CN107584822A - Abnormity folding panel piece wood skin composite plate and abnormity folding panel piece wood skin absorbing process - Google Patents
Abnormity folding panel piece wood skin composite plate and abnormity folding panel piece wood skin absorbing process Download PDFInfo
- Publication number
- CN107584822A CN107584822A CN201710792039.5A CN201710792039A CN107584822A CN 107584822 A CN107584822 A CN 107584822A CN 201710792039 A CN201710792039 A CN 201710792039A CN 107584822 A CN107584822 A CN 107584822A
- Authority
- CN
- China
- Prior art keywords
- wood skin
- plate
- abnormity
- composite plate
- panel piece
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of abnormity folding panel piece wood skin composite plate and abnormity folding panel piece wood skin absorbing process, wherein abnormity folding panel piece wood skin composite plate includes wood skin layer, non-woven fabrics, plate and coating layer；Fitting forms two layers of composite plate structure successively from top to bottom for the wood skin layer, the non-woven fabrics, the plate；Front and back on two layers of composite plate structure sets the coating layer, forms abnormity folding panel piece wood skin composite plate.Meanwhile the present invention makes also using abnormity folding panel piece wood skin absorbing process and forms abnormity folding panel piece wood skin composite plate.Abnormity folding panel piece wood skin composite plate provided by the invention and abnormity folding panel piece wood skin absorbing process, avoid the thick veneer of traditional hand sticker, flatiron 0.2mm and be bonded at folding face prescription formula, brand-new abnormity folding panel piece wood skin composite plate is manufactured that, it has, and performance is superior, all many technical advantages such as practical.
Description
Technical field
The present invention relates to technical field of furniture manufacturing, more particularly to a kind of abnormity folding panel piece wood skin composite plate and abnormity folding
Panel piece wood skin absorbing process.
Background technology
It is well known that veneer furniture is using the timber for having beautiful figure colour, after laminating, is pasted and be in sizing material
Have on panel, make furniture as made of precious wood.Wherein, solid wood veneer veneer furniture is modern handle official bussiness, household
With the main flow of furniture, veneer wood skin thickness is typically from 0.4mm or so thick wood skin；Solid wood veneer veneer furniture its equally can be with
Reach the wooden visual effect of solid wood, it is very popular.
At present, the existing processing technology of solid wood veneer veneer furniture is general directly to be entered using the production board for having posted wood skin
Row production and moulding processing, this production board are only applicable to plane, right angle class process structure；
But (roll over face abnormity plate) when meeting folding face, bent angle class formation, hand sticker can only be used, press 0.2mm thickness
Veneer is bonded at folding face prescription formula and substitutes thick wooden skin process (the thick wood skin for substituting 40S or so implements processing), but veneer
Rolled over after posting by hand at face and the quality problems such as bulge, empty skin easily occur, surface solid wood sense is also unable to reach the effect of thick wood skin
And operating efficiency is low, be not suitable for mass production.
To sum up, how to overcome the above-mentioned technological deficiency of conventional art is that the technology that those skilled in the art are badly in need of solving is asked
Topic.
The content of the invention
It is an object of the invention to provide a kind of abnormity folding panel piece wood skin composite plate and abnormity folding panel piece wood skin absorption
Technique, to solve the above problems.
Invent a kind of curved surface (folding face) plate wood skin absorbing process, can use thickness 40S or so thick wood skin, to there is folding
Face, the plate surface of bent angle carry out absorption cladding, make the product after carrying out, are all worth in quality, efficiency etc.
Improve.
In order to achieve the above object, the technical proposal of the invention is realized in this way：
Present invention also offers a kind of abnormity folding panel piece wood skin composite plate, including wood skin layer, non-woven fabrics, plate and overlay film
Layer；
Fitting forms two layers of composite plate structure successively from top to bottom for the wood skin layer, the non-woven fabrics, the plate；It is described
Front and back on two layers of composite plate structure sets the coating layer, forms abnormity folding panel piece wood skin composite plate.
Preferably, can embodiment as one kind；No aldehyde white adhesive layer is additionally provided between the non-woven fabrics, the plate；
The no aldehyde white adhesive layer is polyvinyl acetate emulsion coating.
Preferably, can embodiment as one kind；The front of the wood skin layer is wood grain face, and the back side of the wood skin layer
Post the non-woven fabrics；The back side of the wood skin layer of non-woven fabrics is posted with the front of the plate by being bonded shape without aldehyde white glue
Into two layers of composite plate structure；
Top surface on two layers of composite plate structure is the wood grain face of the wood skin layer, on two layers of composite plate structure
Bottom surface is the back side of the plate；Two layers of composite plate structure installs the coating layer as overall to its front and back,
Form abnormity folding panel piece wood skin composite plate.
Preferably, can embodiment as one kind；The wood skin layer is that multiple small wood skins are spliced；The small wood skin is
Compound small wood skin, it is from top to bottom successively by decoration wood skin layer, nm antimicrobial surface, substrate layer；Wherein, the decoration wood skin has
Wooden decoration, the nm antimicrobial surface system is with nm silver, nm zinc oxide far infrared composite and UV interfaces paint mixing group
Into.
Preferably, can embodiment as one kind；The thickness of the wood skin layer is 0.4mm-0.6mm；The plate is different
Shape quadrangle plate, the plate longest edge length dimension of its special-shaped quadrangle are less than or equal to 2400mm, and most bond length size is small
In equal to 1200mm, and panel thickness is less than or equal to 50mm.
Correspondingly, present invention also offers a kind of abnormity folding panel piece wood skin absorbing process, following operating procedure system is utilized
Make：
Whole wood skin layer of processing is made, non-woven fabrics is pasted at the back side of whole wood skin layer；
Make and process plate to be adsorbed, the plate surface paint roller without aldehyde white glue, and by that will be pasted without aldehyde white glue
The whole wood skin layer surface for having non-woven fabrics is fitted in two layers of composite plate structure of formation on the surface of the plate to be adsorbed；
The positive and negative two sides implementation overlay film working process of two layers of composite plate structure is made to form abnormity folding panel piece wood
Skin composite plate.
Preferably, can embodiment as one kind；It is described to make whole wood skin layer of processing, in the back side patch of whole wood skin layer
Non-woven fabrics, specifically include following operating procedure：
From the thickness 0.4mm-0.6mm small wood skin of polylith；The small wood skin is compound small wood skin, and it is from top to bottom successively
By decoration wood skin layer, nm antimicrobial surface, substrate layer；Wherein, the decoration wood skin has wooden decoration, the nm antimicrobial surface system
Formed with nm silver, nm zinc oxide far infrared composite and the paint mixing of UV interfaces；Above-mentioned substrate layer is by specific work
Skill handles obtained matrix structure, and the making step of the substrate layer is as follows：Flitch is subjected to slicing or sawing after boiling, obtained
Thickness 0.4-0.6mm wood skin, the wood skin, which is put into the pond of the fire retardant of formula design, soaks, its soak time of different-thickness
For：Thickness is：0.4-0.45mm is then 5-7 hours；Thickness is：0.45-0.5mm is then 7-9 hours；Thickness is：0.5-0.6mm
It is then 9-11 hours；The composition quality ratio (i.e. the formula design of fire retardant) of fire retardant：Isocyanates glue：Phenolic resin glue
Water：Melamine resin adehsive water：Halogen flame retardant powder=1：1：1：0.1；Above-mentioned substrate layer after being dried to aqueous 8-12%,
The technique of compound small wood skin is processed again；The process of compound small wood skin be exactly will decoration wood skin layer, nm antimicrobial surface,
Substrate layer carries out gluing compound again；
The surrounding of every piece small wood skin is cropped neat to form the small wood skin of rectangle, and the small wood skin both ends width one of polylith rectangle
Sample；
The small wood skin of polylith rectangle is spliced into the wood skin layer of one piece of whole rectangular shape using wired or wireless spelling pico farad；
Layer of non-woven fabric is pasted at the back side of whole wood skin layer.
Preferably, can embodiment as one kind；Described make processes plate to be adsorbed, is applied on the surface of the plate
Roller is without aldehyde white glue, and by the way that the whole wood skin layer surface for posting non-woven fabrics is fitted in into the plate to be adsorbed without aldehyde white glue
Two layers of composite plate structure are formed on the surface of part, specifically include following operating procedure：
The plate of special-shaped quadrangle is made, the plate longest edge length dimension of its special-shaped quadrangle is less than or equal to 2400mm,
Most bond length size is less than or equal to 1200mm, and panel thickness is less than or equal to 50mm；
Ensure the surfacing at plate plane, ensure that the surface at plate corner cut needs straight processing；
Remove plate surface dust and debris to be adsorbed；Whole wood skin layer of non-woven fabrics wood grain side on request will be posted
To being placed on plate to be adsorbed, make each marginal dimension of whole wood skin layer at least than the corresponding edge chi of plate to be adsorbed
Modest ability goes out 10cm；
Plate surface to be adsorbed need to adsorb wood skin position paint roller polyvinyl acetate emulsion, and coating weight control is in 200g/
m2-240g/m2；The whole wood skin layer surface for posting non-woven fabrics be fitted in by polyvinyl acetate emulsion to be adsorbed
Two layers of composite plate structure are formed on the surface of the plate.
Preferably, can embodiment as one kind；Overlay film processing is implemented to the positive and negative two sides of two layers of composite plate structure
Processing, which makes, forms abnormity folding panel piece wood skin composite plate, specifically includes following operating procedure：
Two layers of composite plate structure that plate to be adsorbed is formed with whole wood skin layer are put into laminating machine；
Laminating machine technical parameter is adjusted, particular technique parameter adjustment is：Pressure 4kg, 135 ° of electric plate temperature, supporting plate temperature
45 °, adsorption time 3min；By implementing overlay film working process to the positive and negative two sides of two layers of composite plate structure, make and form abnormity
Roll over panel piece wood skin composite plate.
Preferably, can embodiment as one kind；Implement to cover performing the positive and negative two sides to two layers of composite plate structure
Film working process makes to be formed after abnormity folding panel piece wood skin composite plate, in addition to performs following operating procedure：
Abnormity folding panel piece wood skin composite plate after being operated to overlay film carries out trimming processing.
Compared with prior art, this have the advantage that：
A kind of abnormity folding panel piece wood skin composite plate provided by the invention and abnormity folding panel piece wood skin absorbing process, analysis
Above-mentioned abnormity folding panel piece wood skin composite plate and the main technical schemes of abnormity folding panel piece wood skin absorbing process are understood：
On the one hand；The invention provides above-mentioned abnormity folding panel piece wood skin composite plate, analyzes above-mentioned abnormity folding panel piece wood
The primary structural configurations of skin composite plate understand that it is mainly by structure compositions such as wood skin layer, non-woven fabrics, plate and coating layers；Wherein,
Fitting forms two layers of composite plate structure successively from top to bottom for wood skin layer, non-woven fabrics, plate；On two layers of composite plate structure front and
The back side sets coating layer, forms abnormity folding panel piece wood skin composite plate.
The abnormity folding panel piece wood skin composite plate being made up of said structure, simple in construction, practicality is stronger, employs and is rolling over
Composite plate design is carried out on the basis of face, bent angle class formation (rolling over face abnormity plate), forms brand-new abnormity folding panel piece wood skin
Composite plate, it can be applied directly on solid wood veneer veneer furniture, and its surface more aesthetic feeling rich in solid wood, is not in folding face
Locate the quality problems such as bulge, empty skin, while it can also realize a certain degree of bending；To sum up, one kind provided by the invention is different
Shape rolls over panel piece wood skin composite plate, overcomes the technological deficiency of conventional composite plate.
On the other hand, present invention also offers abnormity to roll over panel piece wood skin absorbing process, and which employs brand-new manufacture work
Skill；Main process includes；Whole wood skin layer of processing is made, non-woven fabrics is pasted at the back side of whole wood skin layer；Make processing
Plate to be adsorbed, the plate surface paint roller without aldehyde white glue, and by the way that without aldehyde white glue the described whole of non-woven fabrics will be posted
Open wood skin layer surface and be fitted in two layers of composite plate structure of formation on the surface of the plate to be adsorbed；To two layers of composite plate
Implement overlay film working process and make to form abnormity folding panel piece wood skin composite plate in the positive and negative two sides of structure.
In above-mentioned industrial manufacturing process, whole wood skin layer of processing is made first, and paste nothing at the back side of whole wood skin layer
Spinning cloth, (nonwoven layer makes wood skin not easy to crack, broken to increase the toughness of monoblock wood skin and pulling force；) and then make processing treat
The plate of absorption, the plate surface paint roller without aldehyde white glue, and by the way that described whole of non-woven fabrics will be posted without aldehyde white glue
Wood skin layer surface is fitted in two layers of composite plate structure (i.e. monoblock wood skin layer+(nonwoven of formation on the surface of the plate to be adsorbed
Cloth+without aldehyde white glue) two layers of composite plate structure forming of+plate)；Above-mentioned two layers of composite plate structure is semi-finished product, and it is still needed
Carry out follow-up aluminum coated steel step；The positive and negative two sides of two layers of composite plate structure implement overlay film working process make to be formed it is different
Shape folding panel piece wood skin composite plate (the abnormity folding panel piece wood skin composite plate that aluminum coated steel is formed, suitable for the straight of veneer furniture
Installation is connect, and its toughness is stronger, plasticity is stronger), above-mentioned abnormity folding panel piece wood skin composite plate avoids traditional hand sticker, flatiron
Veneer thick 0.2mm is bonded at folding face prescription formula, and it not use only subversive manufacturing process, while it is also manufactured that entirely
New abnormity folding panel piece wood skin composite plate.
Present invention also offers abnormity to roll over panel piece wood skin absorbing process, and that eliminating folding face corner needs hand sticker, flatiron thin
Wood skin process, process links are reduced, improve operating efficiency；Present invention also offers abnormity to roll over panel piece wood skin absorbing process,
Its special-shaped plate corner folding face disposably adsorbed with plane, avoid special-shaped plate corner because of hand sticker veneer and caused by sky
The quality problems such as skin, bulge, improve the overall quality of product；Present invention also offers abnormity folding panel piece wood skin absorption work
Skill, it is low that it uses the absorption of overlay film machine to solve hand sticker folding panel piece generation efficiency, it has not been convenient to the problem of mass production.
Brief description of the drawings
, below will be to specific in order to illustrate more clearly of the specific embodiment of the invention or technical scheme of the prior art
The required accompanying drawing used is briefly described in embodiment or description of the prior art, it should be apparent that, in describing below
Accompanying drawing is some embodiments of the present invention, for those of ordinary skill in the art, before creative work is not paid
Put, other accompanying drawings can also be obtained according to these accompanying drawings.
Fig. 1 is whole that posts non-woven fabrics in the abnormity folding panel piece wood skin composite plate that the embodiment of the present invention one provides
Wood skin Rotating fields schematic diagram；
Fig. 2 is the plate structure to be adsorbed in the abnormity folding panel piece wood skin composite plate that the embodiment of the present invention one provides
Schematic diagram；
Fig. 3 is that plate surface to be adsorbed in the abnormity folding panel piece wood skin composite plate that the embodiment of the present invention one provides applies
Roller is without effect structure figure after aldehyde white glue；
Whole wood skin layer, which is placed, in the abnormity folding panel piece wood skin composite plate that Fig. 4 provides for the embodiment of the present invention one waits to inhale
The two layers of composite plate structure schematic diagram formed behind attached plate relevant position；
Fig. 5 is the operating process schematic diagram for the abnormity folding panel piece wood skin absorbing process that the embodiment of the present invention two provides.
Label：The small wood skins of 1-；Whole wood skin layer of 2-；3- non-woven fabrics；4- plates；5- rolls over face；6- is without aldehyde white adhesive layer.
Embodiment
Technical scheme is clearly and completely described below in conjunction with accompanying drawing, it is clear that described implementation
Example is part of the embodiment of the present invention, rather than whole embodiments.Based on the embodiment in the present invention, ordinary skill
The every other embodiment that personnel are obtained under the premise of creative work is not made, belongs to the scope of protection of the invention.
In the description of the invention, it is necessary to explanation, the orientation of some instructions or the word of position relationship, its be only for
It is easy to the description present invention and simplifies description, rather than instruction or implies that signified device or element there must be specific side
Position, with specific azimuth configuration and operation, therefore be not considered as limiting the invention.
In the description of the invention, it is necessary to which explanation, " connection " should be interpreted broadly, for example, it may be fixedly connected,
Can also be detachably connected, or be integrally connected；Can be mechanical connection or electrical connection；Can be joined directly together,
It can also be indirectly connected by intermediary, can be the connection of two element internals.For one of ordinary skill in the art
For, the concrete meaning of above-mentioned term in the present invention can be understood with concrete condition.
The present invention is described in further detail below by specific examples of the implementation and with reference to accompanying drawing.
Embodiment one
The embodiment of the present invention one provides a kind of abnormity folding panel piece wood skin composite plate, including wood skin layer (i.e. whole wood skin
Layer 2), non-woven fabrics 3, plate 4 and coating layer (not shown)；
Fitting forms two successively from top to bottom for the wood skin layer (i.e. whole wood skin layer 2), the non-woven fabrics 3, the plate 4
Layer composite plate structure；Front and back on two layers of composite plate structure sets the coating layer, forms abnormity folding panel piece
Wood skin composite plate.
The primary structural configurations for analyzing above-mentioned abnormity folding panel piece wood skin composite plate understand that it is mainly by wood skin layer, nonwoven
The structure compositions such as cloth, plate and coating layer；Wherein, two layers of fitting formation is compound successively from top to bottom for wood skin layer, non-woven fabrics, plate
Harden structure；Front and back on two layers of composite plate structure sets coating layer, forms abnormity folding panel piece wood skin composite plate.
The abnormity folding panel piece wood skin composite plate being made up of said structure, simple in construction, practicality is stronger, employs and is rolling over
Composite plate design is carried out on the basis of face, bent angle class formation (rolling over face abnormity plate), forms brand-new abnormity folding panel piece wood skin
Composite plate, it can be applied directly on solid wood veneer veneer furniture, and its surface more aesthetic feeling rich in solid wood, is not in folding face
Locate the quality problems such as bulge, empty skin, while it can also realize a certain degree of bending；To sum up, one kind provided by the invention is different
Shape rolls over panel piece wood skin composite plate, overcomes the technological deficiency of conventional composite plate.
Preferably, can embodiment as one kind；No aldehyde white adhesive layer is additionally provided between the non-woven fabrics 3, the plate 4
6；The no aldehyde white adhesive layer 6 is polyvinyl acetate emulsion coating.
Pasted it should be noted that being used between above-mentioned non-woven fabrics 3, plate 4 without aldehyde white adhesive layer 6；This is without aldehyde white glue
Belong to the gluing emulsion of environment-friendly type, select use to make product more green, environmentally friendly without aldehyde white glue.
Preferably, can embodiment as one kind；The front of the wood skin layer (i.e. whole wood skin layer 2) is wood grain face, and
Post the non-woven fabrics 3 in the back side of the wood skin layer；Post the back side of the wood skin layer of non-woven fabrics and the front of the plate
Two layers of composite plate structure are formed by being bonded without aldehyde white glue (i.e. without aldehyde white adhesive layer 6)；
Top surface on two layers of composite plate structure is the wood grain face of the wood skin layer, on two layers of composite plate structure
Bottom surface is the back side of the plate；Two layers of composite plate structure installs the coating layer as overall to its front and back,
Form abnormity folding panel piece wood skin composite plate.
Preferably, can embodiment as one kind；The thickness of the wood skin layer (i.e. whole wood skin layer 2) is 0.4mm-
0.6mm；The wood skin layer (i.e. whole wood skin layer 2) is that multiple small wood skins 1 are spliced；The small wood skin is compound small wood skin,
It is from top to bottom successively by decoration wood skin layer, nm antimicrobial surface, substrate layer；Wherein, the decoration wood skin has wooden decoration, should
Nm antimicrobial surface system is formed with nm silver, nm zinc oxide far infrared composite and the paint mixing of UV interfaces.
It should be noted that above-mentioned whole wood skin layer 2 makes what is be spliced by the small wood skin of polylith；Above-mentioned small wood skin is from thick
Spend the 0.4mm-0.6mm small wood skin of polylith (proves by substantial amounts of experiment：Selection uses certain thickness thick wood skin production system
The product made, wood grain concave-convex sense is good, solid wood sense is strong)；The surrounding of every piece small wood skin is cropped neat to form the small wood skin of rectangle, and
The small wood skin both ends width of polylith rectangle is the same；The small wood skin of polylith rectangle is spliced into one piece whole using wired or wireless spelling pico farad
Whole wood skin layer 2 of rectangular shape.
Preferably, can embodiment as one kind；The plate 4 is special-shaped quadrangle plate, the plate of its special-shaped quadrangle
Part longest edge length dimension is less than or equal to 2400mm, and most bond length size is less than or equal to 1200mm, and panel thickness is less than etc.
In 50mm.
It should be noted that above-mentioned plate 4 is the special-shaped quadrangle plate being mainly made up of planar body and folding face 5；On
The manufacture size and structure for stating plate 4 also have specific requirement, and the plate longest edge length dimension of its special-shaped quadrangle is less than
Equal to 2400mm, most bond length size is less than or equal to 1200mm, and panel thickness is less than or equal to 50mm.Meanwhile make whole Zhang Mu
Each marginal dimension of cortex at least grows 10cm (i.e. h in Fig. 4 is at least than the corresponding edge size of plate to be adsorbed
10cm)。
On the abnormity folding panel piece wood skin composite plate in embodiment one：
In summary, abnormity folding panel piece wood skin composite plate provided in an embodiment of the present invention, its structure design are more reasonable；Its
In, its concrete structure all has an original design, and annexation between concrete structure and position relationship have reasonably
Layout designs；Therefore abnormity folding panel piece wood skin composite plate provided in an embodiment of the present invention, its technical construction is more reasonable, employs
Brand-new composite plate structure form, practicality are also stronger.
Embodiment two
Referring to Fig. 5, while referring to 5, referring also to manufacture among Fig. 1-Fig. 4 to be anticipated shown in above-described embodiment one
Process structure diagram.
Correspondingly, present invention also offers a kind of abnormity folding panel piece wood skin absorbing process, following operating procedure system is utilized
Make：
Step S100；Whole wood skin layer 2 of processing is made, non-woven fabrics 3 is pasted at the back side of whole wood skin layer 2；
Step S200；Make and process plate 4 to be adsorbed, it is (white i.e. without aldehyde without aldehyde white glue in the surface paint roller of the plate
Glue-line 6 is pasted), and by the way that the whole wood skin layer surface for posting non-woven fabrics is fitted in into institute to be adsorbed without aldehyde white glue
State two layers of composite plate structure of formation on the surface of plate；
Step S300；The positive and negative two sides implementation overlay film working process of two layers of composite plate structure is made to form abnormity
Roll over panel piece wood skin composite plate.
Present invention also offers abnormity to roll over panel piece wood skin absorbing process, and which employs brand-new manufacturing process；Main
Process includes；Whole wood skin layer of processing is made, non-woven fabrics is pasted at the back side of whole wood skin layer；Make and process plate to be adsorbed
Part, the plate surface paint roller without aldehyde white glue, and by the way that the whole wood skin layer table of non-woven fabrics will be posted without aldehyde white glue
Face is fitted in two layers of composite plate structure of formation on the surface of the plate to be adsorbed；To two layers of composite plate structure just,
Implement overlay film working process and make to form abnormity folding panel piece wood skin composite plate in anti-two sides.
In above-mentioned industrial manufacturing process, whole wood skin layer of processing is made first, and paste nothing at the back side of whole wood skin layer
Spinning cloth, (nonwoven layer makes wood skin not easy to crack, broken to increase the toughness of monoblock wood skin and pulling force；) and then make processing treat
The plate of absorption, the plate surface paint roller without aldehyde white glue, and by the way that described whole of non-woven fabrics will be posted without aldehyde white glue
Wood skin layer surface is fitted in two layers of composite plate structure (i.e. monoblock wood skin layer+(nonwoven of formation on the surface of the plate to be adsorbed
Cloth+without aldehyde white glue) two layers of composite plate structure forming of+plate)；Above-mentioned two layers of composite plate structure is semi-finished product, and it is still needed
Carry out follow-up aluminum coated steel step；The positive and negative two sides of two layers of composite plate structure implement overlay film working process make to be formed it is different
Shape folding panel piece wood skin composite plate (the abnormity folding panel piece wood skin composite plate that aluminum coated steel is formed, suitable for the straight of veneer furniture
Installation is connect, and its toughness is stronger, plasticity is stronger), above-mentioned abnormity folding panel piece wood skin composite plate avoids traditional hand sticker, flatiron
0.2mm veneer is bonded at folding face prescription formula, and it not use only subversive manufacturing process, while it is also manufactured that completely newly
Abnormity folding panel piece wood skin composite plate.
Preferably, can embodiment as one kind；The step S100 (makes whole wood skin layer of processing, in whole Zhang Mu
The back side patch non-woven fabrics of cortex) specifically include following operating procedure；
Step S110；From the thickness 0.4mm-0.6mm small wood skin of polylith；
Step S120；The surrounding of every piece small wood skin is cropped neat to form the small wood skin of rectangle, and the small wood skin two of polylith rectangle
Hold width the same；
Step S130；The small wood skin of polylith rectangle is spliced into one piece of whole rectangular shape using wired or wireless spelling pico farad
Wood skin layer；
Step S140；Layer of non-woven fabric is pasted at the back side of whole wood skin layer.
It should be noted that；Step 1：From the thickness 0.4mm-0.6mm small wood skin of polylith；Step 2：By every piece small wood skin
Surrounding be cropped neat to form the small wood skin of rectangle, and the small wood skin both ends width of polylith rectangle is the same；Step 3：Utilize wired or nothing
Line spells the wood skin layer that the small wood skin of polylith rectangle is spliced into one piece of whole rectangular shape by pico farad；Step 4：In the back of the body of whole wood skin layer
Face need to paste layer of non-woven fabric, to increase the toughness of monoblock wood skin and pulling force, make wood skin it is not easy to crack, it is broken (i.e. reverse side paste one layer
Thin non-woven fabrics, the wood skin during adsorption operations can be avoided to split, damage, improve product qualification rate).
In addition, it is necessary to supplement, the above-mentioned small wood skin in the embodiment of the present invention can be natural small wood skin or
The compound small wood skin of specific structure；Wherein, the embodiment of the present invention on compound small wood skin as most preferred wood skin；This is compound small
Wood skin its from top to bottom successively by decoration wood skin layer, nm antimicrobial surface, substrate layer, wherein, the decoration wood skin has wooden decorations
Line, the nm antimicrobial surface system are formed with nm silver, nm zinc oxide far infrared composite and the paint mixing of UV interfaces.Its
In, the embodiment of the present invention, it passes through the nm antimicrobial surface by the decoration wood skin, the sheet material integrally removed with antibacterial, removed
Outside smelly function, with more the function of natural wood decoration decoration.For up to above-mentioned purpose, the nm antimicrobial surface system of the invention with
Nm silver, nm zinc oxide far infrared composite and UV interfaces paint mixing composition, and provide table by the nm antimicrobial surface
Face antibacterial, deodorization functions, to reach the effect of present invention makes edge-trimming plate tool bending elasticity, antibacterial, deodorization.Wherein, more attach most importance to
What is wanted is that above-mentioned substrate layer is to handle obtained matrix structure by special process, the substrate layer have it is fire-retardant, it is high temperature resistant, wear-resisting
Etc. function；Because the making step of the substrate layer is as follows：Flitch is subjected to slicing or sawing after boiling, obtains thickness 0.4-
0.6mm wood skin, the wood skin, which is put into the pond of the fire retardant of above-mentioned special formulation design, soaks, its soak time of different-thickness
For：Thickness is：0.4-0.45mm is then 5-7 hours；Thickness is：0.45-0.5mm is then 7-9 hours；Thickness is：0.5-0.6mm
It is then 9-11 hours；The composition quality ratio of fire retardant：Isocyanates glue：Phenolic resin glue：Melamine resin adehsive water：
Halogen flame retardant powder=1：1：1：0.1；Above-mentioned substrate layer is after being dried to aqueous 8-12%, then is processed compound small wood skin
Technique；The technology mode of compound small wood skin is exactly that will decorate wood skin layer, nm antimicrobial surface, substrate layer (i.e. at special process
The substrate layer managed) carry out again it is gluing compound.Compound small wood skin after flame retarding process processing, its fire resistance are very tall and erect
More, the B1 levels of national standard GB8624-2012 grading criterias are reached.With fire-retardant, high temperature resistant, wear-resisting, service life length and other effects.
Preferably, can embodiment as one kind；The step S200 (makes and processes plate to be adsorbed, described
The surface paint roller of plate is treated without aldehyde white glue, and by being fitted in the whole wood skin layer surface for posting non-woven fabrics without aldehyde white glue
Two layers of composite plate structure are formed on the surface of the plate of absorption) specifically include following operating procedure；
Step S210；The plate of special-shaped quadrangle is made, the plate longest edge length dimension of its special-shaped quadrangle is less than etc.
In 2400mm, most bond length size is less than or equal to 1200mm, and panel thickness is less than or equal to 50mm；
Step S220；Ensure the surfacing at plate plane, ensure that the surface at plate corner cut needs straight processing；
Step S230；Remove plate surface dust and debris to be adsorbed；Whole wood skin layer of non-woven fabrics will be posted by will
Grain direction is sought, is placed on plate to be adsorbed, makes each marginal dimension of whole wood skin layer at least than pair of plate to be adsorbed
Marginal dimension is answered to grow 10cm；
Step S240；Plate surface to be adsorbed need to adsorb wood skin position paint roller polyvinyl acetate emulsion, coating weight control
System is in 200g/m2-240g/m2；The whole wood skin layer surface for posting non-woven fabrics is fitted in by polyvinyl acetate emulsion
Two layers of composite plate structure are formed on the surface of the plate to be adsorbed.
It should be noted that；Step 1：The plate of special-shaped quadrangle is made, the plate long side length ruler of its special-shaped quadrangle
Very little to be less than or equal to 2400mm, bond length size is less than or equal to 1200mm, and panel thickness is less than or equal to 50mm；Step 2：Ensure
Surfacing at plate plane, ensure that the surface at plate corner cut needs straight processing；Step 3：Remove plate table to be adsorbed
Face dust and debris, whole wood skin layer of non-woven fabrics grain direction on request will be posted, is placed on plate to be adsorbed, makes whole
Each side size of wood skin layer grows 10cm and (ensures whole wood skin layer to plate than the corresponding sides size of plate to be adsorbed
All standing, and ensure that any edge at least grows 10cm)；Step 4：Plate surface to be adsorbed need to adsorb wood skin position paint roller and gather
Vinyl acetate emulsion, coating weight control is in 200g/m2-240g/m2；Non-woven fabrics will be posted by polyvinyl acetate emulsion
The whole wood skin layer surface is fitted in two layers of composite plate structure of formation on the surface of the plate to be adsorbed.
Preferably, can embodiment as one kind；The step S300 is (i.e. to the positive and negative of two layers of composite plate structure
Implement overlay film working process and make to form abnormity folding panel piece wood skin composite plate in two sides) specifically include following operating procedure；
Step S310；Two layers of composite plate structure that plate to be adsorbed is formed with whole wood skin layer are put into laminating machine；
Step S320；Laminating machine technical parameter is adjusted, particular technique parameter adjustment is：Pressure 4kg, electric plate temperature
135 °, 45 ° of supporting plate temperature, adsorption time 3min；By implementing to the positive and negative two sides of two layers of composite plate structure at overlay film processing
Reason, make and form abnormity folding panel piece wood skin composite plate.
It should be noted that；Two layers of composite plate structure that plate to be adsorbed is formed with whole wood skin layer are put into laminating machine
It is interior；Adjustment laminating machine technical parameter is adjusted to：Pressure 4kg, 135 ° of electric plate temperature, 45 ° of supporting plate temperature, adsorption time 3min；
Above-mentioned steps employ high temperature adsorption wood skin and plate mode is implemented, and its technological means is more novel；High temperature adsorption wood skin and plate
Part, it is ensured that sticking effect is more preferable, while improves the properties of product of abnormity folding panel piece wood skin composite plate；It will be apparent that adopt
After special purpose machinery high temperature adsorption, stickup degree is firm between wood skin and special-shaped plate, and the quality problems such as empty skin, bulge will not occur.
Preferably, can embodiment as one kind；After the step 300, in addition to perform following operating procedure：
Step S400；Abnormity folding panel piece wood skin composite plate after being operated to overlay film carries out trimming processing.
It should be noted that after the step S300, in addition to perform following operating procedure：After being operated to overlay film
Abnormity folding panel piece wood skin composite plate carries out trimming processing.Taken out in laminating machine and adsorbed plate (abnormity folding panel piece wood
Skin composite plate), then repair the parts such as the unnecessary wood skin of plate edge using edge iron.
It should be noted that present invention also offers abnormity to roll over panel piece wood skin absorbing process, folding face corner is that eliminated
Hand sticker, flatiron veneer process are needed, process links is reduced, improves operating efficiency and (enumerate：The four directions that 1 square metre of single-block area
The panel of chamfering, mid-plane part use hot press hot pressing lagging 3-5 minutes, and the remaining single worker's hand sticker of corner parts needs
12-15 minutes, above-mentioned two step are disposably completed only to need 7-8 minutes with absorbing process)；
Present invention also offers abnormity to roll over panel piece wood skin absorbing process, and the corner folding face of special-shaped plate and plane are disposable
Absorption, avoid special-shaped plate corner because of hand sticker veneer and caused by the quality problems such as empty skin, bulge, improve the entirety of product
Quality；
Present invention also offers abnormity to roll over panel piece wood skin absorbing process, and which employs machine absorption to solve hand sticker folding face
Plate generation efficiency is low, it has not been convenient to the problem of mass production.
Present invention also offers abnormity to roll over panel piece wood skin absorbing process, and it is implemented, and cost is cheap.
Present invention also offers abnormity to roll over panel piece wood skin absorbing process, and processing mode is more reasonable, more novel, can obtain
High quality brand new form abnormity folding panel piece wood skin composite plate, suitable for extensive, even large area plate
Large quantities of a large amount of productions, significantly improve production efficiency.
Many significant technical advantages based on more than, abnormity folding panel piece wood skin composite plate provided by the invention and abnormity folding
Panel piece wood skin absorbing process will bring good market prospects and economic benefit.
Finally it should be noted that：Various embodiments above is merely illustrative of the technical solution of the present invention, rather than its limitations；To the greatest extent
The present invention is described in detail with reference to foregoing embodiments for pipe, it will be understood by those within the art that：Its according to
The technical scheme described in foregoing embodiments can so be modified, either which part or all technical characteristic are entered
Row equivalent substitution；And these modifications or replacement, the essence of appropriate technical solution is departed from various embodiments of the present invention technology
The scope of scheme.
Claims (10)
1. a kind of abnormity folding panel piece wood skin composite plate, it is characterised in that including wood skin layer, non-woven fabrics, plate and coating layer；
Fitting forms two layers of composite plate structure successively from top to bottom for the wood skin layer, the non-woven fabrics, the plate；Described two layers
Front and back on composite plate structure sets the coating layer, forms abnormity folding panel piece wood skin composite plate.
2. abnormity folding panel piece wood skin composite plate as claimed in claim 1, it is characterised in that
No aldehyde white adhesive layer is additionally provided between the non-woven fabrics, the plate；The no aldehyde white adhesive layer is polyvinyl acetate breast
Liquid coating.
3. abnormity folding panel piece wood skin composite plate as claimed in claim 2, it is characterised in that
The front of the wood skin layer is wood grain face, and the non-woven fabrics is posted at the back side of the wood skin layer；Post the institute of non-woven fabrics
The back side of wood skin layer is stated to form two layers of composite plate structure by being bonded without aldehyde white glue with the front of the plate；
Top surface on two layers of composite plate structure is the wood grain face of the wood skin layer, the bottom surface on two layers of composite plate structure
For the back side of the plate；Two layers of composite plate structure installs the coating layer as overall to its front and back, is formed
Abnormity folding panel piece wood skin composite plate.
4. abnormity folding panel piece wood skin composite plate as claimed in claim 1, it is characterised in that
The wood skin layer is that multiple small wood skins are spliced；
The small wood skin is compound small wood skin, and it is from top to bottom successively by decoration wood skin layer, nm antimicrobial surface, substrate layer；Its
In, the decoration wood skin has wooden decoration, and the nm antimicrobial surface system is with nm silver, nm zinc oxide far infrared composite
And UV interfaces paint mixing composition.
5. abnormity folding panel piece wood skin composite plate as claimed in claim 1, it is characterised in that
The thickness of the wood skin layer is 0.4mm-0.6mm；The plate is special-shaped quadrangle plate, the plate of its special-shaped quadrangle
Longest edge length dimension is less than or equal to 2400mm, and most bond length size is less than or equal to 1200mm, and panel thickness is less than or equal to
50mm。
6. a kind of abnormity folding panel piece wood skin absorbing process, it is characterised in that made using following operating procedure：
Whole wood skin layer of processing is made, non-woven fabrics is pasted at the back side of whole wood skin layer；
Make and process plate to be adsorbed, the plate surface paint roller without aldehyde white glue, and by the way that nothing will be posted without aldehyde white glue
The whole wood skin layer surface for spinning cloth is fitted in two layers of composite plate structure of formation on the surface of the plate to be adsorbed；
Implement overlay film working process to the positive and negative two sides of two layers of composite plate structure and make to form abnormity folding panel piece wood skin and answer
Plywood.
7. abnormity folding panel piece wood skin absorbing process as claimed in claim 6, it is characterised in that
It is described to make whole wood skin layer of processing, non-woven fabrics is pasted at the back side of whole wood skin layer, specifically includes following operating procedure：
From the thickness 0.4mm-0.6mm small wood skin of polylith；The small wood skin is compound small wood skin, and it is from top to bottom successively by filling
Adorn wood skin layer, nm antimicrobial surface, substrate layer；Wherein, the decoration wood skin has wooden decoration, the nm antimicrobial surface system with how
Meter Yin, nm zinc oxide far infrared composite and UV interfaces paint mixing composition；Above-mentioned substrate layer is by special process
Obtained matrix structure is managed, the making step of the substrate layer is as follows：Flitch is subjected to slicing or sawing after boiling, obtains thickness
0.4-0.6mm wood skin, the wood skin, which is put into the pond of the fire retardant of formula design, soaks, and its soak time of different-thickness is：It is thick
Spend and be：0.4-0.45mm is then 5-7 hours；Thickness is：0.45-0.5mm is then 7-9 hours；Thickness is：0.5-0.6mm is then
9-11 hours；The composition quality ratio of fire retardant：Isocyanates glue：Phenolic resin glue：Melamine resin adehsive water：Halogen
Fire-retardant powder=1：1：1：0.1；Above-mentioned substrate layer is after being dried to aqueous 8-12%, then is processed the work of compound small wood skin
Skill；The process of compound small wood skin exactly carries out decoration wood skin layer, nm antimicrobial surface, substrate layer gluing compound again；
The surrounding of every piece small wood skin is cropped neat to form the small wood skin of rectangle, and the small wood skin both ends width of polylith rectangle is the same；
The small wood skin of polylith rectangle is spliced into the wood skin layer of one piece of whole rectangular shape using wired or wireless spelling pico farad；
Layer of non-woven fabric is pasted at the back side of whole wood skin layer.
8. abnormity folding panel piece wood skin absorbing process as claimed in claim 7, it is characterised in that
Described make processes plate to be adsorbed, the plate surface paint roller without aldehyde white glue, and by that will be pasted without aldehyde white glue
The whole wood skin layer surface for having non-woven fabrics is fitted in two layers of composite plate structure of formation on the surface of the plate to be adsorbed,
Specifically include following operating procedure：
The plate of special-shaped quadrangle is made, the plate longest edge length dimension of its special-shaped quadrangle is less than or equal to 2400mm, most short
Edge lengths size is less than or equal to 1200mm, and panel thickness is less than or equal to 50mm；
Ensure the surfacing at plate plane, ensure that the surface at plate corner cut needs straight processing；
Remove plate surface dust and debris to be adsorbed；Whole wood skin layer of non-woven fabrics grain direction on request will be posted, is put
On plate to be adsorbed, grow corresponding edge size of each marginal dimension of whole wood skin layer at least than plate to be adsorbed
10cm；
Plate surface to be adsorbed need to adsorb wood skin position paint roller polyvinyl acetate emulsion, and coating weight control is in 200g/m2-
240g/m2；The whole wood skin layer surface for posting non-woven fabrics is fitted in by institute to be adsorbed by polyvinyl acetate emulsion
State two layers of composite plate structure of formation on the surface of plate.
9. abnormity folding panel piece wood skin absorbing process as claimed in claim 8, it is characterised in that
Implement overlay film working process to the positive and negative two sides of two layers of composite plate structure and make to form abnormity folding panel piece wood skin and answer
Plywood, specifically include following operating procedure：
Two layers of composite plate structure that plate to be adsorbed is formed with whole wood skin layer are put into laminating machine；
Laminating machine technical parameter is adjusted, particular technique parameter adjustment is：Pressure 4kg, 135 ° of electric plate temperature, 45 ° of supporting plate temperature,
Adsorption time 3min；By implementing overlay film working process to the positive and negative two sides of two layers of composite plate structure, making forms special-shaped folding face
Plate wood skin composite plate.
10. abnormity folding panel piece wood skin absorbing process as claimed in claim 9, it is characterised in that
Make to form abnormity folding panel piece performing the positive and negative two sides implementation overlay film working process to two layers of composite plate structure
After wood skin composite plate, in addition to perform following operating procedure：
Abnormity folding panel piece wood skin composite plate after being operated to overlay film carries out trimming processing.