionized water in a reservoir, and add under 400r/min stir speed (S.S.) predetermined ratio mould inhibitor and
Dispersant, rotating speed is improved to 900r/min stirrings 10min；
2) rotating speed is reduced to 400r/min, is added the cellulose stirring 5min of predetermined ratio, is sequentially added predetermined ratio
Antifreezing agent, filler, nano silicon and defoamer；
3) rotating speed is improved to 700r/min, and sequentially adds pH adjusting agent, hardening agent and the emulsion of predetermined ratio, is improved and is turned
Speed to 1400r/min stir 20min；
4) rotating speed is reduced to 800r/min, and sequentially adds the coalescents of predetermined ratio, defoamer, bactericide, wetting
Agent and the Protection glue, to obtain color-mixed base paint,
The preparation method of continuous phase is as follows：
1) deionized water is added in a reservoir, and the mould proof of predetermined ratio is sequentially added under 600r/min stir speed (S.S.)
Agent, bactericide, modified cellulose, hydrophobic auxiliary agent and emulsion, and stir 10min；
2) coalescents, antifreezing agent, defoamer and the pH adjusting agent of predetermined ratio are sequentially added, and stirs 5min；
3) add the thickener of predetermined ratio and stir 10min, to obtain continuous phase.
(3) sealing wax formula and application：
By obtained Protection glue, color-mixed base paint and continuous phase prepared above according to mass ratio be 3：4：3 are mixed to get
Sealing wax.And by the sealing wax coated in the paint film on the wooden cabinet table surface in kitchen, forming similar marbling effect.
The paint film is remarkably improved the hardness and water resistance of wooden cabinet, wooden cabinet is had marmorean U.S. concurrently
See and similar marmorean hardness and water resistance, thus can not only meet kitchen to cabinet table surface high rigidity, scratch resistance, water-fast
Property requirement, moreover it is possible to substitute marble material, reaching reduces decoration cost and green effect.
Embodiment 3
(1) water-water suit in kitchen is formed by the component of following parts by weight respectively：
Protection glue：
It is prepared by basic colored paint：
Continuous phase：
Wherein, wherein, in Protection glue, protection rubber powder is made up of aluminium-magnesium silicate and lithium magnesium silicate；Thinner is sodium pyrophosphate；
Mould inhibitor is the tricresyl phosphate mould inhibitor of model 786；Bactericide is MERGAL K9N；PH adjusting agent is Ai Wangde fourth
Ethylethanolamine.
In color-mixed base paint, mould inhibitor is the tricresyl phosphate mould inhibitor of model 786；Dispersant is ROHM AND HAAS point
Powder 731A；Cellulose is model 250HBR hydroxyethyl cellulose and model HS10W hydroxyethyl cellulose；Antifreezing agent
For the propane diols of emerging foreign Chemical Manufacture；Filler can be kaolin；Defoamer is Kening Co., Ltd model FoamStar A10's
Defoamer；PH adjusting agent is the AMP-95 and Ai Wangde of DOW Chemical butylethanolamine；Hardening agent is that the trade mark is AERODISP
Dispersion and the trade mark be AERODISP G1220 dispersion；Emulsion is silicone modified acrylic resin；Coalescents are 12
Carbon alcohol ester；Bactericide is MERGAL K9N；Wetting agent is modified anion surfactant.
In continuous phase, modified cellulose is organic modified bentonite；Hydrophobic auxiliary agent is water-soluble nonionic surface-active
Agent；Emulsion is silicone modified acrylic resin；Coalescents can be Lauryl Alcohol ester；Antifreezing agent is the third the two of emerging foreign Chemical Manufacture
Alcohol；PH adjusting agent is the AMP-95 of DOW Chemical；Thickener is ACRYSOL TT-935.
(2) preparation method of kitchen water-water suit：
The preparation method of Protection glue is as follows：
1) deionized water is added in a reservoir, and the viscosity reduction of predetermined ratio is sequentially added under 600r/min stir speed (S.S.)
Agent, preservative, bactericide and pH adjusting agent；
2) the protection rubber powder of predetermined ratio is added under 1300r/min stir speed (S.S.), 30min is stirred, to be protected
Protect glue,
The preparation method of color-mixed base paint is as follows：
1) add deionized water in a reservoir, and add under 400r/min stir speed (S.S.) predetermined ratio mould inhibitor and
Dispersant, rotating speed is improved to 700r/min stirrings 10min；
2) rotating speed is reduced to 400r/min, is added the cellulose stirring 5min of predetermined ratio, is sequentially added predetermined ratio
Antifreezing agent, filler, nano silicon and defoamer；
3) rotating speed is improved to 600r/min, and sequentially adds pH adjusting agent, hardening agent and the emulsion of predetermined ratio, is improved and is turned
Speed to 1400r/min stir 20min；
4) rotating speed is reduced to 700r/min, and sequentially adds the coalescents of predetermined ratio, defoamer, bactericide, wetting
Agent and the Protection glue, to obtain color-mixed base paint,
The preparation method of continuous phase is as follows：
1) deionized water is added in a reservoir, and the mould proof of predetermined ratio is sequentially added under 700r/min stir speed (S.S.)
Agent, bactericide, modified cellulose, hydrophobic auxiliary agent and emulsion, and stir 10min；
2) coalescents, antifreezing agent, defoamer and the pH adjusting agent of predetermined ratio are sequentially added, and stirs 5min；
3) add the thickener of predetermined ratio and stir 10min, to obtain continuous phase.
(3) sealing wax formula and application：
By obtained Protection glue, color-mixed base paint and continuous phase prepared above according to mass ratio 3：4：3 water being mixed to get
Paint.And by the sealing wax coated in the paint film on the wooden cabinet table surface in kitchen, forming similar marbling effect.
The paint film is remarkably improved the hardness and water resistance of wooden cabinet, wooden cabinet is had marmorean U.S. concurrently
See and similar marmorean hardness and water resistance, thus can not only meet kitchen to cabinet table surface high rigidity, scratch resistance, water-fast
Property requirement, moreover it is possible to substitute marble material, reaching reduces decoration cost and green effect.
Conclusion：Be set with by using kitchen water-water proposed by the present invention and preparation method thereof, and the guarantor that will be prepared
It is 3 that glue, color-mixed base paint and continuous phase, which are protected, according to mass ratio：4：3 mixing can obtain sealing wax, when the sealing wax is used for into wooden product
Interface binding power is preferable, and wooden product is had stronger hardness, water resistance and a scratch resistance capability, and common exterior wall water-water
Relatively poor with woodwork interface binding power, hardness, water resistance are also relatively poor during for woodwork.
In the description of this specification, reference term " one embodiment ", " some embodiments ", " example ", " specifically show
The description of example " or " some examples " etc. means specific features, structure, material or the spy for combining the embodiment or example description
Point is contained at least one embodiment or example of the present invention.In this manual, to the schematic representation of above-mentioned term not
Identical embodiment or example must be directed to.Moreover, specific features, structure, material or the feature of description can be any
Combined in an appropriate manner in individual or multiple embodiments or example.In addition, in the case of not conflicting, the technology of this area
Different embodiments or example and the feature of different embodiments or example described in this specification can be combined by personnel
And combination.
Although embodiments of the invention have been shown and described above, it is to be understood that above-described embodiment is example
Property, it is impossible to limitation of the present invention is interpreted as, one of ordinary skill in the art within the scope of the invention can be to above-mentioned
Embodiment is changed, changed, replacing and modification.
Claims (10)
- A kind of 1. kitchen water-water suit, it is characterised in that including：Protection glue, the Protection glue is by the protection rubber powder of 5-25 parts by weight, the deionized water of 75-90 parts by weight, 0.1-5 parts by weight Thinner, the mould inhibitor of 0.1-4 parts by weight, the pH adjusting agent composition of the bactericide of 0.1-3 parts by weight and 0.1-1 parts by weight；Color-mixed base paint, the color-mixed base paint by the deionized waters of 45-65 parts by weight, 0.1-0.5 parts by weight mould inhibitor, The dispersant of 0.1-1 parts by weight, the cellulose of 0.5-1 parts by weight, the antifreezing agents of 0.5-1.5 parts by weight, 5-15 parts by weight are filled out Material, the nano silicon of 1-5 parts by weight, the defoamer of 0.5-1.5 parts by weight, the pH adjusting agent of 0.1-0.8 parts by weight, 1-5 The hardening agent of parts by weight, the emulsion of 15-45 parts by weight, the coalescents of 0.5-1.5 parts by weight, 0.1-1 parts by weight bactericide, The wetting agent of 0.2-1 parts by weight and the Protection glue composition of 2-6 parts by weight；Continuous phase, the continuous phase is by the deionized water of 5.5-7.5 parts by weight, the modified cellulose of 5-10 parts by weight, 0.1-0.5 The hydrophobic auxiliary agent of parts by weight, the emulsion of 70-95 parts by weight, the coalescents of 3-10 parts by weight, 5-10 parts by weight antifreezing agent, The pH adjusting agent of 0.1-0.5 parts by weight and the thickener composition of 0.1-0.8 parts by weight,Wherein, the Protection glue, the color-mixed base paint and the continuous phase are separately positioned in different containers.
- 2. water-water suit in kitchen according to claim 1, it is characterised in that the protection rubber powder is by aluminium-magnesium silicate and silicon Sour magnesium lithium composition.
- 3. water-water suit in kitchen according to claim 1, it is characterised in that the thinner is sodium pyrophosphate；It is described Mould inhibitor is tricresyl phosphate；The bactericide is MERGAL K9N.
- 4. water-water suit in kitchen according to claim 1, it is characterised in that the pH adjusting agent is 2- amino -2- first At least one of base -1- propyl alcohol and butylethanolamine.
- 5. water-water suit in kitchen according to claim 1, it is characterised in that the dispersant disperses for ROHM AND HAAS Agent；The antifreezing agent is propane diols；The filler is kaolin；The hardening agent is selected from aqueous silica dispersion, oxidation At least one of aluminium aqueous dispersion, the aqueous dispersion of titanium dioxide and ethylene glycol dispersion.
- 6. water-water suit in kitchen according to claim 1, it is characterised in that the cellulose is hydroxyethyl cellulose； The modified cellulose is organic modified bentonite.
- 7. water-water suit in kitchen according to claim 1, it is characterised in that the emulsion is acid-organosilicon crylic acid tree Fat；The coalescents are Lauryl Alcohol ester；The thickener is ACRYSOL TT-935；The hydrophobic auxiliary agent is water-soluble non- Ionic surfactant.
- A kind of 8. method of the kitchen water-water suit prepared described in claim any one of 1-7, it is characterised in thatThe Protection glue is prepared according to the following steps：(1) add deionized water in a reservoir, and sequentially add under 600r/min stir speed (S.S.) predetermined ratio thinner, Preservative, bactericide and pH adjusting agent；(2) the protection rubber powder of predetermined ratio is added under 1300-1500r/min stir speed (S.S.), 30min is stirred, to obtain Protection glue,The color-mixed base paint is prepared according to the following steps：(1) deionized water is added in a reservoir, and the mould inhibitor of predetermined ratio is added under 300-500r/min stir speed (S.S.) And dispersant, rotating speed is improved to 700-1000r/min stirrings 10min；(2) rotating speed is reduced to 300-500r/min, is added the cellulose stirring 5min of predetermined ratio, is sequentially added predetermined ratio Antifreezing agent, filler, nano silicon and defoamer；(3) rotating speed is improved to 500-900r/min, and sequentially adds pH adjusting agent, hardening agent and the emulsion of predetermined ratio, is improved Rotating speed to 1300-1500r/min stir 20min；(4) rotating speed is reduced to 700-1000r/min, and sequentially adds the coalescents of predetermined ratio, defoamer, bactericide, profit Humectant and the Protection glue, to obtain color-mixed base paint,The continuous phase is prepared according to the following steps：(1) deionized water is added in a reservoir, and the mould proof of predetermined ratio is sequentially added under 600-700r/min stir speed (S.S.) Agent, bactericide, modified cellulose, hydrophobic auxiliary agent and emulsion, and stir 10min；(2) coalescents, antifreezing agent, defoamer and the pH adjusting agent of predetermined ratio are sequentially added, and stirs 5min；(3) add the thickener of predetermined ratio and stir 10min, to obtain continuous phase.
- 9. a kind of sealing wax, it is characterised in that the sealing wax is as the kitchen water-water suit described in any one of claim 1~7 In the Protection glue, the color-mixed base paint and the continuous phase according to mass ratio 3：4：3 are mixed to get.
- A kind of 10. kitchen cabinet, it is characterised in that including：Cabinet, the cabinet are wooden cabinet；AndLacquer painting, the lacquer painting are formed by the way that the sealing wax described in claim 9 is applied into the wooden cabinet surface.