CN107603331A - A kind of ultraviolet light solidifies packaging ink - Google Patents
A kind of ultraviolet light solidifies packaging ink Download PDFInfo
- Publication number
- CN107603331A CN107603331A CN201710915626.9A CN201710915626A CN107603331A CN 107603331 A CN107603331 A CN 107603331A CN 201710915626 A CN201710915626 A CN 201710915626A CN 107603331 A CN107603331 A CN 107603331A
- Authority
- CN
- China
- Prior art keywords
- parts
- ultraviolet light
- added
- aziridine
- glycerine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of ultraviolet light to solidify packaging ink, includes the raw material of following parts by weight：12 parts of organic pigment, 12 parts of glycerine, 0.3 0.5 parts of styrene, 50 80 parts of 2 resins of LX, 12 parts of phenyl glycidyl ether, 0.2 0.4 parts of tricresyl phosphate, 10 20 parts of aziridine, 12 parts of activated carbon, 0.1 0.2 parts of paraffin, 12 parts of Isobutyl methacrylate, 57 parts of titanium dioxide, step by grinding → modification → stirring → drying is made, after the present invention is handled, superfine wrinkle effect can be formed can form superfine frosted finish effect again, the effect of wrinkle and frosted finish effect can also be formed, its adhesive force and folding resistance are excellent, and solvent-free discharge, it is environmentally friendly, for high-grade packages printing.
Description
Technical field
The present invention relates to packaging material paint field, and in particular to a kind of ultraviolet light solidifies packaging ink.
Background technology
Ultraviolet light solidification (UV) ink refers to that in the case where ultraviolet irradiates the ultraviolet light using different wave length and energy makes ink
Film forming and the ink dried.Using different ultraviolet spectras, different-energy can be produced, the monomer in different ink vehicles is polymerize
Into polymer, so the color film of UV ink has good mechanically and chemically performance.The major advantage of UV ink has：(1) do not have to
Solvent；(2) rate of drying is fast, and power consumption is few；(3) good luster, it is bright in luster；(4) water-fast, solvent resistant, anti-wear performance are good.UV ink
Middle light trigger is a kind of easily by light activated compound, is excited into free radical after illumination is absorbed, energy transfer is to photonasty
Molecule or photocrosslinking agent, make UV ink that photocuring reaction occur.The UV curable ink kind for being presently used for silk-screen printing is numerous
It is more, but its performance is single, and decorative effect is single, can only typically print off the pattern of Shamian Island or wrinkle effect.Ink of the present invention can be with
It is once imprinted in gold and silver paperboard or PVC card by screen painting mode, the shortcomings that overcoming conventional art register trouble.
The content of the invention
It is an object of the invention to provide a kind of ultraviolet light to solidify packaging ink.
The purpose of the present invention can be achieved through the following technical solutions：
A kind of ultraviolet light solidifies packaging ink, it is characterised in that includes the raw material of following parts by weight：Organic pigment
1-2 parts, glycerine 1-2 parts, styrene 0.3-0.5 parts, LX-2 resin 50-80 parts, phenyl glycidyl ether 1-2 parts, tripotassium phosphate
Phenyl ester 0.2-0.4 parts, aziridine 10-20 parts, activated carbon 1-2 parts, paraffin 0.1-0.2 parts, Isobutyl methacrylate 1-2 parts,
Titanium dioxide 5-7 parts.
A kind of described ultraviolet light solidification packaging ink, include the raw material of following parts by weight：2 parts of organic pigment,
2 parts of glycerine, 0.5 part of styrene, 70 parts of LX-2 resins, 2 parts of phenyl glycidyl ether, 0.4 part of tricresyl phosphate, aziridine 15
Part, 2 parts of activated carbon, 0.2 part of paraffin, 2 parts of Isobutyl methacrylate, 7 parts of titanium dioxide.
Preparation method comprises the following steps：
(1) LX-2 resins are added into suitable quantity of water, is ground into nano pulp, organic pigment, activity are added at 40-50 DEG C
Charcoal, paraffin, titanium dioxide, after stirring 10-20 minutes, filter, dry, milling；
(2) by glycerine, styrene, phenyl glycidyl ether, tricresyl phosphate, aziridine, Isobutyl methacrylate
Mix, it is standby to obtain modification liquid；
(3) powder obtained by step (1) is added in homogenizer, maintains the temperature at 70-80 DEG C, added modification liquid, stir
After mixing 20-30 minutes, dry, be ground into nanometer powder and produce.
Beneficial effects of the present invention：After present invention processing, can form superfine wrinkle effect can form superfine frosted effect again
Fruit, the effect of wrinkle and frosted finish effect can also be formed, its adhesive force and folding resistance are excellent, and solvent-free discharge, to ring
Border is friendly, for high-grade packages printing.
Embodiment
The present invention is described in further detail with reference to specific embodiment.
Embodiment 1
A kind of ultraviolet light solidifies packaging ink, and preparation method comprises the following steps：
(1) 50kgLX-2 resins are added into suitable quantity of water, is ground into nano pulp, organic pigment is added at 40-50 DEG C
1kg, activated carbon 1kg, paraffin 0.1kg, titanium dioxide 5kg, after stirring 10-20 minutes, filter, dry, milling；
(2) by glycerine 1kg, styrene 0.3kg, phenyl glycidyl ether 1kg, tricresyl phosphate 0.2kg, aziridine
10kg, Isobutyl methacrylate 1kg are mixed, and it is standby to obtain modification liquid；
(3) powder obtained by step (1) is added in homogenizer, maintains the temperature at 70-80 DEG C, added modification liquid, stir
After mixing 20-30 minutes, dry, be ground into nanometer powder and produce.
Embodiment 2
A kind of ultraviolet light solidifies packaging ink, and preparation method comprises the following steps：
(1) 80kgLX-2 resins are added into suitable quantity of water, is ground into nano pulp, organic pigment is added at 40-50 DEG C
2kg, activated carbon 2kg, paraffin 0.2kg, titanium dioxide 7kg, after stirring 10-20 minutes, filter, dry, milling；
(2) by glycerine 2kg, styrene 0.5kg, phenyl glycidyl ether 2kg, tricresyl phosphate 0.4kg, aziridine
20kg, Isobutyl methacrylate 2kg are mixed, and it is standby to obtain modification liquid；
(3) powder obtained by step (1) is added in homogenizer, maintains the temperature at 70-80 DEG C, added modification liquid, stir
After mixing 20-30 minutes, dry, be ground into nanometer powder and produce.
Embodiment 3
A kind of ultraviolet light solidifies packaging ink, and preparation method comprises the following steps：
(1) 70kgLX-2 resins are added into suitable quantity of water, is ground into nano pulp, organic pigment is added at 40-50 DEG C
2kg, activated carbon 2kg, paraffin 0.2kg, titanium dioxide 7kg, after stirring 10-20 minutes, filter, dry, milling；
(2) by glycerine 2kg, styrene 0.5kg, phenyl glycidyl ether 2kg, tricresyl phosphate 0.4kg, aziridine
15kg, Isobutyl methacrylate 2kg are mixed, and it is standby to obtain modification liquid；
(3) powder obtained by step (1) is added in homogenizer, maintains the temperature at 70-80 DEG C, added modification liquid, stir
After mixing 20-30 minutes, dry, be ground into nanometer powder and produce.
Above content is only citing made for the present invention and explanation, and affiliated those skilled in the art are to being retouched
The specific embodiment stated is made various modifications or supplement or substituted using similar mode, without departing from the design of invention
Or surmount scope defined in the claims, protection scope of the present invention all should be belonged to.
Claims (3)
1. a kind of ultraviolet light solidifies packaging ink, it is characterised in that includes the raw material of following parts by weight：Organic pigment 1-
2 parts, glycerine 1-2 parts, styrene 0.3-0.5 parts, LX-2 resin 50-80 parts, phenyl glycidyl ether 1-2 parts, phosphate trimethylbenzene
Ester 0.2-0.4 parts, aziridine 10-20 parts, activated carbon 1-2 parts, paraffin 0.1-0.2 parts, Isobutyl methacrylate 1-2 parts, titanium
White powder 5-7 parts.
2. a kind of ultraviolet light solidification packaging ink according to claim 1, it is characterised in that including following weight
The raw material of part：2 parts of organic pigment, 2 parts of glycerine, 0.5 part of styrene, 70 parts of LX-2 resins, 2 parts of phenyl glycidyl ether, phosphoric acid
0.4 part of front three phenyl ester, 15 parts of aziridine, 2 parts of activated carbon, 0.2 part of paraffin, 2 parts of Isobutyl methacrylate, 7 parts of titanium dioxide.
3. a kind of ultraviolet light solidification packaging ink according to claim 1, it is characterised in that preparation method includes
Following steps：
(1) LX-2 resins are added into suitable quantity of water, is ground into nano pulp, organic pigment, activated carbon, stone are added at 40-50 DEG C
Wax, titanium dioxide, after stirring 10-20 minutes, filter, dry, milling；
(2) glycerine, styrene, phenyl glycidyl ether, tricresyl phosphate, aziridine, Isobutyl methacrylate are mixed,
It is standby to obtain modification liquid；
(3) powder obtained by step (1) is added in homogenizer, maintains the temperature at 70-80 DEG C, add modification liquid, stir 20-
After 30 minutes, dry, be ground into nanometer powder and produce.