CN106916487A - A kind of package typography with pearly-lustre texture and its printing-ink for calling - Google Patents
A kind of package typography with pearly-lustre texture and its printing-ink for calling Download PDFInfo
- Publication number
- CN106916487A CN106916487A CN201710165462.2A CN201710165462A CN106916487A CN 106916487 A CN106916487 A CN 106916487A CN 201710165462 A CN201710165462 A CN 201710165462A CN 106916487 A CN106916487 A CN 106916487A
- Authority
- CN
- China
- Prior art keywords
- ink
- emulsion
- package
- printing
- pearly
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides the printing-ink that a kind of package with pearly-lustre texture is called, and is formed according to weight percent content configuration by following components：Binder 30 60%；Pearlescent pigment 10 30%；Solvent 20 40%；Auxiliary agent 0.1 5%；Binder is the compound of acrylic emulsion and polyaminoester emulsion, it is 25% 50% that acrylic emulsion accounts for the total proportion of ink, it is 5% 10% that polyaminoester emulsion accounts for the total proportion of ink, acrylic acid weight solid content is 50 65% in the acrylic emulsion, and the weight solid content of polyurethane is 50 65% in the polyaminoester emulsion；Pearlescent pigment is pearl essence of the particle diameter between 5 25um；It is the mixture of pure water, ethanol and propylene glycol monomethyl ether composition to state solvent；Auxiliary agent is the mixture of dispersant, defoamer, drying retardant and levelling agent composition；The present invention also provides a kind of package typography with pearly-lustre texture, the typography that the printing-ink is used, and package pearl effect is notable after printing, machine good stability on ink, ink film is high with base material binding strength, and rate of drying is fast, it is energy-saving, environmental protection.
Description
【Technical field】
The present invention relates to ink and its typography, especially a kind of package typography with pearly-lustre texture and its
The printing-ink for calling.
【Background technology】
Green printing had turned into the theme of industry development in recent years, and wherein water-based ink is safe and harmless due to its, green
Environmental protection, is favored by more and more printing enterprises, and its application field is more and more extensive.
The typography of pearly-lustre printing is basically identical with traditional water-based ink typography, and pearly-lustre printing is in recent years in bag
A kind of more popular new special gloss printing, with silver paste etc. in printed matter surface in dress and anti-counterfeit printing, then is added
Upper extremely transparent ink, silver-colored light twinkler reflects a kind of pearl effect of pearlescent through layer of ink.This printed matter tool
There are two major features：One is that different colors can be produced from terms of different refraction angles, and two is the paper that this ink is imprinted on different colours
Zhang Shanghui is changed.Pearly-lustre printing can make flat, simplicity by the personalized design of people and the combination of printing texture
Paper and the substrate surface such as film construct out a brand-new color space and photochromic effect again.On antifalse effect, by
It is the ink for having pearlescent gloss in pearl ink, when printed matter pattern changes angle, the color of ink will become
Change, this is that common ink is beyond one's reach.
In the typography of pearly-lustre printing, its preparation that it is critical only that pearl ink, pearl ink is typically by binder, pearl
Delustering pigment, solvent, auxiliary agent etc. are constituted.The selection of pearlescent pigment is most important, and general pearlescent pigment is core from natural mica piece
The heart, coats particulate metal and is made (such as mica titanium)；Additionally, the quality of pearl ink is heavily dependent on resin carrier pair
The wetting of flake pigment, the dispersed and parallel-oriented degree in ink film；The former is by selected this body structure of resin
And characteristic is determined, the latter then by ink component design and correct will implement typography realize.
Therefore, resin carrier is basis, and formula design and typography are crucial, and preferable ink should have relatively low consolidating
Body content；Therefore, pearlescent pigment usage amount should not be too many, and can be in irregular status because pigment is excessive easily intensive, easily arrange
Row are bad, and layer of ink volume should have larger convergent force in the layer of ink drying process of printing, using convergent force and sheet powder
Self gravitation effect, by the titanium nacreous compression of sheet mica, it is tended to parallel, this is with mill base, the ratio of coating, ink
The factors such as weight, viscosity are closely related, and flake pigment is got over can be arranged parallel to base material, then the pearl effect of pigment is better.
【The content of the invention】
The present invention provide a kind of pearl effect significantly, machine good stability on ink, ink film is high with base material binding strength, drying
Speed is fast, energy-saving, the package typography with pearly-lustre texture of environmental protection and its printing-ink for calling.
To reach above-mentioned improving eyesight, the technical scheme of use is as follows：
The printing-ink that a kind of package with pearly-lustre texture is called, is matched somebody with somebody by following components according to weight percent content
Put and form：
Binder 30-60%；
Pearlescent pigment 10-30%；
Solvent 20-40%；
Auxiliary agent 0.1-5%；
Wherein, the binder is the compound of acrylic emulsion and polyaminoester emulsion, acrylic emulsion account for ink always than
Weight is 25%-50%, and polyaminoester emulsion accounts for the total proportion of ink for 5%-10%, and acrylic acid weight is consolidated in the acrylic emulsion
Content is 50-65%, and the weight solid content of polyurethane is 50-65% in the polyaminoester emulsion；
The pearlescent pigment is pearl essence of the particle diameter between 5-25um；
The solvent is the mixture of pure water, ethanol and propylene glycol monomethyl ether composition；
The auxiliary agent is the mixture of dispersant, defoamer, drying retardant and levelling agent composition.
Preferably, the printing-ink is formed by following components according to weight percent content configuration：
Binder 40-50%；
Pearlescent pigment 18-22%；
Solvent 25-35%；
Auxiliary agent 1.5-5%；
Wherein, the binder is the compound of acrylic emulsion and polyaminoester emulsion, and the acrylic emulsion accounts for ink
Total proportion is 35%-42%, and polyaminoester emulsion accounts for the total proportion of ink for 5%-8%, acrylic acid heavy in the acrylic emulsion
Amount solid content is 50-65%, and the weight solid content of polyurethane is 50-65% in the polyaminoester emulsion；
The pearlescent pigment is pearl essence of the particle diameter between 5-25um；
The solvent is the mixing of the propylene glycol monomethyl ether composition of the pure water, the ethanol of 10-20% and 4-5% of 15-25%
Thing；
The auxiliary agent is dispersant, the defoamer of 0.8-1.2%, the drying retardant of 0.7-1.0% and the 1.0- of 0.5-0.8%
The mixture of 1.5% levelling agent composition.
A kind of package typography with pearly-lustre texture, comprises the following steps：
1), acrylic emulsion and polyaminoester emulsion, water, defoamer are mixed, high-speed stirred dispersion is made pre-emulsion；
2), pearlescent pigment, dispersant, levelling agent, drying retardant, stirring solvent is added to be dispersed into pearl ink；
3), using the pearl ink of modulation, using intaglio ink, gravure ink cell opening degree is controlled in 100um-
Between 130um, between 25um-35um, viscosity control is in 22-25s, heated-air drying, wind under 25 DEG C of normal temperature for ink cell severity control
Fast 60-70m/s, 110 DEG C -120 DEG C of hot blast temperature.
Advantages of the present invention：
Using the pearl ink of the proportioning, using intaglio ink, gravure ink cell opening degree is controlled in 100um-
Between 130um, between 25um-35um, viscosity control is in 22-25s, heated-air drying, wind under 25 DEG C of normal temperature for ink cell severity control
Fast 60-70m/s, 110 DEG C -120 DEG C of hot blast temperature, package pearl effect is notable after printing, machine good stability on ink, ink film
High with base material binding strength, rate of drying is fast, energy-saving, environmental protection.
【Specific embodiment】
Present disclosure is further described below by instantiation.
Embodiment one
The printing-ink that a kind of package with pearly-lustre texture is called, is matched somebody with somebody by following components according to weight percent content
Put and form：
Acrylic emulsion 35%, acrylic acid weight solid content is 55% in the acrylic emulsion,；
Polyaminoester emulsion 8%；The weight solid content of polyurethane is 55% in the polyaminoester emulsion
Pearlescent pigment 18%, the pearlescent pigment is pearl essence of the particle diameter between 5-25um；
Pure water 17.5%；
Ethanol 13%；
Propylene glycol monomethyl ether 4%；
Dispersant 0.8%；
Defoamer 1.2%；
Drying retardant 1.0%；
Levelling agent 1.5%；
This has the package typography of pearly-lustre texture, comprises the following steps：
1), acrylic emulsion and polyaminoester emulsion, water, defoamer are mixed, high-speed stirred dispersion is made pre-emulsion；
2), pearlescent pigment, dispersant, levelling agent, drying retardant, stirring solvent is added to be dispersed into pearl ink；
3), using the pearl ink of modulation, using intaglio ink, gravure ink cell opening degree is 100um, ink cell depth
It is 25um to spend, and viscosity control is in 22s or so, heated-air drying, wind speed 70m/s, 120 DEG C of hot blast temperature under 25 DEG C of normal temperature.
Gained packaging should brush product pearl effect significantly, machine good stability on ink, ink film is high with base material binding strength, dry
Dry speed is fast, energy-saving, environmental protection.
Embodiment two
The printing-ink that a kind of package with pearly-lustre texture is called, is matched somebody with somebody by following components according to weight percent content
Put and form：
Acrylic emulsion 42%, acrylic acid weight solid content is 55% in the acrylic emulsion；
Polyaminoester emulsion 5%, the weight solid content of polyurethane is 55% in the polyaminoester emulsion；
Pearlescent pigment 22%, the pearlescent pigment is pearl essence of the particle diameter between 5-25um；
Pure water 15%；
Ethanol 8%；
Propylene glycol monomethyl ether 5%；
Dispersant 0.5%；
Defoamer 0.8%；
Slow curing 0.7%；
Levelling agent 1.0%；
This has the package typography of pearly-lustre texture, comprises the following steps：
1), acrylic emulsion and polyaminoester emulsion, water, defoamer are mixed, high-speed stirred dispersion is made pre-emulsion；
2), pearlescent pigment, dispersant, levelling agent, drying retardant, stirring solvent is added to be dispersed into pearl ink；
3), using the pearl ink of modulation, using intaglio ink, gravure ink cell opening degree is 130um, ink cell depth
It is 35um to spend, and viscosity control is in 25s or so, heated-air drying, wind speed 60m/s, 110 DEG C or so of hot blast temperature under 25 DEG C of normal temperature.
Gained packaging should brush product pearl effect significantly, machine good stability on ink, ink film is high with base material binding strength, dry
Dry speed is fast, energy-saving, environmental protection.
Embodiment three
The printing-ink that a kind of package with pearly-lustre texture is called, is matched somebody with somebody by following components according to weight percent content
Put and form：
Acrylic emulsion 38%, acrylic acid weight solid content is 55% in the acrylic emulsion；
Polyaminoester emulsion 7%, the weight solid content of polyurethane is 55% in the polyaminoester emulsion；
Pearlescent pigment 20%, the pearlescent pigment is pearl essence of the particle diameter between 5-25um；
Pure water 16.3%；
Ethanol 10%；
Propylene glycol monomethyl ether 5%；
Dispersant 0.7%；
Defoamer 1%；
Drying retardant 0.8%；
Levelling agent 1.2%；
This has the package typography of pearly-lustre texture, comprises the following steps：
1), acrylic emulsion and polyaminoester emulsion, water, defoamer are mixed, high-speed stirred dispersion is made pre-emulsion；
2), pearlescent pigment, dispersant, levelling agent, drying retardant, stirring solvent is added to be dispersed into pearl ink；
3), using the pearl ink of modulation, using intaglio ink, gravure ink cell opening degree is 120um, ink cell depth
It is 30um to spend, and viscosity control is in 23s or so, heated-air drying, wind speed 70m/s, 120 DEG C of hot blast temperature under 25 DEG C of normal temperature.
Gained packaging should brush product pearl effect significantly, machine good stability on ink, ink film is high with base material binding strength, dry
Dry speed is fast, energy-saving, environmental protection.
It is presently preferred embodiments of the present invention that embodiment described above is, and not limits practical range of the invention with this,
Except in the case of being enumerated in specific embodiment；The equivalence changes that all methods and principle according to the present invention are made, all should be covered by
In protection scope of the present invention.
Claims (3)
1. the printing-ink that a kind of package with pearly-lustre texture is called, it is characterized in that, by following components according to weight percent
Formed than content configuration：
Binder 30-60%；
Pearlescent pigment 10-30%；
Solvent 20-40%；
Auxiliary agent 0.1-5%；
Wherein, the binder is the compound of acrylic emulsion and polyaminoester emulsion, and acrylic emulsion accounts for the total proportion of ink and is
25%-50%, polyaminoester emulsion accounts for the total proportion of ink for 5%-10%, acrylic acid weight solid content in the acrylic emulsion
It is 50-65%, the weight solid content of polyurethane is 50-65% in the polyaminoester emulsion；
The pearlescent pigment is pearl essence of the particle diameter between 5-25um；
The solvent is the mixture of pure water, ethanol and propylene glycol monomethyl ether composition；
The auxiliary agent is the mixture of dispersant, defoamer, drying retardant and levelling agent composition.
2. the printing-ink that a kind of package with pearly-lustre texture according to claim 1 is called, it is characterized in that, the print
Brush ink is formed by following components according to weight percent content configuration：
Binder 40-50%；
Pearlescent pigment 18-22%；
Solvent 25-35%；
Auxiliary agent 1.5-5%；
Wherein, the binder is the compound of acrylic emulsion and polyaminoester emulsion, the acrylic emulsion account for ink always than
Weight is 35%-42%, and polyaminoester emulsion accounts for the total proportion of ink for 5%-8%, and acrylic acid weight is consolidated in the acrylic emulsion
Content is 50-65%, and the weight solid content of polyurethane is 50-65% in the polyaminoester emulsion；
The pearlescent pigment is pearl essence of the particle diameter between 5-25um；
The solvent is the mixture of the propylene glycol monomethyl ether composition of the pure water, the ethanol of 10-20% and 4-5% of 15-25%；
The auxiliary agent is dispersant, the defoamer of 0.8-1.2%, the drying retardant of 0.7-1.0% and the 1.0- of 0.5-0.8%
The mixture of 1.5% levelling agent composition.
3. a kind of package typography with pearly-lustre texture, it is characterized in that, comprise the following steps：
1), acrylic emulsion and polyaminoester emulsion, water, defoamer are mixed, high-speed stirred dispersion is made pre-emulsion；
2), pearlescent pigment, dispersant, levelling agent, drying retardant, stirring solvent is added to be dispersed into pearl ink；
3), using the pearl ink of modulation, using intaglio ink, gravure ink cell opening degree is controlled in 100um-130um
Between, between 25um-35um, viscosity control is in 22-25s, heated-air drying, wind speed 60- under 25 DEG C of normal temperature for ink cell severity control
70m/s, 110 DEG C -120 DEG C of hot blast temperature.