CN107586078A - The environmentally friendly cement of useless brick and tile porcelain clinker production anion - Google Patents
The environmentally friendly cement of useless brick and tile porcelain clinker production anion Download PDFInfo
- Publication number
- CN107586078A CN107586078A CN201610562127.1A CN201610562127A CN107586078A CN 107586078 A CN107586078 A CN 107586078A CN 201610562127 A CN201610562127 A CN 201610562127A CN 107586078 A CN107586078 A CN 107586078A
- Authority
- CN
- China
- Prior art keywords
- cement
- environmentally friendly
- anion
- clinker production
- useless brick
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
It is to belong to construction material environmentally friendly cement to manufacture technical field the invention discloses a kind of environmentally friendly cement of useless brick and tile porcelain clinker production anion.It is Strange ice stone, alkaline residue silicate, opal, blast furnace slag fluorescent material, vermiculite, rare earth element slag brick dark grey, zeolite, the broken ceramic bowl bowl tank powder of ferro-silicon slag, illite copper ashes calcium phosphate hypervelocity hard, hetaerolite pulp water glass elastic water-proof latex, the natural dry glue breast composition of tourmaline anion far infrared.In order to solve to build waning for cement used, and building waste, give up brick and tile and useless broken bowl, basin, tank, potsherd, cinder ash, stove, slag.Twice laid, turn waste into wealth.Te Famingben projects：Make full use of the element negative ion far-infrared for being rich in multiple beneficial health in waste residue that the environmentally friendly cement of anion is made, meet market needs, reduce pollution, promote health while provide illumination for people's night traffic, reduce accident, it is ensured that human life property safety.
Description
Technical field：
It is to belong to construction material environment-protective water the invention discloses a kind of environmentally friendly cement of useless brick and tile porcelain clinker production anion
Mud production preparation technique field.
Background technology：
Building cement used is more and more now, and dust in air smog is more caused by seriously polluted in original cement plant
It is unrestrained, it has to close, turn and stop, the producer of production cement is greatly reduced, in order to meet cement demand, with easy and save money
Method, it is the residue after various coal combustions using useless stove slag, it is better from the more sufficient quality of sintering degree, sort out therein
White slag and red slag, cleared organic impurities and silt soil are then clean, dry, levigate, sieve or broken clay fragment of brick, with clay into
It is point The more the better, the fragment of the waste such as the roof clay tile preferably fired with clay, bowl, tank, queen closer cob brick ashes, broken broken china bowl,
Cylinder, basin etc. fire the fragment of vessel with refractory material, and these material systems obtain using bauxite as body material is fired.So system
The cement gone out, there is the characteristic of some alumina cements, i.e., setting rate is fast, intensity is high.Such as the water all prepared with ceramic whiteware fragment
Mud, color is freely beautiful, can be used as pargeting.But preparation process, which should try one's best, does not have to ironware, in order to avoid cement is destroyed after being doped into iron powder
Whiteness.And multipurpose is made in various industrial residues, waste liquid and ore element containing various trace elements anion etc.
The environmentally friendly cement of abandoned mine clinker energy release of trace elements anion fine-purification air, for various buildings.Pavement of road, enclosure wall powder
Brush, lengthened one's life beneficial to health.
The content of the invention：
It is an object of the invention to provide a kind of environmentally friendly cement of useless brick and tile porcelain clinker production anion.
The technology of the present invention solve scheme be：
1st, a kind of environmentally friendly cement of useless brick and tile porcelain clinker production anion, it is characterized in that：By Strange ice stone alkaline residue negative ion powder
Silicate is by following quality proportioning composition %
Preparation and performance：
Above-mentioned material mixing crushing is milled.The intensity and setting rate of the cement are equal with Portland cement
Or it is slightly higher and include various trace elements and natural negative ion generator Strange ice stone, negative ion powder it is spontaneous constantly produce anion it is net
It is shinny for the rendering of road enclosure wall that change space promotes healthy and night to light.
(2) a kind of environmentally friendly cement of useless brick and tile porcelain clinker production anion, it is characterized in that：By opal blast furnace slag opal
Fluorescence radiation powder, % is formed by following quality proportioning
Preparation method：Above-mentioned various material dry mixing are uniform, desiccate standby.
Cement need to use raw material：
1. slag ash, i.e., the residue after various coal combustions, the more sufficient quality of sintering degree are better.Sort out white slag therein
With red slag, cleared organic impurities and sand, then clean → drying was → levigate → to cross square-bottomed bamboo basket.
2. lime, using quick lime, new kiln discharge it is more preferable.Lime block water spray is made its voluntarily efflorescence, sieved with No. 130 sieve
Point.Such as it is powdered lime, should first crosses sieve screening, then square-bottomed bamboo basket is crossed in residue on sieve water spray efflorescence.
3. gypsum, volume is few, plays regulation and thes cement solidifies speed.Gypsum ore can be used, it is also possible to waste gypsum
Mould.Both things are all dihydrate gypsums, after being heated to 107-170 DEG C.Become semi-hydrated gypsum, be also the plaster of paris.By its powder
It is broken and levigate, then above iron pan goes to fry.Treat gypsum powder no longer bubbling in pot, no vapor simultaneously becomes yellow-gray by white and is
Only.
Blast furnace slag
It is mainly derived from high boiler slag, vessel slag and open hearth slag etc..
Blast furnace slag forms %
Vessel slag forms %
Opal is natural negative ion generator, spontaneous constantly to purify air, is beneficial to health.Kaolin is day
Right sterile antiseptic.Three celestial stones can discharge the former infrared material of various trace elements, activating cell, promote circulation, enhancing human body
Health.
3rd, a kind of environmentally friendly cement of useless brick and tile porcelain clinker production anion, it is characterized in that：By vermiculite rare earth element slag brick
Dark grey is lighted cement, and % is formed by following quality proportioning
Preparation method：Ibid.
Vermiculite is natural clay mineral inorganic antiseptic, and chitin is natural antibacterial agent, and aethiops vegetabilis is rich in lot of trace member
Element can supplement the element balance in regulation antagonism human body, make one health.
Rare earth element slag system produces rare earth metal, and annual China will discharge a large amount of rare earth element slags, and its composition is shown in Table.
Rare earth element slag forms %
4th, a kind of environmentally friendly cement of useless brick and tile porcelain clinker production anion, it is characterized in that：By the broken ceramic bowl bowl of zeolite ferro-silicon slag
Tank is lighted cement, and % is formed by following quality proportioning
Preparation method：Ibid.
Raw material need to be used：Damaged china bowl, glazed earthen basin etc. fire the fragment of vessel with refractory material, and these material systems are with bauxite
Obtained for body material is fired.So the cement made, the characteristic with some alumina cements, i.e. setting rate are fast, intensity
It is high.Such as the cement all prepared with ceramic whiteware fragment, color is white as a jade, can be used as pargeting.But preparation process, which should try one's best, does not have to iron
Device, in order to avoid the whiteness of cement is destroyed after being doped into iron powder.The same method processing of its preparation method.
Montmorillonite is sterile antiseptic, and increase antibacterial effect is merged with antiseptic chitosan.Zeolite, coral powder release bear from
Son.Filter poison, take drugs, the effect of ion exchange simultaneously reduces air pollution and various toxin and heavy metal pollution.
Ferro-silicon slag
Steel plant of China, smelting ironworks production ferrosilicon will discharge a large amount of ferro-silicon slags, and it is formed, and it is as shown in the table.
Ferro-silicon slag forms %
5th, a kind of environmentally friendly cement of useless brick and tile porcelain clinker production anion, it is characterized in that：By serpentine copper ashes sulphur calcium molybdate
The firmly luminous cement of hypervelocity, % is formed by following quality proportioning
SO is required in above-mentioned formula3/Al2O3Mole ratio is 0.4-17, CaO/Al2O3Mole ratio is 0.5-1.2, and
And hypervelocity can be made firmly without free CaO.
Vitreous copper Cu2S, color is by lead ash to black.Hardness 2.5-3.0, proportion 5.5-5.8.
The copper ashes composition % that copper smelting goes out
6th, a kind of environmentally friendly cement of useless brick and tile porcelain clinker production anion, it is characterized in that：By hetaerolite pulp water glass elasticity
Marine glue suppurative mastitis light cement, % is formed by following quality proportioning
The luminous latex cement of elastic water-proof has many advantages, such as that its water penetration is small, tough and rich compared with general cement
Elastic, shockproof, resistance to repeated stock, do not peel off or burst apart, it is excellent with the adhesion strength of concrete, steel, timber, brick etc., and have
There is certain anti-chemical corrosive power.
To meet the needs of and reducing cost, latex cement often adds various fillers, as fine sand, granite, rubber granule,
Pitch, slag powders.
For alumina cement with alkalescence, the latex cement after cooperation is more stable.If using portland cement instead, latex mixing water
It should be protected by advance with casein solution during mud, make latex mixing that there is enough stability.Pitch can improve latex cement
Water resistance, waterglass can moisten cement, and sodium silicofluoride then can be used to adjust latex firm time, prevent from being layered.Latex cement
It should be used while allocating, it is impossible to put long.
Zinc-manganese slag
The place of production of copper hetaerolite to be exploited, there will be substantial amounts of slag to produce every year, it can be used as the raw material for producing zinc, manganese fertilizer,
Its composition is shown in Table.
Lead hetaerolite forms %
7th, a kind of environmentally friendly cement of useless brick and tile porcelain clinker production anion, it is characterized in that：It is far red by outdoor electrical stone anion
The elastic luminous cement of the natural dry glue breast of powder, % is formed by following quality proportioning
Compound method：Ibid.
The purposes of elastic gum suppurative mastitis light cement：Be widely used in architectural engineering, as the waterproof layer of underground engineering, hydraulic engineering,
Runway, port and pier, rudder for ship, fabrication facility floor laying.Highway, enclosure wall etc. are runway, bridge, road night illumination to ensure
Safety, reduce accident.
The alkaline residue component of alkali factory is analyzed：Calcium is 31.44%, magnesium 5.83%, potassium 4.02%, sodium 0.78%, aluminium
0.51%th, iron 0.33%, manganese 446mg/kg, P 32 8.5mg/kg, titanium 293.9mg/kg, vanadium 18.6mg/kg, cobalt 13.51mg/
Kg, solvable silicon 11.6mg/kg, strontium 123.9mg/kg, zinc 220.5mg/kg, chromium 87.8mg/kg, beryllium 0.94mg/kg, cadmium
2.91mg/kg, silver-colored ＜ 0.1mg/kg, chlorine 2.87%, pH=11, the fine molecule of these elements distributes is good for space to human body
Health produces extremely beneficial positive role.
Tourmaline is a kind of most wide natural crystal in the material that anion occurs, and it is also characterized by boracic
Aluminium, sodium, iron, magnesium, the silicate of lithium cyclic structure, its main component have Al2O3、SiO2、Fe2O3、TiO2、B2O5Deng using receiving
Rice tourmaline micropowder, it has pyroelectricity and piezoelectricity, therefore is having temperature and pressure, even most small situation of change
Under, the electrical potential difference between anion crystal can be caused, so as to form electric field.High voltage ionizes the air in electric field, quilt
That hits is electronically attached to neighbouring water and oxygen molecule, and enables it to be converted into negative aeroion.It is this far red containing anion
Faint electrolysis occurs for the outer hydrone that can be distributed naturally in use in some hydrones and surrounding air with body
Effect, produce hydroxyl group anion, can adjust the air quality in human peripheral's environment, and with nuisance positively charged in air
Neutralization, becomes macromolecular and ground of landing makes air fresh clearly, makes one to enjoy the space of cleaning, from the injury of air pollution.
Today's society is due to the continuous improvement of living standard, and the food that people take in high fat kind increases, soda acid in human body
Balance is destroyed, and causes acidic materials largely to deposit, and excessive acidic materials are to trigger modern civilization diseases, rich man's disease in vivo
Important risk factor.Negative ion far-infrared tourmaline nano powder energy disperse in this product in atmosphere, can by human body respiration and
Vitro skin osmotic absorption adjusts the acid-base balance of element body fluid, is advantageous to eliminate the toxin of internal acidic metabolite, has
Beneficial to supplementing, adjusting, antagonism in-vivo element balance incessantly, be advantageous to strengthen immunity, prevent and cure diseases, physical fitness.From
Biophysics viewpoint sees, human body is an organism, and each cell is exactly a minicell in organism, in cell membrane
The outer potential difference for having 50-90mV, the bioelectricity that cell battery is provided is the energy of nervous system activity.It is remote containing anion
Infrared-emitting materials, it can accomplish incessantly to human body cell electric energy supplement, and send because several minicells form
Negative ion far-infrared, its effect never fail, and can go deep into the heating of hypodermis 3-5mm automatic heatings, activate deep tissues,
Accelerate metabolism and cell viability to produce anion with keeping simultaneously, may advantageously facilitate health, delaying skin
Cell ageing, physical fitness lengthen one's life.This luminous cement rich in various trace elements anion far infrared rays can become simultaneously
Waste be changed into values, and disperse is in space.These active components can promote health, and provided conveniently for night illumination again, reduce accident,
Ensure human life property safety.
With reference to embodiment, the present invention is further described
Specific implementation method：
Embodiment 1, a kind of environmentally friendly cement of useless brick and tile porcelain clinker production anion, it is characterized in that：Born by Strange ice stone alkaline residue
Ion powder silicate is by following quality proportioning composition %
2nd, a kind of environmentally friendly cement of useless brick and tile porcelain clinker production anion, it is characterized in that：By opal blast furnace slag opal
Fluorescence radiation powder, % is formed by following quality proportioning
3rd, a kind of environmentally friendly cement of useless brick and tile porcelain clinker production anion, it is characterized in that：By vermiculite rare earth element slag brick
Dark grey is lighted cement, and % is formed by following quality proportioning
4th, a kind of environmentally friendly cement of useless brick and tile porcelain clinker production anion, it is characterized in that：By the broken ceramic bowl bowl of zeolite ferro-silicon slag
Tank is lighted cement, and % is formed by following quality proportioning
5th, a kind of environmentally friendly cement of useless brick and tile porcelain clinker production anion, it is characterized in that：By serpentine copper ashes sulphur calcium molybdate
The firmly luminous cement of hypervelocity, % is formed by following quality proportioning
6th, a kind of environmentally friendly cement of useless brick and tile porcelain clinker production anion, it is characterized in that：By hetaerolite pulp water glass elasticity
Marine glue suppurative mastitis light cement, % is formed by following quality proportioning
7th, a kind of environmentally friendly cement of useless brick and tile porcelain clinker production anion, it is characterized in that：It is far red by outdoor electrical stone anion
The elastic luminous cement of the natural dry glue breast of powder, % is formed by following quality proportioning
Compound method：Ibid.
Claims (7)
1. a kind of environmentally friendly cement of useless brick and tile porcelain clinker production anion, it is characterized in that：By Strange ice stone alkaline residue negative ion powder silicic acid
Salt is by following quality proportioning composition %
2. a kind of environmentally friendly cement of useless brick and tile porcelain clinker production anion, it is characterized in that：By opal blast furnace slag opal fluorescence
Luminescent powder, % is formed by following quality proportioning
3. a kind of environmentally friendly cement of useless brick and tile porcelain clinker production anion, it is characterized in that：By vermiculite rare earth element slag brick dark grey
Luminous cement, % is formed by following quality proportioning
4. a kind of environmentally friendly cement of useless brick and tile porcelain clinker production anion, it is characterized in that：By the broken ceramic bowl bowl tank hair of zeolite ferro-silicon slag
Light cement, % is formed by following quality proportioning
5. a kind of environmentally friendly cement of useless brick and tile porcelain clinker production anion, it is characterized in that：Exceeded the speed limit by serpentine copper ashes sulphur calcium molybdate
Firmly luminous cement, % is formed by following quality proportioning
6. a kind of environmentally friendly cement of useless brick and tile porcelain clinker production anion, it is characterized in that：By hetaerolite pulp water glass elastic water-proof
Latex is lighted cement, and % is formed by following quality proportioning
7. a kind of environmentally friendly cement of useless brick and tile porcelain clinker production anion, it is characterized in that：By the remote rouge and powder day of outdoor electrical stone anion
The elastic luminous cement of right dry glue breast, % is formed by following quality proportioning