CN107603322A - A kind of aqueous putty powder and preparation method thereof - Google Patents
A kind of aqueous putty powder and preparation method thereof Download PDFInfo
- Publication number
- CN107603322A CN107603322A CN201710996865.1A CN201710996865A CN107603322A CN 107603322 A CN107603322 A CN 107603322A CN 201710996865 A CN201710996865 A CN 201710996865A CN 107603322 A CN107603322 A CN 107603322A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- aqueous putty
- preparation
- hydroxypropyl methyl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of aqueous putty powder and preparation method thereof, belong to building material technical field.It is made up of the raw material of following parts by weight：4~10 parts of 20~30 parts of silica flour, 5~15 parts of nano zine oxide, 20~30 parts of hydroxypropyl methyl cellulose, 4~10 parts of bagasse fibre, 5~15 parts of DTAC, 20~30 parts of talcum powder, 4~10 parts of fatty alcohol-ether sodium sulfate, 5~15 parts of sepiolite powder and kaolin.The powder of lacquer putty for use on of the present invention, water-fastness, easy construction, hardness is high, film forming is fast, and the holding time is long, easy to use, stable performance, and preparation method is simple, easy to use, cost is low, wide market, is adapted to large-scale production.
Description
Technical field
The present invention relates to a kind of aqueous putty powder and preparation method thereof, belong to building material technical field.
Background technology
Powder of lacquer putty for use on is a kind of ornament materials of smooth surface of wall, is using inorganic coagulation material as base-material, is equipped with and coheres material
Material and other auxiliary agent retrofits form, and are a kind of products essential before coating paints, and painting imposes on priming paint or directly painting
Impose on object, to remove the defects of being uneven on coated article surface.Powder of lacquer putty for use on is extensive as interior wall packing material
Use.But existing interiro wall latex paint powder of lacquer putty for use on causes subsequent construction efflorescence occur there is the shortcomings that water-wash resistance difference
Phenomenon.
The content of the invention
The purpose of the present invention is to make up the deficiencies in the prior art, there is provided a kind of aqueous putty powder and preparation method thereof.This hair
Bright powder of lacquer putty for use on, water-fastness, easy construction, hardness is high, film forming is fast, and the holding time is long, easy to use, stable performance.
The technical scheme that the present invention solves above-mentioned technical problem is as follows：A kind of aqueous putty powder, by following parts by weight
Raw material is made：20~30 parts of silica flour, 5~15 parts of nano zine oxide, 20~30 parts of hydroxypropyl methyl cellulose, bagasse fibre
4~10 parts, 5~15 parts of DTAC, 20~30 parts of talcum powder, 4~10 parts of fatty alcohol-ether sodium sulfate, Hai Pao
4~10 parts of 5~15 parts of stone flour and kaolin.
On the basis of above-mentioned technical proposal, the present invention can also do following improvement.
Further, it is made up of the raw material of following parts by weight：25 parts of silica flour, 10 parts of nano zine oxide, hydroxypropyl methyl
25 parts of cellulose, 7 parts of bagasse fibre, 10 parts of DTAC, 25 parts of talcum powder, fatty alcohol-ether sodium sulfate 7
7 parts of part, 10 parts of sepiolite powder and kaolin.
Further, the viscosity of the hydroxypropyl methyl cellulose is not less than 50,000 mpas.
A kind of preparation method of aqueous putty powder, comprises the following steps：Weigh the raw material of following parts by weight：Silica flour 20
~30 parts, 5~15 parts of nano zine oxide, 20~30 parts of hydroxypropyl methyl cellulose, 4~10 parts of bagasse fibre, dodecyl
5~15 parts of trimethyl ammonium chloride, 20~30 parts of talcum powder, 4~10 parts of fatty alcohol-ether sodium sulfate, 5~15 parts of sepiolite powder and height
4~10 parts of ridge soil, after being well mixed, produce the aqueous putty powder.
On the basis of above-mentioned technical proposal, the present invention can also do following improvement.
Further, the parts by weight of the raw material are：25 parts of silica flour, 10 parts of nano zine oxide, hydroxypropyl methyl fiber
25 parts of element, 7 parts of bagasse fibre, 10 parts of DTAC, 25 parts of talcum powder, 7 parts of fatty alcohol-ether sodium sulfate, sea
7 parts of 10 parts of afrodite powder and kaolin.
Further, the viscosity of the hydroxypropyl methyl cellulose is not less than 50,000 mpas.
A kind of application method of aqueous putty powder as described above, by powder of lacquer putty for use on：Water=1：0.4~0.6 weight ratio, mixing
After uniformly.
The beneficial effects of the invention are as follows：
(1) powder of lacquer putty for use on of the invention, water-fastness, easy construction, hardness is high, film forming is fast, and the holding time it is long, it is easy to use,
Stable performance.
(2) preparation method of the invention is simple, easy to use, cost is low, wide market, is adapted to large-scale production.
Embodiment
The principle and feature of the present invention are described below in conjunction with specific embodiment, example is served only for explaining this hair
It is bright, it is not intended to limit the scope of the present invention.
Embodiment 1：
The aqueous putty powder of the present embodiment, it is made up of the raw material of following weight：Silica flour 20kg, nano zine oxide 15kg,
Hydroxypropyl methyl cellulose 20kg, bagasse fibre 10kg, DTAC 5kg, talcum powder 30kg, fatty alcohol
Ether sodium sulfate 4kg, sepiolite powder 15kg and kaolin 4kg, wherein, the viscosity of the hydroxypropyl methyl cellulose is not less than 50,000
Mpas.
The preparation method of the aqueous putty powder of above-described embodiment, comprises the following steps：Weigh the raw material of following weight：Quartz
Powder 20kg, nano zine oxide 15kg, hydroxypropyl methyl cellulose 20kg, bagasse fibre 10kg, trimethyl chlorination
Ammonium 5kg, talcum powder 30kg, fatty alcohol-ether sodium sulfate 4kg, sepiolite powder 15kg and kaolin 4kg, wherein, the hydroxypropyl first
The viscosity of base cellulose is not less than 50,000 mpas, after being well mixed, produces the aqueous putty powder.
The application method of above-mentioned aqueous putty powder, by powder of lacquer putty for use on：Water=1：0.4 weight ratio, after being well mixed.
Embodiment 2：
The aqueous putty powder of the present embodiment, it is made up of the raw material of following weight：Silica flour 25kg, nano zine oxide 10kg,
Hydroxypropyl methyl cellulose 25kg, bagasse fibre 7kg, DTAC 10kg, talcum powder 25kg, fatty alcohol
Ether sodium sulfate 7kg, sepiolite powder 10kg and kaolin 7kg, wherein, the viscosity of the hydroxypropyl methyl cellulose is not less than 50,000
Mpas.
The preparation method of the aqueous putty powder of above-described embodiment, comprises the following steps：Weigh the raw material of following weight：Quartz
Powder 25kg, nano zine oxide 10kg, hydroxypropyl methyl cellulose 25kg, bagasse fibre 7kg, DTAC
10kg, talcum powder 25kg, fatty alcohol-ether sodium sulfate 7kg, sepiolite powder 10kg and kaolin 7kg, wherein, the hydroxypropyl methyl
The viscosity of cellulose is not less than 50,000 mpas, after being well mixed, produces the aqueous putty powder.
The application method of above-mentioned aqueous putty powder, by powder of lacquer putty for use on：Water=1：0.5 weight ratio, after being well mixed.
Embodiment 3：
The aqueous putty powder of the present embodiment, it is made up of the raw material of following weight：Silica flour 30kg, nano zine oxide 5kg, hydroxyl
Propyl methocel 30kg, bagasse fibre 4kg, DTAC 15kg, talcum powder 20kg, fatty alcohol ether
Sodium sulphate 10kg, sepiolite powder 5kg and kaolin 10kg, wherein, the viscosity of the hydroxypropyl methyl cellulose is not less than 50,000 millis
Pa Sec.
The preparation method of the aqueous putty powder of above-described embodiment, comprises the following steps：Weigh the raw material of following weight：Quartz
Powder 30kg, nano zine oxide 5kg, hydroxypropyl methyl cellulose 30kg, bagasse fibre 4kg, DTAC
15kg, talcum powder 20kg, fatty alcohol-ether sodium sulfate 10kg, sepiolite powder 5kg and kaolin 10kg, wherein, the hydroxypropyl first
The viscosity of base cellulose is not less than 50,000 mpas, after being well mixed, produces the aqueous putty powder.
The application method of above-mentioned aqueous putty powder, by powder of lacquer putty for use on：Water=1：0.6 weight ratio, after being well mixed.
The performance detection of embodiment 1-3 aqueous putty powder is as shown in table 1.
The performance detection of table 1
As can be seen here, aqueous putty powder of the invention, water-fastness, easy construction, hardness is high, film forming is fast, and holding time length,
Easy to use, stable performance.
The foregoing is only presently preferred embodiments of the present invention, be not intended to limit the invention, it is all the present invention spirit and
Within principle, any modification, equivalent substitution and improvements made etc., it should be included in the scope of the protection.
Claims (6)
1. a kind of aqueous putty powder, it is characterised in that be made up of the raw material of following parts by weight：Silica flour 20~30 part, nanometer
5~15 parts of zinc oxide, 20~30 parts of hydroxypropyl methyl cellulose, 4~10 parts of bagasse fibre, DTAC
4~10 parts of 5~15 parts, 20~30 parts of talcum powder, 4~10 parts of fatty alcohol-ether sodium sulfate, 5~15 parts of sepiolite powder and kaolin.
2. a kind of aqueous putty powder according to claim 1, it is characterised in that be made up of the raw material of following parts by weight：
25 parts of silica flour, 10 parts of nano zine oxide, 25 parts of hydroxypropyl methyl cellulose, 7 parts of bagasse fibre, trimethyl chlorine
Change 7 parts of 10 parts of ammonium, 25 parts of talcum powder, 7 parts of fatty alcohol-ether sodium sulfate, 10 parts of sepiolite powder and kaolin.
3. a kind of aqueous putty powder according to claim 1 or 2, it is characterised in that the hydroxypropyl methyl cellulose
Viscosity is not less than 50,000 mpas.
4. a kind of preparation method of aqueous putty powder, it is characterised in that comprise the following steps：Weigh the original of following parts by weight
Material：20~30 parts of silica flour, 5~15 parts of nano zine oxide, 20~30 parts of hydroxypropyl methyl cellulose, bagasse fibre 4~10
Part, 5~15 parts of DTAC, 20~30 parts of talcum powder, 4~10 parts of fatty alcohol-ether sodium sulfate, sepiolite powder 5
~15 parts and 4~10 parts of kaolin, after being well mixed, produce the aqueous putty powder.
A kind of 5. preparation method of aqueous putty powder according to claim 4, it is characterised in that the parts by weight of the raw material
Number is：25 parts of silica flour, 10 parts of nano zine oxide, 25 parts of hydroxypropyl methyl cellulose, 7 parts of bagasse fibre, dodecyl three
7 parts of 10 parts of ammonio methacrylate, 25 parts of talcum powder, 7 parts of fatty alcohol-ether sodium sulfate, 10 parts of sepiolite powder and kaolin.
A kind of 6. preparation method of aqueous putty powder according to claim 4 or 5, it is characterised in that the hydroxypropyl first
The viscosity of base cellulose is not less than 50,000 mpas.